Rapid thermal processed thin films of niobium pentoxide (Nb2 O5) deposited by reactive magnetron sputtering

Niobium pentoxide thin films have been deposited on silicon and platinum-coated silicon substrates by reactive magnetron sputtering. The as-deposited films were amorphous and showed good electrical properties in terms of a dielectric permittivity of about 30, and leakage current density of 10(-6) A cm(-2) al a field of 120 kV cm(-1). A rapid thermal annealing process at 800 degrees C further increased the dielectric constant to 90 and increased the leakage current density to 5 x 10(-6) A cm(-2). The current-voltage characteristics observed at low and high fields suggested a combination of phenomena at different regimes of applied electric field. The capacitance-voltage characteristics performed in the metal-insulator-semiconductor configuration indicated good electronic interfaces with a nominal trap density of 4.5 x 10(12) cm(-2) eV(-1), which is consistent with the behavior observed with conventional dielectrics such as SiO2 on silicon surfaces.

Reactive magnetron co?sputtered antiferroelectric lead zirconate thin films

Antiferroelectric lead zirconate thin films were formed on platinum coated silicon substrates by a reactive magnetron co-sputtering method. The films showed (240) preferred orientation. The crystallization temperatures and the preferred orientation were affected by the lead content in the films. The electric field forced transformation from the antiferroelectric phase to the ferroelectric phase was observed at room temperature with a maximum polarization value of 36 mu C/cm(2). The average field to excite the ferroelectric state and that for the reversion to the antiferroelectric state were 267 and 104 kV/cm respectively. (C) 1995 American Institute of Physics.

Highly Efficient and Thermally Stable Second-Order Nonlinear Optical Chromophores and Electrooptic Polymers

Organic polymeric electro-optic (E-O) materials have attracted significant attention because of their potential use as fast and efficient components of integrated photonic devices (1,2). However, the practical application of these materials in optical devices is somewhat limited by the stringent material requirements imposed by the device design, fabrication processes and operating environments. Among the various material requirements, the most notable ones are large electro-optic coefficients (r(33)) and high thermal stability (3). The design of poled polymeric materials with high electro-optic activity (r(33)) involves the optimization of the percent incorporation of efficient (large beta mu) second order nonlinear optical (NLO) chromophores into the polymer matrices and the effective creation of poling-induced non-centrosymmetric structures. The factors that affect the material stability are a) the inherent thermal stability of the NLO chromophores, b) the chemical stability of the NLO chromophores during the polymer processing conditions, and c) the long-term dipolar alignment stability at high temperatures. Although considerable progress has been made in achieving these properties (4), organic polymeric materials suitable for practical E-O device applications are yet to be developed. This chapter highlights some of our approaches in the optimization of molecular and material nonlinear optical and thermal properties.

Uracil excision repair in Mycobacterium tuberculosis cell-free extracts

Uracil excision repair is ubiquitous in all domains of life and initiated by uracil DNA glycosylases (UDGs) which excise the promutagenic base, uracil, from DNA to leave behind an abasic site (AP-site). Repair of the resulting AP-sites requires an AP-endonuclease, a DNA polymerase, and a DNA ligase whose combined activities result in either short-patch or long-patch repair. Mycobacterium tuberculosis, the causative agent of tuberculosis, has an increased risk of accumulating uracils because of its G + C-rich genome, and its niche inside host macrophages where it is exposed to reactive nitrogen and oxygen species, two major causes of cytosine deamination (to uracil) in DNA. In vitro assays to study DNA repair in this important human pathogen are limited. To study uracil excision repair in mycobacteria, we have established assay conditions using cell-free extracts of M. tuberculosis and M. smegmatis (a fast-growing mycobacterium) and oligomer or plasmid DNA substrates. We show that in mycobacteria, uracil excision repair is completed primarily via long-patch repair. In addition, we show that M. tuberculosis UdgB, a newly characterized family 5 UDG, substitutes for the highly conserved family 1 UDG, Ung, thereby suggesting that UdgB might function as backup enzyme for uracil excision repair in mycobacteria. (C) 2011 Elsevier Ltd. All rights reserved.

Optical and structural properties of reactive ion beam sputter deposited CeO2 films

Optical and structural properties of reactive ion beam sputter deposited CeO2 films as a function of oxygen partial pressures (P-O2) and substrate temperatures (T-s) have been investigated. The films deposited at ambient temperature with P-O2 of 0.01 Pa have shown a refractive index of 2.36 which increased to 2.44 at 400 degrees C. Refractive index and extinction coefficient are sensitive up to a T-s of similar to 200 degrees C. Raman spectroscopy and X-ray diffraction (XRD) have been used to characterise the structural properties. A preferential orientation of (220) was observed up to a T-s of 200 degrees C and it changed to (200) at 400 degrees C: and above. Raman line broadening, peak shift and XRD broadening indicate the formation of nanocrystalline phase for the films deposited up to a substrate temperature of 300 degrees C. However, crystallinity of the films were better for T-s values above 300 degrees C. In general both optical and structural properties were unusual compared to the films deposited by conventional electron beam evaporation, but were similar in some aspects to those deposited by ion-assisted deposition. Apart from thermal effects, this behavior is also attributed to the bombardment of backscattered ions/neutrals on the growing film as well as the higher kinetic energy of the condensing species, together resulting in increased packing density. (C) 1997 Elsevier Science S.A.

Structure of highly conducting amorphous carbon

We report on neutron diffraction study of a new form of conducting amorphous carbon up to Q similar to 14.5 Angstrom(-1). The bond distances from first two peaks in g(r) are 1.45 and 2.49 Angstrom, very similar to those in sputtered truly amorphous carbon films (Li and Lannin, Phys. Rev. Lett. 65 (1990) 1905). The first coordination number is 3.1 (+/- 0.1) indicating predominantly sp(2) hybridisation (ideal no. = 3). However, S(Q) itself shows vestiges of (0 0 2), (1 0) and (1 1) peaks, typical of glassy carbon (Mildner, J. Non-Cryst. Solids 47 (1982) 391). (C) 1998 Elsevier Science B.V. All rights reserved.

Highly selective deprotection of tert-butyl esters using ytterbium triflate as a catalyst under mild conditions

Ytterbium triflate catalyses the deprotection of tert-butyl esters selectively in the presence of other esters under mild conditions in almost quantitative yields. The reactions are carried out in nitromethane (45degrees - 50degreesC) using 5 mole percent of the catalyst.

Analytical Study of Low-Field Diffusive Transport in Highly Asymmetric Bilayer Graphene Nanoribbon

We present a simplified theory of carrier backscattering coefficient in a twofold degenerate asymmetric bilayer graphene nanoribbon (BGN) under the application of a low static electric field. We show that for a highly asymmetric BGN(Delta = gamma), the density of states in the lower subband increases more that of the upper, in which Delta and gamma are the gap and the interlayer coupling constant, respectively. We also demonstrate that under the acoustic phonon scattering regime, the formation of two distinct sets of energy subbands signatures a quantized transmission coefficient as a function of ribbon width and provides an extremely low carrier reflection coefficient for a better Landauer conductance even at room temperature. The well-known result for the ballistic condition has been obtained as a special case of the present analysis under certain limiting conditions which forms an indirect validation of our theoretical formalism.

Photocatalytic activity of ZnO nanostructured film grown by activated reactive

ZnO nanostructured films were deposited at room temperature on glass substrates and cotton fabrics by activated reactive evaporation in a single step without using metal catalyst or templates. Morphological observation has shown that the nanostructured film contains seaurchin-like structures, and this seaurchin containing large number of randomly grown ZnO nanoneedles. Microstructural analysis revealed the single crystalline nature of the grown nanoneedles and their growth direction was indentified to be along [0002]. PL spectrum of nanostructured films has shown a relatively weak near-band-edge emission peak at 380 nm, and a significant broad peak at 557 nm due to the oxygen vacancy-related emission. ZnO nanostructured films grown on glass substrates and cotton fabrics have shown good photocatalytic activity against rhodamine B.

Reactive Diffusion Between Vanadium and Silicon

Interdiffusion study is conducted in the V-Si system to determine integrated diffusion coefficients of the phases. Activation energy values are calculated from the experiments conducted at different temperatures. The average values are found to be 208, 240 and 141 kJ/mol, respectively, for the V(3)Si, V(5)Si(3) and VSi(2) phases. The low activation energy for the VSi(2) phase indicates very high concentration of defects or the significant contribution from the grain boundary diffusion. The error in calculation of diffusion parameters from a very thin phase layer in a multiphase diffusion couple is discussed. Further the data available in the literature in this system is compared and the problems in the indirect methodology followed previously to calculate the diffusion parameters are discussed.

Consumerist Predators"? Emerging lifestyles between McDonaldization and sustainability perspectives: the case of highly qualified employees (HQEs) in India

In industrializing countries new groups of consumers with remarkable purchasing power are emerging. Representing a ?new middle class? they are seen as a carrier and promoter of a so-called ?western way of life? beyond the OECD countries. They are presented as having a consumerist predator lifestyle which stands in conflict with the requirements for a sustainable future. Furthermore, they are imputed a profound lack of a sense of responsibility towards society. However, such a ?civil society spirit? is a core prerequisite for coping with the challenge of changing existing lifestyles to insure a more sustainable future....