Oriented growth of Bi3.25La0.75Ti3O12 thin films on RuO2/SiO2/Si substrates by using the polymeric precursor method: Structural, microstructural and electrical properties

c-axis oriented Bi3.25La0.75Ti3O12 (BLT) thin films were grown on a RuO2 top electrode deposited on a (100) SiO2/Si substrate by the polymeric precursor method. X-ray diffraction and atomic force microscope investigations indicate that the films exhibit a dense, well crystallized microstructure having random orientations with a rather smooth surface morphology. The electrical properties of preferred oriented Bi3.25La0.75Ti3O12 (BLT) thin films deposited on RuO2 bottom electrode leaded to a large remnant polarization (P-r ) of 17.2 mu C/cm(2) and (V-c ) of 1.8 V, fatigue free characteristics up to 10(10) switching cycles and a current density of 2.2 mu A/cm(2) at 5 V. We found that the polarization loss is insignificant with nine write/read voltages at a waiting time of 10,000 s. Independently of the applied electric field the retained switchable polarization approached a nearly steady-state value after a retention time of 10 s.

Multi-layered LiNbO3 films prepared by a polymeric precursor method

The polymeric precursor method was used to prepare multi-layered LiNbO3 films. The overall process consists of preparing a coating solution from the Pechini process and the deposited film is subsequently heat-treated. Two-layered films were prepared by this process, onto (0001) sapphire substrates. Two different routes were investigated for the heat-treatment. The amorphous route consisted of performing, after each deposition, a pre-treatment at low temperature to eliminate the organic material. In this case, the crystallization heat-treatment was performed only after the two layers had been deposited. on the other hand, a process layer-after-layer crystallization was used. Both routes led to (0001) LiNbO3 oriented films. However, only the film prepared by the layer-after-layer crystallization presented an epitaxial growth and a crack-free morphology. Moreover, the layer-after-layer crystallization process led to a film exhibiting the best optical properties. (C) 2001 Elsevier B.V. Ltd. All rights reserved.

Microstructural and ferroelectric properties of PbZr1-xTi(x)O(3) thin films prepared by the polymeric precursor method

The polymeric precursor method was employed in the preparation of PZT thin films on Pt(111)Ti/SiO2/Si(100) substrates. X-ray diffraction patterns revealed the polycrystalline nature of the PZT (53:47) thin films, which had a granular structure and a grain size of approximately 70 nm. A 350-nm thick film was obtained by running three cycles of the dip-coating/heating process. Atomic force microscopy (AFM) analyses showed the surface of these thin films to be smooth, dense and crack-free with low surface roughness (= 2.0 nm). The PZT (53:47) thin films annealed at 700 degreesC showed a well-saturated hysteresis loop. The C-V curves of perovskite thin film displayed normal ferroelectric behavior, while the remanent polarization (2P(r)) and coercive field (E-e) of the film deposited and measured at room temperature were 40 muC/cm(2) and 110 kV/cm, respectively. (C) 2001 Elsevier B.V. B.V. All rights reserved.

Ferroelectric and dielectric properties of lanthanum-modified bismuth titanate thin films obtained by the polymeric precursor method

Lanthanum-modified bismuth titanate, Bi4-xLaxTi3O12 (BLT), thin films with a La concentration of 0.75 was grown on Pt/Ti/SiO2/Si substrates by using the polymeric precursor solution and spin-coating method. The scanning electron microscopy (SEM) showed rounded grains, which is not typical for these system. The BLT films showed well-saturated polarization-electric field curve which 2P(r) = 41.4 muC/cm(2) and V-c = 0.99 V. The capacitance dependence on the voltage is strongly nonlinear, confirming the ferroelectric properties of the film resulting from the domains switching. These properties make BLT a promising material for FERAM applications.

Ba1-xSrxTiO3 thin films by polymeric precursor method

Stoichiometric Ba1-xSrxTiO3 (BST; x = 0.4) thin films were prepared by the polymeric precursor method. High quality polycrystalline films of BST with low roughness (approximate to 3 nm) were obtained from a Pt/Ti/SiO2/Si substrate deposited by spin-coating technique. Microstructure and morphological evaluation were done using grazing incident X-ray diffraction (GIXRD), scanning electron microscopy (SEM), and atomic force microscopy (AFM). Grazing incident angle XRD characterization of these films showed that BST phase crystallizes at 600 degrees C from an inorganic amorphous matrix. No intermediate crystalline phase was identified. A linear relationship between roughness and grain size was observed. (C) 2000 Elsevier B.V. B.V. All rights reserved.

Electrical characterization of lanthanum-modified bismuth titanate thin films obtained by the polymeric precursor method

Lanthanum-modified bismuth titanate, Bi4-xLaxTi3O12 (BLT), thin films with a La concentration ranging from 0 to 0.75 were grown on Pt/Ti/SiO2/Si substrates using a polymeric precursor solution and spin-coating method. The scanning electron microscopy shows a change of morphology with increasing the lanthanum concentration. The BLT films show well-saturated polarization-electric field curves whit remnant polarizations of 14.7, 20.5, 21.5, and 20.4 muC/cm(2) for x = 0, 0.25, 0.50 and 0.75, respectively. The dielectric constant of BLT (x = 0.75 mol% La) is equal to 158 while dielectric loss remain low (tandelta = 0.0018).

Textured PbZr0.3Ti0.7O3 thin films produced by polymeric precursor method using microwave oven

PbZr0.3Ti0.7O3 (PZT) films were produced by polymeric precursor route and deposited by spin-coater technique on Pt(111)/Ti/SiO2/Si(100) substrates. The films were heat-treated using different furnaces: (a) a conventional furnace, at 700 degrees C; and (b) a domestic microwave oven, at 600 degrees C. The X-ray patterns revealed that both films are single phase and reflections were identified as belongs to the PZT phase. The intensity of these reflections showed a (111), (001) and (100) preferred orientation. Morphological and electrical characterizations showed that all samples present a rather different microstructure and both with high spontaneous polarization.

The effect of microwave annealing on the electrical characteristics of lanthanum doped bismuth titanate films obtained by the polymeric precursor method

Lanthanum doped bismuth titanate thin films (Bi3.25La0.75Ti3O12-BLT) were produced by the polymeric precursor method and crystallized in a domestic microwave oven and in conventional furnace. Using platinum coated silicon substrates configuration, ferroelectric properties of the films were determined with remanent polarization P-r and a coercive field E-c of 3.9 mu C/cm(2) and 70 kV/cm for the film annealed in the microwave oven and 20 mu C/cm(2) and 52 kV/cm for the film annealed in conventional furnace, respectively. The films annealed in conventional furnace exhibited excellent retention-free characteristics at low infant periods indicating that BLT thin films can be a promise material for use in nonvolatile memories. on the other hand, the pinning of domains wall causes a strong decay at low infant periods for the films annealed in the microwave furnace which makes undesireable the application for future FeRAMS memories. (c) 2005 Elsevier B.V. All rights reserved.

Synthesis by the polymeric precursor method and characterization of undoped and Sn, Cr and V-doped ZrTiO4

In this work, zirconium titanate doped with 0. 1, 0.2, and 0.4 mole% of tin, chromium and vanadium was synthesized by the polymeric precursors method and characterized by thermal analysis (TG/DTA), X-ray diffraction (XRD), nitrogen adsorption and scanning electronic microscopy (SEM). The powder presented two mass losses attributed to the exit of water and to the pyrolysis of the organic material. The surface area reduction observed from 500 degrees C indicates the beginning of the sintering process. All the dopants led to changes in the lattice parameters and to the decrease of both crystallite size and particle size. (c) 2005 Elsevier B.V. All rights reserved.

Retention characteristics in Bi3.25La0.75Ti3O12 thin films prepared by the polymeric precursor method

Ferroelectric Bi3.25La0.75Ti3O12 (BLT) thin films were deposited on Pt/Ti/SiO2/Si substrates by the polymeric precursor method. The films present c-axis preferred orientation after annealing at 700 degrees C for 2 h in conventional furnace. All the capacitors showed good polarization fatigue characteristics at least up to 1x10(10) bipolar pulse cycles and excellent retention properties up to 1x10(4) s. We found that the polarization loss is insignificant with five write/read voltages at a waiting time of 10 000 S. Independently of the applied electric field the retained switchable polarization approached a nearly steady-state value after a retention time of 10 s. (C) 2005 American Institute of Physics.

Barium strontium titanate powder obtained by polymeric precursor method

Pure barium strontium titanate powder, with Ba/Sr ratio of 80/20 was prepared by the polymeric precursor method (also called Pechini process). The powder was obtained after a calcination at 800 degreesC for 8 h and characterized by XRD, IR, BET and SEM. The requirements to avoid barium carbonate as a secondary phase are presented and discussed in detail. (C) 2003 Elsevier B.V. All rights reserved.

Effect of thermal treatment temperature on the crystallinity and morphology of LiTaO3 thin films prepared from polymeric precursor method

Lithium tantalate thin films (LiTaO3) with (50:50) stoichiometry were prepared by spin coating method using a polymeric organic solution. The films were deposited on silicon (100) substrates with 4 layers. The substrates were previously cleaned and then the solution of lithium tantalate was deposited by adjusting the speed at 5000 rpm. The thin films deposited were thermally treated from 350 to 600degreesC for 3 hours in order to study the influence of the thermal treatment temperature on the crystallinity, microstructure, grain size and roughness of the final film. X-ray diffraction (XRD) results showed that the films are polycrystalline and secondary phases free. The thickness of films was observed by scanning electron microscopy (SEM). The atomic force microscopy (AFM) studies showed that the grain size and roughness are strongly influenced by thermal treatment.

Fatigue-free behavior of Bi3.25La0.75Ti3O12 thin films grown on several bottom eletrodes by the polymeric precursor method

Fatigue-free Bi3.25La0.75Ti3O12 (BLT) thin films were grown on LaNiO3,RuO2, and La0.5Sr0.5CoO3 bottom electrodes in a microwave furnace at 700 degreesC for 10 min. The remanent polarization (P-r) and the drive voltage (V-c) were in the range of 11-23 muC/cm(2) and 0.86-1.56 V, respectively, and are better than the values found in the literature. The BLT capacitors did not show any significant fatigue up to 10(10) read/write switching cycles. (C) 2004 American Institute of Physics.

Microwave synthesis of calcium bismuth niobate thin films obtained by the polymeric precursor method

The crystal structure, surface morphology and electrical properties of layered perovskite calcium bismuth niobate thin films (CaBi2Nb2O9-CBN) deposited on platinum coated silicon substrates by the polymeric precursor method have been investigated. The films were crystallized in a domestic microwave and in a conventional furnace. X-ray diffraction and atomic force microscopy analysis confirms that the crystallinity and morphology of the films are affected by the different annealing routes. Ferroelectric properties of the films were determined with remanent polarization P-r and a drive voltage V-c of 4.2 mu C/cm(2) and 1.7 V for the film annealed in the conventional furnace and 1.0 mu C/cm(2) and 4.0 V for the film annealed in microwave furnace, respectively. A slight decay after 10(8) polarization cycles was observed for the films annealed in the microwave furnace indicating a reduction of the domain wall mobility after interaction of the microwave energy with the bottom electrode. (C) 2006 Elsevier Ltd. All rights reserved.

Effect of preannealing on the morphology of LiTaO3 thin films prepared from the polymeric precursor method

Lithium tantalate (LiTaO3) thin films with 50:50 stoichiometry were deposited on silicon (100) substrates with two layers by the spin coating method using a polymeric organic solution. In order to study the influence of preannealing on the crystallinity, microstructure, grain size and roughness of the final film, two annealing procedures, slow preannealing and fast preannealing, were used. X-ray diffraction (XRD) results showed that LiTaO3 thin films are polycrystalline. It was observed by scanning electron microscopy (SEM) that the thin film, which had been thermally treated using slow preannealing, was characterized by a dense and homogeneous surface. The atomic force microscopy (AFM) studies showed that the roughness is strongly influenced by preannealing temperature. (C) 2003 Elsevier B.V. All rights reserved.