Structural and optical properties of ZnO films on SrTiO3 substrates by MOCVD

ZnO films have been fabricated on (0 0 1), (0 1 1) and (1 1 1) SrTiO3 (STO) substrates by metal-organic chemical vapour deposition (MOCVD). It is interesting that the ZnO films on (0 0 1) and (0 1 1) STO substrates show polar and semipolar orientations, which are different from previous reports, while the same growing direction of polar ZnO with previous results is found on (1 1 1) STO. For the atomic arrangements, two orthogonal domains and a single domain are observed on (0 0 1) and (1 1 1) STO, respectively. Photoluminescence spectra show that every sample has a sharp near-band-edge emission peak at about 3.28 eV without any deep-level emission band between 1.5 and 2.8 eV, implying a high optical quality. A violet emission around 3.0 eV is observed only in ZnO films on (0 0 1) and (0 1 1) STO substrates grown at 600 degrees C, which is discussed briefly. Additionally, the semipolar ZnO does not weaken the emission efficiency along with the reduction in the polarization effect compared with polar ZnO. These results show that high-quality polar and semipolar ZnO films can be grown on STO substrates by MOCVD.

Effect of Nitridation on Morphology, Structural Properties and Stress of AIN Films

We investigate effects of nitridation on AIN morphology, structural properties and stress. It is found that 3 min nitridation can prominently improve AIN crystal structure, and slightly smooth the surface morphology. However, 10 min nitridation degrades out-of-plane crystal structure and surface morphology instead. Additionally, 3-min nitridation introduces more tensile stress (1.5 GPa) in AIN films, which can be attributed to the weaker islands 2D coalescent. Nitridation for 10 min can introduce more defects, or even forms polycrystallinity interlayer, which relaxes the stress. Thus, the stress in AIN with 10 min nitridation decreases to -0.2 GPa compressive stress.

Surface morphology of AlN buffer layer and its effect on GaN growth by metalorganic chemical vapor deposition

The in situ optical reflectivity measurements are employed to monitor the GaN epilayer growth process above low-temperature AlN buffer layer on c-plane sapphire substrate by metalorganic chemical vapor deposition. It is found that the lateral growth of GaN islands and their coalescence is promoted in the initial growth stage if the AlN buffer layer is treated with a long annealing time and has an optimal thickness: As confirmed by atomic force microscopy observations, the quality of GaN epilayers is closely dependent on the surface morphology of AlN buffer layer, especially the grain size and nuclei density after the annealing treatment. (C) 2004 American Institute of Physics.

Effects of polarization field on formation of two-dimensional electron gas in (0001) and (11(2)over-bar0) plane AlGaN/GaN heterostructures

Photoluminescence (PL) and temperature-dependent Hall effect measurements were carried out in (0001) and (11 (2) over bar0) AlGaN/GaN heterostructures grown on sapphire substrates by metalorganic chemical vapor deposition. There are strong spontaneous and piezoelectric electric fields (SPF) along the growth orientation of the (0001) AlGaN/GaN heterostructures. At the same time there are no corresponding SPF along that of the (1120) AlGaN/GaN. A strong PL peak related to the recombination between two-dimensional electron gas (2DEG) and photoexcited holes was observed at 3.258 eV at room temperature in (0001) AlGaN/GaN heterointerfaces while no corresponding PL peak was observed in (11 (2) over bar0). The existence of a 2DEG was observed in (0001) AlGaN/GaN multi-layers with a mobility saturated at 6000 cm(2)/V s below 80 K, whereas a much lower mobility was measured in (11 (2) over bar0). These results indicated that the SPF was the main element to cause the high mobility and high sheet-electron-density 2DEG in AlGaN/GaN heterostructures. (C) 2004 Elsevier B.V. All rights reserved.

Growth of crack-free AlGaN film on thin AlN interlayer by MOCVD

We have studied the effect of low-temperature-deposited (LT) and high-temperature-deposited (FIT) AlN interlayer with various thickness on AlGaN film grown on GaN using c-plane sapphire as substrate. All the Al0.25Ga0.75N films thicker than 1 mum with LT-AlN interlayer or with HT-AlN interlayer were free of cracks, however, their surfaces were different: the Al0.25Ga0.75N films with LT-AlN interlayer showed smooth surface, while those with HT-AlN interlayer exhibit rough surface morphology. The results of X-ray double crystal diffraction and Rutherford backscattering showed that all of the AlGaN films were under compressive strain in the parallel direction. The compressive strain resulted from the effect of interlayer-induced stress relieving and the thermal mismatch for the samples with LT-AlN interlayer, and it was due to the thermal mismatch between AlGaN and the underlying layers for those with HT-AlN interlayer. (C) 2004 Elsevier B.V. All rights reserved.

A Bragg-mirror-based semiconductor saturable absorption mirror at 800 nm with low temperature and surface state hybrid absorber

We present a novel 800-nm Bragg-mirror-based semiconductor saturable absorption mirror with low temperature and surface state hybrid absorber, with which we can realize the passive soliton mode locking of a Ti:sapphire laser pumped by 532-nm green laser which produces pulses as short as 37 fs. The reflection bandwidth of the mirror is 30 nm and the pulse frequency is 107 MHz. The average output power is 1.1 W at the pump power of 7.6 W.

Structural and optical properties of 3D growth multilayer InGaN/GaN quantum dots by metalorganic chemical vapor deposition

Multilayer InGaN/GaN quantum dots (QDs) were grown on sapphire substrates through a three-dimensional growth mode, which was initiated by a special passivation processing introduced into the normal growth procedure. Surface morphology and photoluminescence properties of QDs with different stacking periods (from one to four) were investigated. The temperature dependences of the PL peak energies were found to show a great difference between two-layer and three-layer QDs. The fast redshift and the reversed sigmoidal temperature dependences of the PL energies for the former were attributed to the thermally activated carrier transfer from small to large dots. However, the increase of both the dot size and the spatial space among dots with the growing stacking periods reduced the carrier escape and retrapping. (C) 2004 Elsevier B.V. All rights reserved.

Effect of trimethylgallium flow on the structural and optical properties of InGaN/GaN multiple quantum wells

InGaN/GaN multiple quantum wells (MQWs) are grown by metal-organic chemical vapour deposition on (0001) sapphire substrates. Triple-axis X-ray diffraction (TXRD) and photoluminescence (PL) spectra are used to assess the influence of trimethylgallium (TMGa) flow on structural defects, such as dislocations and interface roughness, and the optical properties of the MQWs. In this paper, a method, involving an ! scan of every satellite peak of TXRD, is presented to measure the mean dislocation density of InGaN/GaN MQWs. The experimental results show that under certain conditions which keep the trimethlyindium flow constant, dislocation density and interface roughness decrease with the increase of TMGa flow, which will improve the PL properties. It can be concluded that dislocations, especially edge dislocations, act as nonradiative recombination centres in InGaN/GaN MQWs. Also noticed is that changing the TMGa flow has more influence on edge dislocations than screw dislocations.

One-step growth of ZnO from film to vertically well-aligned nanorods and the morphology-dependent Raman scattering

We observed a transition from film to vertically well-aligned nanorods for ZnO grown on sapphire (0001) substrates by metalorganic chemical vapor deposition. A growth mechanism was proposed to explain such a transition. Vertically well-aligned homogeneous nanorods with average diameters of similar to 30, 45, 60, and 70 nm were grown with the c-axis orientation. Raman scattering showed that the E-2 (high) mode shifted to high frequency with the decrease of nanorod diameters, which revealed the dependence of nanorod diameters on the stress state. This dependence suggests a stress-driven diameter-controlled mechanism for ZnO nanorod arrays grown on sapphire (0001) substrates. (c) 2005 American Institute of Physics.

Frequency dependence of junction capacitance of GaN p-i-n UV detectors

In this paper frequency dependence of small-signal capacitance of p-i-n UV detectors, which were fabricated on GaN grown on sapphire substrate by metalorganic chemical vapor deposition, has been studied. The Schibli-Milnes model was used to analyze the capacitance-frequency characteristics. According to high frequency C-V measurements, the deep level mean concentration is about 2.98 x 10(20) cm(-3). The deep level is caused by the un-ionised Mg dopant. The calculated Mg activation energy is 260 meV and the hole thermal capture cross section of the deep level is about 2.73 x 10(-22) cm(2). The applicability of the Schibli-Milnes model is also discussed when the concentration of deep levels exceeds that of the heavily doped n-side. It is concluded that the analytic expression of the Schibli-Milnes model can still be used to describe the capacitance-frequency characteristics of GaN p-i-n UV detectors in good agreement with experiment. (c) 2005 Elsevier Ltd. All rights reserved.

Characterization of stress induced in SOS and Si/gamma-Al2O3/Si heteroepitaxial thin films by Raman spectroscopy

Raman spectroscopy technique has been performed to investigate the stress induced in as-grown silicon-on-sapphire (SOS), solid-phase-epitaxy (SPE) re-grown SOS, and Si/gamma-Al2O3/Si double-heteroepitaxial thin films. It was demonstrated that the residual stress in SOS film, arising from mismatch and difference of thermal expansion coefficient between silicon and sapphire, was reduced efficiently by SPE process, and that the stress in Si/gamma-Al2O3/Si thin film is much smaller than that of as-grown SOS and SPE upgraded SOS films. The stress decrease for double heteroepitaxial film Si/gamma-Al2O3/Si mainly arises from the smaller lattice mismatching of 2.4% between silicon top layer and the gamma-Al2O3/Si epitaxiial composite substrate, comparing with the large lattice mismatch of 13% for SOS films. It indicated that gamma-Al2O3/Si as a silicon-based epitaxial substrate benefits for reducing the residual stress for further growth of silicon layer, compared with on bulk sapphire substrate. (c) 2005 Elsevier B.V. All rights reserved.

Effects of different modified underlayer surfaces on growth and optical properties of InGaN quantum dots

InGaN/GaN quantum dots were grown on the sapphire (0 0 0 1) substrate in a metalorganic chemical vapor deposition system. The morphologies of QDs deposited on different modified underlayer (GaN) surfaces, including naturally as grown, Ga-mediated, In-mediated, and air-passivated ones, were investigated by atomic force microscopy (AFM). Photo luminescence (PL) method is used to evaluate optical properties. It is shown that InGaN QDs can form directly on the natural GaN layer. However, both the size and distribution show obvious inhomogeneities. Such a heavy fluctuation in size leads to double peaks for QDs with short growth time, and broad peaks for QDs with long growth time in their low-temperature PL spectra. QDs grown on the Ga-mediated GaN underlayer tends to coalesce. Distinct transform takes place from 3D to 2D growth on the In-mediated ones, and thus the formation of QDs is prohibited. Those results clarify Ga and In's surfactant behavior. When the GaN underlayer is passivated in the air, and together with an additional low-temperature-grown seeding layer, however, the island growth mode is enhanced. Subsequently, grown InGaN QDs are characterized by a relatively high density and an improved Gaussian-like distribution in size. Short surface diffusion length at low growth temperature accounts for that result. It is concluded that reduced temperature favors QD's 3D growth and surface passivation can provide another promising way to obtain high-density QDs that especially suits MOCVD system. (c) 2004 Elsevier Ltd. All rights reserved.

Low-temperature growth of InN by MOCVD and its characterization

Metalorganic chemical vapor deposition growth of InN on sapphire substrate has been investigated between 400 degrees C and 500 degrees C to seek the growth condition of InN buffer layer, i.e. the first step of realization of the two-step growth method. Ex situ characterization of the epilayers by means of atomic force microscope, scanning electron microscope and X-ray diffraction, coupled with in situ reflectance curves, has revealed different growth circumstances at these temperatures, and conclusion has been reached that the most suitable temperature for buffer growth is around 450 degrees C. In addition, the growth rate of InN at the optimized temperature with regard to different precursor flow rates is studied at length. (c) 2004 Elsevier B.V. All rights reserved.

Depth dependent elastic strain in ZnO epilayer: combined Rutherford backscattering/channeling and X-ray diffraction

A ZnO layer was grown by metalorganic chemical vapor deposition (MOCVD) on a sapphire (0 0 0 1) substrate. The perpendicular and parallel elastic strain of the ZnO epilayer, e(perpendicular to) = 0.19%, e(parallel to) = -0.29%, respectively, were derived by using the combination of Rutherford backscattering (RBS)/channeling and X-ray diffraction (XRD). The ratio vertical bar e(parallel to)/ e(perpendicular to)vertical bar = 1.5 indicates that ZnO layer is much stiffer in the a-axis direction than in the c-axis direction. By using RBS/C, the depth dependent elastic strain was deduced. The strain is higher at the depth close to the interface and decreases towards the surface. The negative tetragonal distortion was explained by considering the lattice mismatch and thermal mismatch in ZnO thin film. (c) 2004 Elsevier B.V. All rights reserved.

Effects of growth temperature of AlGaN buffer layer on the properties of A1(0.58)Ga(0.42)N epilayer by NH3-MBE

Al0.58Ga0.42N epilayers are grown by ammonia gas source molecular beam epitaxy (NH3-MBE) on (0001) sapphire substrate using AlGaN buffer layer. The effects of the buffer layer growth temperature on the properties of Al0.58Ga0.42N epilayer are especially investigated. In-situ high-energy electron diffraction (RHEED), double-crystal X-ray diffraction (DCXRD), atomic force microscopy (AFM), photoconductivity measurement and cathodoluminescence (CL) are used to characterize the samples. It is found that high growth temperature of AlGaN buffer layer would improve the crystalline quality, surface smoothness, optical quality and uniformity of the Al0.58Ga0.42N epilayer. The likely reason for such improvements is also suggested. (C) 2007 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim