The effects of Si and Mg doping on the crystalline quality and In distribution in the InGaN films were studied by atomic force microscope (AFM), triple crystal X-ray diffraction (TCXRD) and Rutherford backscattering spectrometry (RBS). The undoped, Si-doped and Mg-doped InGaN films were grown by metalorganic chemical vapor deposition (MOCVD) on (0 0 0 1) sapphire substrates. The electronic concentration in the Si-doped InGaN is about 2 x 10(19) cm(-3). It is found that the crystalline quality and In distribution in InGaN is slightly affected by the Si doping. In the Mg doped-case, the hole concentration is about 4 x 10(18) cm(-3) after annealing treatment. The surface morphology and crystalline quality of the Mg-doped InGaN are deteriorated significantly compared with the undoped InGaN. The growth rate of Mg-doped InGaN is higher than the undoped InGaN. Mg doping enhances the In incorporation in the InGaN alloy. The increase in In composition in the growth direction is more severe than the undoped InGaN. (c) 2006 Elsevier B.V. All rights reserved.
Resumo:
By vertical sedimentation and oblique titration, silica microspheres were grown in different shapes of concave microzones that were etched on a (100) p-silicon substrate. Through scanning electron microscope observation and optical reflective spectra measurement, sedimentation of microspheres in those microzones was compared. An index was introduced to judge the efficiency of sedimentation. The comparison demonstrates that regular hexagons and triangles facilitate the growth of photonic crystals the most. (c) 2006 Optical Society of America
Resumo:
A 1.55-mu m ridge distributed feedback laser and electroabsorption modulator monolithically integrated with a buried-ridge-stripe dual-waveguide spot-size converter (SSC) at the output port for low-loss coupling to a cleaved single-mode optical fiber was fabricated by means of selective area growth, quantum-well intermixing, and dual-core technologies. These devices exhibit threshold current of 28 mA, 3-dB modulation bandwidth of 12.0 GHz, modulator extinction ratios of 25.0-dB dc. The output beam divergence angles of the SSC in the horizontal and vertical directions are as small as 8.0 degrees x 12.6 degrees, respectively, resulting in 3.2-dB coupling loss with a cleaved single-mode optical fiber.
Resumo:
The photoluminescence from ZnS1-xTex alloy with 0 < x < 0.3 was investigated under hydrostatic pressure up to 7 GPa. Two peaks were observed in the alloys with x < 0.01, which are related to excitons bound to isolated Te isoelectronic impurities (Te-1 centers) and Te pairs (Te-2 centers), respectively. Only the Te-2 related emissions were observed in the alloys with 0.01 < x < 0.03. The emissions in the alloys with 0.03 < x < 0.3 are attributed to the excitons bound to the Te-n (n greater than or equal to 3) cluster centers. The pressure coefficient of the Te-1 related peak is 89(4) meV/GPa, about 40% larger than that of the band gap of ZnS. On the other hand, the pressure coefficient of the Te-2 related emissions is only 52(4) meV/GPa, about 15% smaller than that of the ZnS band gap. A simple Koster-Slater model has been used to explain the different pressure behavior of the Te-1 and Te-2 centers. The pressure coefficient of the Te-3 centers is 62(2) meV/GPa. Then the pressure coefficients of the Te-n centers decrease rapidly with further increasing Te composition.
Resumo:
Excitation-power dependence of hydrostatic pressure coefficients (dE/dP) of InxGa1-xN/InyGa1-yN multiple quantum wells is reported. When the excitation power increases from 1.0 to 33 mW, dE/dP increases from 26.9 to 33.8 meV/GPa, which is an increase by 25%. A saturation behavior of dE/dP with the excitation power is observed. The increment of dE/dP with increasing carrier density is explained by an reduction of the internal piezoelectric field due to an efficient screening effect of the free carriers on the field.
Resumo:
Epitaxial growth of AlN has been performed by molecular beam epitaxy (MBE) with ammonia. The structural properties of materials were studied by cross-sectional transmission electron microscopy (TEM), X-ray diffraction (XRD), and atomic force microscopy (AFM). XRD and TEM diffraction pattern confirm the AlN is single crystalline 2H-polytype with the epitaxial relationship of (0001)AlNparallel to(111)Si, [11 (2) over bar0](AlN)parallel to[110](Si), [10 (1) over bar0](AlN)parallel to[11 (2) over bar](Si). Micro-Raman scattering measurement shows that the E-2 (high) and A(1) (LO) phonon mode shift 9 cm(-1) toward the low frequency, which shows the existence of large tensile strain in the AlN films. Furthermore, the appearance of forbidden A, (TO) mode and its anomalous shift toward high frequency was found and explained. (C) 2002 Elsevier Science B.V. All rights reserved.
Resumo:
A new method to form nanoscale InGaN quantum dots using MOCVD is reported, This method is much different from a method. which uses surfactant or the Stranski-Krastannow growth mode. The dots were formed by increasing the energy barrier for adatoms, which are hopping by surface passivation, and by decreasing the growth temperature. Thus, the new method can be called as a passivation-low-temperature method. Regular high-temperature GaN films were grown first and were passivated. A low-temperature thin layer of GaN dot was then deposited on the surface that acted as the adjusting layer. At last the high-density InGaN dots could be fabricated on the adjusting layer. Atomic force microscopy measurement revealed that InGaN dots were small enough to expect zero-dimensional quantum effects: The islands were typically 80 nm wide and 5 nm high. Their density was about 6 x 10(10) cm(-2). Strong photoluminescence emission from the dots is observed at room temperature, which is much stronger than that of the homogeneous InGaN film with the same growth time. Furthermore, the PL emission of the GaN adjusting layer shows 21 meV blueshift compared with the band edge emission of the GaN due to quantum confine effect. (C) 2002 Elsevier Science B.V. All rights reserved.
Resumo:
The surfactant effect of isoelectronic indium doping during metalorganic chemical vapor deposition growth of cubic GaN on GaAs (1 0 0) substrates was studied. Its influence on the optical properties and surface morphology was investigated by using room-temperature photoluminescence (PL) and atomic force microscopy. It is shown that the sample with small amount of In-doping has a narrower PL linewidth, and a smoother surface than undoped cubic GaN layers. A slight red shift of the near-band-edge emission peak was observed. These results revealed that, for small TMIn flow rates, indium played the role of the surfactant doping and effectively improved the cubic GaN film quality; for large TMIn flow rates, the alloying formation of Ga1-xInxN might have occurred. (C) 2002 Elsevier Science B.V. All rights reserved.
Resumo:
The interface diffusion, reaction, and adherence of rapid thermal annealed Ti/ALN were investigated by RES, AES, SIMS, XRD and a scratch test. The experimental results show that diffusion and reaction occurs at the interface of Ti/AlN when the sample is rapidly annealed. During annealing, both the O adsorbed on the surface and doped in the AlN substrate diffuse into the Ti film. At low temperature TiO2 is produced. At higher temperature O reacts with the diffused Al in the Ti film and produces an Al2O3 layer in the middle of the film. N diffuses into the Ti film and produces TiN with an interface reaction. Ti oxide is produced at the interface between the film and the substrate. Scratch test results show that interface adherence is distinctly improved by rapid annealing at low temperature and decreases at higher temperature. (C) 1999 Elsevier Science B.V. All rights reserved.
Resumo:
利用Java媒体框架(JMF)开发的视频点播系统具有开发简单、跨平台、提供QoS保证和交互性好等优点,具有广泛的应用前景.介绍了JMF应用编程接口的特点和结构,阐述了基于JMF开发的跨平台的视频点播系统的整体结构设计,并详细介绍了基于RTP的实时媒体传输、基于RTCP的拥塞控制、完整VCR操作和穿越NAT等关键技术的具体实现.
Resumo:
弹性CA是一种使用入侵容忍技术保护CA密钥的CA系统,它采用了新的私钥分割方法加强了系统的安全性,但其使用的密钥分发中心却不利于CA私钥安全.分布式密钥产生方案就是在传统的弹性CA方案的基础上取消了密钥分发中心,使用分布式的密钥产生和分割机制,从而保证了在CA初始化和整个运行过程中,任意t-1(t为门限值)台服务器都不可能窃得CA私钥,大大加强了CA系统安全.
Resumo:
针对飞行器多航迹规划问题展开研究.在分析多峰值函数优化问题的基础上,提出了一种基于进化计算的飞行器多航迹规划方法.该方法通过使用特定的染色体表示方法和进化算子,可以有效利用各种环境信息,处理各种航迹约束.同时,通过引入聚类算法,将种群中的个体按其空间分布进行聚类,生成若干个不同子种群.在进化过程中,所有个体只在各自的子种群内部进化.当进化结束时,每个子种群将分别生成一条各自的最优航迹,从而为飞行器生成多条不同的可选航迹.仿真结果表明了该方法的有效性.