Proton irradiation-induced defects in undoped GaSb studied by positron lifetime spectroscopy and photoluminescence

Undoped GaSb was irradiated by 2.6 MeV protons. The irradiation-induced defects were studied by positron lifetime spectroscopy (PLS) and photoluminescence (PL). Positron lifetime measurements showed that vacancy-type defects were introduced after irradiation, and divacancies were formed at higher irradiation dose. Annealing experiments revealed there were different annealing steps between the as grown and proton-irradiated samples, the reason for which was tentatively attributed to the formation of divacancies in the proton-irradiated samples during annealing. All the vacancy defects could be annealed out at around 500 degrees C. The PL intensity quickly fell down after proton irradiation and decreased with increasing irradiation dose, indicating that irradiation induced non-irradiative recombination centers, whose candidates were assigned to the vacancy defects induced by proton irradiation.

Optimal teleportation via thermal entangled states of a two-qubit Heisenberg chain

We study the optimal teleportation based on Bell measurements via the thermal states of a two-qubit Heisenberg XXX chain in the presence of the Dzyaloshinsky-Moriya (DM) anisotropic antisymmetric interaction and obtain an optimal unitary transformation. The explicit expressions of the output state and the teleportation fidelity are presented and compared with those of the standard protocol. It is shown that in this protocol the teleportation fidelity is always larger and the unit fidelity is achieved at zero temperature. The DM interaction can enhance the teleportation fidelity at finite temperatures, as opposed to the effect of the interaction in the standard protocol. Cases with other types of anisotropies are also discussed. Copyright (C) EPLA, 2009

Photoluminescence from heterogeneous SiGe/Si nanostructures prepared via a two-step approach strategy

A two-step approach of preparation for SiGe/Si heterogeneous nanostructures, which combined with ultra-high vacuum chemical deposition and electrochemical anodization techniques, is demonstrated. Uniformly distributed nanostructures with a quite uniform distribution of size and morphology are obtained. A strong room-temperature photoluminescence from the nanostructures was observed with a narrow full-width at half-maximum of around 110 meV. The possible origins of the two main peaks at around 1.6 and 1.8 eV have been discussed in detail. The two-step approach is proved to be a promising method to fabricate new Si-based optoelectronic materials. (C) 2009 Elsevier B.V. All rights reserved.

Room temperature photoluminescence of tensile-strained Ge/Si0.13Ge0.87 quantum wells grown on silicon-based germanium virtual substrate

We report a room temperature study of the direct band gap photoluminescence of tensile-strained Ge/Si0.13Ge0.87 multiple quantum wells grown on Si-based germanium virtual substrates by ultrahigh vacuum chemical vapor deposition. Blueshifts of the luminescence peak energy from the Ge quantum wells in comparison with the Ge virtual substrate are in good agreement with the theoretical prediction when we attribute the luminescence from the quantum well to the c Gamma 1-HH1 direct band transition. The reduction in direct band gap in the tensile strained Ge epilayer and the quantum confinement effect in the Ge/Si0.13Ge0.87 quantum wells are directly demonstrated by room temperature photoluminescence.

Chirp-free optical modulation using a silicon push-pull coupling microring

We propose a silicon ring-based optical modulation method to perform chirp-free optical modulations. In this scheme, we locate the light to be modulated at the resonance of the ring and tune the coupling coefficient between the ring and the straight waveguide by using a push-pull coupling structure. The chirp-free phase modulation can be achieved by varying the coupling coefficient in a large range, which can modify the coupling condition of the ring such that the input light experiences an abrupt phase shift of pi at the output. If the coupling coefficient is adjusted in a small range such that the coupling condition of the ring is kept unchanged, only the intensity of the light will be modulated. This leads to chirp-free intensity modulation. Our simulations performed at 10 Gbits/s confirm the feasibility of the proposal. (C) 2009 Optical Society of America

Maximal Heat Generation in Nanoscale Systems

National Basic Research Programme of China G2009CB929300 National Natural Science Foundation of China 10404010 6052100160776061Supported by the National Basic Research Programme of China under Grant No G2009CB929300, and the National Natural Science Foundation of China under Grant Nos 10404010, 60521001 and 60776061.

Bulge testing and fracture properties of plasma-enhanced chemical vapor deposited silicon nitride thin films

The mechanical properties and fracture behavior of silicon nitride (SiNx) thin film fabricated by plasma-enhanced chemical vapor deposition is reported. Plane-strain moduli, prestresses, and fracture strengths of silicon nitride thin film; deposited both oil a bare Si substrate and oil a thermally oxidized Si substrate were extracted using bulge testing combined with a refined load-deflection model of long rectangular membranes. The plane-strain modu i and prestresses of SiNx thin films have little dependence on the substrates, that is, for the bare Si substrate, they are 133 +/- 19 GPa and 178 +/- 22 MPa, respectively, while for the thermally oxidized substrate, they are 140 +/- 26 Gila and 194 +/- 34 MPa, respectively. However, the fracture strength values of SiNx films grown on the two substrates are quite different, i.e., 1.53 +/- 0.33 Gila and 3.08 +/- 0.79 GPa for the bare Si substrate a A the oxidized Si substrate, respectively. The reference stresses were computed by integrating the local stress of the membrane at the fracture over the edge, Surface, and volume of the specimens and fitted with the Weibull distribution function. For SiNx thin film produced oil the bare Si Substrate, the Volume integration gave a significantly better agreement between data and model, implying that the volume flaws re the dominant fracture origin. For SiNx thin film grown on the oxidized Si substrate, the fit quality of surface and edge integration was significantly better than the Volume integration, and the dominant surface and edge flaws could be caused by buffered HF attacking the SiNx layer during SiO2 removal. Crown Copyright (C) 2008 Published by Elsevier B.V. All rights reserved.

Properties of high k gate dielectric gadolinium oxide deposited on Si(100) by dual ion beam deposition (DIBD)

Gadolinium oxide thin films have been prepared on silicon (100) substrates with a low-energy dual ion-beam epitaxial technique. Substrate temperature was an important factor to affect the crystal structures and textures in an ion energy range of 100-500 eV. The films had a monoclinic Gd2O3 structure with preferred orientation ((4) over bar 02) at low substrate temperatures. When the substrate temperature was increased, the orientation turned to (202), and finally, the cubic structure appeared at the substrate temperature of 700 degreesC, which disagreed with the previous report because of the ion energy. The AES studies found that Gadolinium oxide shared Gd2O3 structures, although there were a lot of oxygen deficiencies in the films, and the XPS results confirmed this. AFM was also used to investigate the surface images of the samples. Finally, the electrical properties were presented. (C) 2004 Elsevier B.V. All rights reserved.

Electromagnetic-field-induced cohesive force enhancement in a metallic nanowire

We theoretically study the conducting electronic contribution to the cohesive force in a metallic nanowire irradiated under a transversely polarized external electromagnetic field at low temperatures and in the ballistic regime. In the framework of the free-electron model, we have obtained a time-dependent two-level electronic wavefunction by means of a unitary transformation. Using a thermodynamic statistical approach with this wavefunction, we have calculated the cohesive force in the nanowire. We show that the cohesive force can be divided into two components, one of which is independent of the electromagnetic field (static component), which is consistent with the existing results in the literature. The magnitude of the other component is proportional to the electromagnetic field strength. This extra component of the cohesive force is originally from the coherent coupling between the two lateral energy levels of the wire and the electromagnetic field.

Effect of the oxygen concentration on the properties of Gd2O3 thin films

Gd2O3 thin films were deposited on Si (100) substrates at 650degreesC by a magnetron sputtering system under different Ar/O-2 ratios of 6:1, 4:1 and 2:1. The effect of the oxygen concentration on the properties of oxide thin films was investigated by X-ray diffraction, X-ray photoelectron spectroscopy, atomic force microscopy and capacitance-voltage (C-V)measurement. X-ray diffraction shows that the structure of oxide films changed from the monoclinic Gd2O3 phase to cubic Gd2O3 phase when the oxygen concentration increased. According to C-V measurement, the dielectric constant value of the samples deposited at different Ar/O-2 ratios is about 12. (C) 2004 Elsevier B.V. All rights reserved.

Mn implanted GaAs by low energy ion beam deposition

High dose Mn was implanted into semi-insulating GaAs substrate to fabricate embedded ferromagnetic Mn-Ga binary particles by mass-analyzed dual ion beam deposit system at room temperature. The properties of as-implanted and annealed samples were measured with X-ray diffraction, high-resolution X-ray diffraction to characterize the structural changes. New phase formed after high temperature annealing. Sample surface image was observed with atomic force microscopy. All the samples showed ferromagnetic behaviour at room temperature. There were some differences between the hysteresis loops of as-implanted and annealed samples as well as the cluster size of the latter was much larger than that of the former through the surface morphology. (C) 2004 Elsevier B.V. All rights reserved.

Fabrication of GdSi2 film by low-energy ion-beam implantation

Single-phase gadolinium disilicide was fabricated by a low-energy ion-beam implantation technique. Auger electron spectroscopy and X-ray photoelectron spectroscopy were used to determine the composition and chemical states of the film. The structure of the sample was analyzed by X-ray diffraction and the surface morphology was investigated by scan electron microscopy. Based on the measurements, only orthorhombic GdSi2 phase was found in the sample and the surface morphology was pitting. After annealing at 350degreesC for 30 min at Ar atmosphere, the full-width at half-maximum of GdSi2 became narrower. It indicates that the GdSi2 is crystallized better after annealing. (C) 2003 Elsevier B.V. All rights reserved.

Large-scale synthesis of single-phase, high-quality GaN nanocrystallites

Large-scale synthesis of high-quality GaN nano-crystallites has been achieved by direct reaction of a 4:1 molar Ga/Ga2O3 mixture with ammonia at 950degreesC. X-ray diffraction, transmission electron microscopy, selected-area electron diffraction and high-resolution transmission electron microscopy revealed that the produced GaN nanocrystallites were single hexagonal wurtzite structure with an average particle size around 45 nm. A sharp near band edge emission peak and a blue light emission peak were observed in photoluminescence spectroscopy. The synthesis approach is simple and easy to be commercialized.

Parameters determining crystallinity in beta-SiC thin films prepared by catalytic chemical vapor deposition

The effects of deposition gas pressure and H-2 dilution ratio (H-2/SiH4+CH4+H-2), generally considered two of dominant parameters determining crystallinity in beta-SiC thin films prepared by catalytic chemical vapor deposition (Cat-CVD), often called hot-wire CVD method, on the films properties have been systematically studied. As deposition gas pressure increase from 40 to 1000 Pa, the crystallinity of the films is improved. From the study of H-2 dilution ratio, it is considered that H-2 plays a role as etching gas and modulating the phases in beta-SiC thin films. On the basis of the study on the parameters, nanocrystalline beta-SiC films were successfully synthesized on Si substrate at a low temperature of 300degreesC. The Fourier Transform Infrared Spectroscopy (FTIR) and X-ray diffraction (XRD) spectra show formation of beta-SiC. Moreover, according to Sherrer equation, the average grain size of the films estimated is in nanometer-size. (C) 2003 Elsevier B.V. All rights reserved.

(Ga, Gd, As) film growth on GaAs substrate by low-energy ion-beam deposit

(Ga, Gd, As) film was fabricated by the mass-analyzed dual ion-beam epitaxy system with the energy of 1000 eV at room temperature. There was no new peak found except GaAs substrate peaks (0 0 2) and (0 0 4) by X-ray diffraction. Rocking curves were measured for symmetric (0 0 4) reflections to further yield the lattice mismatch information by employing double-crystal X-ray diffraction. The element distributions vary so much due to the ion dose difference from AES depth profiles. The sample surface morphology indicates oxidizing layer roughness is also relative to the Gd ion dose, which leads to islandlike feature appearing on the high-dose sample. One sample shows ferromagnetic behavior at room temperature. (C) 2003 Elsevier B.V. All rights reserved.