Pressure behaviour of self-assembled In0.55Al0.45As/Al0.5Ga0.5As quantum dots with multi-modal distribution in size

The pressure behaviour of In0.55Al0.45As/Al0.5Ga0.5As self-assembled quantum dots (QDs) has been studied at 15 K in the pressure range of 0-1.3 GPa. The atomic force microscopy image shows that the QDs have a multi-modal distribution in size. Three emission peaks were observed in the photoluminescence (PL) spectra, corresponding to the different QD families. The measured pressure coefficients are 82, 93 and 98 meV GPa(-1) for QDs with average lateral size of 26, 52 and 62 nm, respectively. The pressure coefficient of small QDs is about 17% smaller than that of bulk In0.55Al0.45As An envelope-function calculation was used to analyse the effect of pressure-induced change of barrier height, effective mass and dot size on the pressure coefficients of QDs. The Gamma-X state mixing was also included in the evaluation of the reduction of the pressure coefficients. The results indicate that both the pressure-induced increase of effective mass and Gamma-X mixing respond to the decrease of pressure coefficients, and the Gamma-X mixing is more important for small dots. The calculated Gamma-X interaction potentials are 15 and 10 meV for QDs with lateral size of 26 and 52 nm, respectively. A type-II alignment for the X conduction band is suggested according to the pressure dependence of the PL intensities. The valence-band offset was then estimated as 0.15 +/- 0.02.

Steady and transient optical properties of cubic InGaN epilayers

Photoluminescence (PL) and time-resolved PI, were employed to study the steady and transient optical properties of cubic InxGa1-xN epilayers grown by MBE. The results suggest that the PL transitions in InGaN epilayers are mainly from localized exciton states. The localization energies are estimated to be 60 meV, independent of In composition. The PL decay is characterized by a hi-exponential dependence. The fast process (50 ps at 12K) is related to the fast relaxation of excitons, while a slower contribution (200-270 ps at 12K) is attributed to the decay process of localized excitons.

Room-temperature optical transitions in Mg-doped cubic GaN/GaAs(100) grown by metalorganic chemical vapor deposition

The mechanism of room-temperature optical transitions in a Mg-doped cubic GaN epilayer grown on GaAs(100) by metalorganic chemical vapor deposition has been investigated. By examining the dependence of photoluminescence on the excitation intensity (which varied over four orders) at room temperature, four different emissions with different origins were identified. A blue emission at similar to 3.037 eV was associated with a shallow Mg acceptor, while three different lower-energy emissions at similar to 2.895, similar to 2.716, and similar to 2.639 eV were associated with a deep Mg complex. In addition to a shallow acceptor at E congruent to 0.213 eV, three Mg-related deep defect levels were also found at around 215, 374, and 570 meV (from the conduction band). (C) 2000 American Institute of Physics. [S0021-8979(00)01904-6].

A study of Si1-xGex/Si quantum-well intermixing by photocurrent spectroscopy

Photocurrent spectroscopy has been used to study quantum-well intermixing in this paper. The cut-off wavelength of the photodiodes based on the implanted and annealed materials is significantly reduced, compared with that measured in annealed-only photodetectors. The bandgap of SiGe quantum well in implanted and annealed samples is blue-shifted by up to 97 meV, relative to that in annealed-only samples. (C) 2000 Elsevier Science S.A. All rights reserved.

Effects of rapid thermal annealing on self-assembled InGaAs/GaAs quantum dots superlattice

Postgrowth rapid thermal annealing was used to study the relaxation mechanism and optical properties of InGaAs/GaAs self-assembled quantum dots superlattice grown by molecular beam epitaxy. It is found that a significant narrowing of the luminescence linewidth (from 80 to 42 meV) occurs together with about 86 meV blue shift at annealing temperature up to 950 degrees C. Double crystal X-ray diffraction measurements show that the intensity of the satellite diffraction peak, which corresponds to the quantum dots superlattice, decreased with the increasing annealing temperature and disappeared at 750 degrees C, but recovered and increased again at higher annealing temperatures. This behavior can be explained by two competing relaxation mechanisms; interdiffusion and favored migration. The study indicates that a suitable annealing treatment can improve the structural properties of the quantum dots superlattice. (C) 2000 Elsevier Science B.V. All rights reserved.

Energy bands and acceptor binding energies of GaN

The energy bands of zinc-blende and wurtzite GaN are calculated with the empirical pseudopotential method, and the pseudopotential parameters for Ga and N atoms are-given. The calculated energy bands are in agreement with those obtained by the ab initio method. The effective-mass theory for the semiconductors of wurtzite structure is established, and the effective-mass parameters of GaN for both structures are given The binding energies of acceptor states are calculated by solving strictly the effective-mass equations. The binding energies of donor and acceptor are 24 and 142 meV for the zinc-blende structure, 20 and 131, and 97 meV for the wurtzite structure, respectively, which are consistent with recent experimental results. It is proposed that there are two kinds of acceptor in wurtzite GaN. One kind is the general acceptor such as C, which substitutes N, which satisfies the effective-mass theory. The other kind of acceptor includes Mg, Zn, Cd, etc., the binding energy of these accepters is deviated from that given by the effective mass theory. In this report, wurtzite GaN is grown by the molecular-beam epitaxy method, and the photoluminescence spectra were measured. Three main peaks are assigned to the donor-acceptor transitions from two kinds of accepters. Some of the transitions were identified as coming from the cubic phase of GaN, which appears randomly within the predominantly hexagonal material. [S0163-1829(99)15915-0].

Cubic-phase GaN light-emitting diodes

The feasibility of growing device-quality cubic GaN/GaAs(001) films by metal organic chemical vapor deposition has been demonstrated. The optical quality of the GaN films was characterized by room-temperature photoluminescence measurements, which shows a full width at half maximum of 46 meV. The structural quality of the films was investigated by transmission electron microscopy. There are submicron-size grains free from threading dislocations and stacking faults. More importantly, a cubic-phase GaN blue light-emitting diode has been fabricated. The device process, which is very simple and compatible with current GaAs technology, indicates a promising future for the blue light-emitting diode. (C) 1999 American Institute of Physics. [S0003-6951(99)01416-3].

Cubic InGaN grown by MOCVD

We report on the growth of high-quality cubic phase InGaN on GaAs by MOCVD. The cubic InGaN layers are grown on cubic GaN buffer layers on GaAs (001) substrates. The surface morphology of the films are mirror-like. The cubic nature of the InGaN films is obtained by Xray diffraction (XRD) measurements. The InGaN layers show strong photoluminescence (PL) at room temperature. Neither emission peak from wurtzite GaN nor yellow luminescence is observed in our films. The highest In content as determined by XRD is about 17% with an PL emission wavelength of 450 nm. The FWHM of the cubic InGaN PL peak are 153 meV and 216 meV for 427 nm and 450 nm emissions, respectively. It is found that the In compositions determined from XRD are not in agreement with those estimated from PL measurements. The reasons for this disagreement are discussed.

p-type co-doping study of GaN by photoluminescence

Photoluminescence measurements were performed on p-type co-doping effects of C, As, and Mg in GaN. The dopants were incorporated into GaN by ion implantation performed at 77 K. We find that the 3.42 eV luminescence line is sensitive to hole concentration, and propose that after cartful calibration the 3.42 eV line may be used as a probe to measure hole concentration in GaN. Simply doping one kind of accepters will not result in holes, while co-doping can substantially improve p-type doping efficiency. As + C and As + Mg co-doping induce an acceptor level of 180 meV above the valence band. Mg + C co-doping is the most promising method for p-type doping, the related acceptor level is determined to be as shallow as 130 meV. The improvement of the doping efficiency by co-doping is probably due to the decrease of the acceptor ionization energy. (C) 1999 Elsevier Science B.V. All rights reserved.

Uniformity enhancement of the self-organized InAs quantum dots

Growth interruption was introduced after the deposition of GaAs cap layer, which is thinner than the height of quantum dots. Uniformity of quantum dots has been enhanced because the full-width of half-maximum of photoluminescence decrease from 80 to 27 meV in these samples as the interruption time is increased. Meanwhile, we have observed that the peak position of photoluminescence is a function of interruption time, which can be used to modulate energy level of quantum dots. All of the phenomenon mentioned above can be attributed to the diffusion of In atoms from the tops of InAs islands to the top of GaAs cap layer caused by the difference between the surface energies of InAs and GaAs. (C) 1999 Elsevier Science B.V. All rights reserved.

Pressure behavior of deep centers in ZnSxTe1-x alloys

We have measured photoluminescence of ZnSxTe1-x alloys (x > 0.7) at 300 K and under hydrostatic pressure up to 7 GPa. The spectra contain only a broad emission band under excitation of the 406.7 nm line. Its pressure coefficients are 47, 62 and 45 meV/GPa for x = 0.98, 0.92 and 0.79 samples, which are about 26%, 7% and 38% smaller than that of the band gap in the corresponding alloys. The Stokes shifts between emission and absorption of the bands were calculated by fitting the pressure dependence of the emission intensity, being 0.29, 0.48 and 0.13 eV for the three samples, respectively. The small pressure coefficient and large Stokes shift indicate that the emission band observed in our samples may correspond to the Te isoelectronic center in the ZnSxTe1-x alloy.

Electron irradiation and thermal annealing effect on GaAs solar cells

This paper describes the effect of electron irradiation and thermal annealing on LPE AlGaAs/GaAs heterojunction solar cells with various p/n junction depths. The electron irradiation experiments were performed with energy of 3 MeV, fluences ranging from 1 x 10(14) to 5 x 10(15) e/cm(2). The results obtained demonstrate that the irradiation-induced degradation of performances of the cells is mainly in the short circuit current and could be mostly recovered by annealing at 260 degrees C for 30 min. Four electron traps, E-c - 0.24 eV, E-c - 0.41 eV, E-c - 0.51 eV, E-c - 0.59 eV, were found by DLTS analysis, only two shallow levels of which could be removed by the annealing. (C) 1998 Elsevier Science B.V. All rights reserved.

Photoluminescence properties of SiGe/Si single wells with fluctuating structural parameters

Photoluminescence properties of SiGe/Si single wells with fluctuating structural parameters are studied. Four SiGe/Si single wells have been grown on Si(001) at 750 degrees C by disilane and solid Ge molecular beam epitaxy with varied disilane cracking-temperatures. Intense NP and TO-phonon replicas are detected up to 70 K in the photoluminescence spectra and the activation energy of the thermal quenching of the photoluminescence is 28 +/- 4 meV. The high growth temperature and purposeful introduction of fluctuation of structural parameters may be responsible for the improvement of the thermal quenching property.

New method for the growth of highly uniform quantum dots

A new method is realized for the growth of self-formed quantum dots. We identify that dislocation-free islands can be formed by the strain from the strained superlattice taken as a whole. Unlike the Stranski-Krastanow (S-K) growth mode, the islands do not form during the growth of the corresponding strained single layers. Highly uniform quantum dots can be self-formed via this mechanism. The low temperature spectra of self-formed InGaAs/GaAs quantum dot superlattices grown on a (001) GaAs substrate have a full width at half maximum of 26-34 meV, indicating a better uniformity of quantum dot size than those grown in the S-K mode. This method can provide great degrees of freedom in designing possible quantum dot devices. 1998 Published by Elsevier Science B.V. All rights reserved.

Electronic and vibrational Raman scattering in resonance with yellow luminescence transitions in GaN on sapphire substrate

We analyze low-temperature Raman and photoluminescence spectra of MBE-grown GaN layers on sapphire. Strong and sharp Raman peaks are observed in the low frequency region. These peaks, which are enhanced by excitation in resonance with yellow luminescence transitions, are attributed to electronic transitions related to shallow donor levels in hexagonal GaN. It is proposed that a low frequency Raman peak at 11.7 meV is caused by a pseudo-local vibration mode related to defects involved in yellow luminescence transitions. The dependence of the photoluminescence spectra on temperature gives additional information about the residual impurities in these GaN layers.