Thermal study of selectively plated nickel sulfamate coatings

Nickel sulfamate solution was applied to mild steel substrates by the process of selective plating. The coated samples were heated to temperatures in the range of 50–1000 °C. Thermal analysis, X-ray diffraction and microscopy techniques were used to investigate the effect of secondary heating on the microstructure, mechanical properties and the composition of the surface coatings.

The microscopy analysis showed that the secondary heating caused diffusion within the coating itself and diffusion between the coating and the substrate as concentrations of iron increased in the coating and nickel appeared in the substrate. This diffusion redistribution also caused a phase transformation in the coating as NiO formed on the surface when the coating was heated in a furnace fitted with a nitrogen flow. However this transformation was found not to occur when the coating was heated in a sealed helium environment. Layer and grain growth occurred as temperature increased with the grains taking their preferred orientation as they were heated.

The surface hardness was found to initially rise up from 565 HV to 600 HV when heated to 200 °C. After 200 °C the surface hardness decreased in two stages before falling to 110 HV by 1000 °C. During tensile testing the coated samples performed marginally better in tension than the uncoated samples, however the temperatures used were not elevated high enough to show any real degradation during the tensile testing of the nickel coating that was shown during hardness testing and the microscopy analysis

Animal-borne sensors successfully capture the real-time thermal properties of ocean basins

Climate change is perhaps the most pressing and urgent environmental issue facing the world today. However our ability to predict and quantify the consequences of this change is severely limited by the paucity of in situ oceanographic measurements. Marine animals equipped with sophisticated oceanographic data loggers to study their behavior offer one solution to this problem because marine animals range widely across the world's ocean basins and visit remote and often inaccessible locations. However, unlike the information being collected from conventional oceanographic sensing equipment, which has been validated, the data collected from instruments deployed on marine animals over long periods has not. This is the first long-term study to validate in situ oceanographic data collected by animal oceanographers. We compared the ocean temperatures collected by leatherback turtles (Dermochelys coriacea) in the Atlantic Ocean with the ARGO network of ocean floats and could find no systematic errors that could be ascribed to sensor instability. Animal-borne sensors allowed water temperature to be monitored across a range of depths, over entire ocean basins, and, importantly, over long periods and so will play a key role in assessing global climate change through improved monitoring of global temperatures. This finding is especially pertinent given recent international calls for the development and implementation of a comprehensive Earth observation system ( see http://iwgeo.ssc.nasa.gov/documents.asp?s=review) that includes the use of novel techniques for monitoring and understanding ocean and climate interactions to address strategic environmental and societal needs.

Tripartite nonlocality and continuous-variable entanglement in thermal states of trapped ions

We study a system of three trapped ions in an anisotropic bidimensional trap. By focusing on the transverse modes of the ions, we show that the mutual ion-ion Coulomb interactions set entanglement of a genuine tripartite nature, to some extent persistent to the thermal nature of the vibronic modes. We tackle this issue by addressing a nonlocality test in the phase space of the ionic system and quantifying the genuine residual tripartite entanglement in the continuous variable state of the transverse modes.

Enantioselective dioxygenase-catalysed formation and thermal racemisation of chiral thiophene sulfoxides

Substituted chiral thiophene 1-oxides and their cycloadducts of variable enantiopurity have been isolated as products of dioxygenase-catalysed sulfoxidation of the corresponding thiophenes using intact cells of Pseudomonas putida; thermal racemization (Delta G(double dagger) = 25.1 kcal mol(-1)) of the enantiopure metabolite (1R)-2-methylbenzo[b]thiophene 1-oxide has been observed.

Experimental and Numerical Evaluation of Thermal Performance of Steered Fibre Composite Laminates

For Variable Stiffness (VS) composites with steered curvilinear tow paths, the fiber orientation angle varies continuously throughout the laminate, and is not required to be straight, parallel and uniform within each ply as in conventional composite laminates. Hence, the thermal properties (conduction), as well as the structural stiffness and strength, vary as functions of location in the laminate, and the associated composite structure is often called a “variable stiffness” composite structure. The steered fibers lead not only to the alteration of mechanical load paths, but also to the alteration of thermal paths that may
result in favorable temperature distributions within the laminate and improve the laminate performance. Evaluation of VS laminate performance under thermal loading is the focus of this chapter. Thermal performance evaluations require experimental and numerical analysis of VS laminates under different processing and loading conditions. One of the advantages of using composite materials in many applications is the tailoring capability of the laminate,
not only during the design phase but also for manufacturing. Heat transfer through variable conduction and chemical reaction (degree of cure) occurring during manufacturing (curing) plays an important role in the final thermal and mechanical performance, and shape of composite structures.

Thermal conductivities of ionic liquids over the temperature range from 293 K to 353 K

The thermal conductivities of 11 ionic liquids were determined, over the temperature range from 293 K to 353 K, at atmospheric pressure, using an apparatus based on the transient hot-wire method. For each of the ionic liquids studied, the thermal conductivities were found to be between (0.1 and 0.2) W.m(-1).K-1, with a slight decrease observed on increasing temperature. The uncertainty is estimated to be less than +/- 0.002 W.m(-1).K-1. In all cases, a linear equation was found to give a good fit to the data. The effects of water content and chloride content on the thermal conductivities of some of the ionic liquids were investigated. In each case, the thermal conductivities of the water + ionic liquid and chloride + ionic liquid binary mixtures were found to be less than the weighted average of the pure component thermal conductivities. This effect was adequately modeled using the Jamieson correlation. Chloride contamination at typical postsynthesis levels was found to have no significant effect on the thermal conductivities of the ionic liquid studied.

Improved Thermal Performance of SOI Using Compound Buried Layer

The buried oxide (BOX) layer in silicon on insulator (SOI) was replaced by a compound buried layer (CBL) containing layers of SiO2, polycrystalline silicon (polysilicon), and SiO2. The undoped polysilicon in the CBL acted as a dielectric with a higher thermal conductivity than SiO2. CBL provides a reduced thermal resistance with the same equivalent oxide thickness as a standard SiO2 buried layer. Thermal resistance was further reduced by lateral heat flow through the polysilicon. Reduction in thermal resistance by up to 68% was observed, dependent on polysilicon thickness. CBL SOI substrates were designed and manufactured to achieve a 40% reduction in thermal resistance compared with an 1.0-μm SiO2 BOX. Power bipolar transistors with an active silicon layer thickness of 13.5 μm manufactured on CBL SOI substrates showed a 5%-17% reduction in thermal resistance compared with the standard SOI. This reduction was dependent on transistor layout geometry. Between 65% and 90% of the heat flow from these power transistors is laterally through the thick active silicon layer. Analysis confirmed that CBL SOI provided a 40% reduction in the vertical path thermal resistance. Devices employing thinner active silicon layers will achieve the greater benefit from reduction in vertical path thermal resistance offered by CBL SOI.