Electrical and Mechanical Properties of Post-annealed SiC(x)N(y) Films

Amorphous SiC(x)N(y) films have been deposited on (100) Si substrates by RF magnetron sputtering of a SiC target in a variable nitrogen-argon atmosphere. The as-deposited films were submitted to thermal anneling in a furnace under argon atmosphere at 1000 degrees C for 1 hour. Composition and structure of unannealed and annealed samples were investigated by RBS and FTIR. To study the electrical characteristics of SiC(x)N(y) films, Metal-insulator-semiconductor (MIS) structures were fabricated. Elastic modulus and hardness of the films were determined by nanoindentation. The results of these studies showed that nitrogen content and thermal annealing affect the electrical, mechanical and structural properties of SiC(x)N(y) films.

Nitrogen doping of SiC thin films deposited by RF magnetron sputtering

Silicon carbide thin films (Si(x)C(y)) were deposited in a RF (13.56 MHz) magnetron sputtering system using a sintered SiC target (99.5% purity). In situ doping was achieved by introducing nitrogen into the electric discharge during the growth process of the films. The N(2)/Ar flow ratio was adjusted by varying the N(2) flow rate and maintaining constant the Ar flow rate. The structure, composition and bonds formed in the nitrogen-doped Si (x) C (y) thin films were investigated by X-ray diffraction (XRD), Rutherford backscattering spectroscopy (RBS), Raman spectroscopy and Fourier transform infrared spectrometry (FTIR) techniques. RBS results indicate that the carbon content in the film decreases as the N(2)/Ar flow ratio increases. Raman spectra clearly reveal that the deposited nitrogen-doped SiC films are amorphous and exhibited C-C bonds corresponding to D and G bands. After thermal annealing, the films present structural modifications that were identified by XRD, Raman and FTIR analyses.

Structural and morphological studies on SiOxNy thin films

In this work, the structure and morphology of silicon oxynitride films deposited by the PECVD technique were studied. The films were deposited under two different conditions: (a) SiOxNy with chemical compositions varying from SiO2 to Si3N4 via the control of a N2O + N-2 + SiH4 gas mixture, and (b) Si-rich SiOxNy films via the control of a N2O + SiH4 gas mixture. The analyses were performed using X-ray near edge spectroscopy (XANES) at the Si-K edge, transmission electron microscopy (TEM) and Rutherford backscattering spectroscopy (RBS). For samples with chemical composition varying from SiO2 to Si3N4, the diffraction patterns obtained by TEM exhibited changes with the chemical composition, in agreement with the XANES results. For silicon-rich silicon oxynitride samples, the formation of a-Si clusters was observed and the possibility of obtaining Si nanocrystals after annealing depending on the composition and temperature was realized. (C) 2007 Elsevier B.V. All rights reserved.

Tunable Bragg filter using silicon compound films

In this work, we present the simulation, fabrication and characterization of a tunable Bragg filter employing amorphous dielectric films deposited by plasma enhanced chemical vapor deposition technique on a crystalline silicon substrate. The optical device was built using conventional microelectronic processes and consisted of fifteen periodic intervals of Si3N4 layers separated by air with appropriated thickness and lengths to produce transmittance attenuation peaks in the visible region. For this, previous simulations were realized based in the optical parameters of the dielectric film, which were extracted from ellipsometry and profilometry techniques. For the characterization of the optical interferential filter, a 633 nm monochromatic light was injected on the filter, and then the transmitted output light was collected and conducted to a detector through an optical waveguide made also of amorphous dielectric layers. Afterwards, the optical filter was mounted on a Peltier thermoelectric device in order to control the temperature of the optical device. When the temperature of filter changes, a refractive index variation is originated in the dielectric film due to the thermo-optic effect, producing a shift of attenuation peak, which can be well predicted by numerical simulations. This characteristic allows this device to be used as a thermo-optic sensor. (C) 2007 Elsevier B.V. All rights reserved.

Ultra-thin films of alternating semi-interpenetrating layers of a conducting polymer with thermosetting phenolic resins for sensor application

In this work a new method for crosslinking ultra-thin films with potential applications in sensor systems is proposed. The films were produced by layer-by-layer (LbL) assembly using a conducting polymer, poly(o-ethoxyaniline) (POEA), alternated with a thermosetting resin, novolac-type phenolformaldehyde (PF), crosslinked by a simple thermal treatment. The PF resin served as both alternating and crosslinking agents. The films were characterized by Fourier transform infrared (FTIR) and ultraviolet-visible (UV-Vis) spectroscopy, thermogravimetry (TG), desorption, doping/dedoping cycling and electrical measurements. The results showed that film architecture and crosslinking degree can be controlled by the conditions used for film deposition (number of bilayers, polymer concentration, pH, and deposition time), and crosslinking time. Moreover, this approach offers several advantages such as fast curing time and low cost, indicating that these films can be used to produce sensors with improved stability.

Effects of mechanical properties, residual stress and indenter tip geometry on instrumented indentation data in thin films

In this work, an axisymmetric two-dimensional finite element model was developed to simulate instrumented indentation testing of thin ceramic films deposited onto hard steel substrates. The level of film residual stress (sigma(r)), the film elastic modulus (E) and the film work hardening exponent (n) were varied to analyze their effects on indentation data. These numerical results were used to analyze experimental data that were obtained with titanium nitride coated specimens, in which the substrate bias applied during deposition was modified to obtain films with different levels of sigma(r). Good qualitative correlation was obtained when numerical and experimental results were compared, as long as all film properties are considered in the analyses, and not only sigma(r). The numerical analyses were also used to further understand the effect of sigma(r) on the mechanical properties calculated based on instrumented indentation data. In this case, the hardness values obtained based on real or calculated contact areas are similar only when sink-in occurs, i.e. with high n or high ratio VIE, where Y is the yield strength of the film. In an additional analysis, four ratios (R/h(max)) between indenter tip radius and maximum penetration depth were simulated to analyze the combined effects of R and sigma(r) on the indentation load-displacement curves. In this case, or did not significantly affect the load curve exponent, which was affected only by the indenter tip radius. On the other hand, the proportional curvature coefficient was significantly affected by sigma(r) and n. (C) 2010 Elsevier B.V. All rights reserved.

Numerical study of tensile tests conducted on systems with elastic-plastic films deposited onto elastic-plastic substrates

In this work, a series of two-dimensional plane-strain finite element analyses was conducted to further understand the stress distribution during tensile tests on coated systems. Besides the film and the substrate, the finite element model also considered a number of cracks perpendicular to the film/substrate interface. Different from analyses commonly found in the literature, the mechanical behavior of both film and substrate was considered elastic-perfectly plastic in part of the analyses. Together with the film yield stress and the number of film cracks, other variables that were considered were crack tip geometry, the distance between two consecutive cracks and the presence of an interlayer. The analysis was based on the normal stresses parallel to the loading axis (sigma(xx)), which are responsible for cohesive failures that are observed in the film during this type of test. Results indicated that some configurations studied in this work have significantly reduced the value of sigma(xx) at the film/substrate interface and close to the pre-defined crack tips. Furthermore, in all the cases studied the values of sigma(xx) were systematically larger at the film/substrate interface than at the film surface. (C) 2010 Elsevier B.V. All rights reserved.

Production and characterization of RF-sputtered PbO-GeO(2) amorphous thin films containing silver and gold nanoparticles

In the present work we report the characterization of PbO-GeO(2) films containing silver nanoparticles (NPs). Radio Frequency (RF) co-sputtering was used for deposition of amorphous films on glass substrates. Targets of 60PbO-40GeO(2) (in wt%) and bulk silver with purity of 99.99% were RF-sputtered using 3.5 m Torr of argon. The concentration of silver and gold NPs in the films was controlled varying the RF-power applied to the targets (40-50W for the PbO-GeO(2) target; 6-8 W for the metallic target). The films obtained were annealed in air at different temperatures and various periods of time. Absorption measurements have shown strong NPs surface plasmon bands. Different widths and peak wavelengths were observed, indicating that size, shape and distribution of the silver NPs are dependent on the deposition process parameters and on the annealing of the samples. X-Ray Fluorescence and Transmission Electron Microscopy were also used to characterize the samples. (C) 2010 Elsevier B.V. All rights reserved.

Influence of gold nanoparticles on optically stimulated effects in TeO(2)-ZnO and GeO(2)-PbO amorphous thin films

We have found photoinduced second harmonic generation at wavelength 1064 nm during bicolor Nd:YAG laser coherent treatment of TeO(2)-ZnO and GeO(2)-PbO amorphous films. The maximally achieved second order susceptibility was equal to about 1.02 pm/V. Correlation of the induced second order susceptibility with local sample heating and induced birefringence may indicate an occurrence of local phase transitions from amorphous glass-like phase to non-centrosymmetry metastable phases. (C) 2010 Elsevier B.V. All rights reserved.

Piezoresistive response of ITO films deposited at room temperature by magnetron sputtering

Indium tin oxide (ITO) thin films have been deposited on (100) Si substrates by RF magnetron sputtering from a compact target (90% In(2)O(3)-10% SnO(2) in weight) with 6 in. in diameter. In order to perform electromechanical characterizations of these films, strain gauges were fabricated. An experimental set-up based on bending beam theory was developed to determine the longitudinal piezoresistive coefficient (pi(1)) of the strain gauges fabricated. It has been confirmed that electrical resistance of the strain gauges decreases with load increases which results a negative gauge factor. A model based on the activation energy was used to explain the origin of this negative signal. The influence of the temperature on piezoresistive properties of ITO films was also evaluated.

Thin titanium oxide films deposited by e-beam evaporation with additional rapid thermal oxidation and annealing for ISFET applications

Titanium oxide (TiO(2)) has been extensively applied in the medical area due to its proved biocompatibility with human cells [1]. This work presents the characterization of titanium oxide thin films as a potential dielectric to be applied in ion sensitive field-effect transistors. The films were obtained by rapid thermal oxidation and annealing (at 300, 600, 960 and 1200 degrees C) of thin titanium films of different thicknesses (5 nm, 10 nm and 20 nm) deposited by e-beam evaporation on silicon wafers. These films were analyzed as-deposited and after annealing in forming gas for 25 min by Ellipsometry, Fourier Transform Infrared Spectroscopy (FTIR), Raman Spectroscopy (RAMAN), Atomic Force Microscopy (AFM), Rutherford Backscattering Spectroscopy (RBS) and Ti-K edge X-ray Absorption Near Edge Structure (XANES). Thin film thickness, roughness, surface grain sizes, refractive indexes and oxygen concentration depend on the oxidation and annealing temperature. Structural characterization showed mainly presence of the crystalline rutile phase, however, other oxides such Ti(2)O(3), an interfacial SiO(2) layer between the dielectric and the substrate and the anatase crystalline phase of TiO(2) films were also identified. Electrical characteristics were obtained by means of I-V and C-V measured curves of Al/Si/TiO(x)/Al capacitors. These curves showed that the films had high dielectric constants between 12 and 33, interface charge density of about 10(10)/cm(2) and leakage current density between 1 and 10(-4) A/cm(2). Field-effect transistors were fabricated in order to analyze I(D) x V(DS) and log I(D) x Bias curves. Early voltage value of -1629 V, R(OUT) value of 215 M Omega and slope of 100 mV/dec were determined for the 20 nm TiO(x) film thermally treated at 960 degrees C. (C) 2009 Elsevier B.V. All rights reserved.

Mechanical properties of pea starch films associated with xanthan gum and glycerol

The aim of this study was to evaluate the effect of the addition of xanthan gum and glycerol to the starch of green pea with high content of AM (cv. Utrillo) in the preparation of films and their physical characteristics. Filmogenic solution (FS) with different levels of pea starch (3, 4, and 5%), xanthan gum (0, 0.05, and 0.1%), and glycerol (glycerol-starch ratio of 1: 5 w/w) were studied. The FS was obtained by boiling (5 min), followed by autoclaving for 1 h at 120 degrees C. The films were prepared by casting. Films prepared only with pea starch were mechanically resistant when compared to other films, prepared with corn, cassava, rice, and even other pea cultivars (yellow, commercial). The tensile strength of these films is comparable to synthetic films prepared with high-density polyethylene and linear low-density polyethylene. However, they are films of low elasticity when compared to other films, such as rice starch films, and especially when compared to polyethylene films. The increased concentration of starch in the solution increased the puncture force. The increased concentration of glycerol slightly decreased the film crystallinity and interfered in the mechanical properties of the films, causing reduction of the maximum values of tensile strength, strain at break, and puncture force. The plasticizer also caused an increase of elongation at break. Xanthan gum was important to formation of films; however, it did not affect their mechanical properties.

Use of diamond-like carbon with tungsten (W-DLC) films as biocompatible material

Diamond-like carbon (DLC), also known as amorphous hydrogenated carbon (a-C:H), are a class of materials with excellent mechanical, tribological and biological properties. When the DLC films are enhanced with other elements, all of these properties can be changed within a certain range. In this work, reactive magnetron sputtering was used to deposit W-DLC (hydrogenated tungsten carbide) films on Ti6A14V (implant material). Many films were made using pure tungsten (99.99%) target and different plasmas processes, with different ratio among argon and methane. It was possible to change the films composition (from pure amorphous carbon to carbon enhanced with tungsten) according to ratio of argon and methane plasma. Between all films processed, the carbon films enhanced with tungsten showed good results in the ""in vitro"" cytotoxicity testing. Raman spectroscopy was used to analyze the chemical bonds kinds and the chemical bonds quantities. The Rutherford Back Scattering (RBS) was used to analyze the films compositions. The chemical inertness was analyzed by scanning voltametry. W-DLC thin films obtained in these processes have low roughness, high chemical resistance, good adhesion and show a high biocompatibility, when compared with common DLC thin films. Hence we have concluded that the tungsten concentrations in the DLC films make an important role to improve the properties of the DLC layers. (C) 2007 Elsevier B.V. All rights reserved.

Effect of the Maillard reaction on properties of casein and casein films

The use of biodegradable natural polymers has increased due to the over-solid packaging waste. In this study, a chemical modification of the casein molecule was performed by Maillard reaction, and the modified polymer was evaluated by polyacrylamide gel electrophoresis (PAGE), thermogravimetry/derivative thermogravimetry (TG/DTG), FT-IR, and (1)H-NMR spectroscopy. Subsequently, films based on the modified casein were obtained and characterized by mechanical analysis, water vapor transmission, and erosion behavior. The PAGE results suggested an increase of molecular mass of the modified polymer, and FT-IR spectroscopy data indicated inclusion of C-OH groups into this molecule. The TG/DTG curves of modified casein presented a different thermal decomposition profile compared to the individual compounds. Mechanical tests showed that the chemical modification of the casein molecules provided higher elongation rates (45.5%) to the films, suggesting higher plasticity, than the original molecules (13.4%). The modified casein films presented higher permeability (0.505 +/- A 0.006 mu g/h mm(3)) than the original polymer (0.387 +/- A 0.006 mu g/h mm(3)) films at 90% relative humidity (RH). In pH 1.2, modified casein films presented higher erosion rates (32.690 +/- A 0.692%) than casein films (19.910 +/- A 2.083%) after 8 h, suggesting an increased sensibility for erosion of the modified casein films in acid environment. In water (pH 7.0), the films erosion profiles were similar. Those findings indicate that the modification of molecule by Maillard reaction provided films more plastic, hydrophilic, and sensitive to erosion in acid environment, suggesting that a new polymer with changed properties was founded.

Optical properties of metallic films for vertical-cavity optoelectronic devices

We present models for the optical functions of 11 metals used as mirrors and contacts in optoelectronic and optical devices: noble metals (Ag, Au, Cu), aluminum, beryllium, and transition metals (Cr, Ni, Pd, Pt, Ti, W). We used two simple phenomenological models, the Lorentz-Drude (LD) and the Brendel-Bormann (BB), to interpret both the free-electron and the interband parts of the dielectric response of metals in a wide spectral range from 0.1 to 6 eV. Our results show that the BE model was needed to describe appropriately the interband absorption in noble metals, while for Al, Be, and the transition metals both models exhibit good agreement with the experimental data. A comparison with measurements on surface normal structures confirmed that the reflectance and the phase change on reflection from semiconductor-metal interfaces (including the case of metallic multilayers) can be accurately described by use of the proposed models for the optical functions of metallic films and the matrix method for multilayer calculations. (C) 1998 Optical Society of America.