This thesis is concerned with the adsorption and detachment of polymers at planar, rigid surfaces. We have carried out a systematic investigation of adsorption of polymers using analytical techniques as well as Monte Carlo simulations with a coarse grained off-lattice bead spring model. The investigation was carried out in three stages. In the first stage the adsorption of a single multiblock AB copolymer on a solid surface was investigated by means of simulations and scaling analysis. It was shown that the problem could be mapped onto an effective homopolymer problem. Our main result was the phase diagram of regular multiblock copolymers which shows an increase in the critical adsorption potential of the substrate with decreasing size of blocks. We also considered the adsorption of random copolymers which was found to be well described within the annealed disorder approximation. In the next phase, we studied the adsorption kinetics of a single polymer on a flat, structureless surface in the regime of strong physisorption. The idea of a ’stem-flower’ polymer conformation and the mechanism of ’zipping’ during the adsorption process were used to derive a Fokker-Planck equation with reflecting boundary conditions for the time dependent probability distribution function (PDF) of the number of adsorbed monomers. The numerical solution of the time-dependent PDF obtained from a discrete set of coupled differential equations were shown to be in perfect agreement with Monte Carlo simulation results. Finally we studied force induced desorption of a polymer chain adsorbed on an attractive surface. We approached the problem within the framework of two different statistical ensembles; (i) by keeping the pulling force fixed while measuring the position of the polymer chain end, and (ii) by measuring the force necessary to keep the chain end at fixed distance above the adsorbing plane. In the first case we treated the problem within the framework of the Grand Canonical Ensemble approach and derived analytic expressions for the various conformational building blocks, characterizing the structure of an adsorbed linear polymer chain, subject to pulling force of fixed strength. The main result was the phase diagram of a polymer chain under pulling. We demonstrated a novel first order phase transformation which is dichotomic i.e. phase coexistence is not possible. In the second case, we carried out our study in the “fixed height” statistical ensemble where one measures the fluctuating force, exerted by the chain on the last monomer when a chain end is kept fixed at height h over the solid plane at different adsorption strength ε. The phase diagram in the h − ε plane was calculated both analytically and by Monte Carlo simulations. We demonstrated that in the vicinity of the polymer desorption transition a number of properties like fluctuations and probability distribution of various quantities behave differently, if h rather than the force, f, is used as an independent control parameter.

Biomimetic bilayer membranes made from polymers and lipids

Amphiphile Blockcopolymere sind in der Lage in Wasser Morphologien auszubilden, die analog sind zur hydrophil-hydrophob-hydrophil-Struktur von natürlichen Lipiddoppelschichten. In dieser Arbeit wird zum ersten Mal die Präparation und Charakterisierung von oberflächengestützten Polymerdoppelschichten aus Polybutadien-b-Polyethylenoxid (PB-PEO) beschrieben. Für die Herstellung dieser Strukturen wurden zwei unterschiedliche Präparationsstrategien verfolgt. Der erste Weg besteht aus einer zweistufigen Methode, bei der im ersten Schritt organisierte Monoschichten mittels Langmuir-Blodgett-Transfer auf Gold übertragen und kovalent angebunden werden. Im zweiten Schritt werden hydrophobe Wechselwirkungen ausgenutzt, um über Langmuir-Schaefer-Transfer eine weitere Schicht aufzubringen. Somit wurden homogene Architekturen erzeugt, die oberflächengestützten Lipiddoppelschichten gleichen. Als alternativer, einstufiger Ansatz zur Herstellung von Polymerdoppelschichten wurde das Spreiten von Polymervesikeln auf Gold verfolgt. Auch hierdurch ließen sich Doppelschichtstrukturen mit einer vollständigen Oberflächenbedeckung erzeugen. Die hergestellten Polymerdoppelschichten besitzen eine Dicke von 11-14 nm, die von der Präparationsmethode abhängt. Die Polymerstrukturen weisen bei Trocknung für 1.5 h eine Stabilität gegenüber Luft auf. Bei längeren Trocknungszeiten von ca. 12 h kommt es zu einer Reorganisation der Oberfläche. Dies deutet darauf hin, dass Wasser dazu notwendig ist die Strukturen auf lange Sicht zu stabilisieren. Um die Biokompatibilität der Polymerschichten nachzuweisen, wurden die Wechselwirkungen mit dem membranaktiven Peptid Polymyxin B und dem Transmembranprotein α-Haemolysin gezeigt. Mobilität ist ein wichtiger Faktor für die korrekte Funktion vieler Transmembranproteine. Um die laterale Diffusionsdynamik innerhalb der künstlichen Strukturen zu untersuchen, wurde die Mobilität eines integralen Modellpeptids und von fluoreszierenden Membransonden gemessen. Es konnte mit einzelmolekülempfindlichen Techniken gezeigt werden, dass das α-helikale Peptid und die kleinen Fluoreszenzfarbstoffe frei im hydrophoben Kern der Polymerdoppelschicht diffundieren können. Die Diffusion von beiden Spezies scheint stark von der Fluidität der Polymermatrix beeinflusst zu sein. Ein weiterer Teil dieser Arbeit widmet sich der Entwicklung eines angemessenen, lipidbasierten Referenzsystems für zukünftige Proteinuntersuchungen. Hierzu wurde eine neue Methode zu Herstellung von peptidgestützten Lipiddoppelschichtmembranen entwickelt. Dies wurde durch kovalente Befestigung eines Thiopeptids an einen Goldfilm und darauffolgende Anbindung eines Lipids erreicht. Zur Ausbildung der Lipiddoppelschicht auf dem Lipopeptidunterbau wurder der Rapid Solvent Exchange verwendet. Die Ausbildung der Lipiddoppelschicht wurde sowohl auf microskopischer als auch auf makroskopischer Ebene nachgewiesen. Im letzten Schritt wurde die Anwendbarkeit des Modelsystems für elektrochemische Messungen durch den funktionalen Einbau des Ionentransporters Valinomycin unter Beweis gestellt.

Electrostatic supramolecular assembly of charged dendritic polymers and their biological application

The aim of this study was the development of functional multilayer films through electrostatic layer by layer (LbL) assembly of dendritic macromolecules, the investigation of the fundamental properties of these multilalyered films and the study of their biological applications. rnThe synthesis of the anionic hyperbranched polyglycerols (hbPG) and the preparation of multilayers made of hbPG/phosphorus dendrimer as well as the influences of deposition conditions on multilayers were reported. The thicknesses of multilayer films increase with a decrease of molecular weight of anionic hbPGs. The multilayer films fabricated by low molecular weight hbPGs grow less regularly due to the less charged carboxylic acid groups providing the relative weaker electrostatic forces for the deposition. The thicknesses of multilayer films are reduced with increasing pH values and decreasing the concentration of NaCl. The observed changes of multilayer thickness and surface morphology could be interpreted with the aid of theories regarding the charge density and conformation of the anionic hbPG chains in solution. rnBesides the study of fundamental properties of hbPG/phosphorus multilayer films, antifouling thin films derived from hbPG layers were developed. The antifouling properties of hbPG layers were found to correlate with factors of the molecular weight of anionic hbPG and the film thickness. It was demonstrated that anionic hbPG single layer with highest molecular weight can reduce non specific protein adsorption more efficiently than single layer with lower molecular weight and all the hbPG bilayers possessed excellent property of antifouling. rnPhosphorus dendrimer multilayers were successfully prepared as the platforms to detect DNA immobilization and hybridization. The effect of NaCl concentration on the multilayer film thickness was evaluated to obtain the optimized film thickness. Making use of the multilayer deposited at the optimized condition as a substrate, a high loading of DNA probes was achieved through covalent coupling of probe DNA with the as-formed multilayer films. The hybridization of target DNA with immobilized probe DNA was then carried out and studied by SPFS. The limit of detection upon hybridization was estimated on various dendrimer multilayer platforms. The minimum detection concentration for DNA hybridization is in the same order of magnitude compared with other neutral phosphorus dendrimer systems. Furthermore, the LbL deposition of phosphorus dendrimer multilayers provided a mild and simple way to prepare platforms as DNA microarrays. rnBased on the phosphorus dendrimer multilayer systems, dendritic star polymers were employed which have more reactive groups than that phosphorus dendrimers. The as-assembled dendritic star polymer multilayer films exhibited such distinct morphology characteristics that they underwent extensive structural reorganization upon post-treatment under different pH conditions. Kinetic binding of probe DNA molecules on the outermost negatively charged dendritic surface was studied by SPR as well. The binding capacities of probe DNA on the multilayer surfaces fabricated from the first-generation and the second-generation of dendritic star polymers were compared. The improved binding capacity was achieved from the second-generation of dendritic star polymer multilayer films due to their more reactive groups. DNA hybridization reaction on dendritic multilayer films was investigated by SPFS. The similar hybridization behaviors were found on both multilayer surfaces. Meanwhile, the hybridization kinetic affinities were compared with that of phosphorus dendrimer multilayer surfaces and showed improved detection sensitivity than phosphorus dendrimer multilayer films.rn

Nanoscopic studies of conjugated polymer blends by (electric) scanning probe microscopy

Conjugated polymers and conjugated polymer blends have attracted great interest due to their potential applications in biosensors and organic electronics. The sub-100 nm morphology of these materials is known to heavily influence their electromechanical properties and the performance of devices they are part of. Electromechanical properties include charge injection, transport, recombination, and trapping, the phase behavior and the mechanical robustness of polymers and blends. Electrical scanning probe microscopy techniques are ideal tools to measure simultaneously electric (conductivity and surface potential) and dielectric (dielectric constant) properties, surface morphology, and mechanical properties of thin films of conjugated polymers and their blends.rnIn this thesis, I first present a combined topography, Kelvin probe force microscopy (KPFM), and scanning conductive torsion mode microscopy (SCTMM) study on a gold/polystyrene model system. This system is a mimic for conjugated polymer blends where conductive domains (gold nanoparticles) are embedded in a non-conductive matrix (polystyrene film), like for polypyrrole:polystyrene sulfonate (PPy:PSS), and poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS). I controlled the nanoscale morphology of the model by varying the distribution of gold nanoparticles in the polystyrene films. I studied the influence of different morphologies on the surface potential measured by KPFM and on the conductivity measured by SCTMM. By the knowledge I gained from analyzing the data of the model system I was able to predict the nanostructure of a homemade PPy:PSS blend.rnThe morphologic, electric, and dielectric properties of water based conjugated polymer blends, e.g. PPy:PSS or PEDOT:PSS, are known to be influenced by their water content. These properties also influence the macroscopic performance when the polymer blends are employed in a device. In the second part I therefore present an in situ humidity-dependence study on PPy:PSS films spin-coated and drop-coated on hydrophobic highly ordered pyrolytic graphite substrates by KPFM. I additionally used a particular KPFM mode that detects the second harmonic electrostatic force. With this, I obtained images of dielectric constants of samples. Upon increasing relative humidity, the surface morphology and composition of the films changed. I also observed that relative humidity affected thermally unannealed and annealed PPy:PSS films differently. rnThe conductivity of a conjugated polymer may change once it is embedded in a non-conductive matrix, like for PPy embedded in PSS. To measure the conductivity of single conjugated polymer particles, in the third part, I present a direct method based on microscopic four-point probes. I started with metal core-shell and metal bulk particles as models, and measured their conductivities. The study could be extended to measure conductivity of single PPy particles (core-shell and bulk) with a diameter of a few micrometers.

Morphology and charge transport in conjugated polymers

To assist rational compound design of organic semiconductors, two problems need to be addressed. First, the material morphology has to be known at an atomistic level. Second, with the morphology at hand, an appropriate charge transport model needs to be developed in order to link charge carrier mobility to structure.rnrnThe former can be addressed by generating atomistic morphologies using molecular dynamics simulations. However, the accessible range of time- and length-scales is limited. To overcome these limitations, systematic coarse-graining methods can be used. In the first part of the thesis, the Versatile Object-oriented Toolkit for Coarse-graining Applications is introduced, which provides a platform for the implementation of coarse-graining methods. Tools to perform Boltzmann inversion, iterative Boltzmann inversion, inverse Monte Carlo, and force-matching are available and have been tested on a set of model systems (water, methanol, propane and a single hexane chain). Advantages and problems of each specific method are discussed.rnrnIn partially disordered systems, the second issue is closely connected to constructing appropriate diabatic states between which charge transfer occurs. In the second part of the thesis, the description initially used for small conjugated molecules is extended to conjugated polymers. Here, charge transport is modeled by introducing conjugated segments on which charge carriers are localized. Inter-chain transport is then treated within a high temperature non-adiabatic Marcus theory while an adiabatic rate expression is used for intra-chain transport. The charge dynamics is simulated using the kinetic Monte Carlo method.rnrnThe entire framework is finally employed to establish a relation between the morphology and the charge mobility of the neutral and doped states of polypyrrole, a conjugated polymer. It is shown that for short oligomers, charge carrier mobility is insensitive to the orientational molecular ordering and is determined by the threshold transfer integral which connects percolating clusters of molecules that form interconnected networks. The value of this transfer integral can be related to the radial distribution function. Hence, charge mobility is mainly determined by the local molecular packing and is independent of the global morphology, at least in such a non-crystalline state of a polymer.

Triphenylene-based polymers for organic electronics

An efficient synthesis has been developed toward a novel series of conjugated blue emitting polymers containing triphenylene as repeating unit for polymer light emitting diodes (PLEDs). Soluble triphenylene-based co- and homo-polymers have been synthesized by the palladium-catalyzed Suzuki-Miyaura and the nickel-catalysed Yamamoto polycondensation reactions, respectively. The photophysical properties as well as the application of the polymers in PLED devices are presented here.rnIn addition a simple GNR fabrication method that allows for the production of atomically precise GNRs of different topologies and widths is introduced. This bottom-up approach consists in the surface-assisted coupling of suitably designed molecular triphenylene precursors into linear polyphenylenes and their subsequent cyclodehydrogenation and results in GNRs whose topology, width and edge periphery are defined by the precursor monomers. Various types of atomically precise GNRs thus eventually become available for experimental investigation and exploitation of their many predicted and technologically highly interesting properties. Furthermore, it is anticipated that this bottom-up approach of GNR fabrication will allow the engineering of chemical and electronic properties and the yet elusive realization of theoretically predicted structures such as intraribbon quantum dots, superlattice structures, or magnetic devices based on specific GNR edge states.rn

From amphiphilic block copolymers to ferrocenyl-functionalized polymers for biosensoric applications

The present thesis can be divided in three main parts. In all parts new polymer architecturesrnwere synthesized and characterized concerning their special features.rnThe first part will emphasize the advantage of a polystyrene-block-(hyperbranchedrnpolyglycerol) copolymer in comparison to an analogue polystyrene-block-(linear polyglycerol)rncopolymer. Therefore a synthethic route to prepare linear block copolymersrnhas been developed. Two strategies were examined. One strategy was based on thernclassic, sequential anionic polymerization; the second strategy was based on arn“Click-Chemistry” coupling reaction. In a following step glycidol was hypergraftedrnfrom these block copolymers by applying a hypergrafting reaction with glycidol. Thernbehavior of the amphiphilic block copolymers synthesized was studied in differentrnsolvents. Furthermore the polarity of the solvent was changed to form the correspondingrninverse micelles. DLS, SLS, SEC-MALLS-VISCO, AFM and Cyro TEMrnmeasurements were performed to obtain a visual image from the appearance of thernaggregates. It was found that a linear-hyperbranched architecture is necessary, ifrnwell defined, monodisperse aggregates are required, e.g. for the preparation of orderedrnnanoarrays. Linear-linear block copolymers formed only polydisperse aggregates.rnAdditionally it was found that size distribution could be improved dramaticallyrnby passing the aggregates through a SEC column with large pores. The SEC columnsrnacted like a template in which the aggregates adopt a more stable conformation.rnIn the second part anionic polymerization was employed to synthesize silaneendfunctionalizedrnmacromonomers with different molecular weights based on polybutadienernand polyisoprene. These were polymerized by a hydrosilylation reaction inrnbulk to obtain branched polymers, using Karstedt’s catalyst. Surprisingly the additionrnof monofunctional silanes during the polymerization had only a minimal effect concerningrnthe degree of polymerization. It was possible to introduce silanes without increasingrnthe overall number of reaction steps by a very convenient “pseudo-copolymerization”rnmethod. All branched polymers were analyzed by SEC, SEC-MALLS,rnSEC-viscometry, 1H-NMR-spectroscopy and DSC concerning their branching ratio.rnThe branching parameters for the branched polymers exhibited similar characteristicsrnas hyperbranched polymers based on AB2 monomers. Detailed kinetic study showedrnthat the polymerization occurred very rapidly in comparison to the hydrosilylation polymerizationrnof classical AB2 type carbosilanes monomers.rnThe last part will deal with ferrocenyl-functionalized polymers. On the one hand,rnferrocenyl-functionalized polyglycerols (PG) were studied. Esterification of PGs withrndifferent molecular weight using ferrocenemonocarboxylic acid gave the ferrocenylrnfuntionalized polymers in high yields. On the other hand three different block copolymersrnwere prepared with different ratios of styrene to butadiene units (10:1, 4:1, 2:1).rnThe double bonds of the 1,2-PB block were hydrosilylated using silanes bearing onern(HSiMe2Fc) or two (HSiMeFc2) ferrocene units. High degrees of functionalizationrnwere obtained (up to 83 %). In this manner, six different ferrocenyl-rich block copolymersrnwith different fractions of ferrocene were prepared and analyzed, employingrnNMR-spectroscopy, SEC, SEC/MALLS/viscometry, DLS and cyclic voltammetry. Thernredox properties of the studied polymers varied primarily with the nature of the silanernunit attached. Additionally, the redox properties in solution of the studied polymersrnwere influenced by the block length ratio of the block copolymers. Unexpectedly, withrnincreasing block length of the ferrocenyl block the fraction of active ferrocenes decreased.rnNevertheless, in case of thin monolayer films this behaviour was not observed.rnAll polymers (PG and PS-b-PB based) exhibited good electrochemical propertiesrnin a wide range of solvents, which rendered them very interesting for biosensoricrnapplications.

Synthesis and characterization of temperature- and light-responsive polymers and block copolymers

In summary, thermoresponsive polyacrylamides with various amounts of different photoswitchable side groups, i. e. azobenzene, salicylideneaniline and fulgimide were successfully prepared. As such, in a first step three different chromophores with an amine functionality were synthesized. The synthesis of the stimuli-responsive materials was based on the RAFT polymerization of activated ester acrylates followed by a polymer analogous reaction with different amines. The procedure has been designed to allow the synthesis of well-defined materials with functional groups. All copolymers prepared in this way showed a LCST in aqueous solution. The LCST was in general decreased by increasing the amount of hydrophobic dye incorporated into the thermoresponsive polymer. However, in the case of the fulgimide, the LCST was hardly affected by the chromophore. For azobenzene containing PNIPAM polymers and analogues, higher LCST values were measured after irradiation of the polymer sample solutions with UV-light (Delta LCSTmax = 7.3°C). A reversible light-induced solubility change within a certain temperature range was possible. In contrast to this, irradiated samples of salicylideneaniline containing thermoresponsive copolymers showed an irreversible increase in the LCST (Delta LCSTmax = 13.0°C). Fulgimide chromophores did not influence the LCST of PNIPAM based copolymers after UV-light exposure.rnSimilar to the thermoresponsive polyacrylamides with azobenzene side groups, poly(oligo(ethylene glycol) methyl ether methacrylate) [P(OEGMA)] polymers with azobenzene end groups showed a LCST shift upon UV-irradiation. These polymers were synthesized by RAFT polymerization using a functional chain transfer agent (CTA). For this, PFP-CTA was used as a RAFT-agent for end group functionalization of (thermoresponsive) polymers. In contrast to the statistically arranged copolymers with azobenzene side groups, P(OEGMA) polymers with terminal azobenzene showed a linear increase of the LCST shifts with increasing amount of chromophore (Delta LCSTmax = 4.3°C). Noteworthy, the chemical nature of the end group exhibited a strong influence on the LCST in the case of short thermoresponsive P(OEGMA) polymers.rnThe investigation on temperature- and lightresponsive polymers was transferred onto block copolymers capable to self-assemble into polymeric micelles. Therefore, PEO-b-PNIPAM block copolymers with azobenzene moieties were synthesized successfully. These polymers showed a “smart” behavior in aqueous solution, as the reversible formation and disruption of the micelles could either be controlled by temperature or using light as a stimulus. The usefulness of these materials was demonstrated by encapsulation of a hydrophobic dye in the core of the micelle. Such materials might have a great potential as a model system for several technical or biological applications.rnFinally, double thermoresponsive block copolymers forming micellar structures in a certain temperature range with functional end groups could successfully be synthesized. These “smart materials” based on POEGMA-b-PNIPMAM have been demonstrated to be very promising for a temperature selective immobilization on a protein surface. This might be a suitable concept for further biological applications.rnConcluding, different thermoresponsive copolymers and block copolymers with lightresponsive moieties arranged along the backbone or located at the chain ends were successfully prepared and investigated. By controlling the nature of functional groups and their respective incorporation ratios, the LCST could be dialed in precisely. Further, the LCST of the polymers could be triggered by light. A light-controlled disruption of micellar structures could be shown for functional block copolymers. The importance of end groups of thermoresponsive polymers was demonstrated by a temperature-controlled protein-polymer binding of a terminal biotin-functionalized double thermoresponsive polymer. The synthetic approaches and the material properties presented here should be promising for further research and applications beyond this dissertation.rn

Alpha, Omega end group functionalization of RAFT polymers based on pentafluorophenyl esters and methane thiosulfonates

While polymers with different functional groups along the backbone have intensively been investigated, there is still a challenge in orthogonal functionalization of the end groups. Such well-defined systems are interesting for the preparation of multiblock (co) polymers or polymer networks, for bio-conjugation or as model systems for examining the end group separation of isolated polymer chains. rnHere, Reversible Addition Fragmentation Chain Transfer (RAFT) polymerization was employed as method to investigate improved techniques for an a, w end group functionalization. RAFT produces polymers terminated in an R group and a dithioester-Z group, where R and Z stem from a suitable chain transfer agent (CTA). rnFor alpha end group functionalization, a CTA with an activated pentafluorophenyl (PFP) ester R group was designed and used for the polymerization of various methacrylate monomers, N-isopropylacrylamide and styrene yielding polymers with a PFP ester as a end group. This allowed the introduction of inert propyl amides, of light responsive diazo compounds, of the dyes NBD, Texas Red, or Oregon Green, of the hormone thyroxin and allowed the formation of multiblocks or peptide conjugates. rnFor w end group functionalization, problems of other techniques were overcome through an aminolysis of the dithioester in the presence of a functional methane thiosulfonate (MTS), yielding functional disulfides. These disulfides were stable under ambient conditions and could be cleaved on demand. Using MTS chemistry, terminal methyl disulfides (enabling self-assembly on planar gold surfaces and ligand substitution on gold and semiconductor nanoparticles), butynyl disulfide end groups (allowing the “clicking” of the polymers onto azide functionalized surfaces and the selective removal through reduction), the bio-target biotin, and the fluorescent dye Texas Red were introduced into polymers. rnThe alpha PFP amidation could be performed under mild conditions, without substantial loss of DTE. This way, a step-wise synthesis produced polymers with two functional end groups in very high yields. rnAs examples, polymers with an anchor group for both gold nanoparticles (AuNP) and CdSe / ZnS semi-conductor nanoparticles (QD) and with a fluorescent dye end group were synthesized. They allowed a NP decoration and enabled an energy transfer from QD to dye or from dye to AuNP. Water-soluble polymers were prepared with two different bio-target end groups, each capable of selectively recognizing and binding a certain protein. The immobilization of protein-polymer-protein layers on planar gold surfaces was monitored by surface plasmon resonance.Introducing two different fluorescent dye end groups enabled an energy transfer between the end groups of isolated polymer chains and created the possibility to monitor the behavior of single polymer chains during a chain collapse. rnThe versatility of the synthetic technique is very promising for applications beyond this work.

Application of a hybrid blocking layer in dye-sensitized solar cells

In dye-sensitized solar cells a blocking layer between the transparent electrode and the mesoporous titanium dioxide film is used to prevent short-circuits between the hole-conductor and the front electrode. The conventional approach is to use a compact layer of titanium dioxide prepared by spin coating or spray pyrolysis. The thickness of the blocking layer is critical. On one hand, the layer has to be thick enough to cover the rough substrate completely. On the other hand, the serial resistance increases with increasing film thickness, because the layer acts as an ohmic resistance itself. In this thesis an amphiphilic diblock copolymer is used as a functional template to produce an alternative, hybrid blocking layer. The hybrid blocking layer is thinner than the conventional, compact titanium dioxide film and thereby possesses a higher conductivity. Still, this type of blocking layer covers the rough electrode material completely and avoids current loss through charge recombination. The novel blocking layer is prepared using a tailored, amphiphilic block copolymer in combination with sol-gel chemistry. While the hydrophilic poly(ethylene oxide) part of the polymer coordinates a titanium dioxide precursor to form a percolating network of titania particles, the hydrophobic poly(dimethylsiloxane) part turns into an insulating ceramic layer. With this technique, crack-free films with a thickness down to 24 nm are obtained. The presence of a conductive titanium dioxide network for current flow, which is embedded in an insulating ceramic material, is validated by conductive scanning force microscopy. This is the first time that such a hybrid blocking layer is implemented in a solar cell. With this approach the efficiency could be increased up to 27 % compared to the conventional blocking layer. Thus, it is demonstrated that the hybrid blocking layer represents a competitive alternative to the classical approach.

Laser heating of polymers

Zur Untersuchung von Effekten beim Laserheizen von Polymeren wurde ein Temperaturmessaufbau entwickelt. Das Messprinzip basiert auf der Auswertung der thermischen Emission. Der Messaufbau besteht aus einer hochauflösenden Kamera, ausgestattet mit Bildverstärker, sowie Interferenzfiltern um eine spektrale Auflösung zu gewährleisten und einem gepulster NIR-Heizlaser. Die Pulsdauer des Lasers liegt in der Größenordnung von 10 µs, der Strahldurchmesser durch entsprechende Fokussierung in der Größenordnung von 10 µm. Mittels Fit des Planck‘schen Strahlungsgesetzes an die aufgenommene thermische Emission konnten 2D Temperaturgraphen erhalten werden. Eine Ortsauflösung von 1 µm und eine Zeitauflösung von 1 µs konnten realisiert werden. In Kombination mit Finite-Elemente-Simulationen wurde mit diesem Aufbau die Laserablation verschiedener Polymere untersucht. Dabei hat sich gezeigt, dass bei Polymeren mit einem Glasübergang im Temperaturbereich zwischen Raum- und Zerfallstemperatur, photomechanische Ablation stattfand. Die Ablationsschwelle lag für diese Polymere mehrere 10 K über dem Glasübergang, weit unter der Zerfallstemperatur aus thermogravimetrischen Experimenten mit typischen Heizraten von 10 K/min. Bei hohen Laserenergien und damit verbundenen hohen Temperaturen konnte dagegen thermischer Zerfall beobachtet werden. Ein Übergang des Mechanismus von photomechanischer Ablation zu Ablation durch thermischen Zerfall ergab sich bei Temperaturen deutlich über der Zerfallstemperatur des Polymers aus der Thermogravimetrie. Dies wurde bedingt durch die kurzen Reaktionszeiten des Laserexperiments in der Größenordnung der Pulsdauer und steht im Einklang mit dem Gesetz von Arrhenius. Polymere ohne Glasübergang im Heizbereich zeigten dagegen keine photomechanische Ablation, sondern ausschließlich thermischen Zerfall. Die Ablationsschwelle lag auch hier bei höheren Temperaturen, entsprechend dem Gesetz von Arrhenius. Hohe Temperaturen, mehrere 100 K über der Zerfallstemperatur, ergaben sich darüber hinaus bei hohen Laserenergien. Ein drastisches Überhitzen des Polymers, wie in der Literatur beschrieben, konnte nicht beobachtet werden. Experimentelle Befunde deuten vielmehr darauf hin, dass es sich bei dem heißen Material um thermische Zerfallsprodukte, Polymerfragmente, Monomer und Zerfallsprodukte des Monomers handelte bzw. das Temperaturprofil der Zerfallsreaktion selbst visualisiert wurde.

Polymer surfaces on small length- and short time-scales

The behaviour of a polymer depends strongly on the length- and time scale as well as on the temperature rnat which it is probed. In this work, I describe investigations of polymer surfaces using scanning probe rnmicroscopy with heatable probes. With these probes, surfaces can be heated within seconds down to rnmicroseconds. I introduce experiments for the local and fast determination of glass transition and melting rntemperatures. I developed a method which allows the determination of glass transition and melting rntemperatures on films with thicknesses below 100 nm: A background measurement on the substrate was rnperformed. The resulting curve was subtracted from the measurement on the polymer film. The rndifferential measurement on polystyrene films with thicknesses between 35 nm and 160 nm showed rncharacteristic signals at 95 ± 1 °C, in accordance with the glass transition of polystyrene. Pressing heated rnprobes into polymer films causes plastic deformation. Nanometer sized deformations are currently rninvestigated in novel concepts for high density data storage. A suitable medium for such a storage system rnhas to be easily indentable on one hand, but on the other hand it also has to be very stable towards rnsurface induced wear. For developing such a medium I investigated a new approach: A comparably soft rnmaterial, namely polystyrene, was protected with a thin but very hard layer made of plasma polymerized rnnorbornene. The resulting bilayered media were tested for surface stability and deformability. I showed rnthat the bilayered material combines the deformability of polystyrene with the surface stability of the rnplasma polymer, and that the material therefore is a very good storage medium. In addition we rninvestigated the glass transition temperature of polystyrene at timescales of 10 µs and found it to be rnapprox. 220 °C. The increase of this characteristic temperature of the polymer results from the short time rnat which the polymer was probed and reflects the well-known time-temperature superposition principle. rnHeatable probes were also used for the characterization of silverazide filled nanocapsules. The use of rnheatable probes allowed determining the decomposition temperature of the capsules from few rnnanograms of material. The measured decomposition temperatures ranged from 180 °C to 225 °C, in rnaccordance with literature values. The investigation of small amounts of sample was necessary due to the rnlimited availability of the material. Furthermore, investigating larger amounts of the capsules using rnconventional thermal gravimetric analysis could lead to contamination or even damage of the instrument. rnBesides the analysis of material parameters I used the heatable probes for the local thermal rndecomposition of pentacene precursor material in order to form nanoscale conductive structures. Here, rnthe thickness of the precursor layer was important for complete thermal decomposition. rnAnother aspect of my work was the investigation of redox active polymers - Poly-10-(4-vinylbenzyl)-10H-rnphenothiazine (PVBPT)- for data storage. Data is stored by changing the local conductivity of the material rnby applying a voltage between tip and surface. The generated structures were stable for more than 16 h. It rnwas shown that the presence of water is essential for succesfull patterning.

Sulfur-containing polymers for surface attachment

Different concepts for the synthesis of sulfur-containing polymers as well as their adsorption onto gold surfaces were studied. The present work is divided into three parts. The main part focuses on the synthesis of poly(1,2-alkylene sulfides) (“polysulfides”) with complex architectures on the basis of polyether-based macroinitiators by the anionic ring-opening polymerization of ethylene sulfide and propylene sulfide. This synthetic tool kit allowed the synthesis of star-shaped, brush-like, comb-like and pom-pom-like polysulfides, the latter two with an additional poly(ethylene glycol) chain. Additionally, the number of polysulfide arms as well as the monomer composition could be varied over a wide range to obtain copolymers with multiple thioether functionalities.rnThe second section deals with the synthesis of a novel lipoic acid-based initiator for ring-opening polymerizations for lactones and epoxides. A straightforward approach was selected to accomplish the ability to obtain tailored polymers with a common used disulfide-anchoring group, without the drawbacks of post-polymerization functionalization. rnIn the third part, a new class of block-copolymers consisting of polysulfides and polyesters were investigated. For the first time this approach enabled the use of hydroxyl-terminated poly(propylene sulfide) as macroinitiator for the synthesis of a second block.rnThe adsorption efficiency of those different polymer classes onto gold nanoparticles as well as gold rnsupports was studied via different methods.rn