Reliability and Failure Modes of Implant-Supported Y-TZP and MCR Three-Unit Bridges

Purpose: Chipping within veneering porcelain has resulted in high clinical failure rates for implant-supported zirconia (yttria-tetragonal zirconia polycrystals [Y-TZP]) bridges. This study evaluated the reliability and failure modes of mouth-motion step-stress fatigued implant-supported Y-TZP versus palladium-silver alloy (PdAg) three-unit bridges. Materials and Methods: Implant-abutment replicas were embedded in polymethylmethacrylate resin. Y-TZP and PdAg frameworks, of similar design (n = 21 each), were fabricated, veneered, cemented (n = 3 each), and Hertzian contact-tested to obtain ultimate failure load. In each framework group, 18 specimens were distributed across three step-stress profiles and mouth-motion cyclically loaded according to the profile on the lingual slope of the buccal cusp of the pontic. Results: PdAg failures included competing flexural cracking at abutment and/or connector area and chipping, whereas Y-TZP presented predominantly cohesive failure within veneering porcelain. Including all failure modes, the reliability (two-sided at 90% confidence intervals) for a ""mission"" of 50,000 and 100,000 cycles at 300 N load was determined (Alta Pro, Reliasoft, Tucson, AZ, USA). No difference in reliability was observed between groups for a mission of 50,000. Reliability remained unchanged for a mission of 100,000 for PdAg, but significantly decreased for Y-TZP. Conclusions: Higher reliability was found for PdAg for a mission of 100,000 cycles at 300 N. Failure modes differed between materials.

Progressive recovery of osseoperception as a function of the combination of implant-supported prostheses

The extraction of teeth involves the elimination of extremely sensitive periodontal mechanoreceptors, which play an important role in oral sensory perception. Objectives: The aim of this study was to evaluate the recovery of interocclusal sensory perception for micro-thickness in individuals with different types of implant-supported prostheses. Materials and Methods: Wearers of complete dentures (CDs) comprised the negative control group (group A, n=17). The experimental group consisted of wearers of prostheses supported by osseointegrated implants (Group B, n=29), which was subsequently divided into 4 subgroups: B(1) (n=5) - implant supported overdentures (ISO) occluding with CD; B(2) (n=6) - implant-supported fixed prostheses (ISFP) occluding with CD; B3 (n=8) - wearers of maxillary and mandibular ISFP, and B(4) (n=10) - ISFP occluding with natural dentition (ND). Individuals with ND represented the positive control group (Group C, n=24). Aluminum foils measuring 10 mu m, 24 mu m, 30 mu m, 50 mu m, 80 mu m, and 104 mu m thickness were placed within the premolar area, adding up to 120 tests for each individual. Results: The mean tactile thresholds of groups A, B(1), B(2), B(3), B(4), and C were 92 mu m, 27 mu m, 27 mu m, 14 mu m, 10 mu m, and 10 mu m, respectively. [Correction added after publication online 18 April 2008: in the preceding sentence 92 mu m, 27 mu m, 14 mu m, 10 mu m and 10 mu m, was corrected to 92 mu m, 27 mu m, 27 mu m, 14 mu m, 10 mu m and 10 mu m.] The Kruskal-Wallis test revealed significant difference among groups (P < 0.05). The Dunn test revealed that group A was statistically different from groups C, B(3), and B(4), and that B(1) and B(2) were statistically different from group C. Conclusion: Progressive recovery of osseoperception as a function of the combination of implant-supported prostheses could be observed. Moreover, ISO and/or ISFP combinations may similarly maximize the recovery of osseoperception.

Fatigue life and failure modes of crowns systems with a modified framework design

Objectives: To evaluate the effect of framework design on the fatigue life and failure modes of metal ceramic (MC, Ni-Cr alloy core, VMK 95 porcelain veneer), glass-infiltrated alumina (ICA, In-Ceram Alumina/VM7), and veneered yttria-stabilized tetragonal zirconia polycrystals (Y-TZP, IPSe.max ZirCAD/IPS e.max,) crowns. Methods: Sixty composite resin tooth replicas of a prepared maxillary first molar were produced to receive crowns systems of a standard (MCs, ICAs, and Y-TZPs, n = 10 each) or a modified framework design (MCm, ICAm, and Y-TZPm, n = 10 each). Fatigue loading was delivered with a spherical steel indenter (3.18 mm radius) on the center of the occlusal surface using r-ratio fatigue (30-300 N) until completion of 10(6) cycles or failure. Fatigue was interrupted every 125,000 cycles for damage evaluation. Weibull distribution fits and contour plots were used for examining differences between groups. Failure mode was evaluated by light polarized and SEM microscopy. Results: Weibull analysis showed the highest fatigue life for MC crowns regardless of framework design. No significant difference (confidence bound overlaps) was observed between ICA and Y-TZP with or without framework design modification. Y-TZPm crowns presented fatigue life in the range of MC crowns. No porcelain veneer fracture was observed in the MC groups, whereas ICAs presented bulk fracture and ICAm failed mainly through the veneer. Y-TZP crowns failed through chipping within the veneer, without core fractures. Conclusions: Framework design modification did not improve the fatigue life of the crown systems investigated. Y-TZPm crowns showed comparable fatigue life to MC groups. Failure mode varied according to crown system. (C) 2010 Elsevier Ltd. All rights reserved.

Image quality assessment and medical physics evaluation of different portable dental X-ray units

Introduction: Recently developed portable dental X-ray units increase the mobility of the forensic odontologists and allow more efficient X-ray work in a disaster field, especially when used in combination with digital sensors. This type of machines might also have potential for application in remote areas, military and humanitarian missions, dental care of patients with mobility limitation, as well as imaging in operating rooms. Objective: To evaluate radiographic image quality acquired by three portable X-ray devices in combination with four image receptors and to evaluate their medical physics parameters. Materials and methods: Images of five samples consisting of four teeth and one formalin-fixed mandible were acquired by one conventional wall-mounted X-ray unit, MinRay (R) 60/70 kVp, used as a clinical standard, and three portable dental X-ray devices: AnyRay (R) 60 kVp, Nomad (R) 60 kVp and Rextar (R) 70 kVp, in combination with a phosphor image plate (PSP), a CCD, or a CMOS sensor. Three observers evaluated images for standard image quality besides forensic diagnostic quality on a 4-point rating scale. Furthermore, all machines underwent tests for occupational as well as patient dosimetry. Results: Statistical analysis showed good quality imaging for all system, with the combination of Nomad (R) and PSP yielding the best score. A significant difference in image quality between the combination of the four X-ray devices and four sensors was established (p < 0.05). For patient safety, the exposure rate was determined and exit dose rates for MinRay (R) at 60 kVp, MinRay (R) at 70 kVp, AnyRay (R), Nomad (R) and Rextar (R) were 3.4 mGy/s, 4.5 mGy/s, 13.5 mGy/s, 3.8 mGy/s and 2.6 mGy/s respectively. The kVp of the AnyRay (R) system was the most stable, with a ripple of 3.7%. Short-term variations in the tube output of all the devices were less than 10%. AnyRay (R) presented higher estimated effective dose than other machines. Occupational dosimetry showed doses at the operator`s hand being lowest with protective shielding (Nomad (R): 0.1 mu Gy). It was also low while using remote control (distance > 1 m: Rextar (R) < 0.2 mu Gy, MinRay (R) < 0.1 mu Gy). Conclusions: The present study demonstrated the feasibility of three portable X-ray systems to be used for specific indications, based on acceptable image quality and sufficient accuracy of the machines and following the standard guidelines for radiation hygiene. (C) 2010 Elsevier Ireland Ltd. All rights reserved.

Failure modes of Y-TZP crowns at different cusp inclines

Objectives To compare the reliability of the disto-facial (DF) and mesio-lingual (ML) cusps of an anatomically correct zirconia (Y-TZP) crown system The research hypotheses tested were (1) fatigue reliability and failure mode are similar for the ML and DF cusps, (2) failure mode of one cusp does not affect the failure of the other Methods The average dimensions of a mandibular first molar crown were imported into CAD software, a tooth preparation was modelled by 1 5 mm marginal high reduction of proximal walls and occlusal surface by 2 0 mm The CAD-based tooth preparation was milled and used as a die to fabricate crowns (n = 14) with porcelain veneer on a 0 5 mm Y-TZP core. Crowns were cemented on composite reproductions of the tooth preparation The crowns were step-stress mouth motion fatigued with sliding (0 7 mm) a tungsten-carbide indenter of 6 25 mm diameter down on the inclines of either the DF or ML cusps Use level probability Weibull curve with use stress of 200 N and the reliability for completion of a mission of 50,000 cycles at 200 N load were calculated Results Reliability for a 200 N at 50,000 cycles mission was not different between tested cusps SEM imaging showed large cohesive failures within the veneer for the ML and smaller for the DF Fractures originated from the contact area regardless of the cusp loaded Conclusion No significant difference on fatigue reliability was observed between the DF compared to the ML cusp Fracture of one cusp did not affect the other (c) 2010 Elsevier Ltd All rights reserved

Monolithic CAD/CAM Lithium Disilicate Versus Veneered Y-TZP Crowns: Comparison of Failure Modes and Reliability After Fatigue

Purpose: The aim of this research was to evaluate the fatigue behavior and reliability of monolithic computer-aided design/computer-assisted manufacture (CAD/CAM) lithium disilicate and hand-layer-veneered zirconia all-ceramic crowns. Materials and Methods: A CAD-based mandibular molar crown preparation, fabricated using rapid prototyping, served as the master die. Fully anatomically shaped monolithic lithium disilicate crowns (IPS e.max CAD, n = 19) and hand-layer-veneered zirconia-based crowns (IPS e.max ZirCAD/Ceram, n = 21) were designed and milled using a CAD/CAM system. Crowns were cemented on aged dentinlike composite dies with resin cement. Crowns were exposed to mouth-motion fatigue by sliding a WC-indenter (r = 3.18 mm) 0.7 mm lingually down the distobuccal cusp using three different step-stress profiles until failure occurred. Failure was designated as a large chip or fracture through the crown. If no failures occurred at high loads (> 900 N), the test method was changed to staircase r ratio fatigue. Stress level probability curves and reliability were calculated. Results: Hand-layer-veneered zirconia crowns revealed veneer chipping and had a reliability of < 0.01 (0.03 to 0.00, two-sided 90% confidence bounds) for a mission of 100,000 cycles and a 200-N load. None of the fully anatomically shaped CAD/CAM-fabricated monolithic lithium disilicate crowns failed during step-stress mouth-motion fatigue (180,000 cycles, 900 N). CAD/CAM lithium disilicate crowns also survived r ratio fatigue (1,000,000 cycles, 100 to 1,000 N). There appears to be a threshold for damage/bulk fracture for the lithium disilicate ceramic in the range of 1,100 to 1,200 N. Conclusion: Based on present fatigue findings, the application of CAD/CAM lithium disilicate ceramic in a monolithic/fully anatomical configuration resulted in fatigue-resistant crowns, whereas hand-layer-veneered zirconia crowns revealed a high susceptibility to mouth-motion cyclic loading with early veneer failures. Int J Prosthodont 2010; 23: 434-442.

Fatigue and damage accumulation of veneer porcelain pressed on Y-TZP

Objectives: This study compared the reliability and fracture patterns of zirconia cores veneered with pressable porcelain submitted to either axial or off-axis sliding contact fatigue. Methods: Forty-two Y-TZP plates (12 mm x 12 mm x 0.5 mm) veneered with pressable porcelain (12 mm x 12 mm x 1.2 mm) and adhesively luted to water aged composite resin blocks (12 mm x 12 mm x 4 mm) were stored in water at least 7 days prior to testing. Profiles for step-stress fatigue (ratio 3:2:1) were determined from single load to fracture tests (n = 3). Fatigue loading was delivered on specimen either on axial (n = 18) or off-axis 30 degrees angulation (n = 18) to simulate posterior tooth cusp inclination creating a 0.7 mm slide. Single load and fatigue tests utilized a 6.25 mm diameter WC indenter. Specimens were inspected by means of polarized-light microscope and SEM. Use level probability Weibull curves were plotted with 2-sided 90% confidence bounds (CB) and reliability for missions of 50,000 cycles at 200 N (90% CB) were calculated. Results: The calculated Weibull Beta was 3.34 and 2.47 for axial and off-axis groups, respectively, indicating that fatigue accelerated failure in both loading modes. The reliability data for a mission of 50,000 cycles at 200 N load with 90% CB indicates no difference between loading groups. Deep penetrating cone cracks reaching the core-veneer interface were observed in both groups. Partial cones due to the sliding component were observed along with the cone cracking for the off-axis group. No Y-TZP core fractures were observed. Conclusions: Reliability was not significantly different between axial and off-axis mouth-motion fatigued pressed over Y-TZP cores, but incorporation of sliding resulted in more aggressive damage on the veneer. (C) 2009 Elsevier Ltd. All rights reserved.

Cleft Palate Obturation With Branemark Protocol Implant-Supported Fixed Denture and Removable Obturator

A 41-year-old man with cleft palate presented with a wide dehiscence and missing teeth. Six implants had been placed for fabrication of an overdenture, which was unsatisfactory. A bar was waxed and cast for connection to the implants; precision attachments were placed laterally for retention. A fixed partial denture was fabricated, and milled crowns were fabricated at the molar region to provide a guiding plane for insertion of a removable palatal obturator. Good swallowing and speech outcomes were achieved. This technique provided functional and esthetic benefits, enhanced oral hygiene, and improved the psychological condition of the patient.

Finite Element Analysis of 2 Immediate Loading Systems in Edentulous Mandible: Rigid and Semirigid Splinting of Implants

Purpose: The objective of this study was to evaluate the stress on the cortical bone around single body dental implants supporting mandibular complete fixed denture with rigid (Neopronto System-Neodent) or semirigid splinting system (Barra Distal System-Neodent). Methods and Materials: Stress levels on several system components were analyzed through finite element analysis. Focusing on stress concentration at cortical bone around single body dental implants supporting mandibular complete fixed dentures with rigid ( Neopronto System-Neodent) or semirigid splinting system ( Barra Distal System-Neodent), after axial and oblique occlusal loading simulation, applied in the last cantilever element. Results: The results showed that semirigid implant splinting generated lower von Mises stress in the cortical bone under axial loading. Rigid implant splinting generated higher von Mises stress in the cortical bone under oblique loading. Conclusion: It was concluded that the use of a semirigid system for rehabilitation of edentulous mandibles by means of immediate implant-supported fixed complete denture is recommended, because it reduces stress concentration in the cortical bone. As a consequence, bone level is better preserved, and implant survival is improved. Nevertheless, for both situations the cortical bone integrity was protected, because the maximum stress level findings were lower than those pointed in the literature as being harmful. The maximum stress limit for cortical bone (167 MPa) represents the threshold between plastic and elastic state for a given material. Because any force is applied to an object, and there is no deformation, we can conclude that the elastic threshold was not surpassed, keeping its structural integrity. If the force is higher than the plastic threshold, the object will suffer permanent deformation. In cortical bone, this represents the beginning of bone resorption and/or remodeling processes, which, according to our simulated loading, would not occur. ( Implant Dent 2010; 19:39-49)

Cephalometric evaluation of Class II malocclusion treatment with cervical headgear and mandibular fixed appliances

The present study aimed to evaluate the cephalometric changes in Class II patients treated exclusively with cervical headgear (CHG) in the maxillary arch and fixed appliances in the mandibular arch as compared with a control group. The sample comprised 82 lateral cephalograms obtained pre- (T1) and post- (T2) treatment/observation of 41 subjects, divided into two groups: group 1-25 Class II division 1 patients (20 females and five males), with a mean pre-treatment age of 10.4 years, treated for a mean period of 2.5 years and group 2-16 Class II untreated subjects (12 females and four males), with a mean initial age of 9.9 years, followed for a mean period of 2.2 years. Treatment changes between the groups were compared by means of t-tests. The results showed restriction of maxillary forward displacement and also a restriction in maxillary length growth, improvement in the maxillomandibular relationship, restriction of mandibular incisor vertical development, reduction in overjet and overbite, and improvement in molar relationship. It was concluded that this treatment protocol corrected the Class II malocclusion characteristics primarily through maxillary forward growth restriction.

Influence of endodontic sealers on the bond strength of carbon fiber posts

Objective: The aim of this study was to verify the influence of endodontic sealers on the bond strength of an adhesive system and a resin cement used for carbon posts cementation. Methods: Thirty extracted human premolars were instrumented and randomly divided into three groups according to the tested sealer: EndoFill, Sealapex, or EndoREZ. Specimens were stored at 37 degrees C. After 48 h, half of specimens were prepared to receive the post and the others after 7 days. The posts were cemented with Adper Single Bond/Rely X ARC and stored in distilled water at 37 degrees C for 7 days. After this period, the specimens were sectioned in three slices (coronal, middle, and apical). The push-out test was performed in a universal machine and the debonded area was examined in a stereomicroscope. Results: Data were submitted ANOVA and Tukey test (alpha = 0.05). The EndoFill showed lower bond strength than other sealers (p < 0.01). The EndoREZ sealer was statistically greater than other groups for coronal and middle portions and similar for apical portion (P > 0.05). Coronal and middle portions showed the best results for all groups, mainly when the canal preparation was performed after 48 h (p < 0.01). Mixed failure occurs with more frequency (55.6%) followed by failure in adhesive-dentin interface (34.4%) and adhesive-post interface (10.0%). Conclusion: The use of EndoREZ sealer promoted higher bond strength in root coronal and middle portions when carbon post was fixed with a resin cement. (C) 2007 Wiley Periodicals, Inc.

Photoelastic Stress Analysis of Different Designs of Cement-Retained Fixed Partial Dentures on Morse Taper Oral Implants

There is no consensus in literature regarding the best plan for prosthetic rehabilitation with partial multiple adjacent implants to minimize stress generated in the bone-implant interface. The aim of this study was to evaluate the biomechanical behavior of cemented fixed partial dentures, splinted and nonsplinted, on Morse taper implants and with different types of coating material (ceramic and resin), using photoelastic stress analysis. A photoelastic model of an interposed edentulous space, missing a second premolar and a first molar, and rehabilitated with 4 different types of cemented crowns and supported by 2 adjacent implants was used. Groups were as follows: UC, splinted ceramic crowns; IC, nonsplinted ceramic crowns; UR, splinted resin crowns; and IR, nonsplinted resin crowns. Different vertical static loading conditions were performed: balanced occlusal load, 10 kgf; simultaneous punctiform load on the implanted premolar and molar, 10 kgf; and alternate punctiform load on the implanted premolar and molar, 5 kgf. Changes in stress distribution were analyzed in a polariscope, and digital photographs were taken of each condition to allow comparison of stress pattern distribution around the implants. Cementation of the fixed partial dentures generated stresses between implants. Splinted restorations distributed the stresses more evenly between the implants than nonsplinted when force was applied. Ceramic restorations presented better distribution of stresses than resin restorations. Based on the results obtained, it was concluded that splinted ceramic restorations promote better stress distribution around osseointegrated implants when compared with nonsplinted crowns; metal-ceramic restorations present less stress concentration and magnitude than metal-plastic restorations.

An in vitro study of non-axial forces upon the retention of an O-ring attachment

Objective The purpose of this study was to evaluate the retention force of an O-ring attachment system in different inclinations to the ideal path of insertion, using devices to compensate angulations. Material and methods Two implants were inserted into an aluminum base, and ball attachments were screwed to implants. Cylinders with O-rings were placed on ball attachments and connected to the test device using positioners to compensate implant angulations (0 degrees, 7 degrees, and 14 degrees). Plexiglass bases were used to simulate implant angulations. The base and the test device were positioned in a testing apparatus, which simulated insertion/removal of an overdenture. A total of 2900 cycles, simulating 2 years of overdenture use, were performed and 36 O-rings were tested. The force required for each cycle was recorded with computer software. Longitudinal sections of ball attachment-positioner-cylinder with O-rings of each angulation were obtained to analyze the relationship among them, and O-ring sections tested in each angulation were compared with an unused counterpart. A mixed linear model was used to analyze the data, and the comparison was performed by orthogonal contrasts (alpha=0.05). Results At 0 degrees, the retention force decreased significantly over time, and the retention force was significantly different in all comparisons, except from 12 to 18 months. When the implants were positioned at 7 degrees, the retention force was statistically different at 0 and 24 months. At 14 degrees, significant differences were found from 6 and 12 to 24 months. Conclusions Within the limitations of this study, it was concluded that O-rings for implant/attachments perpendicular to the occlusal plane were adequately retentive over the first year and that the retentive capacity of O-ring was affected by implant inclinations despite the proposed positioners. To cite this article:Rodrigues RCS, Faria ACL, Macedo AP, Sartori IAM, de Mattos MGC, Ribeiro RF. An in vitro study of non-axial forces upon the retention of an O-ring attachment.Clin. Oral Impl. Res. 20, 2009; 1314-1319.doi: 10.1111/j.1600-0501.2009.01742.x.