Void formation and failure in InGaN/AlGaN double heterostructures

Condensed clusters of point defects within an InGaN/AlGaN double heterostructure grown by metal-organic vapor phase epitaxy on sapphire substrate have been observed using transmission electron microscopy. The existence of voids results in failure of the heterostructure in electroluminescence. The voids are 50-100 nm in diameter and are distributed inhomogeneously within In0.25Ga0.75N/AlGaN active layers. The density of the voids was measured as 10(15) cm(-3), which corresponds to a density of dangling bonds of 10(20) cm(-3). These dangling bonds may fully deplete free carriers in this double heterostructure and result in the heterostructure having high resistivity as confirmed by electrical measurement. (C) 2003 Elsevier Science B.V. All rights reserved.

X-ray diffraction analysis of MOCVD grown GaN buffer layers on GaAs(001) substrates

In order to understand the growth feature of GaN on GaAs (0 0 1) substrates grown by metalorganic chemical vapor deposition (MOCVD), the crystallinity of GaN buffer layers with different thicknesses was investigated by using double crystal X-ray diffraction (DCXRD) measurements. The XRD results showed that the buffer layers consist of predominantly hexagonal GaN (h-GaN) and its content increases with buffer layer thickness. The nominal GaN (111) reflections with chi at 54.74degrees can be detected easily, while (0 0 2) reflections are rather weak. The integrated intensity of reflections from (111) planes is 4-6 times that of (0 0 2) reflections. Possible explanations are presented. (C) 2003 Elsevier Science B.V. All rights reserved.

Structure characteristics of InGaN quantum dots fabricated by passivation and low temperature method

Passivation and low temperature method was carried out to grow InGaN/GaN quantum dots (QDs). Atomic force microscope observations were performed to investigate the evolution of the surface morphology of the InGaN QDs superlattices with increasing the superlattices layer number. The result shows that the size of the QDs increases with increasing superlattices layer number. The QDs height and diameter increase from 18 and 50 run for the monolayer InGaN QDs to 37 and 80 urn for the four-stacked InGaN QDs layers, respectively. This result is considered to be due to the stress field from the sub-layer dots. (C) 2003 Elsevier Science B.V. All rights reserved.

Realization of quantum cascade laser operating at room temperature

X-ray diffraction, as an effective probe and simple method, is used to ascertain the precise control of the epilayer thickness and composition. Intersubband absorption from the whole structure of the QC laser is used to monitor the wavelength of the QC laser and the material quality. Path for growth of high-quality InP-based InGaAs/InAlAs quantum cascade laser material is realized. The absorption between two quantized energy levels is achieved at similar to4.7 mum. Room temperature laser action is achieved at lambda approximate to 5.1 - 5.2 mum. For some devices, if the peak output power is kept at 2 mW, quasi-continuous wave operation at room temperature can persist for more than I It. (C) 2002 Elsevier Science B.V. All rights reserved.

The effect of inserting strain-compensated GaNAs layers on the luminescence properties of GaInNAs/GaAs quantum well

Photoluminescence (PL) properties of GaInNAs/GaAs quantum wells (QWs) with strain-compensated GaNAs layers grown by molecular beam epitaxy are investigated. The temperature-dependent PL spectra of GaInNAs/GaAs QW with and without GaNAs layers are compared and carefully studied. It is shown that the introduction of GaNAs layers between well and barrier can effectively extend the emission wavelength, mainly due to the reduction of the barrier potential. The PL peak position up to 1.41 mum is observed at the room temperature. After adding the GaNAs layers into QW structures, there is no essential deterioration of luminescence efficiency. N-induced localization states are also not remarkably influenced. It implies that with optimized growth condition, high-quality GaInNAs/GaAs QWs with strain-compensated GaNAs layers can be achieved. (C) 2003 Elsevier Science B.V. All rights reserved.

Method for measurement of lattice parameter of cubic GaN layers on GaAs (001)

An extended technique derived from triple-axis diffraction setup was proposed to measure lattice parameters of cubic GaN(c-GaN) films. The fully relaxed lattice parameters of c-GaN are determined to be 4.5036+0.0004 Angstrom, which is closer to the values of a hypothetical perfect crystal. The speculated zero setting correction (Deltatheta) is very slight and within the range of the accuracy of measurement. Additionally, we applied this method to analyze strain of four different kinds of c-GaN samples. It is found that in-plane strain caused by large lattice mismatch and thermal expansion coefficients mismatch directly influence the epilayer growth at high temperatures, indicating that the relaxation of tensile strain after thermal annealing helps to improve the crystalline quality of c-GaN films and optical properties. (C) 2003 Elsevier Science B.V. All rights reserved.

High-resolution X-ray diffraction analysis of the Bragg peak integrated intensity in highly mismatched III-N epilayers

A new method of measuring the thickness of GaN epilayers on sapphire (0 0 0 1) substrates by using double crystal X-ray diffraction was proposed. The ratio of the integrated intensity between the GaN epilayer and the sapphire substrate showed a linear relationship with the GaN epilayer thickness up to 2.12 mum. It is practical and convenient to measure the GaN epilayer thickness using this ratio, and can mostly eliminate the effect of the reabsorption, the extinction and other scattering factors of the GaN epilayers. (C) 2003 Elsevier Science B.V. All rights reserved.

Influence of semi-insulating InP substrates on InAlAs epilayers grown by molecular beam epitaxy

Tensile-strained InAlAs layers have been grown by solid-source molecular beam epitaxy on as-grown Fe-doped semi-insulating (SI) InP substrates and undoped SI InP substrates obtained by annealing undoped conductive InP wafers (wafer-annealed InP). The effect of the two substrates on InAlAs epilayers and InAlAs/InP type II heterostructures has been studied by using a variety of characterization techniques. Our calculation data proved that the out-diffusion of Fe atoms in InP substrate may not take place due to their low diffusion, coefficient. Double-crystal X-ray diffraction measurements show that the lattice mismatch between the InAlAs layers and the two substrates is different, which is originated from their different Fe concentrations. Furthermore, photoluminescence results indicate that the type II heterostructure grown on the wafer-annealed InP substrate exhibits better optical and interface properties than that grown on the as-grown Fe-doped substrate. We have also given a physically coherent explanation on the basis of these investigations. (C) 2003 Elsevier Science B.V. All rights reserved.

The effects of rapid thermal annealing on the optical properties of Zn1-xMnxSe epilayer grown by MOCVD on GaAs substrate

Zn1-xMnxSe thin films with different Mn compositions are grown by metal-organic chemical vapor deposition on GaAs substrate. Good crystallinity of sample is evidenced by X-ray diffraction and rocking-curve measurements. Photoluminescence (PL) properties were carefully studied. A dominant PL peak close to the band edge is observed at low temperature for samples with higher Mn concentration. The temperature-dependent PL and time-resolved photoluminescence show that this emission peak is associated with the recombination of exciton bound to Mn-induced impurity bound states. It is found that rapid thermal annealing can induce reorganization of Mn composition in alloys and significantly reduce the density of impurity induced by Mn incorporation and improve the intrinsic interband transition. (C) 2002 Elsevier Science B.V. All rights reserved.

Structural and optical properties of InAlGaN films grown directly on low-temperature buffer layer with (0001)sapphire substrate

Quaternary InAlGaN film has been grown directly on top of low-temperature-deposited GaN buffer layer by low-pressure metalorganic vapor phase epitaxy. High-resolution X-ray diffraction and photoluminescence (PL) results show that the film has good crystal quality and optical property. Temperature-dependent PL and time-resolved PL (TRPL) have been employed to study the carriers recombination dynamics in the film. The TRPL signals can be well fitted as a stretched exponential function exp[-(t/tau)(beta)] from 14 to 250 K, indicating that the emission is attributed to the radiative recombination of excitons localized in disorder quantum nanostructures such as quantum disks originating from indium (In) clusters or In composition fluctuation. The cross-sectional high-resolution electron microscopy measurement further proves that there exist the disorder quantum nanostructures in the quaternary. By investigating the dependence of the exponential parameter beta on the temperature, it is shown that the multiple trapping-detrapping mechanism dominates the diffusion among the localized states. The localized states are considered to have two-dimensional density of states (DOS) at 250 K, since radiative recombination lifetime tau(r) increases linearly with increasing temperature. (C) 2002 Elsevier Science B.V. All rights reserved.

Fabrication of novel double-hetero-epitaxial SOT structure Si/gamma-Al2O3/Si

In this paper, we report the fabrication of Si-based double-hetero-epitaxial silicon on insulator (SOI) structure Si/gamma-Al2O3/Si. Firstly, single crystalline gamma-Al2O3(100) insulator films were grown epitaxially on Si(100) using the sources of TMA (Al(CH3)(3)) and O-2 by very low-pressure chemical vapor deposition. Afterwards, Si(100) epitaxial films were grown on gamma-Al2O3 (100)/Si(100) epi-substrates using a chemical vapor deposition method similar to the silicon on sapphire epitaxial growth. The Si/gamma-Al2O3/Si SOL materials are characterized in detail by reflect high-energy electron diffraction, X-ray diffraction and Auger energy spectrum (AES) techniques. The insulator layer of gamma-Al2O3 has an excellent dielectric property. The leakage current is less than 1 x 10(-10) A/cm(2) when the electric field is below 1.3 MV/ cm. The Si film grown on gamma-Al2O3/Si epi-substrates was single crystalline. Meanwhile, the AES depth profile of the SOL structure shows that the composition of gamma-Al2O3 film is uniform, and the carbon contamination is not observed. Additionally, the gamma-Al2O3/Si epi-substrates are suitable candidates as a platform for a variety of active layers such as GaN, SiC and GeSi. It shows a bright future for microelectronic and optical electronics applications. (C) 2002 Elsevier Science B.V. All rights reserved.

Silicon nanowires grown on a pre-annealed Si substrate

Polycrystalline Si nanowires (poly SiNWS) were successfully synthesized by plasma-enhanced chemical vapor deposition (PECVD) at 440degreesC using silane as the Si source and Au as the catalyst. The diameters of Si nanowires range from 15 to 100nm. The growth process indicates that to fabricate SiNWS by PECVD, pre-annealing at high temperature is necessary. A few interesting nanowires with Au nanoclusters uniformly distributed in the body of the wire were also produced by this technique. (C) 2002 Elsevier Science B.V. All rights reserved.

Structure and optical properties of upper In(Ga)As quantum dots on a different seed layer with a thin GaAs spacer layer

The structure and optical properties of In(Ga)As grown with the introduction of InGaAlAs or InAlAs seed dots layers are investigated. The area density and size homogeneity of the upper InGaAs dots are efficiently improved with the introduction of a layer of high-density buried dots. When the GaAs spacer layer is too thin to cover the seed dots, the upper dots exhibit the characterization of a quantum well. By analyzing the growth dynamics, we refer to it as an empty-core structure dot. (C) 2002 Elsevier Science B.V. All rights reserved.

Structural characterization of epitaxial lateral overgrown GaN on patterned GaN/GaAs(001) substrates

Epitaxial lateral overgrown (ELO) cubic GaN (c-GaN) on SiO2 patterned GaN/GaAs(0 0 1) substrates by metalorganic vapor phase epitaxy was investigated using transmission electron microscopy and X-ray diffraction (XRD) measurements. The density of stacking faults (SFs) in ELO c-GaN was similar to6 x 10(8) cm(-2), while that in underlying GaN template was similar to5 x 10(9) cm(-2). XRD measurements showed that the full-width at half-maximum of c-GaN (0 0 2) rocking curve decreased from 33 to 17.8 arcmin, indicating the improved crystalline quality of ELO c-GaN. The mechanism of SF reduction in ELO c-GaN was also discussed. (C) 2002 Elsevier Science B.V. All rights reserved.

Structural properties and Raman measurement of AlN films grown on Si (111) by NH3-GSMBE

Epitaxial growth of AlN has been performed by molecular beam epitaxy (MBE) with ammonia. The structural properties of materials were studied by cross-sectional transmission electron microscopy (TEM), X-ray diffraction (XRD), and atomic force microscopy (AFM). XRD and TEM diffraction pattern confirm the AlN is single crystalline 2H-polytype with the epitaxial relationship of (0001)AlNparallel to(111)Si, [11 (2) over bar0](AlN)parallel to[110](Si), [10 (1) over bar0](AlN)parallel to[11 (2) over bar](Si). Micro-Raman scattering measurement shows that the E-2 (high) and A(1) (LO) phonon mode shift 9 cm(-1) toward the low frequency, which shows the existence of large tensile strain in the AlN films. Furthermore, the appearance of forbidden A, (TO) mode and its anomalous shift toward high frequency was found and explained. (C) 2002 Elsevier Science B.V. All rights reserved.