Leakage current behavior of Bi3.25La0.75Ti3O12 ferroelectric thin films deposited on different bottom electrodes

Bi3.25La0.75Ti3O12 (BLT) thin films were grown on LaNiO3 (LNO), RuO2 (RuO2) and La0.5Sr0.5CoO3 (LSCO) bottom electrodes by using the polymeric precursor method and microwave furnace. The bottom electrode is found to be an important parameter which affects the crystallization, morphology and leakage current behaviors. The XRD results clearly show that film deposited on LSCO electrode favours the growth of (117) oriented grains whereas in films deposited on LNO and RuO2 the growth of (001) oriented grains dominated. The film deposited on LSCO has a plate-like grain structure, and its leakage current behavior is in agreement with the prediction of the space-charge-limited conduction model. on the other hand, the films deposited on RuO2 and LNO electrodes present a rounded grain shape with some porosity, and its high field conduction is well explained by the Schottky and Poole-Frenkel emission models. The remanent polarization (P-r) and the drive voltage (V-c) were in the range of 11-23 mu C cm(-2) and 0.86-1.56 V, respectively, and are better than the values found in the literature. (c) 2007 Published by Elsevier B.V.

Thickness dependence of leakage current in BaBi2Ta2O9 thin films

BaBi2Ta2O9 thin films having a layered structure were fabricated by metalorganic solution deposition technique. The films exhibited good structural, dielectric, and insulating properties. The room temperature resistivity was found to be in the range of 10(12)-10(14) Omega cm up to 4 V corresponding to a field of 200 kV/cm across the capacitor for films annealed in the temperature range of 500-700 degrees C. The current-voltage (I-V) characteristics as a function of thickness for films annealed at 700 degrees C for 1 h, indicated bulk limited conduction and the log(I) vs V-1/2 characteristics suggested a space-charge-limited conduction mechanism. The capacitance-voltage measurements on films in a metal-insulator-semiconductor configuration indicated good Si/BaBi2Ta2O9 interface characteristics and a SiO2 thickness of similar to 5 nm was measured and calculated. (C) 1999 American Institute of Physics. [S0003-6951(99)00830-X].

Ferroelectric properties and leakage current characteristics of Bi3.25La0.75Ti3O12 thin films prepared by the polymeric precursor method

The ferroelectric properties and leakage current mechanisms of preferred oriented Bi3.25La0.75Ti3O12 (BLT) thin films deposited on La0.5Sr0.5CoO3 by the polymeric precursor method were investigated. These films showed excellent ferroelectric properties in terms of large remnant polarization (2P(r)) of 47.6 mu C/cm(2) and (2E(c)) of 55 kV/cm, fatigue-free characteristics up to 10(10) switching cycles, and a current density of 0.7 mu A/cm(2) at 10 kV/cm. X-ray diffraction and scanning electron microscope investigations indicate that the deposited films exhibit a dense, well-crystallized microstructure having random orientations and with a rather smooth surface morphology. The improved ferroelectric and leakage current characteristics can be ascribed to the platelike grains of the BLT films, which make the domain walls easier to be switched under external field.

Leakage current, ferroelectric and structural properties in Pb(1-x)Ba(x)TiO(3) thin films prepared by chemical route

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structure, ferroelectric/magnetoelectric properties and leakage current density of (Bi0.85Nd0.15)FeO3 thin films

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Comparative degradation of ZnO- and SnO(2)-based polycrystalline non-ohmic devices by current pulse stress

The degradation behaviour of SnO(2)-based varistors (SCNCr) due to current pulses (8/20 mu s) is reported here for the first time in comparison with the ZnO-based commercial varistors (ZnO). Puncturing and/or cracking failures were observed in ZnO-based varistors possessing inferior thermo-mechanical properties in comparison with that found in a SCNCr system free of failures. Both systems presented electric degradation related to the increase in the leakage current and decrease in the electric breakdown field, non-linear coefficient and average value of the potential barrier height. However, it was found that a more severe degradation occurred in the ZnO-based varistors concerning their non-ohmic behaviour, while in the SCNCr system, a strong non-ohmic behaviour remained after the degradation. These results indicate that the degradation in the metal oxide varistors is controlled by a defect diffusion process whose rate depends on the mobility, the concentration of meta-stable defects and the amount of electrically active interfaces. The improved behaviour of the SCNCr system is then inferred to be associated with the higher amount of electrically active interfaces (85%) and to a higher energy necessary to activate the diffusion of the specific defects.

Conventional and microwave sintering of CaCu(3)Ti(4)O(12)/CaTiO(3) ceramic composites: non-ohmic and dielectric properties

The non-ohmic and dielectric properties as well as the dependence on the microstructural features of CaCu(3)Ti(4)O(12)/CaTiO(3) ceramic composites obtained by conventional and microwave sintering were investigated. It was demonstrated that the non-ohmic and dielectric properties depend strongly on the sintering conditions. It was found that the non-linear coefficient reaches values of 65 for microwave-sintered samples and 42 for samples sintered in a conventional furnace when a current density interval of 1-10 mA cm(-2) is considered. The non-linear coefficient value of 65 is equivalent to 1500 for samples sintered in the microwave if a current interval of 5-30 mA is considered as is shortly discussed by Chung et al (2004 Nature Mater. 3 774). Due to a high non-linear coefficient and a low leakage current (90 mu A) under both processing conditions, these samples are promising for varistor applications. The conventionally sintered samples exhibit a higher relative dielectric constant at 1 kHz (2960) compared with the samples sintered in the microwave furnace (2100). At high frequencies, the dielectric constant is also larger in the samples sintered in the conventional furnace. Depending on the application, one or another synthesis methodology is recommended, that is, for varistor applications sintered in a microwave furnace and for dielectric application sintered in a conventional furnace.

Comparison of non-Ohmic accelerated ageing of the ZnO- and SnO2-based voltage dependent resistors

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Enhanced ferroelectric properties of La-substituted BiFeO3 thin films on LaSrCoO3/Pt/TiO2/SiO2/Si (100) substrates prepared by the soft chemical method

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Dielectric properties of Ca(Zr0.05Ti0.95)O-3 thin films prepared by chemical solution deposition

Ca(Zr0.05Ti0.95)O-3 (CZT) thin films were grown on Pt(1 1 1)/Ti/SiO2/Si(1 0 0) substrates by the soft chemical method. The films were deposited from spin-coating technique and annealed at 928 K for 4 h under oxygen atmosphere. CZT films present orthorhombic structure with a crack free and granular microstructure. Atomic force microscopy and field-emission scanning electron microscopy showed that CZT present grains with about 47 nm and thickness about 450 nm. Dielectric constant and dielectric loss of the films was approximately 210 at 100 kHz and 0.032 at 1 MHz. The Au/CZT/Pt capacitor shows a hysteresis loop with remnant polarization of 2.5 mu C/cm(2), and coercive field of 18 kV/cm, at an applied voltage of 6 V. The leakage current density was about 4.6 x 10(-8) A/cm(2) at 3 V. Dielectric constant-voltage curve is located at zero bias field suggesting the absence of internal electric fields. (c) 2006 Elsevier B.V. All rights reserved.

Ferroelectric and dielectric properties of Ba0.5Sr0.5(Ti0.80Sn0.20)O-3 thin films grown by the soft chemical method

Polycrystalline Ba0.5Sr0.5(Ti0.80Sn0.20)O-3 (BST:Sn) thin films with a perovskite structure were prepared by the soft chemical method on a platinum-coated silicon substrate from spin-coating technique. The resulting thin films showed a dense structure with uniform grain size distribution. The dielectric constant of the films estimated from C-V curve is around 1134 and can be ascribed to a reduction in the oxygen vacancy concentration. The ferroelectric nature of the film indicated by butterfly-shaped C-V curves and confirmed by the hysteresis curve, showed remnant polarization of 14 mu C/cm(2) and coercive field of 74 kV/cm at frequency of 1 MHz. At the same frequency, the leakage current density at 1.0 V is equal to 1.5 x 10(-7) A/cm(2). This work clearly reveals the highly promising potential of BST:Sn for application in memory devices. (c) 2006 Elsevier B.V. All rights reserved.

Characterization of lanthanum-doped bismuth titanate thin films prepared by polymeric precursor method

Lanthanum-modified bismuth titanate, Bi4-xLaxTi3O12 (BLT), with x ranging from 0 to 0.75 was grown on Pt/Ti/SiO2/Si substrates using a polymeric precursor solution and spin-coating method. The dielectric constant of highly doped bismuth titanate was equal to 148 while dielectric losses remained low (tan delta = 0.0018), and the films showed well-saturated polarization-electric field curves (2P(r) = 40.6 muC/cm(2) and V-c = 0.99 V). The leakage current densities improve for the lanthanum-doped system. For five-layered BLT films with x = 0.75, a charge storage density of 35 fC/mum(2) and a thickness of 320 nm were found. (C) 2004 Elsevier B.V. All rights reserved.

Effect of annealing atmosphere on phase formation and electrical characteristics of bismuth ferrite thin films

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Size effects of polycrystalline lanthanum modified Bi4Ti3O12 thin films

The film thickness dependence on the ferroelectric properties of lanthanum modified bismuth titanate Bi3.25La0.75Ti3O12 was investigated. Films with thicknesses ranging from 230 to 404 nut were grown on platinum-coated silicon substrates by the polymeric precursor method. The internal strain is strongly influenced by the film thickness. The morphology of the film changes as the number of layers increases indicating a thickness dependent grain size. The leakage current, remanent polarization and drive voltage were also affected by the film thickness. (c) 2007 Elsevier Ltd. All rights reserved.

Rietveld analysys and electrical properties of lanthanum doped BiFeO3 ceramics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)