Scanning Electron Microscopy Studies on Tear and Wear Failure of Short Kevlar Fiber-Thermoplastic- Polyurethane Composite

Tear and wear properties of short kevlar fiber, thermoplastic polcurethane (TPU) composite with respect to fiber loading-and fiber onentation has been studied and the fracture surfaces were examined under scanning electron microscope (SEM). Tear strength first decreased up to 20 phr fiber loading and then gradually increased with increasing fiber loading. Anisotropy in tear strength was evident beyond a fiber loading of 20 phr. Tear fracture surface of unfilled TPU showed sinusoidal folding characteristics of high strength matrix. At low fiber loading the tear failure was mainly due to fibermatrix failure whereas at higher fiber loading the failure occurred by fiber breakage. Abrasion loss shows a continuous rise with increasing fiber loading, the loss in the transverse orientation of fibers being higher than that in the longitudinal orientation. The abraded surface showed lone cracks and ridges parallel to the direction of abrasion indicating an abrasive wear mechanism. In the presence of fber the abrasion loss was mainly due to fiber low.

Laser induced surface damage, thermal transport and microhardness studies on certain organic and semiorganic nonlinear optical crystals

N-alkyl-2,6-dimethyl-4(1H)-pyridinones, salts of 4-dimethylaminopyridine and 2-amino-5-nitropyridine are considered to be potential candidates for nonlinear optical (NLO) applications, in particular for the generation of blue-green laser radiation. Single crystals were grown following the slow evaporation technique at constant temperature. Single-shot laserinduced surface damage thresholds in the range 3–10 GW/cm2 were measured using a 18 ns Q-switched Nd:YAG laser. The surface morphologies of the damaged crystals were examined under an optical microscope and the nature of damage identified. The Vicker’s microhardness was determined at a load of 98.07 mN. The thermal transport properties, thermal diffusivity (α), thermal effusivity (e), thermal conductivity (K) and heat capacity (Cp), of the grown crystals were measured by an improved photopyroelectric technique at room temperature. All the results are presented and discussed.

Femtosecond imaging-mode laser-induced breakdown spectroscopy

Many nonlinear optical microscopy techniques based on the high-intensity nonlinear phenomena were developed recent years. A new technique based on the minimal-invasive in-situ analysis of the specific bound elements in biological samples is described in the present work. The imaging-mode Laser-Induced Breakdown Spectroscopy (LIBS) is proposed as a combination of LIBS, femtosecond laser material processing and microscopy. The Calcium distribution in the peripheral cell wall of the sunflower seedling (Helianthus Annuus L.) stem is studied as a first application of the imaging-mode LIBS. At first, several nonlinear optical microscopy techniques are overviewed. The spatial resolution of the imaging-mode LIBS microscope is discussed basing on the Point-Spread Function (PSF) concept. The primary processes of the Laser-Induced Breakdown (LIB) are overviewed. We consider ionization, breakdown, plasma formation and ablation processes. Water with defined Calcium salt concentration is used as a model of the biological object in the preliminary experiments. The transient LIB spectra are measured and analysed for both nanosecond and femtosecond laser excitation. The experiment on the local Calcium concentration measurements in the peripheral cell wall of the sunflower seedling stem employing nanosecond LIBS shows, that nanosecond laser is not a suitable excitation source for the biological applications. In case of the nanosecond laser the ablation craters have random shape and depth over 20 µm. The analysis of the femtosecond laser ablation craters shows the reproducible circle form. At 3.5 µJ laser pulse energy the diameter of the crater is 4 µm and depth 140 nm for single laser pulse, which results in 1 femtoliter analytical volume. The experimental result of the 2 dimensional and surface sectioning of the bound Calcium concentrations is presented in the work.

Development of hybrid UV VCSEL with organic active material and dielectric DBR mirrors for medical, sensoric and data storage applications

Lasers play an important role for medical, sensoric and data storage devices. This thesis is focused on design, technology development, fabrication and characterization of hybrid ultraviolet Vertical-Cavity Surface-Emitting Lasers (UV VCSEL) with organic laser-active material and inorganic distributed Bragg reflectors (DBR). Multilayer structures with different layer thicknesses, refractive indices and absorption coefficients of the inorganic materials were studied using theoretical model calculations. During the simulations the structure parameters such as materials and thicknesses have been varied. This procedure was repeated several times during the design optimization process including also the feedback from technology and characterization. Two types of VCSEL devices were investigated. The first is an index coupled structure consisting of bottom and top DBR dielectric mirrors. In the space in between them is the cavity, which includes active region and defines the spectral gain profile. In this configuration the maximum electrical field is concentrated in the cavity and can destroy the chemical structure of the active material. The second type of laser is a so called complex coupled VCSEL. In this structure the active material is placed not only in the cavity but also in parts of the DBR structure. The simulations show that such a distribution of the active material reduces the required pumping power for reaching lasing threshold. High efficiency is achieved by substituting the dielectric material with high refractive index for the periods closer to the cavity. The inorganic materials for the DBR mirrors have been deposited by Plasma- Enhanced Chemical Vapor Deposition (PECVD) and Dual Ion Beam Sputtering (DIBS) machines. Extended optimizations of the technological processes have been performed. All the processes are carried out in a clean room Class 1 and Class 10000. The optical properties and the thicknesses of the layers are measured in-situ by spectroscopic ellipsometry and spectroscopic reflectometry. The surface roughness is analyzed by atomic force microscopy (AFM) and images of the devices are taken with scanning electron microscope (SEM). The silicon dioxide (SiO2) and silicon nitride (Si3N4) layers deposited by the PECVD machine show defects of the material structure and have higher absorption in the ultra violet range compared to ion beam deposition (IBD). This results in low reflectivity of the DBR mirrors and also reduces the optical properties of the VCSEL devices. However PECVD has the advantage that the stress in the layers can be tuned and compensated, in contrast to IBD at the moment. A sputtering machine Ionsys 1000 produced by Roth&Rau company, is used for the deposition of silicon dioxide (SiO2), silicon nitride (Si3N4), aluminum oxide (Al2O3) and zirconium dioxide (ZrO2). The chamber is equipped with main (sputter) and assisted ion sources. The dielectric materials were optimized by introducing additional oxygen and nitrogen into the chamber. DBR mirrors with different material combinations were deposited. The measured optical properties of the fabricated multilayer structures show an excellent agreement with the results of theoretical model calculations. The layers deposited by puttering show high compressive stress. As an active region a novel organic material with spiro-linked molecules is used. Two different materials have been evaporated by utilizing a dye evaporation machine in the clean room of the department Makromolekulare Chemie und Molekulare Materialien (mmCmm). The Spiro-Octopus-1 organic material has a maximum emission at the wavelength λemission = 395 nm and the Spiro-Pphenal has a maximum emission at the wavelength λemission = 418 nm. Both of them have high refractive index and can be combined with low refractive index materials like silicon dioxide (SiO2). The sputtering method shows excellent optical quality of the deposited materials and high reflection of the multilayer structures. The bottom DBR mirrors for all VCSEL devices were deposited by the DIBS machine, whereas the top DBR mirror deposited either by PECVD or by combination of PECVD and DIBS. The fabricated VCSEL structures were optically pumped by nitrogen laser at wavelength λpumping = 337 nm. The emission was measured by spectrometer. A radiation of the VCSEL structure at wavelength 392 nm and 420 nm is observed.

Optimierung der laserinduzierten Plasmaspektroskopie an Metallen durch Femtosekunden-Doppelpulse für die Entwicklung eines hochauflösenden 3D-Rasterabbildungsverfahrens

Die laserinduzierte Plasmaspektroskopie (LIPS) ist eine spektrochemische Elementanalyse zur Bestimmung der atomaren Zusammensetzung einer beliebigen Probe. Für die Analyse ist keine spezielle Probenpräparation nötig und kann unter atmosphärischen Bedingungen an Proben in jedem Aggregatzustand durchgeführt werden. Femtosekunden Laserpulse bieten die Vorteile einer präzisen Ablation mit geringem thermischen Schaden sowie einer hohen Reproduzierbarkeit. Damit ist fs-LIPS ein vielversprechendes Werkzeug für die Mikroanalyse technischer Proben, insbesondere zur Untersuchung ihres Ermüdungsverhaltens. Dabei ist interessant, wie sich die initiierten Mikrorisse innerhalb der materialspezifschen Struktur ausbreiten. In der vorliegenden Arbeit sollte daher ein schnelles und einfach zu handhabendes 3D-Rasterabbildungsverfahren zur Untersuchung der Rissausbreitung in TiAl, einer neuen Legierungsklasse, entwickelt werden. Dazu wurde fs-LIPS (30 fs, 785 nm) mit einem modifizierten Mikroskopaufbau (Objektiv: 50x/NA 0.5) kombiniert, welcher eine präzise, automatisierte Probenpositionierung ermöglicht. Spektrochemische Sensitivität und räumliches Auflösungsvermögen wurden in energieabhängigen Einzel- und Multipulsexperimenten untersucht. 10 Laserpulse pro Position mit einer Pulsenergie von je 100 nJ führten in TiAl zum bestmöglichen Kompromiss aus hohem S/N-Verhältnis von 10:1 und kleinen Lochstrukturen mit inneren Durchmessern von 1.4 µm. Die für das Verfahren entscheidende laterale Auflösung, dem minimalen Lochabstand bei konstantem LIPS-Signal, beträgt mit den obigen Parametern 2 µm und ist die bislang höchste bekannte Auflösung einer auf fs-LIPS basierenden Mikro-/Mapping-Analyse im Fernfeld. Fs-LIPS Scans von Teststrukturen sowie Mikrorissen in TiAl demonstrieren eine spektrochemische Sensitivität von 3 %. Scans in Tiefenrichtung erzielen mit denselben Parametern eine axiale Auflösung von 1 µm. Um die spektrochemische Sensitivität von fs-LIPS zu erhöhen und ein besseres Verständnis für die physikalischen Prozesse während der Laserablation zu erhalten, wurde in Pump-Probe-Experimenten untersucht, in wieweit fs-Doppelpulse den laserinduzierten Abtrag sowie die Plasmaemission beeinflussen. Dazu wurden in einem Mach-Zehnder-Interferometer Pulsabstände von 100 fs bis 2 ns realisiert, Gesamtenergie und Intensitätsverhältnis beider Pulse variiert sowie der Einfluss der Materialparameter untersucht. Sowohl das LIPS-Signal als auch die Lochstrukturen zeigen eine Abhängigkeit von der Verzögerungszeit. Diese wurden in vier verschiedene Regimes eingeteilt und den physikalischen Prozessen während der Laserablation zugeordnet: Die Thermalisierung des Elektronensystems für Pulsabstände unter 1 ps, Schmelzprozesse zwischen 1 und 10 ps, der Beginn des Abtrags nach mehreren 10 ps und die Expansion der Plasmawolke nach über 100 ps. Dabei wird das LIPS-Signal effizient verstärkt und bei 800 ps maximal. Die Lochdurchmesser ändern sich als Funktion des Pulsabstands wenig im Vergleich zur Tiefe. Die gesamte Abtragsrate variiert um maximal 50 %, während sich das LIPS-Signal vervielfacht: Für Ti und TiAl typischerweise um das Dreifache, für Al um das 10-fache. Die gemessenen Transienten zeigen eine hohe Reproduzierbarkeit, jedoch kaum eine Energie- bzw. materialspezifische Abhängigkeit. Mit diesen Ergebnissen wurde eine gezielte Optimierung der DP-LIPS-Parameter an Al durchgeführt: Bei einem Pulsabstand von 800 ps und einer Gesamtenergie von 65 nJ (vierfach über der Ablationsschwelle) wurde eine 40-fache Signalerhöhung bei geringerem Rauschen erzielt. Die Lochdurchmesser vergrößerten sich dabei um 44 % auf (650±150) nm, die Lochtiefe um das Doppelte auf (100±15) nm. Damit war es möglich, die spektrochemische Sensitivität von fs-LIPS zu erhöhen und gleichzeitig die hohe räumliche Auflösung aufrecht zu erhalten.

Growth and Characterization of LiCoO₂ Thin Films for Microbatteries

LiCoO₂thin films have been grown by pulsed laser deposition on stainless steel and SiO₂/Si substrates. The film deposited at 600°C in an oxygen partial pressure of 100mTorr shows an excellent crystallinity, stoichiometry and no impurity phase present. Microstructure and surface morphology of thin films were examined using a scanning electron microscope. The electrochemical properties of the thin films were studied with cyclic voltammetry and galvanostatic charge-discharge techniques in the potential range 3.0-4.2 V. The initial discharge capacity of the LiCoO2 thin films deposited on the stainless steel and SiO₂/Si substrates reached 23 and 27 µAh/cm², respectively.

Laser stripe peak detector for 3D scanners: a FIR filter approach

The accuracy of a 3D reconstruction using laser scanners is significantly determined by the detection of the laser stripe. Since the energy pattern of such a stripe corresponds to a Gaussian profile, it makes sense to detect the point of maximum light intensity (or peak) by computing the zero-crossing point of the first derivative of such Gaussian profile. However, because noise is present in every physical process, such as electronic image formation, it is not sensitive to perform the derivative of the image of the stripe in almost any situation, unless a previous filtering stage is done. Considering that stripe scanning is an inherently row-parallel process, every row of a given image must be processed independently in order to compute its corresponding peak position in the row. This paper reports on the use of digital filtering techniques in order to cope with the scanning of different surfaces with different optical properties and different noise levels, leading to the proposal of a more accurate numerical peak detector, even at very low signal-to-noise ratios

Macrodisco y glaucoma en individuos estudiados con tomografía óptica coherente

Introducción: El glaucoma representa la tercera causa de ceguera a nivel mundial y un diagnóstico oportuno requiere evaluar la excavación del nervio óptico que está relacionada con el área del mismo. Existen reportes de áreas grandes (macrodiscos) que pueden ser protectoras, mientras otros las asocian a susceptibilidad para glaucoma. Objetivo: Establecer si existe asociación entre macrodisco y glaucoma en individuos estudiados con Tomografía Optica Coherente (OCT ) en la Fundación Oftalmológica Nacional. Métodos: Estudio transversal de asociación que incluyó 25 ojos con glaucoma primario de ángulo abierto y 74 ojos sanos. A cada individuo se realizó examen oftalmológico, campo visual computarizado y OCT de nervio óptico. Se compararon por grupos áreas de disco óptico y número de macrodiscos, definidos según Jonas como un área de la media más dos desviaciones estándar y según Adabache como área ≥3.03 mm2 quien evaluó población Mexicana. Resultados: El área promedio de disco óptico fue 2,78 y 2,80 mm2 glaucoma Vs. sanos. De acuerdo al criterio de Jonas, se observó un macrodisco en el grupo sanos y según criterio de Adabache se encontraron ocho y veinticinco macrodiscos glaucoma Vs. sanos. (OR=0,92 IC95%=0.35 – 2.43). Discusión: No hubo diferencia significativa (P=0.870) en el área de disco entre los dos grupos y el porcentaje de macrodiscos para los dos grupos fue similar, aunque el bajo número de éstos no permitió concluir en términos estadísticos sobre la presencia de macrodisco y glaucoma.

Coloraciones histológicas vs microscopia electrónica de transmision para detección de Biopeliculas en pacientes con Rinosinusitis Crónica en el Hospital Universitario de la Samaritana en el año 2011

Objetivo: Determinar la concordancia entre microscopia de luz vs microscopia electrónica de transmisión para la detección de Biopeliculas en pacientes con Rinosinusitis Crónica Diseño: Estudio de concordancia. Materiales y Métodos: Analizamos 34 muestras de pacientes llevados a Cirugía Endoscópica Funcional por Rinosinusitis Crónica. Fueron procesadas para valoración mediante microscopia de luz usando Hematoxilina-Eosina, Gram, Acido Peryódico de Schiff, Giemsa y Microscopia Electrónica de Transmisión (MET). Resultados: No se identificaron Biopelícula en ninguna de las muestras analizadas bajo Microscopía Electrónica de Transmisión (MET), estos resultados son concordantes con los resultados obtenidos con las coloraciones histológicas Hematoxilina-Eosina (H-E), Gram, Giemsa y Acido Peryódico de Schiff (PAS), mostrando una concordancia absoluta con test de Kappa para resultados negativos del 100%. Conclusión: Existe una alta concordancia entre los hallazgos observados entre la MET y la Microscopia de luz para los resultados negativos

Problems with determining the particle size distribution of chalk soil and some of their implications

Particle size distribution (psd) is one of the most important features of the soil because it affects many of its other properties, and it determines how soil should be managed. To understand the properties of chalk soil, psd analyses should be based on the original material (including carbonates), and not just the acid-resistant fraction. Laser-based methods rather than traditional sedimentation methods are being used increasingly to determine particle size to reduce the cost of analysis. We give an overview of both approaches and the problems associated with them for analyzing the psd of chalk soil. In particular, we show that it is not appropriate to use the widely adopted 8 pm boundary between the clay and silt size fractions for samples determined by laser to estimate proportions of these size fractions that are equivalent to those based on sedimentation. We present data from field and national-scale surveys of soil derived from chalk in England. Results from both types of survey showed that laser methods tend to over-estimate the clay-size fraction compared to sedimentation for the 8 mu m clay/silt boundary, and we suggest reasons for this. For soil derived from chalk, either the sedimentation methods need to be modified or it would be more appropriate to use a 4 pm threshold as an interim solution for laser methods. Correlations between the proportions of sand- and clay-sized fractions, and other properties such as organic matter and volumetric water content, were the opposite of what one would expect for soil dominated by silicate minerals. For water content, this appeared to be due to the predominance of porous, chalk fragments in the sand-sized fraction rather than quartz grains, and the abundance of fine (<2 mu m) calcite crystals rather than phyllosilicates in the clay-sized fraction. This was confirmed by scanning electron microscope (SEM) analyses. "Of all the rocks with which 1 am acquainted, there is none whose formation seems to tax the ingenuity of theorists so severely, as the chalk, in whatever respect we may think fit to consider it". Thomas Allan, FRS Edinburgh 1823, Transactions of the Royal Society of Edinburgh. (C) 2009 Natural Environment Research Council (NERC) Published by Elsevier B.V. All rights reserved.

Immunohistochemical localization of inhibin/activin alpha, beta(A) and beta(B) subunits and follistatin in bovine oocytes during in vitro maturation and fertilization

The aim of this study was to evaluate the distribution of inhibin/activin alpha, beta(A) and beta(B) subunits and follistatin in immature oocytes and in matured oocytes before and after IVF. Denuded oocytes were submitted to a whole-mount immunofluorescence procedure. Specimens were imaged and fluorescent intensities quantified by scanning laser confocal microscopy. Immunoreactivity for inhibin alpha subunit (both alpha(C) and pro-alpha. regions), abundant in the ooplasm of immature oocytes, decreased after maturation (a 68% and 88% decrease, respectively; P < 0.001), but increased after IVF by 2- and 5.7-fold, respectively (P < 0.01). Intense staining for PA was detected in immature oocytes (predominantly in the outer ooplasm and zona pellucida) but after maturation and fertilization it was localized mainly in the zona pellucida, perivitelline space and oolemma. Immunoreactivity for RA in the ooplasm decreased by 58% after maturation (P < 0.001) but increased again by 75% after fertilization (P < 0.01). Immunoreactivity for beta(B) was localized mainly in the zona pellucida and did not change after maturation. However, immurloreactivity for beta(B) was not detected in the zona pellucida after fertilization, but remained unchanged in unfertilized oocytes. Immunoreactivity for follistatin was detected in the ooplasm and zona pellucida of immature oocytes but decreased progressively in the ooplasm after maturation (a 63% decrease; P < 0.001) and did not change after IVF. Examination of partially denuded cumulus-oocyte complexes confirmed abundant expression of alpha(C), pro-alpha, beta(A) and follistatin immunoreactivity in cumulus cells, whereas beta(B) subunit staining was weak or absent in cumulus cells, but intense in the zona pellucida. In conclusion, the present study shows that qualitative and quantitative changes in the distribution of inhibin/activin subunits and follistatin accompany oocyte maturation and fertilization. The possibility, indicated by these observations, that activin A and activin B may play distinct roles in bovine oocyte maturation and fertilization warrants further study.

Scanning LDV for vibration measurement of filiform hairs in crickets in response to induced airflow - art. no. 63450E

Cercal hairs represent in cricket a wind sensitive escape system, able to detect the airflow generated from predating species. These sensors have been studied as a biomimetic concept to allow the development of MEMS for biomedical use. In particular, the behaviour of the hairs, including airflow response, resonant frequency and damping, has been investigated up to a frequency of 20 kHz. The microscopic nature of the hairs, the complex vibrations of excited hairs and the high damping of the system suggested that the use of Laser Doppler vibrometry could possibly improve the test performance. Two types of tests were performed: in the first case the hairs were indirectly excited using the signal obtained from a vibrating aluminium plate, whilst in the second case the hairs were directly excited using a white noise chirp. The results from the first experiment indicated that the hairs move in-phase with the exciting signal up to frequencies in the order of 10 kHz, responding to the vibration modes of the plate with a signal attenuation of 12 to 20 dB. The chirp experiment revealed the presence of rotational resonant modes at 6850 and 11300 Hz. No clear effect of hair length was perceivable on the vibration response of the filiform sensors. The obtained results proved promising to support the mechanical and vibration characterisation of the hairs and suggest that scanning Laser vibrometry can be used extensively on highly dampened biological materials.

Mapping fibre orientation in complex-shaped biological systems with micrometre resolution by scanning X-ray microdiffraction

A fully automated procedure to extract and to image local fibre orientation in biological tissues from scanning X-ray diffraction is presented. The preferred chitin fibre orientation in the flow sensing system of crickets is determined with high spatial resolution by applying synchrotron radiation based X-ray microbeam diffraction in conjunction with advanced sample sectioning using a UV micro-laser. The data analysis is based on an automated detection of azimuthal diffraction maxima after 2D convolution filtering (smoothing) of the 2D diffraction patterns. Under the assumption of crystallographic fibre symmetry around the morphological fibre axis, the evaluation method allows mapping the three-dimensional orientation of the fibre axes in space. The resulting two-dimensional maps of the local fibre orientations - together with the complex shape of the flow sensing system - may be useful for a better understanding of the mechanical optimization of such tissues.

Viscoelastic properties of high pressure and heat induced tofu gels

Tofu gels were rheologically examined to determine their storage or elastic (G′) and loss or viscous (G″) moduli as a function of frequency within their linear viscoelastic limits. The tofu gels were made using either glucono-δ-lactone (GDL) or calcium sulphate (CaSO4·2H2O), followed by either heat treatment (heated soymilk at 97 °C prior to coagulation and subsequently held at 70 °C for 60 min, HT) or high pressure treatment (400 MPa at 20 °C for 10 min, HP). The overall moduli values of the GDL gels and CaSO4·2H2O gels of both physical treatments were similar, each gave frequency profiles expected for weak viscoelastic materials. However, although both temperature and high pressure treatments could be used to produce tofu gels, the final products were not the same. Pressure formed gels, despite having a higher overall “consistency” (increasing values of their moduli), had a proportionately higher contribution from the loss modulus (increased tan δ). Differences could also be observed using confocal scanning laser microscopy. While such treatment may give rise to differing systems/structures, with new or modified organoleptic properties, the more “open” structures obtained by pressure treatment may well cause processing difficulties if subsequent reworking or moulding is required.

Viscoelastic properties of high pressure and heat induced tofu gels

Tofu gels were rheologically examined to determine their storage or elastic (G') and loss or viscous (G '') moduli as a function of frequency within their linear viscoelastic limits. The tofu gels were made using either glucono-delta-lactone (GDL) or calcium sulphate (CaSO4 center dot 2H(2)O), followed by either heat treatment (heated soymilk at >= 97 degrees C prior to coagulation and subsequently held at 70 degrees C for 60 min, HT) or high pressure treatment (400 MPa at 20 degrees C for 10 min, HP). The overall moduli values of the GDL gels and CaSO4 center dot 2H(2)O gels of both physical treatments were similar, each gave frequency profiles expected for weak viscoelastic materials. However, although both temperature and high pressure treatments could be used to produce tofu gels, the final products were not the same. Pressure formed gels, despite having a higher overall "consistency" (increasing values of their moduli), had a proportionately higher contribution from the loss modulus (increased tan delta). Differences could also be observed using confocal scanning laser microscopy. While such treatment may give rise to differing systems/structures, with new or modified organoleptic properties, the more "open" structures obtained by pressure treatment may well cause processing difficulties if subsequent reworking or moulding is required. (c) 2007 Elsevier Ltd. All rights reserved.