氧分压对电子束蒸发SiO2薄膜机械性质和光学性质的影响

采用ZYGO MarkⅢ-GPI数字波面干涉仪、NamoScopeⅢa型原子力显微镜对不同氧分压下电子束蒸发方法制备的SiO2薄膜中的残余应力及表面形貌进行了研究，结果发现：随着氧分压的增大，薄膜中的压应力值逐渐减小，最后变为张应力状态；同时薄膜的表面粗糙度也随着氧分压的增大而逐渐增大，另外，折射率对氧分压也非常敏感，随着氧分压的增大呈现出了减小的趋势，这些现象主要是由于氧分压的改变使得SiO2薄膜结构发生了变化引起的。

应用离子后处理技术提高薄膜激光损伤阈值

利用电子束热蒸发方法在K9玻璃基底上沉积氧化锆薄膜,并对其中一些样品用低能O2^+进行了后处理.采用表面热透镜技术测量薄膜样品表面弱吸收,采用显微镜观察样品离子后处理前后的显微缺陷密度.测试结果表明:经离子后处理样品表面的缺陷密度从18.6/mm^2降低到6.2/mm^2,且其激光损伤阈值从15.9 J/cm^2提高到23.1 J/cm^2,样品的平均吸收率从处理前的1.147×10^-4降低到处理后的9.56×10^-5.通过对处理前后样品的表面微缺陷密度、吸收率及损伤形貌等的分析发现:离子后处理可以降

HfO2 膜料中的杂质对薄膜损伤及性能的影响

By analysis of impurity elements in HfO2 coating material, the influence of main impurity elements on the characteristic of coatings were studied. The results indicate that the metal elements and absorptive dielectric elements damage the HfO2 coatings. The more the Zr element content is, the more the absorption is for the coatings in ultraviolet wave. The negative ion element will become the gas source center and form an ejection in the process of evaporation of coating material, so decrease the damage threshold of the coatings.

氧分压对ZrO2薄膜激光损伤阈值的影响

在不同的氧分压下用电子束热蒸发的方法制备了ZrO2薄膜。分别通过X射线衍射、光学光谱、热透镜技术、抗激光辐照等测试，对所制备样品的微结构、折射率、吸收率及激光损伤阈值进行了测量。实验结果表明，薄膜中晶粒主要是四方相为主的多晶结构，并且随着氧分压的增加，结晶度、折射率以及弱吸收均逐渐降低。薄膜的激光损伤阈值开始随着氧分压增加从18．5J／cm^2逐渐增加，氧分压为9×10^-3Pa时达到最大，值为26．7J／cm^2，氧分压再增加时则又降低到17．5J／cm^2。由此可见，氧分压引起的薄膜微结构变化是ZrO

微缺陷对薄膜滤光片环境稳定性的影响

用热蒸发方法沉积了薄膜滤光片．并将样品分别在去离子水中浸泡10天和30天．通过分光光度计、光学暗场显微镜、及扫描电子显微镜等多种测试手段，对诱导透射滤光片在潮湿环境下的稳定性进行了研究．实验发现，在潮湿环境下滤光片产生的膜层分离都是从薄膜中微缺陷点处开始发生和发展的，微缺陷是影响滤光片环境稳定性的重要原因之一，其中杂质和针孔是滤光片中两种最常见的微缺陷．EDS能谱分析进一步表明，薄膜中杂质缺陷成分即为Al2O3膜料本身，所以不能推测，薄膜沉积中的喷溅可能是微缺陷产生的根本原因，抑制喷溅可以有效提高薄膜滤光

共蒸法制备非均匀膜的速率控制分析

渐变折射率薄膜，又称为非均匀膜。利用德鲁德理论分析了混合介质膜的介电常量与各个膜料的介电常量之间的关系，介绍了共蒸法制备非均匀膜的制备机理。对混合膜的沉积速率为两种膜料的沉积速率之和的情况，分别从两种膜料的单分子体积是否相等和总的沉积速率是否为常数两个方面，探讨了双源共蒸法制备的非均匀膜的折射率分布规律与膜料的沉积速率之间的关系，并给出了几种常见的折射率分布如线性变化、正弦变化、指数变化和双曲变化规律的膜料沉积速率表达式。最后以混合介质膜的总沉积速率为常数、折射率按照线性变化为例进行了说明。

线性共蒸法制备渐变折射率薄膜的光学特性分析

利用德鲁德理论和洛伦兹一洛伦茨理论，从介电常数分析人手，探讨了混合介质膜的折射率表达式，给出利用双源共蒸法镀制的渐变折射率薄膜在混合介质膜的总沉积速率恒定、两种膜料的单分子大小近似相等和沉积速率均为线性变化时的折射率表达式；从正变和负变、单周期和多周期、不同的周期数和不同的单周期厚度几个方面对渐变折射率薄膜的光学特性进行了模拟分析和讨论；对渐变折射率薄膜的实现、应用以及实验制备中有待进一步解决和处理的问题进行了讨论。

Laser induced damage of multi-layer dielectric used in pulse compressor gratings

Laser induced damage threshold (LIDT) of multi-layer dielectric used in pulse compressor gratings (PCG) was investigated. The sample was prepared by e-beam evaporation (EBE). LIDT was detected following ISO standard 11254-1.2. It was found that LIDTs of normal and 51.2 deg. incidence (transverse electric (TE) mode) were 14.14 and 9.31 J/cm2, respectively. A Nomarski microscope was employed to map the damage morphology, and it was found that the damage behavior was pit-concave-plat structure for normal incidence, while it was pit structure for 51.2 deg. incidence with TE mode. The electric field distribution was calculated to illuminate the difference of LIDT between the two incident cases.

Laser-induced damage morphology of high-reflective optical coatings

Two different kinds of 1064 nm high-reflective (HR) coatings, with and without SiO2 protective layer, were prepared by electron beam evaporation. Three-dimensional damage morphology, caused by a Nd:YAG pulsed laser, was investigated for these HR coatings. Development of laser-induced damage on HR coatings was revealed by both temperature field calculation and discrete meso-element simulation. Theoretical results met experimental very well. (C) 2004 Elsevier B.V. All rights reserved.

Influence of negative ion element impurities on laser induced damage threshold of HfO2 thin film

Negative ion element impurities breakdown model in HfO2 thin film was reported in this paper. The content of negative ion elements were detected by glow discharge mass spectrum analysis (GDMS); HfO2 thin films were deposited by the electron-beam evaporation method. The weak absorption and laser induced damage threshold (LIDT) of HfO2 thin films were measured to testify the negative ion element impurity breakdown model. It was found that the LIDT would decrease and the absorption would increase with increasing the content of negative ion element. These results indicated that negative ion elements were harmful impurities and would speed up the damage of thin film. (c) 2006 Elsevier B.V. All rights reserved.

倾斜角沉积技术制备ZnS双折射雕塑薄膜

使用倾斜角沉积（GLAD）的电子束蒸发技术，制备了倾斜角度在60°～85°之间的ZnS双折射雕塑薄膜（STF）。使用X射线衍射（XRD）和扫描电镜（SEM）检测了ZnS薄膜的结晶状态和断面形貌，使用Lamda-900分光光度计测量了薄膜在不同的偏振光入射时的透过率。研究发现，室温下倾斜沉积ZnS薄膜断面为倾斜柱状结构，且薄膜的结晶程度不高。在相同的监控厚度时，随倾斜角度增大，沉积到基片上的薄膜厚度逐渐变小，但仍然大于余弦曲线显示的理论厚度。根据偏振光垂直入射时薄膜的透过光谱计算了不同角度沉积的薄膜的折射率

Investigation on microstructure and optical properties of titanium dioxide coatings annealed at various temperature

TiO2 coatings were prepared on fused silica with conventional electron beam evaporation deposition. After TiO2 thin films were annealed at different temperatures for 4 h, several properties were investigated by X-ray diffraction (XRD), spectrometer.. photoelectron spectroscopy (XPS) and AFM. It was found that with the annealing temperature increasing, the transmittance of TiO2 coatings decreased, and the cutoff wavelength shifted to long wavelength in near ultraviolet band. Especially, when coatings were annealed at high temperature, the optical loss is very serious, which can be attributed to the scattering and the absorption of TiO2 coatings. XRD patterns revealed that only anatase phase was observed in TiO2 coatings regardless of the different annealing temperatures. XPS results indicated that the fine chemical shift of TiO2 2p(1/2) should be attributed to existence of oxygen vacancies around Ti+4 ion. The investigation on surface morphology by AFM showed that the RMS of titania thin films gradually increases from less than 0.40 nm to 5.03 nm and it should be ascribed to the growth of titanium dioxide grain size with the increase of annealing temperature. (C) 2005 Elsevier B.V. All rights reserved.

Stress, absorptance and laser-induced damage threshold properties of 355-nm HR coatings

A number of 355-nm Al2O3/MgF2 high-reflectance (HR) coatings were prepared by electron-beam evaporation. The influences of the number of coating layers and deposition temperature on the 355-nm Al2O3/MgF2 HR coatings were investigated. The stress was measured by viewing the substrate deformation before and after coating deposition using an optical interferometer. The laser-induced damage threshold (LIDT) of the samples was measured by a 355-nm Nd:YAG laser with a pulse width of 8 ns. Transmittance and reflectance of the samples were measured by a Lambda 900 spectrometer. It was found that absorptance was the main reason to result in a low LIDT of 355-nm Al2O3/MgF2 HR coatings. The stress in Al2O3/MgF2 HR coatings played an unimportant role in the LIDT, although MgF2 is known to have high tensile stress.

Layer uniformity of glancing angle deposition

Some results of an investigation on the layer thickness uniformity of glancing angle deposition are presented. A zirconia monolayer has been deposited by glancing angle deposition to analyze the layer thickness uniformity. The experimental results indicate that the thickness variation over the substrate is less than 0. 1%, which is considered as good uniformity. It is found that the non-uniformity of experimental results is larger than that of the theoretical results. (c) 2005 Elsevier Ltd. All rights reserved.

Study of Al2O3/MgF2 HR coatings at 355 nm

With the present work we tried to study the effective methods to improve the laser-induced damage threshold (LIDT) and reflectance of HR coatings at 355 nm. The work presented in this paper wits part of an ongoing study about vacuum annealing. It was dedicated to study the effects Of Vacuum annealing with different temperature gradients on the structure, optical properties and laser-induced damage threshold (LIDT) of 355nm Al2O3/MgF2HR coatings. A number of samples were prepared by electron beam evaporation using the same deposition process with an optimal deposition temperature of 280 degrees C. After deposition, samples were annealed in the coating chamber for 3 h with different temperature gradients. Morphologies of the samples were observed by Leica-DMRXE. Microscope, Structure of the samples had been characterized by X-ray diffraction (XRD). Transmittance and reflectance of the samples were measured by Lambda 900 Spectrometer, The LIDT of the samples was measured by a 355 nm Nd:YAG laser with a pulse width of 8 ns. It was found that the temperature gradient of vacuum annealing had significant effects on the morphology, structure, absorption, and LIDT of the samples, (c) 2005 Elsevier Ltd. All rights reserved.