Dielectric properties of Ca(Zr0.05Ti0.95)O-3 thin films prepared by chemical solution deposition

Ca(Zr0.05Ti0.95)O-3 (CZT) thin films were grown on Pt(1 1 1)/Ti/SiO2/Si(1 0 0) substrates by the soft chemical method. The films were deposited from spin-coating technique and annealed at 928 K for 4 h under oxygen atmosphere. CZT films present orthorhombic structure with a crack free and granular microstructure. Atomic force microscopy and field-emission scanning electron microscopy showed that CZT present grains with about 47 nm and thickness about 450 nm. Dielectric constant and dielectric loss of the films was approximately 210 at 100 kHz and 0.032 at 1 MHz. The Au/CZT/Pt capacitor shows a hysteresis loop with remnant polarization of 2.5 mu C/cm(2), and coercive field of 18 kV/cm, at an applied voltage of 6 V. The leakage current density was about 4.6 x 10(-8) A/cm(2) at 3 V. Dielectric constant-voltage curve is located at zero bias field suggesting the absence of internal electric fields. (c) 2006 Elsevier B.V. All rights reserved.

Temperature dependence of dielectric properties for Ba(Zr0.25Ti0.75)O-3 thin films obtained from the soft chemical method

Ba(Zr0.25Ti0.75)O-3(BZT) thin films prepared by the polymeric precursor method (PPM) were annealed at 500, 600, and 700 degrees C for 4h. All films crystallized in the perovskite structure present a crack-free microstructure. Dielectric properties of the BZT thin films were investigated as a function of frequency and applied voltage. The dielectric constant of the films were 36, 152 and 145 at 1 kHz, while the dielectric loss were 0.08, 0.08, and 0.12 at 1 MHz. (c) 2007 Elsevier B.V. All rights reserved.

Ferroelectric and dielectric behaviour of Bi0.92La0.08FeO3 multiferroic thin films prepared by soft chemistry route

Bi0.92La0.08FeO3 (BLFO) thin films were grown on platine substrates by the soft chemical route. Ferroelectric and dielectric behaviors of BLFO films deposited by spin-coating technique and annealed at 773 K for 2 h in air atmosphere were explained. BLFO thin films obtained presents a rhombohedral structure. The BLFO films present dielectric and ferroelectric behaviors with dielectric permittivity and dielectric loss of approximately 81 and 0.0144 at 1 kHz. The Au/BLFO/Pt capacitor shows a hysteresis loop with remnant polarization of 20.6 mu C/cm(2) and coercive field of 53.88 kV/cm. The polarization switching and the fatigue behavior of the BLFO films were significantly enhanced.

Dielectric investigations of vanadium modified barium zirconium titanate ceramics obtained from mixed oxide method

Vanadium modified barium zirconium titanate ceramics Ba(Zr(0.10)Ti(0.90))O(3):2V (BZT:2V) were prepared from the mixed oxide method. According to X-ray diffraction analysis, addition of vanadium leads to ceramics free of secondary phases. Electrical characteristics reveal a dielectric permittivity at around 15,000 with low dielectric loss with a remnant polarization (P(r))of 8 mu C/cm(2) at 2 kV/cm. From the obtained results, we assume that vanadium substitution in the BZT lattice affects dielectric characteristics due to the electron-relaxation-mode in which carriers (polarons, protons, and so on) are coupled with existing dielectric modes. (C) 2009 Published by Elsevier B.V.

Influence of strains and defects on ferroelectric and dielectric properties of thin-film barium-strontium titanates

Pristine, W and Mn 1% doped Ba(0.6)Sr(0.4)TiO(3) epitaxial thin films grown on the LaAlO(3) substrate were deposited by pulsed laser deposition (PLD). Dielectric and ferroelectric properties were determined by the capacitance measurements and X-ray diffraction was used to determine both residual elastic strains and defect-related inhomogeneous strains-by analyzing diffraction line shifts and line broadening, respectively. We found that both elastic and inhomogeneous strains are affected by doping. This strain correlates with the change in Curie-Weiss temperature and can qualitatively explain changes in dielectric loss. To explain the experimental findings, we model the dielectric and ferroelectric properties of interest in the framework of the Landau-Ginzburg-Devonshire thermodynamic theory. As expected, an, elastic-strain contribution due to the epilayer-substrate misfit has an important influence on the free-energy. However, additional terms that correspond to the defect-related inhomogeneous strain had to be introduced to fully explain the measurements.

Effects of powder preparation and sintering procedure on microstructure and dielectric properties of PLZT ceramics

PLZT ceramics belong to one of the very important groups of functional materials that make a basis for the production of a large range of electronic devices. The microstructure and properties of ceramics depend on the powder preparation and thermal processing conditions. Various techniques have been used to obtain chemically homogeneous and fine starting powders. PLZT powders have been prepared by two different production routes: by a modified Pechini method, using a polymeric precursor method (PMM) and by a partial oxalate method. A two-step sintering process, including a hot pressing, was carried out at 1100 and 1200degreesC Distinct phases obtained during the sintering process have been investigated by SEM and EDS techniques and dielectric properties such as permittivity and dielectric loss were measured in a frequency range from 1 to 20 kHz.. A significant difference in microstructure and dielectric properties, depending on powder origin and sintering procedure, has been noticed.

Dielectric and piezoelectric properties of the mechanochemically prepared PZT ceramics

Mechanochemical synthesis was applied to obtain nanocrystalline powders of composition Pb(Zr0.52Ti0.48)O-3 (PZT). Milling was performed in a planetary ball mill using vials and balls made of zirconia or steel-in order to investigate influence of milling media on the electrical properties of resulting ceramics. PZT ceramics showed high values for dielectric constant (epsilon(r)), reaching 970 at room temperature, as well as low dielectric loss (tandelta) under the optimal processing conditions. High values of remanent polarization (P-r) indicate high internal polarizability. The best samples showed piezoelectric strain constant d(33) = 347 pC/N and planar coupling factor k(P) = 0.44. Milling in ZrO2 medium prevents powder contamination and provides reproducibility of milling process. Also, PZT obtained from the powders milled in ZrO2 exhibited lower values of dielectric loss, in comparison with the PTZ obtained from the powders milled in Fe. This suggests that contamination of the powder with Fe could result in an increase of conductivity in final product. (C) 2004 Kluwer Academic Publishers.

Dielectric properties of Na1-xLixNbO3 ceramics from powders obtained by chemical synthesis

Ultra-fine powders of Na1-xLixNbO3 (x=0; 0.06; 0.09; 0.12) were synthesized by the Polymeric Precursors Method. Such powders had their orthorhombic structures determined by X-ray diffraction and their surface area determined by BET isotherms (less than 10 m(2) g(-1)). Densification was followed by dilatometric study. The powders, calcined at 700 degrees C for 5 h, were sintered at 1290 degrees C during 2 h under ambient atmosphere with no application of extra pressure. The samples with relative densities higher than 95% were analyzed by impedance spectroscopy at room temperature, under a signal amplitude of 1 V-rms. Dielectric constants of about 180 and dielectric loss factor of about 0.03 were measured showing small dependence with frequency. The electrical properties were similar to those obtained for samples sintered by hot pressing. (C) 1999 Elsevier B.V. Limited and Techna S.r.l. All rights reserved.

Microstructure, dielectric properties and optical band gap control on the photoluminescence behavior of Ba[Zr0.25Ti0.75]O-3 thin films

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

The dielectric suppress and the control of semiconductor non-Ohmic feature of CaCu3Ti4O12 by means of tin doping

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Dielectric properties of soft chemical method derived CaCu3Ti4O12 thin films onto Pt/TiO2/Si(100) substrates

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Microstructure, crystalline phase, and dielectric property analyses of TiO2 composition with ZrO2 addition

For microwave applications, including mobile and satellite communications, ceramic resonators should have a high dielectric constant, low dielectric losses, and high frequency stability. In this sense, TiO2-ZrO 2 ceramics have been investigated as a function of sintering behavior, phase composition, and microstructure. The ceramics were densified reaching a value of about 86% of theoretical density at 1400°C sintering temperature. The ceramics are prepared by mixing raw materials with the following TiO2-ZrO2 weight % ratio: 100 to 0, 90 to 10, and 80 to 20, respectively. The measured dielectric constants are between 79 and 88 values, while the quality factor due to dielectric losses are between 2820 and 5170. These results point out the influence of Ti/Zr ratio on controlling the dielectric properties. © (2010) Trans Tech Publications.

Structural and dielectric properties of polyvinyl alcohol/barium zirconium titanate polymer-ceramic composite

The polyvinyl alcohol (PVA)/barium zirconium titanate Ba[Zr0.1Ti0.9]O3 (BZT) polymer-ceramic composites with different volume percentage are obtained from solution mixing and hot-pressing method. Their structural and electrical properties are characterized by X-ray diffraction (XRD), Rietveld refinement, cluster modeling, scanning electron microscope and dielectric study. XRD patterns of PVA/BZT polymer-ceramics composite (with 50% volume fractions) indicate no obvious differences than the XRD patterns of pure BZT which shows that the crystal structure is still stable in the composite. The scanning electron micrograph indicates that the BZT ceramic is dispersed homogeneously in the polymer matrix without agglomeration. The dielectric permittivity (ε r) and the dielectric loss (tan δ) of the composites increase with the increase of the volume fraction of BZT ceramic. Theoretical models are employed to rationalize the dielectric behavior of the polymer composites. The dielectric properties of the composites display good stability within a wide range of temperature and frequency. The excellent dielectric properties of these polymer-ceramic composites indicate that the BZT/PVA composites can be a candidate for embedded capacitors. © 2013 Elsevier B.V.

Low frequency dielectric spectroscopy of bitumen binders as an indicator of adhesion potential to quartz aggregates using Portland cement

The purpose of this investigation was to interpret the bitumen-aggregate adhesion based on the dielectric spectroscopic response of individual material components utilizing their dielectric constants, refractive indices and average tangent of the dielectric loss angle (average loss tangent). Dielectric spectroscopy of bitumen binders at room temperature was performed in the frequency range of 0.01–1000 Hz. Dielectric spectroscopy is an experimental method for characterizing the dielectric permittivity of a material as a function of frequency. Adhesion data has been determined using the Rolling bottle method. The results show that the magnitude of the average tangent of the dielectric loss angle (average loss tangent) depends on bitumen type. The average loss tangent in the frequency range 0.01–1 Hz is introduced as a potential indicator for predicting polarizability and, thereby, adhesion potential of bitumen binders to quartz aggregates when using Portland cement. In order to obtain acceptable adhesion of 70/100 penetration grade bitumen binders and quartz aggregates when using Portland cement, it is suggested that the binder have an average tan δ > 0.035 in the frequency range 0.01–1 Hz.

Electrical and dielectric properties of uncoated and coated wood-free paper for electrophotography

The print substrate influences the print result in dry toner electrophotography, which is a widely used digital printing method. The influence of the substrate can be seen more easily in color printing, as that is a more complex process compared to monochrome printing. However, the print quality is also affected by the print substrate in grayscale printing. It is thus in the interests of both substrate producers and printing equipment manufacturers to understand the substrate properties that influence the quality of printed images in more detail. In dry toner electrophotography, the image is printed by transferring charged toner particles to the print substrate in the toner transfer nip, utilizing an electric field, in addition to the forces linked to the contact between toner particles and substrate in the nip. The toner transfer and the resulting image quality are thus influenced by the surface texture and the electrical and dielectric properties of the print substrate. In the investigation of the electrical and dielectric properties of the papers and the effects of substrate roughness, in addition to commercial papers, controlled sample sets were made on pilot paper machines and coating machines to exclude uncontrolled variables from the experiments. The electrical and dielectric properties of the papers investigated were electrical resistivity and conductivity, charge acceptance, charge decay, and the dielectric permittivity and losses at different frequencies, including the effect of temperature. The objective was to gain an understanding of how the electrical and dielectric properties are affected by normal variables in papermaking, including basis weight, material density, filler content, ion and moisture contents, and coating. In addition, the dependency of substrate resistivity on the electric field applied was investigated. Local discharging did not inhibit transfer with the paper roughness levels that are normal in electrophotographic color printing. The potential decay of paper revealed that the charge decay cannot be accurately described with a single exponential function, since in charge decay there are overlapping mechanisms of conduction and depolarization of paper. The resistivity of the paper depends on the NaCl content and exponentially on moisture content although it is also strongly dependent on the electric field applied. This dependency is influenced by the thickness, density, and filler contents of the paper. Furthermore, the Poole-Frenkel model can be applied to the resistivity of uncoated paper. The real part of the dielectric constant ε’ increases with NaCl content and relative humidity, but when these materials cannot polarize freely, the increase cannot be explained by summing the effects of their dielectric constants. Dependencies between the dielectric constant and dielectric loss factor and NaCl content, temperature, and frequency show that in the presence of a sufficient amount of moisture and NaCl, new structures with a relaxation time of the order of 10-3 s are formed in paper. The ε’ of coated papers is influenced by the addition of pigments and other coating additives with polarizable groups and due to the increase in density. The charging potential decreases and the electrical conductivity, potential decay rate, and dielectric constant of paper increase with increasing temperature. The dependencies are exponential and the temperature dependencies and their activation energies are altered by the ion content. The results have been utilized in manufacturing substrates for electrophotographic color printing.