Comparative X-ray photoelectron spectroscopic study on the desulfurization of thiophene by Raney Nickel and rapidly quenched skeletal nickel

The desulfurization of thiophene on Raney Ni and rapidly quenched skeletal Ni (RQ Ni) has been studied in ultrahigh vacuum (UHV) by X-ray photoelectron spectroscopy (XPS). The Raney Ni or RQ Ni can be approximated as a hydrogen-preadsorbed polycrystalline Ni-alumina composite. It is found that thiophene molecularly adsorbs on Raney Ni or RQ Ni at 103 K. At 173 K, thiophene on alumina is desorbed, while thiophene in direct contact with the metallic Ni in Raney Ni undergoes C-S bond scission, leading to carbonaceous species most probably in the metallocycle-like configuration and atomic sulfur. On RQ Ni, the temperature for thiophene dissociation is about 100 K higher than that on Raney Ni. The lower reactivity of RQ Ni toward thiophene is tentatively attributed to lattice expansion of Ni crystallites in RQ Ni due to rapid quenching. The existence of alumina and hydrogen may block the further cracking of the metallocycle-like species on Raney Ni and RQ Ni at higher temperatures, which has been the dominant reaction pathway on Ni single crystals. By 473 K, the C Is peak has disappeared, leaving nickel sulfide on the surface.

Reliability study of the electroless Ni–P layer against solder alloy

Copper (Cu) has been widely used in the under bump metallurgy of chip and substrate metallization for chip packaging. However, due to the rapid formation of Cu–Sn intermetallic compound (IMC) at the tin-based solder/Cu interface during solder reaction, the reliability of this type of solder joint is a serious concern. In this work, electroless nickel–phosphorous (Ni–P) layer was deposited on the Cu pad of the flexible substrate as a diffusion barrier between Cu and the solder materials. The deposition was carried out in a commercial acidic sodium hypophosphite bath at 85 °C for different pH values. It was found that for the same deposition time period, higher pH bath composition (mild acidic) yields thicker Ni–P layer with lower phosphorous content. Solder balls having composition 62%Sn–36%Pb–2%Ag were reflowed at 240 °C for 1 to 180 min on three types of electroless Ni–P layers deposited at the pH value of 4, 4.8 and 6, respectively. Thermal stability of the electroless Ni–P barrier layer against the Sn–36%Pb–2%Ag solder reflowed for different time periods was examined by scanning electron microscopy equipped with energy dispersed X-ray. Solder ball shear test was performed in order to find out the relationship between the mechanical strength of solder joints and the characteristics of the electroless Ni–P layer deposited. The layer deposited in the pH 4 acidic bath showed the weak barrier against reflow soldering whereas layer deposited in pH 6 acidic bath showed better barrier against reflow soldering. Mechanical strength of the joints were deteriorated quickly in the layer deposited at pH 4 acidic bath, which was found to be thin and has a high phosphorous content. From the cross-sectional studies and fracture surface analyses, it was found that the appearance of the dark crystalline phosphorous-rich Ni layer weakened the interface and hence lower solder ball shear strength. Ni–Sn IMC formed at the interfaces was found to be more stable at the low phosphorous content (∼14 at.%) layer. Electroless Ni–P deposited at mild acidic bath resulting phosphorous content of around 14 at.% is suggested as the best barrier layer for Sn–36%Pb–2%Ag solder.

Cyclic voltammetry and spectroelectrochemical study of nickel and cobalt diphenyltetraazaannulene complexes

The absorption spectra. cyclic voltammetry and spectroelectrochemistry of [Ni(II)DPTAA] and [Co(II)DPTAA] (DPTAA = 6,13-diphenyldibenzo[b,i][1,4,8,11] tetraaza[14]annulene) complexes in DMF are reported in detail. The ligand oxidation is observed for [Ni(II)DPTAA] at +0.70 V vs. SCE whereas Ni2(+/+) occurs at - 1.60 V. For [Co(II)DPTAA], a ligand oxidation redox couple is seen at +0.56 V while the Co2+/+ and Co2+/3+ redox couples appear at -1.21 and +0.24 V, respectively. All observed redox couples are assigned to reversible one-electron processes on account of peak separations and scan-rate dependency. These processes were further investigated by spectroelectrochemistry for [Co(II)DPTAA]. For [Co(II)DPTAA], axial ligation of pyridine was found to shift the Co2+/3+ redox couple more negative. while the ligand oxidation was shifted to more positive potentials. From a spectrophotometric titration of [Co(II)DPTAA] with pyridine an equilibrium constant, K-f, was determined for the binding of pyridine to [Co(II)DPTAA]. This was found to be 10.2 dm(3) mol(-1), slightly lower than that of [Co(II)TAA], indicating the influence of the phenyl groups. From this value and shifts in the Co2+/3+ redox couple upon ligation, an equilibrium constant for the binding of pyridine to [Co(III)DPTAA], K'(f), was found to be 5.06 x 10(6) dm(3) mol(-1). (c) 2007 Elsevier B.V. All rights reserved.

Growth and properties of gold and nickel nanorods in thin film alumina

Arrays of nickel and gold nanorods have been grown on glass and silicon substrates using porous alumina templates of less than 500 nm thickness. A method is demonstrated for varying the diameter of the nanorods whilst keeping the spacing constant. Optical extinction spectra for the gold nanorods show two distinct maxima associated with the transverse and longitudinal axes of the rods. Adding small quantities of oxygen to the aluminium before anodization is found to improve the sharpness of the extinction peaks. The spectral position of the longitudinal peak is shown to be sensitive to the nanorod diameter for constant length and spacing. For the nickel nanorods it is shown that the magnetic properties are governed by both interactions between the wires and shape anisotropy.

Energy levels and radiative rates for transitions in Mg-like iron, cobalt and nickel

Energy levels and radiative rates for electric dipole (E1) transitions among the lowest 141 levels of the (IS2 2s(2) 2P(6)) 3l(2) , 3l3l', and 3l4l configurations of Fe XV, Co XVI, and Ni XVII are calculated through the CIV3 code using extensive configuration-interact ion (CI) wavefunctions. The important relativistic effects are included through the Breit-Pauli approximation. In order to keep the calculated energy splittings close to the experimental values, we have made small adjustments to the diagonal elements of the Hamiltonian matrices. The energy levels, including their orderings, are in excellent agreement with the available experimental results for all three ions. However, experimental energies are only available for a few levels. Since mixing among some levels is found to be very strong, it becomes difficult to identify these uniquely. Additionally, some discrepancies with other theoretical work (particularly for Ni XVII) are very large. Therefore, in order to confirm the level ordering as well as to assess the accuracy of energy levels and radiative rates, we have performed two other independent calculations using the GRASP and FAC codes. These codes are fully relativistic, but the CI in the calculations is limited to the basic (minimum) configurations only. This enables us to assess the importance of including elaborate Cl for moderately charged ions. Additionally, we report results for electric quadrupole (E2), magnetic dipole (MI), and magnetic quadrupole (M2) transitions, and list lifetimes for all levels. Comparisons are made with other available experimental and theoretical results, and the accuracy of the present results is assessed. (c) 2007 Elsevier Inc. All rights reserved.