Thermal study of selectively plated nickel sulfamate coatings

Nickel sulfamate solution was applied to mild steel substrates by the process of selective plating. The coated samples were heated to temperatures in the range of 50–1000 °C. Thermal analysis, X-ray diffraction and microscopy techniques were used to investigate the effect of secondary heating on the microstructure, mechanical properties and the composition of the surface coatings.

The microscopy analysis showed that the secondary heating caused diffusion within the coating itself and diffusion between the coating and the substrate as concentrations of iron increased in the coating and nickel appeared in the substrate. This diffusion redistribution also caused a phase transformation in the coating as NiO formed on the surface when the coating was heated in a furnace fitted with a nitrogen flow. However this transformation was found not to occur when the coating was heated in a sealed helium environment. Layer and grain growth occurred as temperature increased with the grains taking their preferred orientation as they were heated.

The surface hardness was found to initially rise up from 565 HV to 600 HV when heated to 200 °C. After 200 °C the surface hardness decreased in two stages before falling to 110 HV by 1000 °C. During tensile testing the coated samples performed marginally better in tension than the uncoated samples, however the temperatures used were not elevated high enough to show any real degradation during the tensile testing of the nickel coating that was shown during hardness testing and the microscopy analysis

Characterization of Nickel Germanide Schottky Contacts for the Fabrication of Germanium p-channel MOSFETs

Nickel germanide Schottky contacts, formed by rapid thermal annealing of thin nickel films, have been characterized on n-type germanium wafers for a range of RTA temperatures. The highest Schottky barrier heights for electrons (= 0.6-0.7 eV) were obtained for RTA temperatures of approximately 300°C. For this RTA schedule, the corresponding barrier height for holes is close to zero, ideal for Schottky contacted p-channel germanium MOSFETs. When the RTA temperature was increased to 400oC, a dramatic reduction in electron barrier height (< 0.1 eV) was observed. This RTA schedule, therefore, appears ideal for ohmic source/drain contacts to n channel germanium MOSFETs. From sheet resistance measurements and XRD characterization, nickel germanide formation was found to occur at 300oC and above. The NiGe phase was dominant for RTA temperatures up to at least 435oC.

Precipitation, microstructure and mechanical properties of low nickel maraging steel

A maraging steel with a composition of Fe–12·94Ni–1·61Al–1·01Mo–0·23Nb (wt-%) was investigated. Optical, scanning electron and transmission electron microscopy and X-ray diffraction analysis were employed to study the microstructure of the steel after different aging periods at temperatures of 450–600°C. Hardness and Charpy impact toughness of the steel were measured. The study of microstructure and mechanical properties showed that nanosized precipitates were formed homogeneously during the aging process, which resulted in high hardness. As the aging time is prolonged, precipitates grow and hardness increases. Fractography of the as forged steel has shown mixed ductile and brittle fracture and has indicated that the steel has good toughness. Relationships among heat treatment, microstructure and mechanical properties are discussed. Further experiments using tensile testing and impact testing for aged steel were carried out.

Formation of nickel-thiolate aggregates via reaction with CH2Cl2

Reaction of the mononuclear nickel-thiolate complex [Ni(L-1)(dppe)] with CH2Cl2 affords the novel pentanuclear complex Ni5Cl2(L-1)(4)(dppe)(2)], while [Ni(L-1)(dcpe)] reacts with CH2Cl2 to give the binuclear species [Ni2Cl2(L-2)(dcpe)(2)] in which two L-1 units are linked by a methylene group derived from CH2Cl2.

Microstructure and mechanical properties of low nickel maraging steel

Austenitization with lower temperature and intercritical annealing were introduced in the treatment of a maraging steel with a composition of Fe–12.94Ni–1.61Al–1.01Mo–0.23Nb (wt.%). Scanning electron microscopy was employed to study the microstructure after austenitization at 950 °C and intercritical annealing, followed by aging at 485 and 600 °C. X-ray diffraction (XRD) analysis was applied to evaluate the formation of retained or reverted austenite. Thermodynamic calculation was employed to calculate equilibrium phase mole fractions. Hardness and Charpy impact toughness of the steel were measured. Intercritical annealing treatments did not result in significant increase of hardness either before or after aging. The Charpy impact toughness of the alloy in aged condition was enhanced after austenitization at 950 °C. No austenite was observed in XRD. However, suspected reverted austenite was found after austenitization at 950 °C followed by aging at 600 °C for 4 h. Relationships among heat treatment, microstructure and mechanical properties are discussed.