Tungsten Silicide Contacts to Polycrystalline Silicon and Silicon-Germanium Alloys

Novel CVD WSi2 technology with low series and contact resistance in SiGe HBTs was achieved. Specific contact resistance to Si1-xGex with 0

Catalytic Role of Metal Oxides in Gold-Based Catalysts: A First Principles Study of CO Oxidation on TiO2 Supported Au

CO oxidation on TiO2 supported Au has been studied using density functional theory calculations. Important catalytic roles of the oxide have been identified: (i) CO oxidation occurs at the interface between Au and the oxide with a very small barrier; and (ii) O-2 adsorption at the interface is the key step in the reaction. The physical origin of the oxide promotion effect has been further investigated: The oxide enhances electron transfer from the Au to the antibonding states of O-2, giving rise to (i) strong ionic bonding between the adsorbed O-2, Au, and the Ti cation; and (ii) a significant activation of O-2 towards CO oxidation.

Germanium MOS Capacitors with Hafnium Dioxide and Silicon Dioxide Dielectrics

Germanium (Ge) does not grow a suitable oxide for MOS devices. The Ge/dielectric interface is of prime importance to the operation of photo-detectors and scaled MOSTs. Therefore there is a requirement for deposited or bonded dielectric materials. MOS capacitors have been formed on germanium substrates with three different dielectric materials. Firstly, a thermally grown and bonded silicon dioxide (SiO2) layer, secondly, SiO2 deposited by atmospheric pressure CVD ‘silox’, and thirdly a hafnium oxide (HfO2) high-k dielectric deposited by atomic layer deposition (ALD). Ge wafers used were p-type 1 0 0 2 O cm. C–V measurements have been made on all three types of capacitors to assess the interface quality. ALD HfO2 and silox both display acceptable C–V characteristics. Threshold voltage and maximum and minimum capacitance values closely match expected values found through calculation. However, the bonded SiO2 has non-ideal C–V characteristics, revealing the presence of a high density of interface states. A H2/N2 post metal anneal has a detrimental effect on C–V characteristics of HfO2 and silox dielectrics, causing a shift in the threshold voltage and rise in the minimum capacitance value. In the case of hafnium dioxide, capacitor properties can be improved by performing a plasma nitridation of the Ge surface prior to dielectric deposition.

Atomic layer deposition of hafnium oxide dielectrics on silicon and germanium substrates

Hafnium oxide films have been deposited at 250 °C on silicon and germanium substrates by atomic layer deposition (ALD), using tetrakis-ethylmethylamino hafnium (TEMAH) and water vapour as precursors in a modified Oxford Instruments PECVD system. Self-limiting monolayer growth has been verified, characterised by a growth rate of 0.082 nm/ cycle. Layer uniformity is approximately within ±1% of the mean value. MOS capacitors have been fabricated by evaporating aluminium electrodes. CV analysis has been used to determine the bulk and interface properties of the HfO 2, and their dependence on pre-clean schedule, deposition conditions and post-deposition annealing. The dielectric constant of the HfO 2 is typically 18. On silicon, best results are obtained when the HfO 2 is deposited on a chemically oxidised hydrophilic surface. On germanium, best results are obtained when the substrate is nitrided before HfO 2 deposition, using an in-situ nitrogen plasma treatment. © Springer Science+Business Media, LLC 2007.