GROWTH OF HIGH-QUALITY GALLIUM-ARSENIDE ON HF-ETCHED SILICON (001) BY CHEMICAL BEAM EPITAXY

HF etching followed by relatively low temperature (almost-equal-to 600-degrees-C) pretreatment is shown to provide a suitable substrate for the heteroepitaxial growth of GaAs on Si(100) by CBE using TEGa and AsH3 as sources. Rutherford backscattering (RBS), photoluminescence (PL), transmission electron microscopy (TEM), and Raman measurements show the low-defect nature of the GaAs epilayer.

DELINEATION OF DEFECTS IN SIMOX STRUCTURES USING A CHEMICAL ETCHING TECHNIQUE

Residual defects in the overlayer of fully annealed SIMOX material have been studied by means of a chemical etching technique. The etching procedure has been calibrated and an optimum recipe is reported. Observations using optical microscopy and transmission electron microscopy have been used to quantify the defect densities and good agreement between the two techniques has been established, confirming that the optimised chemical etching process can be used with confidence to determine the dislocation density for values < 10(7) cm-2.

PHOTOLUMINESCENCE SPECTRA OF STRAINED HETEROSTRUCTURE OF INP ON GAAS SUBSTRATE GROWN BY METAL-ORGANIC CHEMICAL VAPOR-DEPOSITION

A high-energy shift of the band-band recombination has been observed in photoluminescence spectra of the strained InP layer grown on GaAs substrate. The InP layer is under biaxial compressive strain at temperatures below the growth temperature, because the thermal expansion coefficient of InP is smaller than that of GaAs. The strain value determined by the energy shift of the band-edge peak is in good agreement with the calculated thermal strain. A band to carbon acceptor recombination is also identified.

Photoluminescence studies on the interaction of near-surface GaAs/AlxGa1-xAs quantum wells with chemical adsorbates

The chemical adsorption of sodium sulphide, ferrocene, hydroquinone and p-methyl-nitrobenzene onto the surface of a GaAs/AlxGa1-xAs multiquantum well semiconductor was characterized by steady state and time-resolved photoluminescence (PL) spectroscopy. The changes in the PL response, including the red shift of the emission peak of the exciton in the quantum well and the enhancement of the PL intensity, are discussed in terms of the interactions of the adsorbed molecules with surface states.

Kinetics and transport model for the chemical vapor epitaxy of GexSi1-x

A numerical model that combines mass transport and surface kinetics was applied, for the first time, to the chemical vapor epitaxy of GexSi1-x. The temperature, velocity and concentration fields were calculated from the conservation equations for energy, momentum and species coupled with the boundary conditions on the growth surface which were determined by surface kinetics. The deposition rates of Si and Ge were assumed to be limited, respectively, by surface kinetics and mass transport. A theoretical relation between the initial conditions and the Ge composition in the solid was established. The calculated growth rate as well as the Ge composition in the solid and its dependence on growth temperature agree well with experimental data.

PHOTOLUMINESCENCE STUDIES OF CHEMICAL ADSORPTION OF GAAS/ALXGA1-XAS MULTIQUANTUM-WELL SEMICONDUCTOR

Adsorption of ferrocene and p-methylnitrobenzene on a GaAs/AlxGa1-xAs multiquantum well semiconductor is characterized by the changes in the photoluminescent response in terms of the interactions of adsorbed molecules with surface states.

ENHANCEMENT EFFECT OF PLASMA-ENHANCED CHEMICAL-VAPOR-DEPOSITED SIN CAPPING LAYER ON DIELECTRIC CAP QUANTUM-WELL DISORDERING

Quantum well disordering of GaAs/AlGaAs multiple quantum well(MQW) has been accomplished with only plasma enhanced chemical vapor deposited (PECVD) SiN cap layer growth. The amount of blue shift increases with SiN growing time. This result has been explained by the vacancy indiffusion during PECVD SiN growth. Rapid thermal annealing (RTA) of the sample after SiN cap layer growth at 850 degrees C for 35 s caused a larger amount of blue shift than those obtained without RTA. By considering the model of Al diffusion from AlGaAs barrier into GaAs QWs together with the result from photoluminescence (PL) measurement, Al diffusion coefficients were calculated. The Al diffusion coefficient due to PECVD SiN was estimated at about 3 x10(-17) cm(2)/s. It was possible to extract the effect of RTA on the QW disordering, which showed that the amount of the blue shift and the Al diffusion coefficient due only to RTA increases with SiN cap layer thickness as reported by Chi et al.(10))

METAL-ORGANIC CHEMICAL-VAPOR-DEPOSITION GROWTH OF GAN

Single-crystal GaN films have been deposited on (01 (1) over bar 2) sapphire substrates using trimethylgallium (TMGa) and NH3 as sources. The morphological, crystalline, electrical and optical characterizations of GaN film are investigated. The carrier concentration ofundoped GaN increases with decreasing input NH3-to-TMGa molar flow ratio.

Chemical etching of a GaSb crystal incorporated with Mn grown by the Bridgman method under microgravity conditions

A GaSb crystal incorporated with Mn has been grown by the Bridgman method on the Polizon facility onboard the FOTON-M3 spacecraft. Structural defects and growth striations have been successfully revealed by the chemical etching method. By calculating various parameters of the convection, the striation patterns can be explained, and the critical value of the Taylor number, which characterizes the convective condition of the rotating magnetic field induced azimuthal flow, was shown. The stresses generated during crystal growth can be reflected by the observations of etch pit distribution and other structural defects. Suggestions for improving the space experiment to improve the quality of the crystal are given.

Low-Temperature Growth of ZnO Films on GaAs by Metal Organic Chemical Vapor Deposition

ZnO thin films were grown on GaAs （001） substrates by metal-organic chemical vapor deposition （MOCVD） at low temperatures ranging from 100 to 400℃. DEZn and 1-12 O were used as the zinc precursor and oxygen precursor, respectively. The effects of the growth temperatures on the growth characteristics and optical properties of ZnO films were investigated. The X-ray diffraction measurement （XRD） results indicated that all the thin films were grown with highly c- axis orientation. The surface morphologies and crystal properties of the films were critically dependent on the growth temperatures. Although there was no evidence of epitaxial growth, the scanning electron microscopy （SEM） image of ZnO film grown at 400℃ revealed the presence of ZnO microcrystallines with closed packed hexagon structure. The photoluminescence spectrum at room temperature showed only bright band-edge （3. 33eV） emissions with little or no deep-level e- mission related to defects.

Zn-doped InGaAs Base Heterojunction Bipolar Transistors Grown by Low Pressure Metal Organic Chemical Vapor Deposition

High performance InP/InGaAs heterojunction bipolar transistors(HBTs) have been widely used in high-speed electronic devices and optoelectronic integrated circuits. InP-based HBTs were fabricated by low pressure metal organic chemical vapor deposition(MOCVD) and wet chemical etching. The sub-collector and collector were grown at 655 ℃ and other layers at 550 ℃. To suppress the Zn out-diffusion in HBT, base layer was grown with a 16-minute growth interruption. Fabricated HBTs with emitter size of 2.5×20 μm~2 showed current gain of 70~90, breakdown voltage(BV_(CE0))>2 V, cut-off frequency(f_T) of 60 GHz and the maximum relaxation frequency(f_(MAX)) of 70 GHz.

Homoepitaxial Growth and Characterization of 4H-SiC Epilayers by Low-Pressure Hot-Wall Chemical Vapor Deposition

Horizontal air-cooled low-pressure hot-wall CVD (LP-HWCVD) system is developed to get highly qualitical 4H-SiC epilayers.Homoepitaxial growth of 4H-SiC on off-oriented Si-face (0001) 4H-SiC substrates is performed at 1500℃ with a pressure of 1.3×103Pa by using the step-controlled epitaxy.The growth rate is controlled to be about 1.0μm/h.The surface morphologies and structural and optical properties of 4H-SiC epilayers are characterized with Nomarski optical microscope,atomic force microscopy (AFM),X-ray diffraction,Raman scattering,and low temperature photoluminescence (LTPL).N-type 4H-SiC epilayers are obtained by in-situ doping of NH3 with the flow rate ranging from 0.1 to 3sccm.SiC p-n junctions are obtained on these epitaxial layers and their electrical and optical characteristics are presented.The obtained p-n junction diodes can be operated at the temperature up to 400℃,which provides a potential for high-temperature applications.