激光辐照引起Ge2Sb2Te5非晶态薄膜的电/光性质变化

研究了激光辐照引起Ge2Sb2Te5非晶态薄膜的电/光性质变化,当激光功率为580mW时薄膜的方块电阻有四个数量级（10^7～10^3Ω/□）的突变;对电阻发生突变前、中、后的三个样品进行了XRD测试,结果表明,随着激光功率的增大,薄膜由非晶态向晶态转变,用椭偏仪测试了结构转变前、中、后三个样品的光学常数,在可见光范围内薄膜的光学常数在波长相同情况下有：n（非晶态）〉n（中间态）〉n（晶态）,k（晶态）〉k（中间态）〉k（非晶态）,α（晶态）〉α（中间态）〉α（非晶态）,结合电阻变化曲线和XRD图谱讨论了激光辐照Ge2Sb2Te5非晶态薄膜的电/光性质变化同激光功率和结构转变之间的关系.

Write-once medium with Fe-Doped BiOx thin films for blue laser recording

Fe:BiOx films are fabricated on K9 glass substrates by rf-magnetron sputtering of a BiFeO target under argon atmosphere with increasing sputtering power from 80 to 200 W at room temperature. It is found that the thin films grown at the sputtering power of 160W can be formed at an appropriate deposition rate and have an improved surface morphology. The XPS result reveals that the films investigated are comprised of Bi, Fe and O elements. A typical XRD pattern shows that no phase transition occurs in the films up to 400 degrees C. The results of the blue laser recording test demonstrate that the Fe:BiOx films have good writing sensitivity for blue laser beam (406.7 nm) and good stability after reading 10000 times. The recording marks of 200nm or less are obtained. These results indicate that the introduction of Fe into BiOx films can reduce the mark size and improve the stability of the films.

Si underlayer induced nano-ablation in AgInSbTe thin films

AgInSbTelSi thin films on glass substrates are prepared by dc magnetron sputtering at room temperature. Using Si underlayer as the thermal diffusion layer, the super-resolution nano-ablation holes with a size of 70nm in the AgInSbTe phase change films are obtained by a far-field focused laser experimental setup, with laser wavelength 405nm and objective-lens numerical aperture 0.90. The nano-ablation formation mechanism is analysed and discussed via the thermal diffusion of sample structures.

Structural change of laser-irradiated Ge2Sb2Te5 films studied by electrical property measurement

Sheet resistance of laser-irradiated Ge2Sb2Te5 thin films prepared by magnetron sputtering was measured by the four-point probe method. With increasing laser power the sheet resistance undergoes an abrupt drop from 10(7) to 10(3) Omega/square at about 580 mW. The abrupt drop in resistance is due to the structural change from amorphous to crystalline state as revealed by X-ray diffraction (XRD) study of the samples around the abrupt change point. Crystallized dots were also formed in the amorphous Ge2Sb2Te5 films by focused short pulse laser-irradiated, the resistivities at the crystallized dots and the non-crystallized area are 3.375 x 10(-3) and 2.725 Omega m, sheet resistance is 3.37 x 10(4) and 2.725 x 10(7) Omega/square respectively, deduced from the I-V Curves that is obtained by conductive atomic force microscope (C-AFM). (C) 2008 Elsevier B.V. All rights reserved.

Si（111）衬底上ZnO薄膜的磁控溅射法制备及表征

采用磁控溅射法在(111)单晶硅衬底上沉积了ZnO薄膜，并研究了退火温度对ZnO薄膜晶体质量、晶粒度大小、应力和光致发光谱的影响。X射线衍射(XRD)表明薄膜为高度c轴择优取向。不同退火温度下的ZnO薄膜应力有明显变化。应力分布最为均匀的退火温度为500℃。室温下对ZnO薄膜进行了光谱分析，可观测到明显的紫光发射(波长为380nm左右)。实验结果表明，用磁控溅射法在单晶硅衬底上能获得高质量的ZnO薄膜。

射频磁控溅射法制备TiO2-xNX薄膜的结构性能研究

利用射频磁控溅射法室温下在Si（100）衬底上制备了N掺杂的TiO2薄膜，并且采用x射线衍射（XRD）、X射线光电子能谱（XPS）和透射光谱对薄膜进行了表征。XRD结果表明在纯Ar和N2（33．3％）／Ar气氛下制备的TiO2-xNx薄膜均为单一的金红石相，薄膜结晶性良好，呈高度（211）择优取向，而在N2（50．0％）／Ar下制备的薄膜结晶性明显变差；对于N掺杂的TiO2薄膜，XPS表明部分N原子进入TiO2晶格，并且以N—Ti—O、N—O键以及间隙式N原子形式存在；透射光谱表明掺N后的TiO2薄膜吸收边发生了红移。

非晶硅薄膜制备及其晶化特性研究

用磁控溅射法在K9玻璃上沉积了非晶硅（a—Si）膜和a—Si／Al膜，并将其在流动的N2气氛下进行退火。对退火前后的样品进行Raman光谱、XRD和SEM表征和分析。Raman光谱表明随着退火温度的升高，a-Si膜的散射峰出现了明显的蓝移，但XRD结果表明薄膜仍为非晶态；而a—Si／Al膜在温度很低时就已经开始晶化。

LiGaO_2衬底上ZnO外延膜的结构与光学特性

采用磁控溅射法在(001)、(100)及(010)LiGaO2衬底上制备了ZnO薄膜,通过X射线衍射(XRD)、原子力显微镜(AFM)、透过光谱以及光致发光谱(PL)对薄膜的结构、形貌及光学性质进行了表征。结果表明LiGaO2衬底不同晶面上制备的ZnO薄膜具有不同的择优取向,在(001)(、100)及(010)LiGaO2上分别获得了[0001][、1100]及[1120]取向的ZnO薄膜;不同取向的ZnO薄膜表面形貌差异较大;薄膜在可见光波段具有较高的透过率;在ZnO薄膜的光致发光谱中只观察到了位于378 nm的紫外发射峰,而深能级发射几乎观察不到,(1100)取向的薄膜紫外发射峰强度最大,半高宽也最小,薄膜光致发光性质的差异主要和晶粒尺寸有关。

Growth and characterization of ZnO films on (0 0 1), (1 0 0) and (0 1 0) LiGaO2 substrates

ZnO films were fabricated on LiGaO2 (0 0 1), (10 0) and (0 10) planes by RF magnetron sputtering. The structural, morphological and optical properties of as-grown ZnO films were investigated by X-ray diffraction (XRD), atomic force microscopy (AFM), Raman spectra and photoluminescence (PL) spectra. It is found that the orientation of ZnO films is strongly dependent on the substrate plane. [0 0 0 11, [1 (1) over bar 00] and [11 (2) over bar0] oriented ZnO films are deposited on LiGaO2 (001), (100) and (010), respectively. AFM shows the (0001) ZnO film consists of well-aligned regular hexagonal grains. Raman spectra reveal a tensile stress in the (0 0 0 1) ZnO film and a compressive stress in (110 0) and (112 0) ZnO films. PL spectra of all ZnO films exhibit only a near-band-edge UV emission peak. (C) 2008 Elsevier B.V. All rights reserved.

Study of thin-film SO2 gas sensors by photometric and ellipsometric methods

Pt-, Pd-, and Zr-doped SnO2 thin films and dopant-free VOx films were fabricated by planar magnetron sputtering. Tests for sensitivity to SO2 for all samples were conducted at 180 degreesC, and the sensitivities were investigated ex situ with photometric and ellipsometric methods at room temperature. It was found that the optical sensitivities as well as the sensitive wavelength region for SnO2 films could be tuned by doping. The Pd-doped SnO2 films had good sensitivity in the visible range, and the Zr-doped in the near IR. The dominant sensitive wavelength region for VOx films fell into the visible range, and the ratio of the sensitivity in the visible to that in the near IR increased with O-2/Ar in the depositing atmosphere. (C) 2001 society of Photo-Optical instrumentation Engineers .

Effect of chromium intermediate layer on properties of silver coatings

Coatings with layer structures of Ag/glass, Ag/Cr/glass, and Ag/Cr-Ag/Cr/glass deposited with magnetron sputtering are investigated. The results indicate that the performance for reflectance, hardness, adherence, and humidity durability of the silver coatings with Ag/Cr/glass and Ag/Cr-Ag/Cr/glass structures are better than pure silver film. In addition, the silver coatings with an Ag/Cr-Ag/glass structure present more advantages than that of the Ag/Cr/glass. Reasons are analyzed accordingly. (C) 2004 Society of Photo-Optical Instrumentation Engineers.

离子束溅射法薄膜生长中结瘤微缺陷的生长机理

用离子束溅射法制备了锆单层薄膜．用设计新型夹具和预置种子方法，对薄膜中结瘤微缺陷的生长过程进行了研究．在高分辨率光学显微镜和扫描电子显微镜下观察发现，结瘤在其生长初期呈现出分形的特征．用分子动力学和薄膜生长的扩散限制聚集模型，薄膜中结瘤微缺陷成核时的分形现象得到了很好的解释．

微缺陷对薄膜滤光片环境稳定性的影响

用热蒸发方法沉积了薄膜滤光片．并将样品分别在去离子水中浸泡10天和30天．通过分光光度计、光学暗场显微镜、及扫描电子显微镜等多种测试手段，对诱导透射滤光片在潮湿环境下的稳定性进行了研究．实验发现，在潮湿环境下滤光片产生的膜层分离都是从薄膜中微缺陷点处开始发生和发展的，微缺陷是影响滤光片环境稳定性的重要原因之一，其中杂质和针孔是滤光片中两种最常见的微缺陷．EDS能谱分析进一步表明，薄膜中杂质缺陷成分即为Al2O3膜料本身，所以不能推测，薄膜沉积中的喷溅可能是微缺陷产生的根本原因，抑制喷溅可以有效提高薄膜滤光

磁控反应溅射法制备渐变折射率薄膜的模型分析

阐述了磁控反应溅射法制备渐变折射率薄膜的机理；探讨了磁控反应溅射法制备渐变折射率薄膜的理论模型，给出了渐变折射率薄膜的折射率与反应气体分压的关系，在一定的沉积参数下，由要得到的膜层折射率随膜层几何厚度的变化规律可推导出反应气体分压比随时间的变化规律；最后以制备折射率线性变化的薄膜为例说明了如何推导得到反应气体分压比随时间的变化规律．

Influence of buffer layer thickness on the structure and optical properties of ZnO thin films

A series of ZnO thin films were deposited on ZnO buffer layers by DC reactive magnetron sputtering. The buffer layer thickness determination of microstructure and optical properties of ZnO films was investigated by X-ray diffraction (XRD), photoluminescence (PL), optical transmittance and absorption measurements. XRD results revealed that the stress of ZnO thin films varied with the buffer layer thickness. With the increase of buffer layer thickness, the band gap edge shifted toward longer wavelength. The near-band-edge (NBE) emission intensity of ZnO films deposited on ZnO buffer layer also varied with the increase of thickness due to the spatial confinement increasing the Coulomb interaction between electrons and holes. The PL measurement showed that the optimum thickness of the ZnO buffer layer was around 12 nm. (c) 2005 Elsevier B.V. All rights reserved.