SHORT PERIOD InAs/GaSb SUPERLATTICE INFRARED DETECTOR ON GaAs SUBSTRATES

Two type II superlattices (SLs) InAs(2ML)/GaSb(8ML) and InAs(8ML)/GaSb(8ML) were grown on GaAs substrates by molecular-beam epitaxy. High resolution X-ray diffraction showed the periods of the two SLs were 31.2 angstrom and 57.3 angstrom, respectively. Room-temperature optical transmittance spectra showed that there were clear absorption edges at 2.1 mu m and 5 mu m for the two SLs. The SWIR and MWIR photoconductor devices were fabricated by standard lithography and etched by tartaric acid solution. The spectral response and blackbody tests were carried out at low and room temperatues. The results show that the 50% cutoff wavelengths of the two photoconductors are 2.1 mu m and 5.0 mu m respectively and D-bb* is above 2 x 10(8) cmHz(1/2)/W for two kinds of photoconductors at 77K. D-bb* is above 10(8) cmHz(1/2)/W for SWIR photoconductor at room temperature.

Distribution of dislocations in GaSb and InSb epilayers grown on GaAs (001) vicinal substrates

GaSb and InSb epilayers grown on GaAs (001) vicinal substrates misoriented toward (111) plane were studied using high resolution x-ray diffraction. The results show that GaSb and InSb epilayers take on positive crystallographic tilt, and the asymmetric distribution of 60 degrees misfit dislocations in {111} glide planes have an effect on the tilt. In addition, the vicinal substrate influences the distribution of the threading dislocations in {111} glide planes, and the density of dislocation in the (111) plane is higher than in the ((1) over bar(1) over bar1) plane. A model was proposed to interpret the distribution of full width at half maximum, which can help us understand the formation and glide process of the dislocations. (C) 2009 American Institute of Physics. [DOI 10.1063/1.3115450]

Integratable and High Speed Complex-Coupled MQW-DFB Lasers Fabricated on Semi-Insulating Substrates

A novel integratable and high speed InGaAsP multi-quantum well (MQW) complex-coupled distributed feedback (DFB) laser is successfully fabricated on a semi-insulating substrate. The fabricated ridge DFB laser exhibits a threshold current of 26 mA, a slope efficiency of 0.14 W.A(-1) and a side mode suppression ratio of 40 dB together with a 3 dB bandwidth of more than 8 GHz. The device is suitable for 10 Gbit/s optical fiber communication.

Anomalous coarsening of self-assembled InAs quantum dots on vicinal GaAs (100) substrates

The formation process of InAs quantum dots (QDs) on vicinal GaAs (1 0 0) substrates is studied by atomic force microscopy (AFM). It is found that after 1.2 MLs of InAs deposition, while the QDs with diameters less than the width of the multi-atomic steps are shrinking, the larger QDs are growing. Photoluminescence measurements of the uncapped QDs correspond well to the AFM structure observations of the QDs. We propose that the QDs undergo an anomalous coarsening process with modified growth kinetics resulting from the restrictions of the finite terrace sizes. A comparison between the QDs on the vicinal GaAs (1 0 0) substrates and the QDs on the exact GaAs (1 0 0) further verifies the effect of the multi-atomic steps on the formation of QDs.

Molecular Beam Epitaxy of GaSb on GaAs Substrates with AlSb Buffer Layers

We investigate the molecular beam epitaxy growth of GaSb films on GaAs substrates using AlSb buffer layers. Optimization of AlSb growth parameter is aimed at obtaining high GaSb crystal quality and smooth GaSb surface. The optimized growth temperature and thickness of AlSb layers are found to be 450 degrees C and 2.1 nm, respectively. A rms surface roughness of 0.67 nm over 10 x 10 mu m(2) is achieved as a 0.5 mu m GaSb film is grown under optimized conditions.

Growth of c-oriented ZnO films on (001) SMO3 substrates by MOCVD

The growth direction of ZnO thin films grown by metal-organic chemical vapor deposition (MOCVD) is modulated by pretreatment of (001) SMO3 (STO) substrates. ZnO films show a-oriented smooth surface with epitaxial relationship of < 001 > ZnO//< 110 > STO on as-received SfO, and c-axis columnar growth with < 010 > ZnO//< 110 > STO on etched STO, respectively. The orientation alteration of ZnO films is supposed to be caused by the change of STO surface polarity. In addition, the c-ZnO films exhibit an enhanced photoluminescence (PL) intensity due to the improved crystal quality, while the blueshift of PL peak is attributed to the smaller tensile strain. These results show that high quality c-ZnO, which is essential for electronic and optoelectronic device applications, can be grown on (001) SfO by MOCVD. (C) 2008 Elsevier B.V. All rights reserved.

Comparison of short period InAs/GaSb superlattices on GaSb and GaAs substrates

Type II superlattices (SLs) short period InAs(4ML)/GaSb(8ML) were grown by molecular-beam epitaxy on lattice-mismatched GaAs substrates and on GaSb substrates. A smooth GaSb epilayer was formed on GaAs substrates by inserting mulit-buffer layers including an interfacial misfit mode AlSb quantum dot layer and AlSb/GaSb superlattices smooth layer. SLs grown on GaAs substrates (GaAs-based SLs) showed well-resolved satellite peaks in XRD. GaSb-based SLs with better structural quality and smoother surface showed strong photoluminescence at 2.55 mu m with a full width at half maximum (FWHM) of 20 meV, narrower than 31 meV of GaAs-based SLs. Inferior optical absorption of GaAs-based SL was observed in the range of 2-3 mu m. Photoresponse of GaSb-based SLs showed the cut-off wavelength at 2.6 mu m.

Shape stability of InAs self-assembled islands on vicinal GaAs(001) substrates

We have grown InAs self-assembled islands on vicinal GaAs( 001) substrates. Atomic force microscopy and photoluminescence studies show that the islands have a clear bimodal size distribution. While most of the small islands whose growth is limited by the width of one multi-atomic step have compact symmetric shapes, a large fraction of the large islands limited by the width of one step plus one terrace have asymmetric shapes which are elongated along the multi-atomic step lines. These results can be attributed to the shape-related energy of the islands at different states of their growth. (C) 2008 Elsevier B. V. All rights reserved.

Growth of nonpolar a-plane GaN on nano-patterned r-plane sapphire substrates

Sapphire substrates were nano-patterned by inductive coupled plasma etching process. Nonpolar a-plane GaN films were grown on planar and nano-patterned r-plane sapphire substrates by metal organic chemical vapor deposition. The anisotropic characteristic and the crystalline quality of the a-plane GaN films were studied through XRD rocking curves. The cross section and surface morphologies of the a-plane GaN films were studied using SEM and AFM measurements, respectively. The crystal quality and surface flatness of the nonpolar a-plane GaN were greatly improved through the usage of the nano-patterned r-plane sapphire substrates. (C) 2008 Elsevier B.V. All rights reserved.

Structural and optical properties of ZnO films on SrTiO3 substrates by MOCVD

ZnO films have been fabricated on (0 0 1), (0 1 1) and (1 1 1) SrTiO3 (STO) substrates by metal-organic chemical vapour deposition (MOCVD). It is interesting that the ZnO films on (0 0 1) and (0 1 1) STO substrates show polar and semipolar orientations, which are different from previous reports, while the same growing direction of polar ZnO with previous results is found on (1 1 1) STO. For the atomic arrangements, two orthogonal domains and a single domain are observed on (0 0 1) and (1 1 1) STO, respectively. Photoluminescence spectra show that every sample has a sharp near-band-edge emission peak at about 3.28 eV without any deep-level emission band between 1.5 and 2.8 eV, implying a high optical quality. A violet emission around 3.0 eV is observed only in ZnO films on (0 0 1) and (0 1 1) STO substrates grown at 600 degrees C, which is discussed briefly. Additionally, the semipolar ZnO does not weaken the emission efficiency along with the reduction in the polarization effect compared with polar ZnO. These results show that high-quality polar and semipolar ZnO films can be grown on STO substrates by MOCVD.

Size distributions of quantum islands on stepped substrates

The size distributions of self-assembled quantum islands on stepped substrates are studied using kinetic Monte Carlo simulations. It is found that the energy barrier E-SW between the step and the terrace region is the key factor in affecting the size distribution of islands. With small E-SW (<= 0.1 eV), lines of uniform islands can be obtained at relative low surface coverage. As the surface coverage is increased, wirelike islands can be obtained. Scaling behavior is obeyed for the size distributions of the wirelike islands. When the size distributions are separated into their width and length components, however, scaling is only observed in the length distribution of the wirelike islands. With larger E-SW, the size distribution of islands shows a clear bimodal size distribution and anomalous growth temperature dependent island size evolutions are observed. The simulation results reproduce qualitatively the phenomena observed in the cases of InAs islands grown on stepped GaAs substrates. (c) 2009 American Institute of Physics. [doi:10.1063/1.3248367]

The effect of single AlGaN interlayer on the structural properties of GaN epilayers grown on Si (111) substrates

High-quality and nearly crack-free GaN epitaxial layer was obtained by inserting a single AlGaN interlayer between GaN epilayer and high-temperature AlN buffer layer on Si (111) substrate by metalorganic chemical vapor deposition. This paper investigates the effect of AlGaN interlayer on the structural proper-ties of the resulting GaN epilayer. It confirms from the optical microscopy and Raman scattering spectroscopy that the AlGaN interlayer has a remarkable effect on introducing relative compressive strain to the top GaN layer and preventing the formation of cracks. X-ray diffraction and transmission electron microscopy analysis reveal that a significant reduction in both screw and edge threading dislocations is achieved in GaN epilayer by the insertion of AlGaN interlayer. The process of threading dislocation reduction in both AlGaN interlayer and GaN epilayer is demonstrated.

Photoluminescence characteristics of GaAsSbN/GaAs epilayers lattice-matched to GaAs substrates

The photoluminescence (PL) characteristics of GaAsSbN/GaAs epilayers grown by molecular beam epitaxy (MBE) are carefully investigated. The results show that antimony (Sb) incorporation into GaNAs material has less influence on the N-induced localization states. For the same N concentration, GaAsSbN material can reach an emission wavelength near 1.3 mum more easily than GaInNAs material. The rapid thermal annealing (RTA) experiment shows that the annealing induced rearrangement of atoms and related blueshift in GaAsSbN epilayers are smaller than those in GaNAs and GaInNAs epilayers. The GaAsSbN material can keep a longer emission wavelength near 1.3 mum-emission even after the annealing treatment. Raman spectroscopy analysis gives further insight into the structure stability of GaAsSbN material after annealing. (C) 2004 Elsevier Ltd. All rights reserved.

The fabrication of self-aligned InAs nanostructures on GaAs(331)A substrates

Self-aligned InAs quantum wires (QWRs) or three-dimensional (3D) islands are fabricated on GaAs(331)A substrates by molecular beam epitaxy (MBE). InAs QWRs are selectively grown on the step edges formed by GaAs layers. The surface morphology of InAs nanostructures is carefully investigated by atomic force microscopy (AFM) measurements. Different growth conditions, such as substrate temperature, growth approaches, and InAs coverage, exert a great effect on the morphology of InAs islands. Low substrate temperatures favour the formation of wirelike nanostructures, while high substrate temperatures favour 3D islands. The shape transition is attributed to the trade-off between surface energy and strain energy. A qualitative agreement of our experimental data with the theoretical results derived from the model proposed by Tersoff and Tromp is achieved.

Effect of annealing on optical properties of InAs quantum dots grown by MOCVD on GaAs (100) vicinal substrates

Thermal annealing effect on InAs quantum dots grown on vicinal (100) GaAs substrates is studied in comparison with dots on exact (100) GaAs substrates. We find that annealing acts stronger effect on dots with vicinal substrates by greatly accelerating the degradation of material quality. as well as slightly increasing the blueshift of the emission wavelength and the narrowing of PL linewidth. It is attributed to the higher strain in the dots formed on the vicinal substrates.