Determination of the properties of an experimental glass polyalkenoate cement prepared from niobium silicate powder containing fluoride

Objectives. The purpose of this paper is to modify the conventional calcium fluoro-aluminosilicate glass, which is used in the formation of glass ionomer cements (CIGs) by the niobium addition and to study the properties of GICs obtained.Materials and methods. Sol-gel process was used to prepare the powder at lower temperature than fusion method. Glass-ceramic powder obtained in this way was used to prepare the GICs. The properties such as working and setting times, microhardness and diametral tensile strength were evaluated for the experimental GICs and a commercial luting cement.Results. The ideal powder:liquid (P:L) ratio determined to prepare the experimental GICs was equal to 1:1. The cements prepared using this ratio showed working and setting times similar to the commercial GICs. in mechanical tests it was observed that microhardness and diametral tensile strength of the experimental GICs decreased significantly with the reduction of P:L ratio. on the other hand, the results obtained in microhardness tests indicated that the presence of niobium was a positive factor.Significance. The chemical process allows the development of glass-ceramic powder at 600 degrees C which is the goal of the present paper. It was concluded that GICs containing niobium might be used in dental applications and these results encourage further researches on other compositions. (c) 2007 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Physicochemical properties of endodontic sealers of different bases

Objective: To assess the setting time (ST), flow (FL), radiopacity (RD), solubility (SB) and dimensional change following setting (DC) of different sealers (AH Plus (R), Polifil, Apexit Plus (R), Sealapex (R), Endomethasone (R) and Endofill (R)) according to American National Standards Institute/American Dental Association (ANSI/ADA) Specification 57. Material and methods: Five samples of each material were used for each test. For ST, cast rings were filled with sealers and tested with a Gillmore needle. For FL, the sealer was placed on a glass plate. After 180 s, another plate with 20 g and a load of 100 g were applied on the material, and the diameters of the discs formed were measured. In RD, circular molds were filled with the sealers, radiographed and analyzed using Digora software. For SB, circular molds were filled with the sealers, a nylon thread was placed inside the material and another glass plate was positioned on the set, pressed and stored at 37 degrees C. Samples were weighed, placed in water, dried and reweighed. The water used for SB was analyzed by atomic absorption spectrometry. For DC, circular molds were filled with the sealers, covered by glass plates and stored at 37 degrees C. Samples were measured and stored in water for 30 days. After this period, they were dryed and measured again. Results: Regarding ST, AH Plus (R), Apexit (R) and Endofil (R) sealers are in accordance with ANSI/ADA standards. Endomethasone's manufacturer did not mention the ST; Polifil is an experimental sealer and Sealapex (R) did not set. Considering RD, SB and DC, all sealers were in accordance with ANSI/ADA. The spectrometric analysis showed that a significant amount of K+ and Zn2(+) ions was released from Apexit Plus (R) and Endofill (R), respectively. Conclusion: Except for DC, all other physicochemical properties of the tested sealers conformed to ANSI/ADA requirements.

Thermophysical Properties of Industrial Sugar Cane Juices for the Production of Bioethanol

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Magnetic properties of poly(3-hexylthiophene)

A room temperature ferromagnetic phase is observed in samples of poly(3-hexylthiophene) partially doped with ClO (4) over bar. The magnetic behavior presents a strong dependence on the sample preparation conditions, in particular, a dependence with the final potential of the sample after reduction. The origin of the ferromagnetism is proposed to be associated with interactions between spin 1/2 polarons formed in the polymeric chain upon doping. The dependence of saturation and spontaneous magnetization as the function of the final potential after reduction shows a way to control the magnetic properties of this polymer. (C) 2008 Elsevier B.V. All rights reserved.

Efficiency of ethanol conversion induced by controlled modification of pore structure and acidic properties of alumina catalysts

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Influence of thickness on crystallization and properties of LiNbO3 thin films

Thin films of lithium niobate were deposited on Pt/Ti/SiO2 (111) substrates by spin coating from the polymeric precursor method (Pechini process). Annealing in static air was performed at 500 degreesC for 3 h. The obtained films were characterized by X-ray diffraction and atomic force microscopy. The dielectric constant, dissipation factor and resistance were measured in frequency region from 10 Hz to 10 MHz and the hysteresis loop was obtained. The influence of number of layers on crystallization, morphology and properties of LiNbO3 thin films is discussed. (C) 2003 Elsevier B.V. All rights reserved.

Electrical properties of lanthanum doped Bi4Ti3O12 thin films annealed in different atmospheres

Pure-and lanthanun doped Bi4Ti3O12 thin films were deposited on Pt/Ti/SiO2/Si substrate using a polymeric precursor solution. Annealing in static air and oxygen atmosphere was performed at 700 degrees C for 2 h. The obtained films were characterized by X-ray diffraction and atomic force microscopy. The dielectric constant and dissipation factor were measured in the frequency region from 1 kHz to 1 MHz. Electrical characterization of the films pointed to ferroelectricity via hysteresis loop. Films annealed in static air possess a dielectric constant higher than films annealed in oxygen atmosphere due to differences in the grain size, crystallinity and structural defects. A regularly shaped hystereses loop is observed after annealing in static air. The obtained results suggest that the annealing in oxygen atmosphere can increase the trapped charge and the relaxation phenomenon. (c) 2006 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Aspects of solid state formation and properties of Sn(0.9)Ti(0.1)O(2) system doped with CoO and Nb(2)O(5)

The effect of calcination temperature during the formation of the solid solution Sn(0.9)Ti(0.1)O(2) doped with 1.00 mol % CoO and 0.05 mol % Nb(2)O(5) is presented. The structural characteristics of this system were studied using X-ray diffraction, and the changes in phase formation were analyzed using the Rietveld method. With an increase in calcination temperature, there is increasing miscibility of Ti into the (Ti,Sn)O(2) phase and near 1000 degrees C, and the remaining TiO(2) (anatase) was transformed into the rutile phase. The sintering process, monitored using dilatometry, suggests two mass transport mechanisms, one activated close to 900 degrees C associated with the presence of TiO(2) (anatase) and the second mechanism, occurring between 1200 and 1300 degrees C, is attributed to a faster grain boundary diffusion caused by oxygen vacancies. (C) 2008 International Centre for Diffraction Data.

Surface structure and electronic properties of Pt-Fe/C nanocatalysts and their relation with catalytic activity for oxygen reduction

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Rietveld analysys and electrical properties of lanthanum doped BiFeO3 ceramics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Microstructure and electrical properties of (Ta, Co, Pr) doped TiO2 based electroceramics

The addition of different dopants affects the densification, mean grain size and electrical properties of TiO2-based varistor ceramics. This paper discusses the microstructural and electrical properties of (Ta, Co, Pr) doped TiO2 systems, demonstrating that some of these systems display electrical properties that allow for their use as low voltage varistor. Dopants such as Ta2O5 play a special role in the formation of barriers at the grain boundary and in the nonlinear behavior in TiO2-based systems. The higher values of nonlinear coefficient and breakdown electric field were obtained in the system just doped with Ta2O5 and CoO.

The role of the Eu3+ ions in structure and photoluminescence properties of SrBi2Nb2O9 powders

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Photolumiscent Properties of Nanorods and Nanoplates Y2O3:Eu3+

Nanorods and nanoplates of Y2O3:Eu3+ powders were synthesized through the thermal decomposition of the Y(OH)(3) precursors using a microwave-hydrothermal method in a very short reaction time. These powders were analyzed by X-ray diffraction, field emission scanning electron microscopy, Fourrier transform Raman, as well as photoluminescence measurements. Based on these results, these materials presented nanoplates and nanorods morphologies. The broad emission band between 300 and 440 nm ascribed to the photoluminescence of Y2O3 matrix shifts as the procedure used in the microwave-hydrothermal assisted method changes in the Y2O3:Eu3+ samples. The presence of Eu3+ and the hydrothermal treatment time are responsible for the band shifts in Y2O3:Eu3+ powders, since in the pure Y2O3 matrix this behavior was not observed. Y2O3:Eu3+ powders also show the characteristic Eu3+ emission lines at 580, 591, 610, 651 and 695 nm, when excited at 393 nm. The most intense band at 610 nm is responsible for the Eu3+ red emission in these materials, and the Eu3+ lifetime for this transition presented a slight increase as the time used in the microwave-hydrothermal assisted method increases.

Synthesis, characterization and photophysical properties of Eu3+ doped in BaMoO4

In this work Ba0.99Eu0.01MoO4 (BEMO) powders were prepared by the first time by the Complex Polymerization Method. The structural and optical properties of the BEMO powders were characterized by Fourier Transform Infra-Red (FTIR), X-ray Diffraction (XRD), Raman Spectra, High-Resolution Scanning Electron Microscopy (HR-SEM) and Photoluminescent Measurements. XRD show a crystalline scheelite-type phase after the heat treatment at temperatures greater than 400 degrees C. The ionic radius of Eu3+ (0.109 nm) is lower than the Ba2+ (0.149 nm) one. This difference is responsible for the decrease in the lattice parameters of the BEMO compared to the pure BaMoO4 matrix. This little difference in the lattice parameters show that Eu3+ is expected to occupy the Ba2+ site at different temperatures, stayed the tetragonal (S-4) symmetry characteristic of scheelite-type crystalline structures of BaMoO4. The emission spectra of the samples, when excited at 394 nm, presented the D-5(1)-> F-7(0, 1 and 2) and D-5(0)-> F-7(0, 1, 2, 3 and 4) Eu3+ transitions at 523, 533, 554, 578, 589, 614, 652 and 699 nm, respectively. The emission spectra of the powders heat-treated at 800 and 900 degrees C showed a marked increase in its intensities compared to the materials heat-treated from 400 to 700 C. The decay times for the sample were evaluated and all of them presented the average value of 0.61 ms. Eu3+ luminescence decay time follows one exponential curve indicating the presence of only one type of Eu3+ symmetry site.

Thermal, structural and optical properties of new tungsten lead-pyrophosphate glasses

Crystalline lead-pyrophosphate precursor was prepared in aqueous solution from lead nitrate and phosphoric acid and characterized by X-ray diffraction, thermogravimetry and Raman scattering. This crystalline lead-phosphate was then used to prepare glass samples in the binary system Pb(2)P(2)O(7)-WO(3). Dependence of WO(3) content on thermal, structural and optical properties were investigated by thermal analysis (DSC), Raman spectroscopy, UV-visible and near-infrared absorption and M-Line technique to access refractive index values. Incorporation of WO(3) in the lead-pyrophosphate matrix enhances the glass transition temperature and thermal stability against devitrification, favors formation of P-O-W bonds and WO(6) clusters. In addition, optical properties are strongly modified with a redshift of the optical bandgap with WO(3) incorporation as well as an increase of the refractive index from 1.89 to 2.05 in the visible. (C) 2011 Elsevier B.V. All rights reserved.