Dielectric properties of Na1-xLixNbO3 ceramics from powders obtained by chemical synthesis

Ultra-fine powders of Na1-xLixNbO3 (x=0; 0.06; 0.09; 0.12) were synthesized by the Polymeric Precursors Method. Such powders had their orthorhombic structures determined by X-ray diffraction and their surface area determined by BET isotherms (less than 10 m(2) g(-1)). Densification was followed by dilatometric study. The powders, calcined at 700 degrees C for 5 h, were sintered at 1290 degrees C during 2 h under ambient atmosphere with no application of extra pressure. The samples with relative densities higher than 95% were analyzed by impedance spectroscopy at room temperature, under a signal amplitude of 1 V-rms. Dielectric constants of about 180 and dielectric loss factor of about 0.03 were measured showing small dependence with frequency. The electrical properties were similar to those obtained for samples sintered by hot pressing. (C) 1999 Elsevier B.V. Limited and Techna S.r.l. All rights reserved.

Role of oxygen vacancies in the magnetic and dielectric properties of the high-dielectric-constant system CaCu3Ti4O12: An electron-spin resonance study

We report experiments of electron spin resonance (ESR) of Cu2+ in polycrystalline samples of CaCu3Ti4O12 post-annealed in different atmospheres. After being synthesized by solid state reaction, pellets of CaCu3Ti4O12 were annealed for 24 h at 1000 degrees C under air, Ar or O-2. Our temperature dependent ESR data revealed for all samples nearly temperature independent g value (2.15(1)) and linewidth for T > T-N approximate to 25 K. However, the values of ESR linewidth are strongly affected by the oxygen content in the sample. For instance, argon post-annealed samples show a much larger linewidth than the O-2 or air post-annealed samples. We attribute this broadening to an increase of the dipolar homogeneous broadening of the Cu2+ ESR lines due to the presence of oxygen vacancies which induce an S=1/2 spin inside the TiO6 octahedra. Correlation between a systematic dependence of the ESR linewidth on the oxygen content and the high dielectric constant of these materials is addressed. Also, ESR, magnetic susceptibility, and specific heat data for a single crystal of CaCu3Ti4O12 and for polycrystals of CdCu3Ti4O12 are reported.

Effects of post-annealing on the dielectric properties of Au/BaTiO3/Pt thin film capacitors

Barium titanate thin films were prepared by the polymeric precursor method and deposited onto Pt/Ti/SiO2/Si substrates. X-ray diffraction (XRD), scanning electron microscopy (SEM) and atomic force microscopy (AFM), Fourier transform infrared spectroscopy (FT-IR) and micro-Raman spectroscopy were used to investigate the formation of the BaTiO3 perovskite phase. Afterwards, the films were submitted to post-annealing treatments in oxygen and nitrogen atmospheres at 300 degreesC for 2 h, and had their dielectric properties measured. It was observed that the electric properties of the thin films are very sensitive to the nature of the post-annealing atmosphere. This study demonstrates that post-annealing in an oxygen atmosphere increases the dielectric relaxation phenomenon and that post-annealing in a nitrogen atmosphere produces a slight dielectric relaxation. (C) 2004 Elsevier B.V All rights reserved.

Non-Ohmic and dielectric properties of a Ca2Cu2Ti4O12 polycrystalline system

An investigation was made into the non-Ohmic and dielectric properties of a Ca2Cu2Ti4O12 perovskite-type system. Compared to the traditional CaCu3Ti4O12-based composition, the imbalance between the Ca and Cu atoms caused the formation of a polycrystalline system presenting similar to 33.3 mol % of CaCu3Ti4O12 (traditional composition) and similar to 66.7 mol % of CaTiO3. As for non-Ohmic properties, the effect of this Ca and Cu atom imbalance was that a nonlinear electric behavior of similar to 1500 was obtained. This high nonlinear electrical behavior emerged in detriment to the ultrahigh dielectric property frequently reported. The high non-Ohmic property was explained by the existence of Schottky-type barriers, whose formation mechanism may be similar to that proposed for traditional metal oxide non-Ohmic devices, according to similarities discussed herein. (c) 2006 American Institute of Physics.

Non-Linear Dielectric Properties of PLMN-PT Relaxor Ferroelectrics

Recent investigations on the non-linear (NL) dielectric properties of relaxor ferroelectrics systems, not only as ceramic bodies, but also, in thin films, have showed a significant technological and scientific interest. The most common practical applications of relaxors include multilayer capacitors and actuators. In this work, non-linear dielectric properties of hot-pressed (1-x)[Pb1 -(3/2) yLayMg1/3Nb2/3O3]-xPbTiO3 (PLMN-PT) ferroelectric ceramics were investigated. The NL properties were obtained by using the measurements of the dielectric permittivity of the material as a function of the AC electric field with variable amplitude in the frequency and temperature range of 100 Hz-1 MHz and 50-450 K, respectively. An anomalous behavior of the non-linear dielectric response was observed when submitted to high electric fields levels. The obtained results were analyzed concerning one of the models for the dielectric response of relaxors ferroelectrics materials currently discussed in the literature.

Structure, microstructure and dielectric properties of 100-x(Bi0.5Na0.5)TiO3-x[SrTiO3] composites ceramics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structural refinement, optical and microwave dielectric properties of BaZrO3

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structural and dielectric properties of Ba0.5Sr0.5(SnxTi1-x)O-3 ceramics obtained by the soft chemical method

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Dielectric properties of pure and lanthanum modified bismuth titanate thin films

We investigated the dielectric properties of pure and lanthanum modified bismuth titanate thin films obtained by the polymeric precursor method. X-ray diffraction of the film annealed at 300 degrees C for 2h indicates a disordered structure. Lanthanum addition increases gradually the dielectric permittivity of films, keeping unchanged their loss tangent. From C-V curve we can see no hysteresis behavior indicating the absence of domain structure. The decrease in the conductivity for the heavily doped Bi4Ti3O12 (BIT) must be associated to the unidentified crystal defects. For comparison, dielectric properties of crystalline BIT film were also investigated. (C) 2007 Published by Elsevier B.V.

Dielectric properties of soft chemical method derived CaCu3Ti4O12 thin films onto Pt/TiO2/Si(100) substrates

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Dielectric properties of Pb Nb2 O6 ferroelectric ceramics at cryogenic temperatures

Complex dielectric permittivity measurements in Pb Nb2 O6 ceramics were performed in a frequency and temperature range of 1 kHz-1 MHz and from 15 to 900 K, respectively. The results revealed two dielectric anomalies showing typical characteristics of relaxor ferroelectric materials at cryogenic temperatures. Comparison with other tetragonal tungsten bronze (TTB) structure-type materials suggests the existence of successive phase transitions, which until now were not reported. The observed low temperature dielectric behaviors seem to be due to intrinsic physical characteristics related to the TTB structure. © 2007 American Institute of Physics.

Structural and dielectric properties of relaxor Sr0.5Ba 0.5Bi2Nb2O9 ceramic

Sr0.5Ba0.5Bi2Nb2O 9 ceramic was prepared by a conventional solid state reaction method and studied using X-ray powder diffraction and dielectric measurements. At room temperature, an orthorhombic structure was confirmed and their parameters were obtained using the Rietveld method. Dielectric properties were studied in a broad range of temperatures and frequencies. Typical relaxor behaviour was observed with strong dispersion of the complex relative dielectric permittivity. The temperature of the maximum dielectric constant Tm decreases with increasing frequency, and shifts towards higher temperature side. The activation energy Ea≈0·194±0·03 eV and freezing temperature Ta≈371±2 K values were found using the Vogel-Fulcher relationship. Conduction process in the material may be due to the hopping of charge carriers at low temperatures and small polarons and/or singly ionised oxygen vacancies at higher temperatures. © 2010 Maney Publishing.

Sintering temperature influence on microwave dielectric properties of TiO2-ZrO2 ceramics

Dielectric ceramics have been widely investigated and used for microwave applications such as resonators and filters. The present study deals with the influence of sintering temperature on microwave dielectric properties of TiO2 ceramics with 10, 20, and 30 wt% ZrO2. Three compositions have been developed through mixing procedures and then tested for each sintering temperature: 1500 and 1400°C. X-ray diffraction and scanning electron microscopy are carried out aiming to explain the ceramic behavior of each sample. The dielectric constants of different ceramics for both temperatures varied from 85.4 to 62.6, while their quality factor due to dielectric losses varied from 3110 to 1630. The Q decrease is attributed to the non uniform grain growth and to the obtained crystalline phases. The best microwave parameters were obtained for the ceramics sintered at 1400°C, which can be applied in microwave circuits as dielectric resonators. © (2010) Trans Tech Publications.

Structural and dielectric properties of polyvinyl alcohol/barium zirconium titanate polymer-ceramic composite

The polyvinyl alcohol (PVA)/barium zirconium titanate Ba[Zr0.1Ti0.9]O3 (BZT) polymer-ceramic composites with different volume percentage are obtained from solution mixing and hot-pressing method. Their structural and electrical properties are characterized by X-ray diffraction (XRD), Rietveld refinement, cluster modeling, scanning electron microscope and dielectric study. XRD patterns of PVA/BZT polymer-ceramics composite (with 50% volume fractions) indicate no obvious differences than the XRD patterns of pure BZT which shows that the crystal structure is still stable in the composite. The scanning electron micrograph indicates that the BZT ceramic is dispersed homogeneously in the polymer matrix without agglomeration. The dielectric permittivity (ε r) and the dielectric loss (tan δ) of the composites increase with the increase of the volume fraction of BZT ceramic. Theoretical models are employed to rationalize the dielectric behavior of the polymer composites. The dielectric properties of the composites display good stability within a wide range of temperature and frequency. The excellent dielectric properties of these polymer-ceramic composites indicate that the BZT/PVA composites can be a candidate for embedded capacitors. © 2013 Elsevier B.V.

Influence of Sm3+ doping on the dielectric properties of CaCu3Ti4O12 ceramics synthesized via autocombustion

Ca-1 -xSmxCu3Ti4O12 (x = 0.0, 0.2, 03) electronic ceramics were fabricated via the chemical route using metal nitrate solutions in order to improve the dielectric properties of this ceramic. X-ray diffraction (XRD) analysis indicated the formation of a single CaCu3Ti4O12 (CCTO). Grain size of the samples doped with Sm3+ was in the range of 1-2 mu m, as opposed to 50-100 mu m in the pure samples of CCTO. The cutoff frequency with the doping was remarkably shifted, from 1 MHz (pure CCTO) to 10 MHz (doped CCTO). Meanwhile, the real dielectric (epsilon(r)) and imaginary dielectric (epsilon '') constants showed a decrease as the doping was increased. (C) 2013 Elsevier B.V. All rights reserved.