The investigation on strain relaxation and double peaks in photoluminescence of InGaN/GaN MQW layers

Two emission peaks were observed in the low temperature photoluminescence (LTPL) spectra of an InGaN/GaN multiple quantum well (MQW) structure before and after nanopillar fabrication. After nanopillar fabrication it is found that among the two peaks the longer wavelength peak exhibits a clear blue shift and has a much stronger enhancement in LTPL intensity than the shorter one. Combined with x-ray diffraction and spatially resolved cathodoluminescence analyses, the difference induced by nanopillar fabrication is ascribed to different strain relaxation states in the lower and upper quantum well layers. It is found that the lower QW layers of the as-grown MQW which causes the longer wavelength PL peak are more strained, while the upper ones are almost fully strain-relaxed. Therefore, the nanopillar fabrication induces much less strain relaxation in the upper part of the MQW than in the lower one.

Correlations between antibunching and blinking of photoluminescence from a single CdSe quantum dot

The antibunching and blinking from a single CdSe/ZnS nanocrystal with an emission wavelength of 655 nm were investigated under different excitation powers. The decay process of the photoluminescence from nanocrystal was fitted into a stretched exponential, and the small lifetime and the small stretching exponent under a high excitation power were explained by using nonradiative multi-channel model. The probability of distributions for off-times from photoluminescence intermittence was fitted into the power law, and the power exponents were explained by using a tunneling model. For higher excitation power, the Auger-assisted tunneling model takes effect, where the tunneling rate increases and the observed lifetime decreases. For weak excitation power, the electron directly tunnels between the nanocrystal and trapping state without Auger assistance. The correlation between antibunching and blinking from the same nanocrystal was analyzed.

All-optical continuously tunable delay with a high linear-chirp-rate fiber Bragg grating based on four-wave mixing in a highly-nonlinear photonic crystal fiber

A scheme for hi-fi all-optical continuously tunable delay is proposed. The signal wavelength is converted to a desired idler wavelength and converted back after being delayed by a high linear-chirp-rate (HLCR) fiber Bragg grating (FBG) based on four-wave mixing (FWM) in a highly-nonlinear photonic crystal fiber (HN-PCF). In our experiment, 400 ps (more than 8 full width of half maximum, FWHM) tunable delay is achieved for a 10 GHz clock pulse with relative pulse width broaden ratio (RPWBR) of 2.08%. The power penalty is only 0.3 dB at 10(-9) BER for a 10 Gb/s 2(31)-1 pseudo random bit sequence (PRBS) data. (c) 2009 Elsevier B.V. All rights reserved.

Spin-Polarized Localized Exciton Photoluminescence Dynamics in GaInNAs Quantum Wells

We have investigated spin polarization-related localized exciton photoluminescence (PL) dynamics in GaInNAs quantum wells by time-resolved PL spectroscopy. The emission energy dependence of PL polarization decay time as well as polarization-independent PL decay time suggests that the acoustic phonon scattering in the process of localized exciton transfer from the high-energy localized states to the low-energy ones dominates the PL polarization relaxation. By increasing the excitation power from 1 to 10 mW, the PL polarization decay time is changed from 0.17 to more than 1 ns, which indicates the significant effect of the trapping of localized electrons by nonradiative recombination centers. These experimental findings indicate that the spin-related PL polarization in diluted nitride semiconductors can be manipulated through carrier scattering and recombination process. (C) 2009 The Japan Society of Applied Physics

Photoluminescence of Charged Low-Density InAs/GaAs Quantum Dots

We obtain low-density charged InAs quantum dots with an emission wavelength below 1 mu m using a low InAs growth rate. The quantum dots have a bimodal size distribution with an emission wavelength of around 1340 nm and 1000 nm, respectively. We observe the photoluminescence of the singly charged exciton in the modulation doped quantum dots in 77 K.

Time-Resolved Photoluminescence of Metamorphic InGaAs Quantum Wells

We investigate the temperature dependence of photoluminescence (PL) and time-resolved PL on the metamorphic InGaAs quantum wells (QWs) with an emission wavelength of 1.55 mu m at room temperature. Time-resolved PL measurements reveal that the optical properties can be partly improved by introducing antimony (Sb) as a surfactant during the sample growth. The temperature dependence of the radiative lifetime is measured, showing that for QWs grown with Sb assistance, the intrinsic exciton emission is dominated when the temperature is below 60 K, while the nonradiative process becomes activated with further increases in temperature. However, without Sb assistance, the nonradiative centers are activated when the temperature is higher than 20 K.

Photoluminescence characteristics of GaAsSbN/GaAs epilayers lattice-matched to GaAs substrates

The photoluminescence (PL) characteristics of GaAsSbN/GaAs epilayers grown by molecular beam epitaxy (MBE) are carefully investigated. The results show that antimony (Sb) incorporation into GaNAs material has less influence on the N-induced localization states. For the same N concentration, GaAsSbN material can reach an emission wavelength near 1.3 mum more easily than GaInNAs material. The rapid thermal annealing (RTA) experiment shows that the annealing induced rearrangement of atoms and related blueshift in GaAsSbN epilayers are smaller than those in GaNAs and GaInNAs epilayers. The GaAsSbN material can keep a longer emission wavelength near 1.3 mum-emission even after the annealing treatment. Raman spectroscopy analysis gives further insight into the structure stability of GaAsSbN material after annealing. (C) 2004 Elsevier Ltd. All rights reserved.

Photoluminescence characterization of nanocrystalline ZnO array

High-density and uniform well-aligned ZnO sub-micron rods are synthesized on the silicon substrate over a large area. The morphology, and structure of the ZnO sub-micron rods are investigated by x-ray diffraction, transmission electron microscopy and Raman spectra. It is found that the ZnO sub-micron rods are of high crystal quality with the diameter in the range of 400-600 nm and the length of several micrometres long. The optical properties were studied bill photoluminescence spectra. The results show that the intensity of the ultraviolet emission at 3.3 eV is rather high, meanwhile the deep level transition centred at about 2.38 eV is weak. The free exciton emission could also be observed at low, temperature, which implies the high optical quality of the ZnO sub-micron rods. This growth technique provides one effective way to fabricate the high crystal quality ZnO nanowires array, which is very important for potential applications in the new-type optoelectronic nanodevices.

Raman scattering and photoluminescence studies of Er-implanted and Er+ O coimplanted GaN

Raman measurements and photoluminescence (PL) were performed on the metal-organic chemical-vapor deposition epitaxially grown GaN before and after the implantation with Er and Er+O. Several Raman defect modes have emerged from the implantation-damaged samples. The structures around 300 and 595 cm(-1) modes are attributed to the disorder-activated Raman scattering, whereas the 670 cm(-1) peak is assigned to nitrogen-vacancy-related defect scattering. One additional peak at 360 cm(-1) arises after Er+O coimplantation. This Raman peak is attributed to the O-implantation-induced defect complex. The appearance of the 360 cm(-1) mode results in the decrease of the Er3+ -related infrared PL intensity for the GaN:Er+O samples. (C) 2004 American Institute of Physics.

Novel room temperature photoluminescence of Ge/Si islands in multilayer structure grown on silicon-on-insulator substrate

Novel room temperature photoluminescence (PL) of the Ge/Si islands in multilayer structure grown on silicon-on-insulator substrates is investigated. The cavity formed by the mirrors at the surface and the buried SiO2 interface has a strong effect on the PL emission. The peak position is consistent with the theoretical calculation and independent of the exciting power, which is the evidence of cavity effect on the room temperature photoluminescence. (C) 2004 Elsevier B.V. All rights reserved.

Molecular beam epitaxy growth and photoluminescence of type-II (GaAs1-xSbx/InyGa1-yAs)/GaAs bilayer quantum well

We report a systematical study on the molecular beam epitaxy growth and optical property of (GaAs1-xSbx/In-y Ga1-yAs)/GaAs bilayer quantum well (BQW) structures. It is shown that the growth temperature of the wells and the sequence of layer growth have significant influence on the interface quality and the subsequent photoluminescence (PL) spectra. Under optimized growth conditions, three high-quality (GaAsSb0.29/In0.4GaAs)/GaAs BQWs are successfully fabricated and a room temperature PL at 1314 nm is observed. The transition mechanism in the BQW is also discussed by photoluminescence and photoreflectance measurements. The results confirm experimentally a type-II band alignment of the interface between the GaAsSb and InGaAs layers.

Relationship between the electric performance and the photoluminescence spectra of resonant tunnelling diodes

Resonant tunnelling diodes with different structures were grown. Their photoluminescence spectra were investigated. By contrast, the luminescence in the quantum well is separated from that of other epilayers. The result is obtained that the exciton of the luminescence in the quantum well is partly come from the cap layer in the experiment. So the photoluminescence spectrum is closely related to the electron transport in the resonant tunnelling diode structure. This offers a method by which the important performance of resonant tunnelling diode could be forecast by analysing the integrated photoluminescence intensities.

Structure and photoluminescence studies of Pr-implanted GaN

The structure and photoluminscence (PL) properties of Pr-implanted GaN thin films have been studied. RBS/channeling technique was used to explore the damage recovery at high annealing temperature and study the dependence of the radiation damage with ion implantation direction. A complete recovery of the ion implantation damage cannot be achieved at annealing temperatures up to 1050degreesC. It is found that the channeling implantation results in the decrease of the damage. The PL experimental results indicate that the PL efficiency increases exponentially with annealing temperature up to the maximum temperature of 1050degreesC. Moreover, the PL intensity is also seriously affected by ion implantation geometries. The PL intensity for the sample implanted along channeled direction is nearly 2 times more intense than that observed from the sample implanted along random direction. The thermal quenching of PL intensity from 10 to 300K for sample annealed at 1050degreesC is only 30%. (C) 2004 Elsevier B.V. All rights reserved.

Cavity-enhanced photoluminescence of SiGe/Si multiquantum wells grown on silicon-on-insulator substrate

Sharp and strong room-temperature photoluminescence (PL) of the Si0.59Ge0.41/Si multiquantum wells grown on the silicon-on-insulator substrate is investigated. The cavity formed by the mirrors at the surface and the buried SiO2 interface enhances the PL emission and has a wavelength-selective effect on the luminescence. The peak position is consistent with the simulation result and independent of the exciting power, which indicates a strong cavity effect on the room-temperature PL. (C) 2004 American Institute of Physics.

Dependence of implantation-induced damage with photoluminescence intensity in GaN : Er

Erbium was implanted with energies 200 or 400 keV into epitaxial (0 0 0 1) GaN grown on (0 0 0 1) Al2O3 substrate at room temperature (RT) and 400degreesC. Both random (10degrees tilt from c-axis) and channeled (along c-axis) implantations were studied. RBS/Channeling technique was used to study the dependences of the radiation damage with ion implantation energy, direction and temperature. It was found that the channeling implantation or elevating temperature implantation both resulted in the decrease of the damage. Moreover, the Photoluminscence (PL) properties of Er-implanted GaN thin filius were also studied. The experimental results indicate that the PL intensity can be enhanced by raising implantation energy or implanting along channeling direction. (C) 2004 Elsevier B.V. All rights reserved.