薄膜材料对TiO2基薄膜激光损伤阈值的影响

abstract {The optical property, structure, surface properties (roughness and defect density) and laser-induced damage threshold (LIDT) of TiO₂ films deposited by electronic beam (EB) evaporation of TiO₂ (rutile), TiO₂ (anatase) and TiO₂ + Ta₂O₅ composite materials are comparatively studied. All films show the polycrystalline anatase TiO₂ structure. The loose sintering state and phase transformation during evaporating TiO₂ anatase slice lead to the high surface defect density, roughness and extinction coefficient, and low LIDT of films. The TiO₂ + Ta₂O₅ composite films have the lowest extinction coefficient and the highest LIDT among all samples investigated. Guidance of selecting materials for high LIDT laser mirrors is given.}

用于掺钛蓝宝石激光系统的高反膜的激光损伤

用电子束蒸发制备了用于掺钛蓝宝石啁啾脉冲放大激光系统的TiO2/HfO2/SiO2高反膜，其带宽约为176nm（R>98%, λ0=800nm），激光损伤阈值（LIDT）为2.4 J/cm2。通过TiO2和HfO2单层膜的透过光谱计算了这两种材料的折射率和消光系数。高反膜的性能主要由高折射率材料决定：折射率越高，反射带越宽；消光系数越小，薄膜吸收越小，LIDT越高。最后，讨论了高反膜的激光损伤机制。

Ta2O5膜在532, 800 和 1064 nm波长的n-on-1体系下的激光损伤阈值研究

Ta2O5膜采用传统的电子束蒸发方法制备，并在氧气中673 K的条件下进行了退火12 h处理。首先在1-on-1体系下对Ta2O5膜进行了532和1064 nm波长下的激光损伤阈值（LIDT） 研究，然后在n-on-1体系下分别对532，800和1064 nm三种波长下的激光损伤阈值进行了研究。结果表明在n-on-1体系下Ta2O5膜在532和1064 nm波长下的阈值均高于1-on-1体系下的阈值。此外，在n-on-1体系下，薄膜的阈值随波长增加而增大。同时发现，在氧气中进行退火对Ta2O5膜的光学性能

Effects of oxygen partial pressure on packing density and laser damage threshold of TiO2 thin films

TiO2 films are deposited by electron beam evaporation as a function of oxygen partial pressure. The packing density, refractive index, and extinction coefficient all decrease with the increase of pressure, which also induces the change of the film's microstructure, such as the increase of voids and H2O concentration in the film. The laser-induced damage threshold (LIDT) of the film increases monotonically with the rise of pressure in this experiment. The porous structure and low nonstoichiometric defects absorption contribute to the film's high LIDT. The films prepared at the lowest and the highest pressure show nonstoichiometric and surface-defects-induced damage features, respectively.(C) 2007 American Institute of Physics.

Comparison of femtosecond and nanosecond laser-induced damage in HfO2 single-layer film and HfO2-SiO2 high reflector

HfO2 single layers, 800 run high-reflective (HR) coating, and 1064 ran HR coating were prepared by electron-beam evaporation. The laser-induced damage thresholds (LIDTs) and damage morphologies of these samples were investigated with single-pulse femtosecond and nanosecond lasers. It is found that the LIDT of the HfO2 single layer is higher than the HfO2-SiO2 HR coating in the femtosecond regime, while the situation is opposite in the nanosecond regime. Different damage mechanisms are applied to study this phenomenon. Damage morphologies of all samples due to different laser irradiations are displayed. (c) 2007 Optical Society of America.

Effect of SiO2 protective layer on the femtosecond laser-induced damage of HfO2/SiO2 multilayer high-reflective coatings

Two kinds of HfO2/SiO2 800 nm high-reflective (HR) coatings, with and without SiO2 protective layer were deposited by electron beam evaporation. Laser-induced damage thresholds (LIDT) were measured for all samples with femtosecond laser pulses. The surface morphologies and the depth information of all samples were observed by Leica optical microscopy and WYKO surface profiler, respectively. It is found that SiO2 protective layer had no positive effect on improving the LIDT of HR coating. A simple model including the conduction band electron production via multiphoton ionization and impact ionization is used to explain this phenomenon. Theoretical calculations show that the damage occurs first in the SiO2 protective layer for HfO2/SiO2 HR coating with SiO2 protective layer. The relation of LIDT for two kinds of HfO2/SiO2 HR coatings in calculation agrees with the experiment result. (c) 2006 Elsevier B.V. All rights reserved.

沉积温度对LaF3薄膜性能的影响

abstract {LaF₃ single-layer coatings were prepared by thermal boat evaporation at the deposition temperatures of 189, 255, 277 and 321°C respectively. The crystal structures of the coatings were characterized by X-ray diffraction (XRD). A spectrophotometer was employed to measure its transmittance. Moreover, refractive index, extinction coefficient and cut-off wavelength were obtained from the measured transmittance spectral curve. The residual stress was evaluated by the Stoney's equation and optical interferometer. Laser induce damage threshold (LIDT) was performed by a tripled Nd:YAG laser system. The results show that the crystallization status becomes better with the deposition temperature increasing. Correspondingly, the grain size also gets larger. Meanwhile, the coatings become more compact and the refractive index increases. However, the absorption of coatings seriously rises and the cut-off wavelength drifts to the long wave. In addition, the residual stress also increases and the intrinsic stress plays a determinant role in the coating. The LIDT of the coating also enhances at high temperature.}

沉积速率对热舟蒸发LaF3薄膜性能的影响

用热舟蒸发方法在不同的沉积速率下制备了LaF3单层膜,并对部分单层膜进行了真空退火。分别采用X射线衍射(XRD),Lambda 900 光谱仪和355 nm Nd∶YAG脉冲激光测试了薄膜的晶体结构、透射光谱和激光损伤阈值(LIDT),并通过透射光谱计算得到样品的折射率和消光系数。实验结果表明,增大沉积速率有利于LaF3薄膜的结晶和择优生长,可以提高薄膜的致密性和折射率,但薄膜的抗激光损伤能力有所下降;沉积速率太大,又会恶化薄膜的结晶性能,同时薄膜中产生大量孔洞,薄膜的机械强度降低,导致薄膜的折射率减小和

1064nm与532nm激光对电子束蒸发制备的HfO2／SiO2高反膜损伤比较

研究了电子束蒸发制备的HfO2／SiO2高反膜在1064nm与532nm激光辐照下的损伤行为。基频激光辐照时损伤形貌主要为节瘤缺陷喷溅留下的锥形坑。当能量密度较大时出现分层剥落；二倍频激光损伤主要是由电子缺陷引起的平底坑，辐照脉冲能量密度稍高时也会产生吸收性缺陷引起的锥形坑，但电子缺陷的损伤阈值更低；随着辐照脉冲能量密度的增大分层剥落逐渐成为主要的损伤形貌。分析认为，辐照激光波长的变化。引起吸收机制的变化从而导致了损伤阈值及损伤机制的差异。

热舟蒸发LaF_3薄膜的紫外性能研究

研究了沉积温度对热舟蒸发氟化镧薄膜结构和光学性能的影响,沉积温度从200℃上升到350℃,间隔为50℃.采用分光光度计测量了样品的透射率和反射率光谱曲线,并在此基础上进行了光学损耗、光学常数以及带隙和截止波长的计算.采用表面轮廓仪进行了表面形貌和表面粗糙度的标定,采用X射线衍射(XRD)方法测量了不同沉积温度下样品的微结构.发现在短波长波段,随着沉积温度的升高,光学损耗增加,晶粒尺寸增大,表面粗糙度略有增加.不过散射损耗在光学损耗中所占比例均很小,光学损耗的增加主要由吸收损耗引起.随着沉积温度的升高,折射率与消光系数增大,带隙变小,相对应的截止波长向长波方向移动.

低损耗193nm增透膜

计算了适用于193nm增透膜设计与制备的基底与薄膜材料的光学常数,并在此基础上对193nm增透膜进行了设计、制备与性能分析.发现基底材料的吸收损耗对增透膜元件的影响很大,超过一定值时,增透膜元件的设计透过率将达不到理想水平.对单面增透膜的设计与制备结果表明,当吸收损耗降低到一定程度,散射损耗成为不可忽略的因素.采用热舟蒸发方法实现了性能良好的193nm减反射膜,剩余反射率在0.2%以下.

Influence of oxygen plasma treatment on properties of ZrO2 films prepared by e-beam evaporation techniques

Zirconia films were prepared by e-beam evaporation, and oxygen plasma treatment was used to modify film properties. Spectrophotometry, x-ray diffractometry (XRD), and atomic force microscopy were used to characterize refractive index, extinction coefficient, rnicrostructure, and surface roughness, respectively. The experimental results indicate that both refractive index and extinction coefficient of the films were reduced slightly after oxygen plasma treatment, with the decrease of intrinsic stress and surface roughness. From XRD spectra, the intensity decrease of the T(110) diffraction peak was clearly observed after the treatment, which was caused by the restructuring of the film atoms. (C) 2008 Elsevier Ltd. All rights reserved.

Investigation of damage threshold to TiO2 coatings at different laser wavelength and pulse duration

Laser-induced damages to TiO2 single layers and TiO2/SiO2 high reflectors at laser wavelength of 1064 nm, 800 run, 532 urn, and pulse width of 12 ns, 220 ps, 50 fs, 8 ns are investigated. All films are prepared by electron beam evaporation. The relations among microstructure, chemical composition, optical properties and laser-induced damage threshold (LIDT), have been researched. The dependence of damage mechanism on laser wavelength and pulse width is discussed. It is found that from 1064 nm to 532 nm, LIDT is mainly absorption related, which is determined by film's extinction coefficient and stoichiometric defects. The rapid decrease of LIDT at 800 nm is due to the pulse width factor. TiO2 coatings are mainly thermally by damaged at long pulse (tau >= 220 ps). The damage shows ablation feature at 50 fs. (C) 2007 Elsevier B.V. All rights reserved.

Temperature fields of 355 nm HR coatings based on the interface absorption model

Temperature fields of 355 nm high-reflectance (HR) coatings were investigated based on the interface absorption model. It was found that the highest temperature in the HR coatings increased with an increase in the extinction coefficient of the interface A, B, C, Al2O3 and MgF2. The highest temperature of HR coatings that can be reached increased quickly with the increase in the extinction coefficient of interface A in particular. The temperature rises of 355 nm HR coatings at different layers and different deposition temperatures were investigated based on experiments also. The damage mechanism of 355 nm HR coatings was confirmed with temperature fields and the interface absorption model.

引入过渡层提高介质减反膜的抗激光损伤阈值

提出了一种用于提高介质减反膜的损伤阈值的新的方法，在H2.5L (H:HfO2, L:SiO2)的膜层与基底之间引入4个1/4光学厚度的SiO2薄膜，发现抗激光损伤阈值提高了50%，并且保持1064nm处的反射率低于0.09%。本文分析了造成这一提高的机制，一定厚度的氧化硅过渡层的引入是一种提高介质减反膜的损伤阈值的灵活有效的方法。