Comparison of short period InAs/GaSb superlattices on GaSb and GaAs substrates

Type II superlattices (SLs) short period InAs(4ML)/GaSb(8ML) were grown by molecular-beam epitaxy on lattice-mismatched GaAs substrates and on GaSb substrates. A smooth GaSb epilayer was formed on GaAs substrates by inserting mulit-buffer layers including an interfacial misfit mode AlSb quantum dot layer and AlSb/GaSb superlattices smooth layer. SLs grown on GaAs substrates (GaAs-based SLs) showed well-resolved satellite peaks in XRD. GaSb-based SLs with better structural quality and smoother surface showed strong photoluminescence at 2.55 mu m with a full width at half maximum (FWHM) of 20 meV, narrower than 31 meV of GaAs-based SLs. Inferior optical absorption of GaAs-based SL was observed in the range of 2-3 mu m. Photoresponse of GaSb-based SLs showed the cut-off wavelength at 2.6 mu m.

Dependence of current-voltage characteristics of pseudomorphic AlAs/In0.53Ga0.47As/InAs resonant tunnelling diodes on quantum well widths

This paper studies the dependence of I - V characteristics on quantum well widths in AlAs/In0.53Ga0.47As and AlAs/In0.53Ga0.47As/InAs resonant tunnelling structures grown on InP substrates. It shows that the peak and the valley current density in the negative differential resistance region are closely related with quantum well width. The measured peak current density, valley current densities and peak-to-valley current ratio of resonant tunnelling diodes are continually decreasing with increasing well width.

Time-Resolved Photoluminescence of Metamorphic InGaAs Quantum Wells

We investigate the temperature dependence of photoluminescence (PL) and time-resolved PL on the metamorphic InGaAs quantum wells (QWs) with an emission wavelength of 1.55 mu m at room temperature. Time-resolved PL measurements reveal that the optical properties can be partly improved by introducing antimony (Sb) as a surfactant during the sample growth. The temperature dependence of the radiative lifetime is measured, showing that for QWs grown with Sb assistance, the intrinsic exciton emission is dominated when the temperature is below 60 K, while the nonradiative process becomes activated with further increases in temperature. However, without Sb assistance, the nonradiative centers are activated when the temperature is higher than 20 K.

Growth of nano-structures on composition-modulated InAlAs surfaces

InAs self-organized nanostructures were grown with variant deposition thickness and growth rate on closely matched InAlAs/InP by molecular-beam epitaxy. The structural properties. of InAs and InAlAs layer were studied. It is found that the InAs morphology is insensitive to the growth conditions. Transmission electron microscopy and reflectance difference spectroscopy measurements show that the InAlAs matrix presents lateral composition modulation which gives birth to surface anisotropy. Based on the dependence of the InAs morphology on the anisotropy of the InAlAs layer, a modified Stranski-Krastanow growth mode is presented to describe the growth of the nanostructure on a composition-modulated surface.

Photoluminescence characterization of nanocrystalline ZnO array

High-density and uniform well-aligned ZnO sub-micron rods are synthesized on the silicon substrate over a large area. The morphology, and structure of the ZnO sub-micron rods are investigated by x-ray diffraction, transmission electron microscopy and Raman spectra. It is found that the ZnO sub-micron rods are of high crystal quality with the diameter in the range of 400-600 nm and the length of several micrometres long. The optical properties were studied bill photoluminescence spectra. The results show that the intensity of the ultraviolet emission at 3.3 eV is rather high, meanwhile the deep level transition centred at about 2.38 eV is weak. The free exciton emission could also be observed at low, temperature, which implies the high optical quality of the ZnO sub-micron rods. This growth technique provides one effective way to fabricate the high crystal quality ZnO nanowires array, which is very important for potential applications in the new-type optoelectronic nanodevices.

Phase-separation suppression in GaN-rich side of GaNP alloys grown by metal-organic chemical vapor deposition

The GaN-rich side of GaNP ternary alloys has been successfully synthesized by light-radiation heating and low-pressure metal-organic chemical vapor deposition. X-ray diffraction (XRD) rocking curves show that the ( 0002) peak of GaNP shifts to a smaller angle with increasing P content. From the GaNP photoluminescence (PL) spectra, the red shifts from the band-edge emission of GaN are determined to be 73, 78 and 100 meV, respectively, in the GaNP alloys with the P contents of 1.5%, 5.5% and 7.5%. No PL peak or XRD peak related to GaP is observed, indicating that phase separation induced by the short-range distribution of GaP-rich regions in the GaNP layer has been effectively suppressed. The phase-separation suppression in the GaNP layer is associated with the high growth rate and the quick cooling rate under the given growth conditions, which can efficiently restrain the accumulation of P atoms in the GaNP layer.

High-indium-content InxGa1-xAs/GaAs quantum wells with emission wavelengths above 1.25 mu m at room temperature

High-indium-content InxGa1-xAs/GaAs single/multi-quantum well (SQW/MQW) structures have been systematically investigated. By optimizing the molecular-beam epitaxy growth conditions, the critical thickness of the strained In0.475Ga0.525As/GaAs QWs is raised to 7 nm, which is much higher than the value given by the Matthews and Blakeslee model. The good crystalline quality of the strained InGaAs/GaAs MQWs is proved by x-ray rocking curves. Photoluminescence measurements show that an emission wavelength of 1.25 mum at room temperatures with narrower full width at half maximum less than 30 meV can be obtained. The strain relaxation mechanism is discussed using the Matthews-Blakeslee model. (C) 2004 American Institute of Physics.

InAs nanostructure grown with different growth rate in InAlAs matrix on InP (001) substrate

InAs self-organized nanostructures in In0.52Al0.48As matrix have been grown on InP (001) substrates by molecular beam epitaxy. The morphologies of the nanostructures are found to be strongly dependent on the growth rate of the InAs layer. By increasing the growth rate from 0.005 to 0.35 ML/s, the morphology of the nanostructure changes from wire to elongated dot and then changes back to wire again. Polarized photoluminescence of the InAs quantum wires and quantum dots are performed at 77 K, which are characterized by strong optical anisotropies. (C) 2003 Elsevier B.V. All rights reserved.

Microstructural and compositional characteristics of GaN films grown on a ZnO-buffered Si(111) wafer

Polycrystalline GaN thin films have been deposited epitaxially on a ZnO-buffered (111)-oriented Si substrate by molecular beam epitaxy. The microstructural and compositional characteristics of the films were studied by analytical transmission electron microscopy (TEM). A SiO2 amorphous layer about 3.5 nm in thickness between the Si/ZnO interface has been identified by means of spatially resolved electron energy loss spectroscopy. Cross-sectional and plan-view TEM investigations reveal (GaN/ZnO/SiO2/Si) layers exhibiting definite a crystallographic relationship: [111](Si)//[111](ZnO)//[0001](GaN) along the epitaxy direction. GaN films are polycrystalline with nanoscale grains (similar to100 nm in size) grown along [0001] direction with about 20degrees between the (1 (1) over bar 00) planes of adjacent grains. A three-dimensional growth mode for the buffer layer and the film is proposed to explain the formation of the as-grown polycrystalline GaN films and the functionality of the buffer layer. (C) 2004 Elsevier Ltd. All rights reserved.

Effect of the InAlAs and InGaAs combination strain-reducing layer on 1.3 mu m emission self-assembled InAs/GaAs quantum dots

Self-assembled InAs quantum dots (QDs) with differing deposition thicknesses covered by InxAl1-xAs (x = 0.2, 0.3) and In0.2Ga0.8As combination strain-reducing layers (CSRLs) were grown by molecular beam epitaxy. Their structural and optical properties were investigated by atomic force microscopy and photoluminescence spectroscopy, respectively. The emission peak position of InAs QDs capped by CSRL can reach 1.34 mum at room temperature with a relatively larger energy splitting of 93 meV between the ground and first excited states.

Ordering growth of InAs quantum dots on ultra-thin InGaAs strained layer

InAs quantum dots (QDs) were grown On Ultra-thin In0.15Ga0.85As strained layers by molecular beam epitaxy on GaAs (00 1) substrates. Combining reflection high-energy electron diffraction, atomic force microscopy and transmission electron microscopy, we analyzed the stress field of dislocations in the strained layer/substrate interface. Specially, we revealed the relative position of QDs and dislocations. We found that the difference of the stress field around dislocations is prominent when the strained layer is ultra-thin and the stress field will directly affect the following growth. On the strained layer surface, In0.15Ga0.85As ridges will form at the inclined upside of dislocations. Then, InAs QDs will prefer nucleating on the ridges, there is relatively small stress between InAs and In0.15Ga0.85As. By selecting ultra-thin In0.15Ga0.85As layer (50 nm) and controlling the QD layer at just form QDs, we obtained ordered InAs QDs. (C) 2004 Elsevier B.V. All rights reserved.

Raman scattering of folded acoustic phonons in self-assembled Si/Ge dot superlattices

Self-assembled Si/Ge dot multilayers with small, uncorrelated dots fabricated by molecular beam epitaxy in the Stranski-Krastanov growth mode are studied by Raman scattering of folded longitudinal acoustic (FLA) modes. The FLA Raman spectra are analyzed and modeled with respect to mode frequencies and the spectral envelope of mode intensities. The deduced average superlattice properties are consistent with results from atomic force microscopy. The simple Rytov model used for Si/Ge layer structures reproduces very well the frequencies of the FLA modes up to 150 cm(-1). The nonlinearity of phonon dispersion curves in bulk Si for large momenta, however, becomes important for modeling the higher frequencies of observed FLA modes up to 22nd order. The effective dot layer width and an activation energy for thermal intermixing of 2.1+/-0.2 eV are determined from the spectral envelopes of FLA mode intensities of as-grown and annealed Si/Ge dot multilayers. (C) 2004 American Institute of Physics.

Effect of SiO2 encapsulation on the nitrogen reorganization in a GaNAs/GaAs single quantum well

Effects of SiO2 encapsulation and rapid thermal annealing on the optical properties of a GaNAs/GaAs single quantum well (SQW) are studied by low-temperature photoluminescence (LTPL). After annealing at 800degreesC for 30s, a blueshift of the LTPL peak energy for the SiO2-capped region is 25meV and that for the bare region is 0.8meV. The results can attribute to the nitrogen reorganization in the GaNAs/GaAs SQW. It is also shown that the nitrogen reorganization can be obviously enhanced by SiO2 cap-layer. A simple model is used to describe the SiO2-enhanced blueshift of the LTPL peak energy. The estimated activation energy of the N atomic reorganization for the samples annealing with and without SiO2 cap-layer are 2.9eV and 3.1eV, respectively.

Temperature-induced switching-over of the luminescence transitions in GaInNAs/GaAs quantum wells

Photoluminescence (PL) spectra of the GaInNAs/GaAs single quantum well (SQW) with different N compositions are carefully studied in a range of temperatures and excitation power densities. The anomalous S-shape temperature dependence of the PL peak is analysed based on the competition and switching-over between the peaks related to N-induced localized states and the peak related to interband excitonic recombination. It is found that with increasing N composition, the localized energy increases and the turning point of the S-shape temperature dependence occurs at higher temperature, where the localized carriers in the bandtail states obtain enough thermal activation energy to be dissociated and delocalized. The rapid thermal annealing (RTA) effectively reduces the localized energy and causes a decrease of the switching-over temperature.

Electronic properties of GaAs/GayIn1-yNxAs1-y-xSby superlattices

Using Keating's semiempirical valence force field model and Monte Carlo simulation, we calculate the bond distributions and atom positions of GaAs/GaInNAsSb superlattices. The electronic structures of the superlattices are calculated using the folded spectrum method combined with an empirical pseudopotential proposed by Williamson The effects of N and Sb on superlattice energy levels are discussed. The deterioration of the optical properties induced by N is explained by the localization of the conduction-band states around the N atom. The electron and hole effective masses of the superlattices are calculated and compared with the effective masses of the GaAs and GaInAs.