Study of metal oxide-semiconductor capacitors with rf magnetron sputtering TiO(x) and TiO(x)N(y) gate dielectric layer

Metal oxide-semiconductor capacitors with TiO(x) deposited with different O(2) partial pressures (30%, 35%, and 40%) and annealed at 550, 750, and 1000 degrees C were fabricated and characterized. Fourier transform infrared, x-ray near edge spectroscopy, and elipsometry measurements were performed to characterize the TiO(x) films. TiO(x)N(y) films were also obtained by adding nitrogen to the gaseous mixture and physical results were presented. Capacitance-voltage (1 MHz) and current-voltage measurements were utilized to obtain the effective dielectric constant, effective oxide thickness, leakage current density, and interface quality. The results show that the obtained TiO(x) films present a dielectric constant varying from 40 to 170 and a leakage current density (for V(G)=-1 V, for some structures as low as 1 nA/cm(2), acceptable for complementary metal oxide semiconductor circuits fabrication), indicating that this material is a viable, in terms of leakage current density, highk substitute for current ultrathin dielectric layers. (C) 2009 American Vacuum Society. [DOI: 10.1116/1.3043537]

Optical third-harmonic spectroscopy of the magnetic semiconductor EuTe

EuTe possesses the centrosymmetric crystal structure m3m of rocksalt type in which the second-harmonic generation is forbidden in electric dipole approximation but the third-harmonic generation (THG) is allowed. We studied the THG spectra of this material and observed several resonances in the vicinity of the band gap at 2.2-2.5 eV and at higher energies up to 4 eV, which are related to four-photon THG processes. The observed resonances are assigned to specific combinations of electronic transitions between the ground 4f(7) state at the top of the valence band and excited 4f(6)5d(1) states of Eu(2+) ions, which form the lowest energy conduction band. Temperature, magnetic field, and rotational anisotropy studies allowed us to distinguish crystallographic and magnetic-field-induced contributions to the THG. A strong modification of THG intensity for the 2.4 eV band and suppression of the THG for the 3.15 eV band was observed in applied magnetic field. Two main features of the THG spectra were assigned to 5d(t(2g)) and 5d(e(g)) subbands at 2.4 eV and 3.15 eV, respectively. A microscopic quantum-mechanical model of the THG response was developed and its conclusions are in qualitative agreement with the experimental results.

Anomalous lattice parameter of magnetic semiconductor alloys

The addition of transition metals to III-V semiconductors radically changes their electronic, magnetic, and structural properties. We show by ab initio calculations that in contrast to the conventional semiconductor alloys, the lattice parameter in magnetic semiconductor alloys, including those with diluted concentration, strongly deviates from Vegard's law. We find a direct correlation between the magnetic moment and the anion-transition metal bond lengths and derive a simple and general formula that determines the lattice parameter of a particular magnetic semiconductor by considering both the composition and magnetic moment. This dependence can explain some experimentally observed anomalies and stimulate other kind of investigations.

Substrate/semiconductor interface effects on the emission efficiency of luminescent polymers

The importance of interface effects for organic devices has long been recognized, but getting detailed knowledge of the extent of such effects remains a major challenge because of the difficulty in distinguishing from bulk effects. This paper addresses the interface effects on the emission efficiency of poly(p-phenylene vinylene) (PPV), by producing layer-by-layer (LBL) films of PPV alternated with dodecylbenzenesulfonate. Films with thickness varying from similar to 15 to 225 nm had the structural defects controlled empirically by converting the films at two temperatures, 110 and 230 degrees C, while the optical properties were characterized by using optical absorption, photoluminescence (PL), and photoluminescence excitation spectra. Blueshifts in the absorption and PL spectra for LBL films with less than 25 bilayers (<40-50 nm) pointed to a larger number of PPV segments with low conjugation degree, regardless of the conversion temperature. For these thin films, the mean free-path for diffusion of photoexcited carriers decreased, and energy transfer may have been hampered owing to the low mobility of the excited carriers. The emission efficiency was then found to depend on the concentration of structural defects, i.e., on the conversion temperature. For thick films with more than 25 bilayers, on the other hand, the PL signal did not depend on the PPV conversion temperature. We also checked that the interface effects were not caused by waveguiding properties of the excited light. Overall, the electronic states at the interface were more localized, and this applied to film thickness of up to 40-50 nm. Because this is a typical film thickness in devices, the implication from the findings here is that interface phenomena should be a primary concern for the design of any organic device. (C) 2011 American Institute of Physics. [doi:10.1063/1.3622143]

Comparative analysis of triple band S-C-L erbium-doped fibre and semiconductor optical amplifier for CWDM applications

The authors present a comparative analysis between a triple-band S-C-L erbium-doped fibre amplifier and a commercial semiconductor optical amplifier in a CWDM application scenario. Both technologies were characterised for gain and noise figures from 1480 to 1610 nm (S, C and L bands) and their systemic performances were evaluated in terms of bit error rate measurements for a wide range of optical power levels.

Study of reactive sputtering titanium oxide for metal-oxide-semiconductor capacitors

Metal oxide semiconductor (MOS) capacitors with titanium oxide (TiO(x)) dielectric layer, deposited with different oxygen partial pressure (30,35 and 40%) and annealed at 550, 750 and 1000 degrees C, were fabricated and characterized. Capacitance-voltage and current-voltage measurements were utilized to obtain, the effective dielectric constant, effective oxide thickness, leakage current density and interface quality. The obtained TiO(x) films present a dielectric constant varying from 40 to 170 and a leakage current density, for a gate voltage of - 1 V, as low as 1 nA/cm(2) for some of the structures, acceptable for MOS fabrication, indicating that this material is a viable high dielectric constant substitute for current ultra thin dielectric layers. (C) 2009 Elsevier B.V. All rights reserved.

Synthesis and characterization of semiconductor polymers having different phenylene-vinylene conjugation lengths

We have synthesized phenylene-vinylene (PV) polymers containing segments with different conjugation lengths interspaced by random distributed aliphatic segments. Infrared (IR) and ultraviolet-visible (UV-vis) spectroscopies, hydrogen nuclear magnetic resonance ((1)H NMR) spectrometry and differential scanning calorimetry (DSC) were used to characterize the prepared copolymers` structures. Polymers molecular weights were determined by gel permeation chromatography (GPC). The effect of polymer structure and composition on emission properties was studied by fluorescence (PL) spectroscopy under different irradiation wavelength. The emission energy shift due to segments with longer conjugation lengths was minor owed to the low polymerization degree achieved.

Polarized photoluminescence from surface-passivated lead sulfide nanocrystals

Effective surface passivation of lead sulfide (PbS) nanocrystals (NCs) in an aqueous colloidal solution has been achieved following treatment with CdS precursors. The resultant photoluminescent emission displays two distinct components, one originating from the absorption band edge and the other from above the absorption band edge. We show that both of these components are strongly polarized but display distinctly different behaviours. The polarization arising from the band edge shows little dependence on the excitation energy while the polarization of the above-band-edge component is strongly dependent on the excitation energy. In addition, time-resolved polarization spectroscopy reveals that the above-band-edge polarization is restricted to the first couple of nanoseconds, while the band edge polarization is nearly constant over hundreds of nanoseconds. We recognize an incompatibility between the two different polarization behaviours, which enables us to identify two distinct types of surface-passivated PbS NC.

Separating fluorescent species of aqueous PbS semiconductor nanocrystals using micro-emulsions

Colloidal PbS nanocrystals over-coated with CdS are prepared in aqueous solutions and exhibit strong photoluminescence with two distinct peaks in the visible regime. A photoluminescence peak is observed at 640 nm, which is attributed to the band edge recombination in the PbS nanocrystals, and another peak at 510 nm, which is above the band edge of the PbS nanocrystals. The two PL peaks are isolated by extracting separate species of nanocrystal based upon their surface morphology. Micro-emulsions of hexane:PVA are used to remove the species containing the PL peak at 640 nm from the solution, leaving a singular peak at 510 nm. We show conclusively that the double-peaked structure observed in the photoluminescence spectra of PbS nanocrystals over-coated with CdS is due to the presence of two distinctly different nanocrystal species.

Encoding combinatorial libraries: A novel application of fluorescent silica colloids

A major challenge associated with using large chemical libraries synthesized on microscopic solid support beads is the rapid discrimination of individual compounds in these libraries. This challenge can be overcome by encoding the beads with 1 mum silica colloidal particles (reporters) that contain specific and identifiable combinations of fluorescent byes. The colored bar code generated on support beads during combinatorial library synthesis can be easily, rapidly, and inexpensively decoded through the use of fluorescence microscopy. All reporters are precoated with polyelectrolytes [poly(acrylic acid), PAA, poly(sodium 4-styrenesulfonate PSSS, polyethylenimine, PEI, and/or poly(diallyldimethylammonium chloride), PDADMAC] with the aim of enhancing surface charge, promoting electrostatic attraction to the bead, and facilitating polymer bridging between the bead and reporter for permanent adhesion. As shown in this article, reporters coated with polyelectrolytes clearly outperform uncoated reporters with regard to quantity of attached reporters per bead (54 +/- 23 in 2500 mum(2) area for PEI/PAA coated and 11 +/- 6 for uncoated reporters) and minimization of cross-contamination (1 red reporter in 2500 mum(2) area of green-labeled bead for PEI/PAA coated and 26 +/- 15 red reporters on green-labeled beads for uncoated reporters after 10 days). Examination of various polyelectrolyte systems shows that the magnitude of the xi -potential of polyelectrolyte-coated reporters (-64 mV for PDADMAC/PSSS and -42 mV for PEI/PAA-coated reporters) has no correlation with the number of reporters that adhere to the solid support beads (21 +/- 16 in 2500 mum(2) area for PDADMAC/PSSS and 54 +/- 23 for PEI/PAA-coated reporters). The contribution of polymer bridging to the adhesion has a far greater influence than electrostatic attraction and is demonstrated by modification of the polyelectrolyte multilayers using gamma irradiation of precoated reporters either in aqueous solution or in polyelectrolyte solution.

Measuring the decoherence rate in a semiconductor charge qubit

We describe a method by which the decoherence time of a solid-state qubit may be measured. The qubit is coded in the orbital degree of freedom of a single electron bound to a pair of donor impurities in a semiconductor host. The qubit is manipulated by adiabatically varying an external electric field. We show that by measuring the total probability of a successful qubit rotation as a function of the control field parameters, the decoherence rate may be determined. We estimate various system parameters, including the decoherence rates due to electromagnetic fluctuations and acoustic phonons. We find that, for reasonable physical parameters, the experiment is possible with existing technology. In particular, the use of adiabatic control fields implies that the experiment can be performed with control electronics with a time resolution of tens of nanoseconds.

Multi-fluorescent silica colloids for encoding large combinatorial libraries

Large chemical libraries can be synthesized on solid-support beads by the combinatorial split-and-mix method. A major challenge associated with this type of library synthesis is distinguishing between the beads and their attached compounds. A new method of encoding these solid-support beads, 'colloidal bar-coding', involves attaching fluorescent silica colloids ('reporters') to the beads as they pass through the compound synthesis, thereby creating a fluorescent bar code on each bead. In order to obtain sufficient reporter varieties to bar code extremely large libraries, many of the reporters must contain multiple fluorescent dyes. We describe here the synthesis and spectroscopic analysis of various mono- and multi-fluorescent silica particles for this purpose. It was found that by increasing the amount of a single dye introduced into the particle reaction mixture, mono- fluorescent silica particles of increasing intensities could be prepared. This increase was highly reproducible and was observed for six different fluorescent dyes. Multi-fluorescent silica particles containing up to six fluorescent dyes were also prepared. The resultant emission intensity of each dye in the multi-fluorescent particles was found to be dependent upon a number of factors; the hydrolysis rate of each silane-dye conjugate, the magnitude of the inherent emission intensity of each dye within the silica matrix, and energy transfer effects between dyes. We show that by varying the relative concentration of each silane-dye conjugate in the synthesis of multi-fluorescent particles, it is possible to change and optimize the resultant emission intensity of each dye to enable viewing in a fluorescence detection instrument.