Sphärische Bürsten in polymeren Schmelzen

Colloidal nanoparticles are additives to improve or modify several properties of thermoplastic or elastic polymers. Usually colloid-polymer mixtures show phase separation due to the depletion effect. The strategy to overcome this depletion demixing was to prepare surface-modified colloidal particles, which can be blended with linear polymer chains homogeneous. A successful synthesis strategy for the preparation of hairy nanospheres was developed by grafting polystyrene macromonomer chains onto polyorganosiloxane microgels. The number of hairs per particle with a core radius of approximately 10nm exceeded 150 hairs in all cases. The molecular weight of the hairs variied between 4000-18000g/mol.The compatibility of these hairy spheres mixed with linear polymer chains was investigated by AFM, TEM and SAXS. Homogeneous mixtures were found if the molecular weight of the polymer hairs on the particle surface is at least as large as the molecular weight of the matrix chains. If the chains are much shorter than the hairs, the colloidal hair corona is strongly swollen by the matrix polymer, leading to a long-range soft interparticle repulsion ('wet brush'). If hairs and chains are comparable in length, the corona shows much less volume swelling, leading to a short-range repulsive potential similar to hard sphere systems ('dry brush'). Polymerketten und Kolloidpartikel entmischen aufgrund von Depletion-Wechselwirkungen. Diese entropisch bedingte Entmischung konnte durch das Ankoppeln von Polymerhaaren verschiedenen Molekulargewichts auf die Kugeloberflächen der Kolloide bis zu hohen Konzentrationen vermieden werden. Zur Darstellung sphärischer Bürsten und haariger Tracerpartikel wurde eine neue Synthesestrategie ausgearbeitet und erfolgreich umgesetzt.Das Kompatibilitätsverhalten dieser sphärischen Bürsten in der Schmelze von Polymerketten als Matrix wurde mittels Elektronenmikroskopie und Kleinwinkelröntgenstreuung untersucht. Die Mischungen setzten sich aus sphärischen Bürsten und Matrixketten mit unterschiedlichen Molekulargewichten zusammen.Es zeigte sich, daß die Mischbarkeit entschieden durch das Verhältnis von Haarlänge zu Länge der Matrixketten beeinflußt wird.Aus den Untersuchungen des Relaxationsverhaltens mittels Rheologie und SAXS ergibt sich, daß das Konzept der 'dry brush'- und 'wet brush'-Systeme auf diese Mischungen übertragbar ist. Die Volumenquellung der Haarcorona durch die Matrixketten ist, wie die Experimente gezeigt haben, bereits im Fall von Polymeren mit relativ niedrigen Molekulargewichten zu beobachten. Sie ist umso stärker ausgeprägt, je größer das Längenverhältnis zwischen Polymerhaaren und Matrixketten ist. Die Quellung bedeutet eine Vergrößerung des effektiven Radius der Partikel und entspricht somit einer Erhöhung des effektiven Volumenbruchs. Dies führt zur Ausbildung einer höheren Ordnung und zu einem Einfrieren der Relaxation dieser strukturellen Ordnung führt.

Trasporto di materia in membrane polimeriche e nanocomposite per la separazione di gas

Membrane-based separation processes are acquiring, in the last years, an increasing importance because of their intrinsic energetic and environmental sustainability: some types of polymeric materials, showing adequate perm-selectivity features, appear rather suitable for these applications, because of their relatively low cost and easy processability. In this work have been studied two different types of polymeric membranes, in view of possible applications to the gas separation processes, i.e. Mixed Matrix Membranes (MMMs) and high free volume glassy polymers. Since the early 90’s, it has been understood that the performances of polymeric materials in the field of gas separations show an upper bound in terms of permeability and selectivity: in particular, an increase of permeability is often accompanied by a decrease of selectivity and vice-versa, while several inorganic materials, like zeolites or silica derivates, can overcome this limitation. As a consequence, it has been developed the idea of dispersing inorganic particles in polymeric matrices, in order to obtain membranes with improved perm-selectivity features. In particular, dispersing fumed silica nanoparticles in high free volume glassy polymers improves in all the cases gases and vapours permeability, while the selectivity may either increase or decrease, depending upon material and gas mixture: that effect is due to the capacity of nanoparticles to disrupt the local chain packing, increasing the dimensions of excess free volume elements trapped in the polymer matrix. In this work different kinds of MMMs were fabricated using amorphous Teflon® AF or PTMSP and fumed silica: in all the cases, a considerable increase of solubility, diffusivity and permeability of gases and vapours (n-alkanes, CO2, methanol) was observed, while the selectivity shows a non-monotonous trend with filler fraction. Moreover, the classical models for composites are not able to capture the increase of transport properties due to the silica addition, so it has been necessary to develop and validate an appropriate thermodynamic model that allows to predict correctly the mass transport features of MMMs. In this work, another material, called poly-trimethylsilyl-norbornene (PTMSN) was examined: it is a new generation high free volume glassy polymer that, like PTMSP, shows unusual high permeability and selectivity levels to the more condensable vapours. These two polymer differ each other because PTMSN shows a more pronounced chemical stability, due to its structure double-bond free. For this polymer, a set of Lattice Fluid parameters was estimated, making possible a comparison between experimental and theoretical solubility isotherms for hydrocarbons and alcoholic vapours: the successfully modelling task, based on application of NELF model, offers a reliable alternative to direct sorption measurement, which is extremely time-consuming due to the relevant relaxation phenomena showed by each sorption step. For this material also dilation experiments were performed, in order to quantify its dimensional stability in presence of large size, swelling vapours.

Sviluppo e caratterizzazione di impianti e membrane polimeriche per la medicina rigenerativa

Nell’ambito di questa Tesi sono state affrontate le fasi di progettazione, sviluppo e caratterizzazione di materiali biomimetici innovativi per la realizzazione di membrane e/o costrutti 3D polimerici, come supporti che mimano la matrice extracellulare, finalizzati alla rigenerazione dei tessuti. Partendo dall’esperienza di ISTEC-CNR e da un’approfondita conoscenza chimica su polimeri naturali quali il collagene, è stata affrontata la progettazione di miscele polimeriche (blends) a base di collagene, addizionato con altri biopolimeri al fine di ottimizzarne i parametri meccanici e la stabilità chimica in condizioni fisiologiche. I polimeri naturali chitosano ed alginato, di natura polisaccaridica, già noti per la loro biocompatibilità e selezionati come additivi rinforzanti per il collagene, si sono dimostrati idonei ad interagire con le catene proteiche di quest’ultimo formando blends omogenei e stabili. Al fine di ottimizzare l’interazione chimica tra i polimeri selezionati, sono stati investigati diversi processi di blending alla base dei quali è stato applicato un processo complesso di co-fibrazione-precipitazione: sono state valutate diverse concentrazioni dei due polimeri coinvolti e ottimizzato il pH dell’ambiente di reazione. A seguito dei processi di blending, non sono state registrate alterazioni sostanziali nelle caratteristiche chimiche e nella morfologia fibrosa del collagene, a riprova del fatto che non hanno avuto luogo fenomeni di denaturazione della sua struttura nativa. D’altro canto entrambe le tipologie di compositi realizzati, possiedano proprietà chimico-fisiche peculiari, simili ma non identiche a quelle dei polimeri di partenza, risultanti di una reale interazione chimica tra le due molecole costituenti il blending. Per entrambi i compositi, è stato osservato un incremento della resistenza all’attacco dell’enzima collagenasi ed elevato grado di swelling, quest’ultimo lievemente inferiore per il dispositivo contenente chitosano. Questo aspetto, negativo in generale per quanto concerne la progettazione di impianti per la rigenerazione dei tessuti, può avere aspetti positivi poiché la minore permeabilità nei confronti dei fluidi corporei implica una maggiore resistenza verso enzimi responsabili della degradazione in vivo. Studi morfologici al SEM hanno consentito di visualizzare le porosità e le caratteristiche topografiche delle superfici evidenziando in molti casi morfologie ibride che confermano il buon livello d’interazione tra le fasi; una più bassa omogeneità morfologica si è osservata nel caso dei composti collagene-alginato e solo dopo reidratazione dello scaffold. Per quanto riguarda le proprietà meccaniche, valutate in termini di elasticità e resistenza a trazione, sono state rilevate variazioni molto basse e spesso dentro l’errore sperimentale per quanto riguarda il modulo di Young; discorso diverso per la resistenza a trazione, che è risultata inferiore per i campione di collagene-alginato. Entrambi i composti hanno comunque mostrato un comportamento elastico con un minore pre-tensionamento iniziale, che li rendono promettenti nelle applicazioni come impianti per la rigenerazione di miocardio e tendini. I processi di blending messi a punto nel corso della ricerca hanno permesso di ottenere gel omogenei e stabili per mezzo dei quali è stato possibile realizzare dispositivi con diverse morfologie per diversi ambiti applicativi: dispositivi 2D compatti dall’aspetto di membrane semitrasparenti idonei per rigenerazione del miocardio e ligamenti/tendini e 3D porosi, ottenuti attraverso processi di liofilizzazione, con l’aspetto di spugne, idonei alla riparazione/rigenerazione osteo-cartilaginea. I test di compatibilità cellulare con cardiomioblasti, hanno dimostrato come entrambi i materiali compositi realizzati risultino idonei a processi di semina di cellule differenziate ed in grado di promuovere processi di proliferazione cellulare, analogamente a quanto avviene per il collagene puro.

Ternäre polymerhaltige Lösungen - Phasenverhalten und Grenzflächenspannung

Im Rahmen dieser Arbeit wurden experimentelle und theoretische Untersuchungen zum Phasen- und Grenzflächenverhalten von ternären Systemen des Typs Lösungsmittel/Fällungsmittel/Polymer durchgeführt. Diese Art der Mischungen ist vor allem für die Planung und Durchführung der Membranherstellung von Bedeutung, bei der die genaue Kenntnis des Phasendiagramms und der Grenzflächenspannung unabdingbar ist. Als Polymere dienten Polystyrol sowie Polydimethylsiloxan. Im Fall des Polystyrols kam Butanon-2 als Lösungsmittel zum Einsatz, wobei drei niedrigmolekulare lineare Alkohole als Fällungsmittel verwendet wurden. Für Polydimethylsiloxan eignen sich Toluol als Lösungsmittel und Ethanol als Fällungsmittel. Durch Lichtstreumessungen, Dampfdruckbestimmungen mittels Headspace-Gaschromatographie (VLE-Gleichgewichte) sowie Quellungsgleichgewichten lassen sich die thermodynamischen Eigenschaften der binären Subsysteme charakterisieren. Auf Grundlage der Flory-Huggins-Theorie kann das experimentell bestimmte Phasenverhalten (LLE-Gleichgewichte) in guter Übereinstimmung nach der Methode der Direktminimierung der Gibbs'schen Energie modelliert werden. Zieht man die Ergebnisse der Aktivitätsbestimmung von Dreikomponenten-Mischungen mit in Betracht, so ergeben sich systematische Abweichungen zwischen Experiment und Theorie. Sie können auf die Notwendigkeit ternärer Wechselwirkungsparameter zurückgeführt werden, die ebenfalls durch Modellierung zugänglich sind.Durch die aus den VLE- und LLE-Untersuchungen gewonnenen Ergebnissen kann die sog. Hump-Energie berechnet werden, die ein Maß für die Entmischungstendenz darstellt. Diese Größe eignet sich gut zur Beschreibung von Grenzflächenphänomenen mittels Skalengesetzen. Die für binäre Systeme gefundenen theoretisch fundierten Skalenparameter gelten jedoch nur teilweise. Ein neues Skalengesetz lässt erstmals eine Beschreibung über die gesamte Mischungslücke zu, wobei ein Parameter durch eine gemessene Grenzflächenspannung (zwischen Fällungsmittel/Polymer) ersetzt werden kann.

Studies of OPA1 pathogenic mechanisms in Dominant Optic Atrophy and novel protein function in mitochondrial DNA stability

The mitochondrion is an essential cytoplasmic organelle that provides most of the energy necessary for eukaryotic cell physiology. Mitochondrial structure and functions are maintained by proteins of both mitochondrial and nuclear origin. These organelles are organized in an extended network that dynamically fuses and divides. Mitochondrial morphology results from the equilibrium between fusion and fission processes, controlled by a family of “mitochondria-shaping” proteins. It is becoming clear that defects in mitochondrial dynamics can impair mitochondrial respiration, morphology and motility, leading to apoptotic cell death in vitro and more or less severe neurodegenerative disorders in vivo in humans. Mutations in OPA1, a nuclear encoded mitochondrial protein, cause autosomal Dominant Optic Atrophy (DOA), a heterogeneous blinding disease characterized by retinal ganglion cell degeneration leading to optic neuropathy (Delettre et al., 2000; Alexander et al., 2000). OPA1 is a mitochondrial dynamin-related guanosine triphosphatase (GTPase) protein involved in mitochondrial network dynamics, cytochrome c storage and apoptosis. This protein is anchored or associated on the inner mitochondrial membrane facing the intermembrane space. Eight OPA1 isoforms resulting from alternative splicing combinations of exon 4, 4b and 5b have been described (Delettre et al., 2001). These variants greatly vary among diverse organs and the presence of specific isoforms has been associated with various mitochondrial functions. The different spliced exons encode domains included in the amino-terminal region and contribute to determine OPA1 functions (Olichon et al., 2006). It has been shown that exon 4, that is conserved throughout evolution, confers functions to OPA1 involved in maintenance of the mitochondrial membrane potential and in the fusion of the network. Conversely, exon 4b and exon 5b, which are vertebrate specific, are involved in regulation of cytochrome c release from mitochondria, and activation of apoptosis, a process restricted to vertebrates (Olichon et al., 2007). While Mgm1p has been identified thanks to its role in mtDNA maintenance, it is only recently that OPA1 has been linked to mtDNA stability. Missense mutations in OPA1 cause accumulation of multiple deletions in skeletal muscle. The syndrome associated to these mutations (DOA-1 plus) is complex, consisting of a combination of dominant optic atrophy, progressive external ophtalmoplegia, peripheral neuropathy, ataxia and deafness (Amati- Bonneau et al., 2008; Hudson et al., 2008). OPA1 is the fifth gene associated with mtDNA “breakage syndrome” together with ANT1, PolG1-2 and TYMP (Spinazzola et al., 2009). In this thesis we show for the first time that specific OPA1 isoforms associated to exon 4b are important for mtDNA stability, by anchoring the nucleoids to the inner mitochondrial membrane. Our results clearly demonstrate that OPA1 isoforms including exon 4b are intimately associated to the maintenance of the mitochondrial genome, as their silencing leads to mtDNA depletion. The mechanism leading to mtDNA loss is associated with replication inhibition in cells where exon 4b containing isoforms were down-regulated. Furthermore silencing of exon 4b associated isoforms is responsible for alteration in mtDNA-nucleoids distribution in the mitochondrial network. In this study it was evidenced that OPA1 exon 4b isoform is cleaved to provide a 10kd peptide embedded in the inner membrane by a second transmembrane domain, that seems to be crucial for mitochondrial genome maintenance and does correspond to the second transmembrane domain of the yeasts orthologue encoded by MGM1 or Msp1, which is also mandatory for this process (Diot et al., 2009; Herlan et al., 2003). Furthermore in this thesis we show that the NT-OPA1-exon 4b peptide co-immuno-precipitates with mtDNA and specifically interacts with two major components of the mitochondrial nucleoids: the polymerase gamma and Tfam. Thus, from these experiments the conclusion is that NT-OPA1- exon 4b peptide contributes to the nucleoid anchoring in the inner mitochondrial membrane, a process that is required for the initiation of mtDNA replication and for the distribution of nucleoids along the network. These data provide new crucial insights in understanding the mechanism involved in maintenance of mtDNA integrity, because they clearly demonstrate that, besides genes implicated in mtDNA replications (i.e. polymerase gamma, Tfam, twinkle and genes involved in the nucleotide pool metabolism), OPA1 and mitochondrial membrane dynamics play also an important role. Noticeably, the effect on mtDNA is different depending on the specific OPA1 isoforms down-regulated, suggesting the involvement of two different combined mechanisms. Over two hundred OPA1 mutations, spread throughout the coding region of the gene, have been described to date, including substitutions, deletions or insertions. Some mutations are predicted to generate a truncated protein inducing haploinsufficiency, whereas the missense nucleotide substitutions result in aminoacidic changes which affect conserved positions of the OPA1 protein. So far, the functional consequences of OPA1 mutations in cells from DOA patients are poorly understood. Phosphorus MR spectroscopy in patients with the c.2708delTTAG deletion revealed a defect in oxidative phosphorylation in muscles (Lodi et al., 2004). An energetic impairment has been also show in fibroblasts with the severe OPA1 R445H mutation (Amati-Bonneau et al., 2005). It has been previously reported by our group that OPA1 mutations leading to haploinsufficiency are associated in fibroblasts to an oxidative phosphorylation dysfunction, mainly involving the respiratory complex I (Zanna et al., 2008). In this study we have evaluated the energetic efficiency of a panel of skin fibroblasts derived from DOA patients, five fibroblast cell lines with OPA1 mutations causing haploinsufficiency (DOA-H) and two cell lines bearing mis-sense aminoacidic substitutions (DOA-AA), and compared with control fibroblasts. Although both types of DOA fibroblasts maintained a similar ATP content when incubated in a glucose-free medium, i.e. when forced to utilize the oxidative phosphorylation only to produce ATP, the mitochondrial ATP synthesis through complex I, measured in digitonin-permeabilized cells, was significantly reduced in cells with OPA1 haploinsufficiency only, whereas it was similar to controls in cells with the missense substitutions. Furthermore, evaluation of the mitochondrial membrane potential (DYm) in the two fibroblast lines DOA-AA and in two DOA-H fibroblasts, namely those bearing the c.2819-2A>C mutation and the c.2708delTTAG microdeletion, revealed an anomalous depolarizing response to oligomycin in DOA-H cell lines only. This finding clearly supports the hypothesis that these mutations cause a significant alteration in the respiratory chain function, which can be unmasked only when the operation of the ATP synthase is prevented. Noticeably, oligomycin-induced depolarization in these cells was almost completely prevented by preincubation with cyclosporin A, a well known inhibitor of the permeability transition pore (PTP). This results is very important because it suggests for the first time that the voltage threshold for PTP opening is altered in DOA-H fibroblasts. Although this issue has not yet been addressed in the present study, several are the mechanisms that have been proposed to lead to PTP deregulation, including in particular increased reactive oxygen species production and alteration of Ca2+ homeostasis, whose role in DOA fibroblasts PTP opening is currently under investigation. Identification of the mechanisms leading to altered threshold for PTP regulation will help our understanding of the pathophysiology of DOA, but also provide a strategy for therapeutic intervention.

Herstellung und physikochemische Charakterisierung von planaren gestützten Lipid-Modellmembran-Systemen

Es wurden funktionalisierte polymerunterstützte planare Phospholipid-Modellmembran-Systeme hergestellt und auf jeder Präparationsstufe eingehend charakterisiert. Dünne Polysaccharidfilme wurden in der Form von quellbaren Gelen auf oxidische Oberflächen aufgebracht und bezüglich ihres Quellungsverhaltens und der Oberflächeneigenschaften in Abhängigkeit vom Wassergehalt untersucht. Lipidmonoschichten unterschiedlicher Zusammensetzung wurden mittels Langmuir-Blodgett-Tranfer auf Polymersubstrate übertragen und bezüglich der Stärke der Lipid/Polymer Wechselwirkung, der lateralen Selbstdiffusion in Abhängigkeit von der Wasseraktivität, dem Spreitverhalten der monomolekularen Membran auf dem Substrat in Abhängigkeit von der Wasseraktivität und dem Lateraldruck der Monoschicht, sowie des Ausmaßes der Hydratation im Kopfgruppenbereich der Lipidmembran in Abhängigkeit von der Wasseraktivität mittels Fluoreszensondenmethoden (Fluoreszenzerholung nach Photobleichung (FRAP), Fluoreszenzmikroskopie und Fluoreszenzspektroskopie) untersucht. Diffusions- und Spreitverhalten von amphiphilen Monoschichten auf Polymersubstraten wurden auf der Basis von in dieser Arbeit entwickelten physikalischen Modellen diskutiert. Mittels Langmuir-Schäfer Transfer wurde auf polymerunterstützte Lipidmonoschichten eine zweite Monoschicht übertragen. Die somit erhaltenen Lipid-Doppelschichtmembranen wurden bezüglich ihrer Stabilität, der lateralen Struktur, der lateralen Selbstdiffusion, des Spreitverhaltens auf unbedeckte Bereiche sowie der Stärke der Membran/Substrat Wechselwirkung vermittels Fluoreszenzmikroskopie, FRAP und Interferenz-Kontrast-Mikroskopie (RICM) untersucht. Schließlich wurden substratgestützte Doppelschicht-Lipidmembranen mit als Protonenpumpen fungierenden integralen Membranproteinen versehen. Die laterale Selbstdiffusion der rekonstituierten Proteinmoleküle wurde mittels FRAP, die funktionale Aktivität der Protonenpumpen mit einem Ionen-sensitiven Feldeffekttransistor-Array analysiert.

High pressure surface plasmon spectroscopy

Der Einfluß von Druck auf die Eigenschaften dünner dielektrischer Filme wurde mit Hilfe von Oberflächenplasmonen-Spektroskopie untersucht. Die Arbeit kann aus der Perspektive der Materialcharakterisierung und aus apparativer Sicht betrachtet werden, da z.B. eine neue Hochdruckzelle konstruiert wurde, die kombinierte Oberflächenplasmonen-Elektrochemie Messungen erlaubt. SiO2-Solgel Filme wurden optimiert und auf ihre Widerstandsfähigkeit in Bufferlösungen und ihre Oberflächeneigenschaften hin untersucht. Eine Anwendung lag in der Charakterisierung von thermoresponsiven Acrylsäureisopropylamid Hydrogelen, die einen Volumenphasenübergang aufwiesen, dessen Eigenschaften durch Druck und die Beschränktheit des Films auf die Oberfläche beeinflußt wurden.Die Charakterisierung von DNA Hybridisierungsreaktionen an Oberflächen wurde mit einer Fluoreszenz-erweiterten Hochdruckapparatur durchgeführt. Zunächst wurde die Stabilität der zugrundeliegenden Bindematrix sichergestellt. Bei DNA Einzelsträngen führten Temperatur und Druck zu jeweils verringertem bzw. erhöhtem Signal. Entropie und Änderungen der Lösungsmitteleigenschaften wurden für die Signaländerungen verantwortlich gemacht. Die Eigenschaften der Doppelhelix wurden im Langmuir-Bild beschrieben. Der Brechungsindex von Kohlendioxid wurde bis zu 200 MPa gemessen und mit vorhandenen Gleichungen verglichen. Weiterhin wurde das Schwellverhalten von PMMA in scCO2/MMA-Mischungen untersucht. Mit Druck und MMA-Konzentration nimmt das Polymer vermehrt Kohlendioxid auf. Dadurch schwillt es an und sein Brechungsindex nimmt ab. Berechnungen unter Annahme einer idealen Mixtur ergaben gute qualitative Übereinstimmung mit den Meßwerten.Abschließend wurde eine neue Elektrochemie-Hochdruckzelle vorgestellt, die an Kaliumhexacyanoferrat(III)-(II) getestet wurde. Die Elektropolymerisation von Thiophen optisch untersucht.

Assembly and characterization of supramolecular architectures for biosensor applications

The research has included the efforts in designing, assembling and structurally and functionally characterizing supramolecular biofunctional architectures for optical biosensing applications. In the first part of the study, a class of interfaces based on the biotin-NeutrAvidin binding matrix for the quantitative control of enzyme surface coverage and activity was developed. Genetically modified ß-lactamase was chosen as a model enzyme and attached to five different types of NeutrAvidin-functionalized chip surfaces through a biotinylated spacer. All matrices are suitable for achieving a controlled enzyme surface density. Data obtained by SPR are in excellent agreement with those derived from optical waveguide measurements. Among the various protein-binding strategies investigated in this study, it was found that stiffness and order between alkanethiol-based SAMs and PEGylated surfaces are very important. Matrix D based on a Nb2O5 coating showed a satisfactory regeneration possibility. The surface-immobilized enzymes were found to be stable and sufficiently active enough for a catalytic activity assay. Many factors, such as the steric crowding effect of surface-attached enzymes, the electrostatic interaction between the negatively charged substrate (Nitrocefin) and the polycationic PLL-g-PEG/PEG-Biotin polymer, mass transport effect, and enzyme orientation, are shown to influence the kinetic parameters of catalytic analysis. Furthermore, a home-built Surface Plasmon Resonance Spectrometer of SPR and a commercial miniature Fiber Optic Absorbance Spectrometer (FOAS), served as a combination set-up for affinity and catalytic biosensor, respectively. The parallel measurements offer the opportunity of on-line activity detection of surface attached enzymes. The immobilized enzyme does not have to be in contact with the catalytic biosensor. The SPR chip can easily be cleaned and used for recycling. Additionally, with regard to the application of FOAS, the integrated SPR technique allows for the quantitative control of the surface density of the enzyme, which is highly relevant for the enzymatic activity. Finally, the miniaturized portable FOAS devices can easily be combined as an add-on device with many other in situ interfacial detection techniques, such as optical waveguide lightmode spectroscopy (OWLS), the quartz crystal microbalance (QCM) measurements, or impedance spectroscopy (IS). Surface plasmon field-enhanced fluorescence spectroscopy (SPFS) allows for an absolute determination of intrinsic rate constants describing the true parameters that control interfacial hybridization. Thus it also allows for a study of the difference of the surface coupling influences between OMCVD gold particles and planar metal films presented in the second part. The multilayer growth process was found to proceed similarly to the way it occurs on planar metal substrates. In contrast to planar bulk metal surfaces, metal colloids exhibit a narrow UV-vis absorption band. This absorption band is observed if the incident photon frequency is resonant with the collective oscillation of the conduction electrons and is known as the localized surface plasmon resonance (LSPR). LSPR excitation results in extremely large molar extinction coefficients, which are due to a combination of both absorption and scattering. When considering metal-enhanced fluorescence we expect the absorption to cause quenching and the scattering to cause enhancement. Our further study will focus on the developing of a detection platform with larger gold particles, which will display a dominant scattering component and enhance the fluorescence signal. Furthermore, the results of sequence-specific detection of DNA hybridization based on OMCVD gold particles provide an excellent application potential for this kind of cheap, simple, and mild preparation protocol applied in this gold fabrication method. In the final chapter, SPFS was used for the in-depth characterizations of the conformational changes of commercial carboxymethyl dextran (CMD) substrate induced by pH and ionic strength variations were studied using surface plasmon resonance spectroscopy. The pH response of CMD is due to the changes in the electrostatics of the system between its protonated and deprotonated forms, while the ionic strength response is attributed from the charge screening effect of the cations that shield the charge of the carboxyl groups and prevent an efficient electrostatic repulsion. Additional studies were performed using SPFS with the aim of fluorophore labeling the carboxymethyl groups. CMD matrices showed typical pH and ionic strength responses, such as high pH and low ionic strength swelling. Furthermore, the effects of the surface charge and the crosslink density of the CMD matrix on the extent of stimuli responses were investigated. The swelling/collapse ratio decreased with decreasing surface concentration of the carboxyl groups and increasing crosslink density. The study of the CMD responses to external and internal variables will provide valuable background information for practical applications.

EPR-Spektroskopie zur Untersuchung von Struktur und Dynamik in Polymer-Ton-Nanokompositen

Ziel der vorliegenden Arbeit war die Untersuchung von Struktur und Dynamik in Polymer-Ton-Nanokompositen mittels EPR-Spektroskopie; damit sollten ein Beitrag zur Analyse der Tensidschicht in solchen Systemen geleistet und die Ergebnisse anderer Messmethoden ergänzt werden. Die Tensidschicht in Polymer-Ton-Nanokompositen nimmt großen Einfluss auf das System, denn sie bestimmt die Wechselwirkung zwischen Ton und Polymer: Damit hydrophiler Ton gut mit hydrophobem Polymer (hier Polystyrol) mischbar ist, muss das Schichtsilikat zunächst mit Tensiden organisch-modifiziert werden; dies geschieht durch Kationenaustausch der Natriumionen im Ton gegen Tenside. Um mit Hilfe der EPR einen Einblick in die Tensidschicht zu gewinnen, muss etwa 1% der zur Tonmodifizierung eingesetzten Amphiphile spinmarkiert sein. So gelang es im Rahmen dieser Arbeit, Tenside mit verschiedenen Kopfgruppen, nämlich Trimethylammonium- bzw. Trimethylphosphoniumtenside, zu synthetisieren und sie an verschiedenen Positionen ihrer hydrophoben Alkylkette mit einem Nitroxidradikal zu markieren. Das Nitroxidradikal diente als Spinsonde für die EPR-Experimente. Neben der Synthese verschiedener, spinmarkierter Amphiphile, der anschließenden Darstellung organisch-modifizierten Tons (Kationenaustausch) und verschiedener Polymer-Ton-Nanokomposite (Schmelzinterkalation) wurden alle Proben mittels EPR-Spektroskopie untersucht; dabei wurden sowohl cw- als auch gepulste Messtechniken eingesetzt. Aus cw-Experimenten ging hervor, dass die Dynamik der gesamten Tensidschicht mit der Temperatur zunimmt und die Mobilität der hydrophoben Tensidalkylkette mit wachsendem Abstand zu ihrer Kopfgruppe wächst. Zugabe von Polymer behindert bei steigender Temperatur das Anschwellen des Tons bei Aufschmelzen der Tensidschicht; die Dynamik des Systems ist eingeschränkt. Mit Hilfe gepulster EPR-Messungen (ENDOR und ESEEM), die Informationen über Abstände bzw. Kontakt in den untersuchten Systemen lieferten, ließ sich ein Strukturmodell der Polymer-Ton-Nanokomposite skizzieren, das Vorstellungen anderer, älterer Methoden unterstützt: Hierbei richten sich die Tenside in Multischichten unterschiedlicher Mobilität parallel zur Tonoberfläche aus.

Untersuchung des Reorientierungsverhaltens und Strukturierung dünner amphiphiler Blockcopolymerfilme zum Aufbau von Kompositen

Grundlage für die hier gezeigte Arbeit stellt die Eigenschaft von amphiphilen Blockcopolymeren dar immer den Block mit der niedrigsten Grenzflächenenergie zum angrenzenden Medium an die Oberfläche zu bringen. Durch einen Austausch des Mediums an der Grenzfläche zum Blockcopolymer kann eine Reorientierung erzwungen werden, wenn die Grenzflächenenergie des anderen Blocks nun die niedrigere Grenzflächenenergie besitzt. Dieses Verhalten von dünnen amphiphilen Blockcopolymerfilmen wurde zur Strukturierung von Oberflächen ausgenutzt und in nachfolgenden Synthesen weiter verstärkt. Um dies zu erreichen wurde das zur Strukturierung erforderliche Poly(4-Octylstyrol)block(4-hydroxystyrol) durch kontrollierte radikalische Polymerisationsmethode mit dem Tempo Unimer (2,2,6,6-Tetramethyl-1-1(1-phenyl-ethoxy)-piperidin) synthetisiert. Für die geplanten Reorientierungen und Modifizierungen von Oberflächen wurden dünne Filme durch Schleuderbeschichtung auf verschiedenen Substraten (Siliziumwafern, Glassubstraten und Goldoberflächen) hergestellt. Das Verhalten der Oberflächen von diesen Filmen wurde durch Kontaktwinkelmessungen untersucht. Auf diese Weise konnte gezeigt werden, dass die Oberfläche von Polymerfilmen nach der Präparation aus dem hydrophoben Block des Polymers gebildet wird. Durch Kontakt des Polymerfilms mit Wasser kann dieser zur Reorientierung gebracht werden, so dass der hydrophile Block des Polymers an der Oberfläche erscheint. Dieses Verhalten wurde zur Strukturierung mit softlithographischen Techniken genutzt. Dazu wurden hydrophil/hydrophob strukturierte Oberflächen durch Aufsetzen von hydrophoben PDMS-Stempeln, die Teile der Oberfläche selektiv abdeckten, und Einbringen von Wasser in die dabei entstehenden Kapillaren hergestellt. Dies ermöglichte es die Oberfläche selektiv im Größenbereich von 500nm bis zu 50µm zu strukturieren und an den reaktiven Bereichen Materialien, wie z.B. Kupfer, Titandioxid, Polyelektrolyte, photonische Kristalle und angegraftete Polymere, mit verschiedenen Methoden selektiv auf die Oberfläche aufzubringen. Um den Reorganisationsprozess der Oberfläche genauer zu studieren, wurde ein für diese Aufgabe besser geeignetes Polymer (Poly(Styrol)-block-poly(essigsäure-2-(2-(4-vinyl-phenoxy)-ethoxy)ethylester)) synthetisiert. Aus diesem Blockcopolymer wurden wieder dünne Filme durch Spincoaten hergestellt. Die Reorientierung dieses Polymers in 70°C warmen Wasser konnte durch Kontaktwinkelmessungen und NEXAFS Spektroskopie nachgewiesen werden. Mit Hilfe der NEXAFS Spektroskopie konnte festgestellt werden, dass die Geschwindigkeit der Reorientierung durch eine exponentielle Funktion beschrieben werden kann. Eine Auswertung der Geschwindigkeitskonstante für die Reorientierung einer hydrophilen zu einer hydrophoben Oberfläche des Polymers bei 60°C führt zu =75min. Aufgrund des exponentiellen Charakters der Reorientierung macht es den Anschein, dass die Reorientierung bei verschiedenen Reorientierungstemperaturen bis zu einem gewissen Grad erfolgt und dann stoppt. Eine weitere Reorientierung scheint erst wieder bei einer Temperaturerhöhung zu beginnen. Aus AFM Messungen ist ein Beginnen der Reorientierung durch Bildung kleiner Löcher in der Polymeroberfläche zu erkennen, die sich zu runden Erhöhungen und Vertiefungen vergrößern, um letztendlich in ein spinodales Entmischungsmuster über zu gehen. Dieses heilt dann im Laufe der Zeit langsam durch Verschwinden der hydrophilen Bereiche langsam aus. Der Beginn des zuvor beschriebenen Reorientierungsprozesses einer hydrophilen Oberfläche in eine hydrophobe konnte sowohl in den AFM, als auch in den NEXAFS-Messungen zu ca. 50°C bestimmt werden.

Structuring of polymer surface by evaporation of sessile microdrops

In this thesis, we investigated the evaporation of sessile microdroplets on different solid substrates. Three major aspects were studied: the influence of surface hydrophilicity and heterogeneity on the evaporation dynamics for an insoluble solid substrate, the influence of external process parameters and intrinsic material properties on microstructuring of soluble polymer substrates and the influence of an increased area to volume ratio in a microfluidic capillary, when evaporation is hindered. In the first part, the evaporation dynamics of pure sessile water drops on smooth self-assembled monolayers (SAMs) of thiols or disulfides on gold on mica was studied. With increasing surface hydrophilicity the drop stayed pinned longer. Thus, the total evaporation time of a given initial drop volume was shorter, since the drop surface, through which the evaporation occurs, stays longer large. Usually, for a single drop the volume decreased linearly with t1.5, t being the evaporation time, for a diffusion-controlled evaporation process. However, when we measured the total evaporation time, ttot, for multiple droplets with different initial volumes, V0, we found a scaling of the form V0 = attotb. The more hydrophilic the substrate was, the more showed the scaling exponent a tendency to an increased value up to 1.6. This can be attributed to an increasing evaporation rate through a thin water layer in the vicinity of the drop. Under the assumption of a constant temperature at the substrate surface a cooling of the droplet and thus a decreased evaporation rate could be excluded as a reason for the different scaling exponent by simulations performed by F. Schönfeld at the IMM, Mainz. In contrast, for a hairy surface, made of dialkyldisulfide SAMs with different chain lengths and a 1:1 mixture of hydrophilic and hydrophobic end groups (hydroxy versus methyl group), the scaling exponent was found to be ~ 1.4. It increased to ~ 1.5 with increasing hydrophilicity. A reason for this observation can only be speculated: in the case of longer hydrophobic alkyl chains the formation of an air layer between substrate and surface might be favorable. Thus, the heat transport to the substrate might be reduced, leading to a stronger cooling and thus decreased evaporation rate. In the second part, the microstructuring of polystyrene surfaces by drops of toluene, a good solvent, was investigated. For this a novel deposition technique was developed, with which the drop can be deposited with a syringe. The polymer substrate is lying on a motorized table, which picks up the pendant drop by an upward motion until a liquid bridge is formed. A consecutive downward motion of the table after a variable delay, i.e. the contact time between drop and polymer, leads to the deposition of the droplet, which can evaporate. The resulting microstructure is investigated in dependence of the processes parameters, i.e. the approach and the retraction speed of the substrate and the delay between them, and in dependence of the intrinsic material properties, i.e. the molar mass and the type of the polymer/solvent system. The principal equivalence with the microstructuring by the ink-jet technique was demonstrated. For a high approach and retraction speed of 9 mm/s and no delay between them, a concave microtopology was observed. In agreement with the literature, this can be explained by a flow of solvent and the dissolved polymer to the rim of the pinned droplet, where polymer is accumulated. This effect is analogue to the well-known formation of ring-like stains after the evaporation of coffee drops (coffee-stain effect). With decreasing retraction speed down to 10 µm/s the resulting surface topology changes from concave to convex. This can be explained with the increasing dissolution of polymer into the solvent drop prior to the evaporation. If the polymer concentration is high enough, gelation occurs instead of a flow to the rim and the shape of the convex droplet is received. With increasing delay time from below 0 ms to 1s the depth of the concave microwells decreases from 4.6 µm to 3.2 µm. However, a convex surface topology could not be obtained, since for longer delay times the polymer sticks to the tip of the syringe. Thus, by changing the delay time a fine-tuning of the concave structure is accomplished, while by changing the retraction speed a principal change of the microtopolgy can be achieved. We attribute this to an additional flow inside the liquid bridge, which enhanced polymer dissolution. Even if the pendant drop is evaporating about 30 µm above the polymer surface without any contact (non-contact mode), concave structures were observed. Rim heights as high as 33 µm could be generated for exposure times of 20 min. The concave structure exclusively lay above the flat polymer surface outside the structure even after drying. This shows that toluene is taken up permanently. The increasing rim height, rh, with increasing exposure time to the solvent vapor obeys a diffusion law of rh = rh0  tn, with n in the range of 0.46 ~ 0.65. This hints at a non-Fickian swelling process. A detailed analysis showed that the rim height of the concave structure is modulated, unlike for the drop deposition. This is due to the local stress relaxation, which was initiated by the increasing toluene concentration in the extruded polymer surface. By altering the intrinsic material parameters i.e. the polymer molar mass and the polymer/solvent combination, several types of microstructures could be formed. With increasing molar mass from 20.9 kDa to 1.44 MDa the resulting microstructure changed from convex, to a structure with a dimple in the center, to concave, to finally an irregular structure. This observation can be explained if one assumes that the microstructuring is dominated by two opposing effects, a decreasing solubility with increasing polymer molar mass, but an increasing surface tension gradient leading to instabilities of Marangoni-type. Thus, a polymer with a low molar mass close or below the entanglement limit is subject to a high dissolution rate, which leads to fast gelation compared to the evaporation rate. This way a coffee-rim like effect is eliminated early and a convex structure results. For high molar masses the low dissolution rate and the low polymer diffusion might lead to increased surface tension gradients and a typical local pile-up of polymer is found. For intermediate polymer masses around 200 kDa, the dissolution and evaporation rate are comparable and the typical concave microtopology is found. This interpretation was supported by a quantitative estimation of the diffusion coefficient and the evaporation rate. For a different polymer/solvent system, polyethylmethacrylate (PEMA)/ethylacetate (EA), exclusively concave structures were found. Following the statements above this can be interpreted with a lower dissolution rate. At low molar masses the concentration of PEMA in EA most likely never reaches the gelation point. Thus, a concave instead of a convex structure occurs. At the end of this section, the optically properties of such microstructures for a potential application as microlenses are studied with laser scanning confocal microscopy. In the third part, the droplet was confined into a glass microcapillary to avoid evaporation. Since here, due to an increased area to volume ratio, the surface properties of the liquid and the solid walls became important, the influence of the surface hydrophilicity of the wall on the interfacial tension between two immiscible liquid slugs was investigated. For this a novel method for measuring the interfacial tension between the two liquids within the capillary was developed. This technique was demonstrated by measuring the interfacial tensions between slugs of pure water and standard solvents. For toluene, n-hexane and chloroform 36.2, 50.9 and 34.2 mN/m were measured at 20°C, which is in a good agreement with data from the literature. For a slug of hexane in contact with a slug of pure water containing ethanol in a concentration range between 0 and 70 (v/v %), a difference of up to 6 mN/m was found, when compared to commercial ring tensiometry. This discrepancy is still under debate.

Synthese und Charakterisierung einer Hydrogelmatrix für die Multianalyt-Sensorik

Gegenstand und Ziel der vorliegenden Arbeit war die Synthese und Charakterisierung einer Hydrogelmatrix, welche für die Herstellung eines vielseitig verwendbaren Sensors, der mehrere Analyten (Proteine, DNA etc.) in hoher Verdünnung (c0 < 50 fM) aus kleinsten Probenmengen (Volumina <20 nl) schnell (t < 1 min) und parallel nachweisen kann, Verwendung finden soll. Der Fokus der Arbeit lag dabei in der Synthese und Charakterisierung von Copolymeren als Hydrogelmatrix, welche geeignetes temperaturabhängiges Verhalten zeigen. Die Copolymere wurden in eine dreidimensionale Netzwerkstruktur überführt und auf einer Goldoberfläche kovalent angebunden, um Delamination zu vermeiden und die Untersuchung mittels Oberflächenplasmonenresonanz-Spektroskopie (SPR) und Optischer Wellenleiter-Spektroskopie (OWS) zu erlauben. Weiterhin wurde das temperaturabhängige Verhalten der Polymernetzwerke in Wasser mittels optischen Messungen (SPR/OWS) untersucht, um Erkenntnisse über die Quell- und Kollabiereigenschaften des Hydrogels zu gewinnen. Um temperaturschaltbare Hydrogele herzustellen, wurden auf N-Isopropylacrylamid (NIPAAm) basierende Polymere synthetisiert. Es wurde sowohl die für Hydrogele übliche Methode der freien radikalischen Vernetzungspolymerisation in Wasser, wie eine neue, auf Benzophenoneinheiten basierende Syntheseroute, welche die freie radikalische Polymerisation in organischem Medium nutzt, verwendet. Die synthetisierten Polymere sind Copolymere aus N‑Isopropylacrylamid (NIPAAm) und 4-Methacryloyloxybenzophenon (MABP). NIPAAm ist dabei für das temperaturschaltbare Verhalten der Gele verantwortlich und MABP dient als Photovernetzer. Weitere Copolymere, die neben den genannten Monomeren noch andere Funktionen, wie z.B. ionische Gruppen oder Aktivesterfunktionen enthalten, wurden ebenfalls synthetisiert. Das temperaturabhängige Quellverhalten in Bezug auf die chemische Zusammensetzung wurde mit der Oberflächenplasmonenresonanz-Spektroskopie (SPR) und Optischen Wellenleiter-Spektroskopie (OWS) untersucht. Es zeigte sich, dass die Anwesenheit von Salz im Hydrogel (Natriumacrylat als Monomer, P4S) Inhomogenität, in Form eines Brechungsindexgradienten senkrecht zur Substratoberfläche, hervorruft. Dies ist nicht der Fall, wenn statt des Salzes die Säure (Methacrylsäure als Monomer, P4A) verwendet wird. Durch die Inhomogenität lassen sich die Filme mit dem Natriummethacrylat nicht mehr mit dem, üblicherweise zur Auswertung genutzten, Kastenmodell beschreiben. Die Anwendung der Wentzel-Kramers-Brillouin-Näherung (WKB) auf die Messdaten führt hingegen zu dem gewünschten Ergebnis. Man findet ein kastenähnliches Brechungsindexprofil für das Hydrogel mit der Säure (P4A) und ein Gradientenprofil für das Gel mit dem Salz (P4S). Letzteres ist nicht nur hydrophiler und insgesamt stärker gequollen, sondern ragt auch weiter in die überstehende Wasserphase hinein. Anhand eines säurehaltigen Hydrogels (P8A) konnte der quellungshemmende Einfluss von hohen Salzkonzentrationen gezeigt werden. Weiterhin wurde während des Quellvorgangs eine gewisse Anisotropie gefunden, die aber im vollständig gequollenen und vollständig kollabierten Zustand nicht mehr vorliegt. Anhand eines Hydrogels ohne ionisierbare Gruppen (P9) wurde die Reversibilität des Quell- und Kollabiervorgangs gezeigt. Bei einem Vergleich zwischen einem säurehaltigen Hydrogel (P8A, Quellgrad von 7,3) und einem ohne ionisierbare Gruppen (P9, Quellgrad von 6,1), hat die Anwesenheit der 8 mol% Säuregruppen eine leichte Verstärkung der Quellung um den Faktor 1,2 bewirkt. Rasterkraftmikroskopische Untersuchungen (AFM) an diesen beiden Hydrogelen im getrockneten Zustand, haben gezeigt, dass nach dem Quellen, Kollabieren und Trocknen bei beiden Gelen Porenstrukturen sehr unterschiedlicher Ausmaße vorliegen.

Polymer properties measured by micromechanical cantilever technique

Surface stress changes induced by specific adsorption of molecules were investigated using a micromechanical cantilever sensor (MCS) device. 16 MCS are grouped within four separate wells. Each well can be addressed independently by different liquid enabling functionalization of MCS separately by flowing different solutions through each well and performing sensing and reference experiments simultaneously. In addition, each well contains a fixed reference mirror, which allows measuring the absolute bending of MCS. The effect of the flow rate on the MCS bending change was found to be dependent on the absolute bending value of MCS. In addition, the signal from the reference mirror can be used to follow refractive index changes upon mixing different solutions. Finite element simulation of solution exchange in wells was compared with experiment results. Both revealed that one solution can be exchanged by another one after a total volume of 200 µl has flown through. Using MCS, the adsorption of thiolated deoxyribonucleic acid (DNA) molecules and 6-mercapto-1-hexanol (MCH) on gold surfaces, and the DNA hybridization were performed. The nanomechanical response is in agreement with data reported by Fritz et al.1 Thus, the multiwell device is readily applicable for sensing of multiple chemical and biological recognition events in a single step. In this context controlled release and uptake of drugs are currently widely discussed. As a model system, we have used polystyrene (PS) spheres with diameters in the order of µm. The swelling behavior of individual PS spheres in toluene vapor was studied via mass loading by means of micromechanical cantilever sensors. For 4–8% cross-linked PS a mass increase of 180% in saturated toluene vapor was measured. In addition, the diameter change in saturated toluene vapor was measured and the corresponding volume increase of 200% was calculated. The mass of the swollen PS sphere decreases with increasing exposure time to ultraviolet (UV) light. The swelling response is significantly different between the first and the second exposure to toluene vapor. This is attributed to the formation of a cross-linked shell at the surface of the PS spheres. Shape persistent parts were observed for locally UV irradiated PS spheres. These PS spheres were found to be fluorescent and cracks occur after exposure in toluene liquid. The diffusion time of dye molecules in PS spheres increases with increasing chemical cross-linking density. This concept of locally dissolving non cross-linked PS from the sphere was applied to fabricate donut structures on surfaces. Arrays of PS spheres were fabricated using spin coating. The donut structure was produced simply after liquid solvent rinsing. The complete cross-linking of PS spheres was found after long exposure time to UV. We found that stabilizers play a major role in the formation of the donut nanostructures.

Functional polymer coatings — My-Patterning and My-Analysis

In dieser Arbeit werden Strukturen beschrieben, die mit Polymeren auf Oberflächen erzeugt wurden. Die Anwendungen reichen von PMMA und PNIPAM Polymerbürsten, über die Restrukturierung von Polystyrol durch Lösemittel bis zu 3D-Strukturen, die aus PAH/ PSS Polyelektrolytmultischichten bestehen. Im ersten Teil werden Polymethylmethacrylat (PMMA) Bürsten in der ionischen Flüssigkeit 1-Butyl-3-Methylimidazolium Hexafluorophospat ([Bmim][PF6]) durch kontrollierte radikalische Polymerisation (ATRP) hergestellt. Kinetische Untersuchungen zeigten ein lineares und dichtes Bürstenwachstum mit einer Wachstumsrate von 4600 g/mol pro nm. Die durchschnittliche Pfropfdichte betrug 0.36 µmol/m2. Als Anwendung wurden Mikrotropfen bestehend aus der ionischen Flüssigkeit, Dimethylformamid und dem ATRP-Katalysator benutzt, um in einer definierten Geometrie Polymerbürsten auf Silizium aufzubringen. Auf diese Weise lässt sich eine bis zu 13 nm dicke Beschichtung erzeugen. Dieses Konzept ist durch die Verdampfung des Monomers Methylmethacrylat (MMA) limitiert. Aus einem 1 µl großen Tropfen aus ionischer Flüssigkeit und MMA (1:1) verdampft MMA innerhalb von 100 s. Daher wurde das Monomer sequentiell zugegeben. Der zweite Teil konzentriert sich auf die Strukturierung von Oberflächen mit Hilfe einer neuen Methode: Tintendruck. Ein piezoelektrisch betriebenes „Drop-on-Demand“ Drucksystem wurde verwendet, um Polystyrol mit 0,4 nl Tropfen aus Toluol zu strukturieren. Die auf diese Art und Weise gebildeten Mikrokrater können Anwendung als Mikrolinsen finden. Die Brennweite der Mikrolinsen kann über die Anzahl an Tropfen, die für die Strukturierung verwendet werden, eingestellt werden. Theoretisch und experimentell wurde die Brennweite im Bereich von 4,5 mm bis 0,21 mm ermittelt. Der zweite Strukturierungsprozess nutzt die Polyelektrolyte Polyvinylamin-Hydrochlorid (PAH) und Polystyrolsulfonat (PSS), um 3D-Strukturen wie z.B. Linien, Schachbretter, Ringe, Stapel mit einer Schicht für Schicht Methode herzustellen. Die Schichtdicke für eine Doppelschicht (DS) liegt im Bereich von 0.6 bis 1.1 nm, wenn NaCl als Elektrolyt mit einer Konzentration von 0,5 mol/l eingesetzt wird. Die Breite der Strukturen beträgt im Mittel 230 µm. Der Prozess wurde erweitert, um Nanomechanische Cantilever Sensoren (NCS) zu beschichten. Auf einem Array bestehend aus acht Cantilevern wurden je zwei Cantilever mit fünf Doppelschichten PAH/ PSS und je zwei Cantilever mit zehn Doppelschichten PAH/ PSS schnell und reproduzierbar beschichtet. Die Massenänderung für die individuellen Cantilever war 0,55 ng für fünf Doppelschichten und 1,08 ng für zehn Doppelschichten. Der daraus resultierende Sensor wurde einer Umgebung mit definierter Luftfeuchtigkeit ausgesetzt. Die Cantilever verbiegen sich durch die Ausdehnung der Beschichtung, da Wasser in das Polymer diffundiert. Eine maximale Verbiegung von 442 nm bei 80% Luftfeuchtigkeit wurde für die mit zehn Doppelschichten beschichteten Cantilever gefunden. Dies entspricht einer Wasseraufnahme von 35%. Zusätzlich konnte aus den Verbiegungsdaten geschlossen werden, dass die Elastizität der Polyelektrolytmultischichten zunimmt, wenn das Polymer gequollen ist. Das thermische Verhalten in Wasser wurde im nächsten Teil an nanomechanischen Cantilever Sensoren, die mit Poly(N-isopropylacrylamid)bürsten (PNIPAM) und plasmapolymerisiertem N,N-Diethylacrylamid beschichtet waren, untersucht. Die Verbiegung des Cantilevers zeigte zwei Bereiche: Bei Temperaturen kleiner der niedrigsten kritischen Temperatur (LCST) ist die Verbiegung durch die Dehydration der Polymerschicht dominiert und bei Temperaturen größer der niedrigsten kritischen Temperatur (LCST) reagiert der Cantilever Sensor überwiegend auf Relaxationsprozesse innerhalb der kollabierten Polymerschicht. Es wurde gefunden, dass das Minimum in der differentiellen Verbiegung mit der niedrigsten kritischen Temperatur von 32°C und 44°C der ausgewählten Polymeren übereinstimmt. Im letzten Teil der Arbeit wurden µ-Reflektivitäts- und µ-GISAXS Experimente eingeführt als neue Methoden, um mikrostrukturierte Proben wie NCS oder PEM Linien mit Röntgenstreuung zu untersuchen. Die Dicke von jedem individuell mit PMMA Bürsten beschichtetem NCS ist im Bereich von 32,9 bis 35,2 nm, was mit Hilfe von µ-Reflektivitätsmessungen bestimmt wurde. Dieses Ergebnis kann mit abbildender Ellipsometrie als komplementäre Methode mit einer maximalen Abweichung von 7% bestätigt werden. Als zweites Beispiel wurde eine gedruckte Polyelektrolytmultischicht aus PAH/PSS untersucht. Die Herstellungsprozedur wurde so modifiziert, dass Goldnanopartikel in die Schichtstruktur eingebracht wurden. Durch Auswertung eines µ-GISAXS Experiments konnte der Einbau der Partikel identifiziert werden. Durch eine Anpassung mit einem Unified Fit Modell wurde herausgefunden, dass die Partikel nicht agglomeriert sind und von einer Polymermatrix umgeben sind.

Stress – structure correlations in grafted polymer films

In der vorliegenden Arbeit wurden experimentelle Untersuchungen zu gepfropften Polymerfilmen durchgeführt. Dabei wurden endgepfropfte poly-methyl-methacrylate (PMMA) Bürsten hergestellt durch „grafting from“ Methoden und polystyrol (PS)/ poly-vinyl-methyl-ether (PVME) Polymerfilme gepfropft auf UV sensitiven Oberflächen untersucht. Zur Strukturuntersuchung wurden die hergestellten Systeme wurden mit Rasterkraftmikroskopie (engl.: Surface Probe Microscopy, SPM), Röntgen - und Neutronenreflektivitätsmessungen, sowie mit Röntgenstreuung unter streifenden Einfall (engl.: Grazing Incidence Small Angle X-Ray Scattering, GISAXS) untersucht. rnEs wurde gezeigt, dass ein aus der Transmissionsstreuung bekanntes Model auch für auch für die GISAXS Analyse polydisperser Polymerdomänen und Kolloidsysteme verwendet werden kann. Der maximale Fehler durch die gemachten Näherungen wurde auf < 20% abgeschätzt.rnErgebnisse aus der Strukturanalyse wurden mit mechanischen Filmeigenschaften verknüpft. Dazu wurden mechanische Spannungsexperimente durchgeführt. Hierzu wurden die zu untersuchenden Filme selektiv auf einzelne Mikro-Federbalken-Sensoren (engl.: Micro Cantilever Sensor, MCS) der MCS Arrays aufgebracht. Dies wurde durch Maskierungstechniken und Mikro-Kontaktdrucken bewerkstelligt. rnPhasenübergansexperimente der gepfropften PS/PVME Filme haben gezeigt, dass die Möglichkeit einer Polymer/Polymer Phasenseparation stark von Propfpunktdichte der gebundenen Polymerketten mit der Oberfläche abhängt. PS/PVME Filmsysteme mit hohen Pfropfpunktdichten zeigten keinen Phasenübergang. Bei niedrig gepfropften Filmsystemen waren hingegen Polymer/Polymer Phasenseparationen zu beobachten. Es wurde geschlussfolgert, dass die gepfropften Polymersysteme einen hinreichenden Grad an entropischen Freiheitsgraden benötigen um eine Phasenseparation zu zeigen. Mechanische Spannungsexperimente haben dabei das Verstehen der Phasenseparationsmechanismen möglich gemacht.rnAus Quellexperimenten dichtgepfropfter PMMA Bürsten, wurden Lösungsmittel-Polymer Wechselwirkungsparameter (-Parameter) bestimmt. Dabei wurde festgestellt, dass sich die erhaltenen Parameter aufgrund von Filmbenetzung und entropischen Effekten maßgeblich von den errechneten Bulkwerten unterscheiden. Weiterhin wurden nicht reversible Kettenverschlaufungseffekt beobachtet.