Fabrication and optical characterization of GaN-based nanopillar light emitting diodes

InGaN/GaN-multiple-quantum-well-based light emitting diode ( LED) nanopillar arrays with a diameter of approximately 200nm and a height of 700nm are fabricated by inductively coupled plasma etching using Ni self-assembled nanodots as etching mask. In comparison to the as-grown LED sample an enhancement by a factor of four of photoluminescence ( PL) intensity is achieved after the fabrication of nanopillars, and a blue shift and a decrease of full width at half maximum of the PL peak are observed. The method of additional wet etching with different chemical solutions is used to remove the etch-induced damage. The result shows that the dilute HCl ( HCl:H2O=1:1) treatment is the most effective. The PL intensity of nanopillar LEDs after such a treatment is about 3.5 times stronger than that before treatment.

Structural and optical characterization of Zn1-xCdxO thin films deposited by dc reactive magnetron sputtering

Zn1-xCdxO crystal thin films with different compositions were prepared on silicon and sapphire substrates by the dc reactive magnetron sputtering technique. X-ray diffraction measurements show that the Zn1-xCdxO films are of completely (002)-preferred orientation for x less than or equal to 0.6. For x = 0.8, the Elm is a mixture of ZnO hexagonal wurtzite crystals and CdO cubic crystals. For pure CdO, it is highly (200) preferential-oriented. Photoluminescence spectrum measurement shows that the Zn1-xCdxO (x = 0.2) thin film has a redshift of 0.14 eV from that of ZnO reported previously.

Structural and optical characterization of InAs nanostructures grown on (001) and high index InP substrates

The effects of InP substrate orientations on self-assembled InAs quantum dots (QDs) have been investigated by molecular beam epitaxy (MBE). A comparison between atomic force microscopy (AFM) and photoluminescence (PL) spectra shows that a high density of smaller InAs islands can be obtained by using such high index substrates. On the other hand, by introducing a lattice-matched underlying In0.52Al0.24Ga0.24As layer, the InAs QDs can be much more uniform in size and have a great improvement in PL properties. More importantly, 1.55-mu m luminescence at room temperature (RT) can be realized in InAs QDs deposited on (001) InP substrate with underlying In0.52Al0.24Ga0.24As layer. (C) 2000 Elsevier Science B.V. All rights reserved.

X-ray diffraction and optical characterization of interdiffusion in self-assembled InAs/GaAs quantum-dot superlattices

We report on the characterization of thermally induced interdiffusion in InAs/GaAs quantum-dot superlattices with high-resolution x-ray diffraction and photoluminescence techniques. The dynamical theory is employed to simulate the measured x-ray diffraction rocking curves of the InAs/GaAs quantum-dot superlattices annealed at different temperatures. Excellent agreement between the experimental curves and the simulations is achieved when the composition, thickness, and stress variations caused by interdiffusion are taken in account. It is found that the significant In-Ga intermixing occurs even in the as-grown InAs/GaAs quantum dots. The diffusion coefficients at different temperatures are estimated. (C) 2000 American Institute of Physics. [S0003-6951(00)02440-2].

Optical characterization of high-purity cubic GaN grown on GaAs (001) substrate by metalorganic chemical vapor deposition

The optical properties of cubic GaN films have been investigated in the temperature range of 10-300 K. Five peaks were observed at 10 K. From the dependence of photoluminescence emissions on the temperature and excitation intensity, we have assigned two of the five peaks (2.926 and 2.821 eV) to donor-acceptor pair (DAP) transitions. Furthermore, these two peaks were found to be related to a common shallow donor involved in the peak position previously reported at 3.150 eV. The intensities of DAP transitions were much weaker than that of excitonic emission even at low temperature, indicating a relatively high purity of our samples. (C) 2000 American Institute of Physics. [S0003-6951(00)00921-9].

Structural and optical characterization of InAs nanostructures grown on high-index InP substrates

The structural and optical properties of InAs layers grown on high-index InP surfaces by molecular beam epitaxy are investigated in order to understand the self-organization of quantum dots and quantum wires on novel index surfaces. Four different InP substrate orientations have been examined, namely, (1 1 1)B, (3 1 1)A, and (3 1 1)B and (1 0 0). A rich variety of InAs nanostructures is formed on the surfaces. Quantum wire-like morphology is observed on the (1 0 0) surface, and evident island formation is found on (1 1 1)A and (3 1 1)B by atomic force microscopy. The photoluminescence spectra of InP (1 1 1)A and (3 1 1)B samples show typical QD features with PL peaks in the wavelength range 1.3-1.55 mu m with comparable efficiency. These results suggest that the high-index substrates are promising candidates for production of high-quality self-organized QD materials for device applications. (C) 1999 Elsevier Science B.V. All rights reserved.

Optical characterization of InAs monolayer quantum structures grown on (311)A, (311)B, and (100)GaAs substrates

Low-temperature photoluminescence and excitation spectra from InAs monolayer quantum structures, grown on (311)A, (311)B, and (100) GaAs substrates, are investigated, The structures were grown simultaneously by conventional molecular-beam epitaxy (MBE), The experimental results show that the quality of InAs monolayer on (311)B GaAs substrate is obviously better in crystal quality than those on the two other oriented GaAs substrates. In addition, the transition peaks of the InAs layer grown on (311) GaAs substrates shift to higher energy with respect to that from the InAs layer grown on (100) GaAs substrate.

Optical characterization of the Ge/Si (001) islands in multilayer structure

We show that the observed temperature dependence of the photoluminescence (PL) features can be consistently explained in terms of thermally activated carrier transfer processes in a multilayer structure of the self-organized Ge/Si(001) islands. The type II (electron confinement in Si) behavior of the Ge/Si islands is verified. With elevated temperature, the thermally activated electrons and holes enter the Ge islands from the Si and from the wetting layer (WL), respectively. An involvement of the type I (spatially direct) into type II (spatially indirect) recombination transition takes place at a high temperature.

Preparation and optical characterization of an organoeuropium-doped sol-gel transparent luminescence thin film

Binary and ternary europium complexes with dibenzplymethane (DBM) and 1,10-phenanthroline (phen) were synthesized and doped into a sol-gel luminescence thin film and polyvinylbutyral (PVB) film. The luminescent spectra and lifetime of the films were measured. The final results showed that Eu(III) characteristic emission bands were observed in the spectra of all the doped films. Longer lifetimes and a higher photo-stability were observed in SiO2:Eu(III) complex luminescent thin films than in PVB:Eu(III) complex films that contained a corresponding amount of pure complexes. Heat-stability tests showed that SiO2:Eu(III) complex thin films still showed certain fluorescence after heat-treatment at a temperature of 130 degreesC, while little fluorescence could be observed in PVB:Eu(III) complex films under a UV lamp. (C) 2001 Elsevier Science B.V. All rights reserved.

Strain and photoluminescence characterization of cubic (In,Ga)N films grown on GaAs(001) substrates

Cubic InxGa1-xN films were successfully grown on GaAs(001) substrates by metalorganic chemical-vapor deposition. The values of x content ranging from 0.10 to 0.24 obtained at different growth conditions were measured by double-crystal x-ray diffraction (XRD). The perpendicular and parallel elastic strain of the In0.2Ga0.8N layer, epsilon(perpendicular to)=0.4% and epsilon(parallel to)=-0.4% for GaN and epsilon(perpendicular to)=0.37% and epsilon(parallel to)=-0.37% for InGaN, respectively, were derived using the XRD measurements. The inhomogeneous strain and the average grain size of the In0.2Ga0.8N/GaN films were also studied by XRD. Photoluminescence spectra were used to measure the optical characterization of the InxGa1-xN thin films with different In composition, and the near-band-edge emission dependence of cubic InxGa1-xN on the x value is nearly linear with In content x less than or equal to 0.24. (C) 2000 American Institute of Physics. [S0021-8979(00)03908-6].

Characterization and analysis of two-dimensional GaAs-based photonic crystal nanocavities at room temperature

This paper describes the design and fabrication process of a two-dimensional GaAs-based photonic crystal nanocavity and analyzes the optical characterization of cavity modes at room temperature. Single InAs/InGaAs quantum dots (QDs) layer was embedded in a GaAs waveguide layer grown on an Al0.7Ga0.3As layer and GaAs substrate. The patterning of the structure and the membrane release were achieved by using electron-beam lithography, reaction ion etching, inductively coupled plasma etching and selective wet etching. The micro-luminescence spectrum is recorded from the fabricated nanocavities, and it is found that some high-order cavity modes are clearly observed besides the lowest-order resonant mode is exhibited in spite of much high rate of nonradiative recombination. The variance of resonant modes is also discussed as a function of r/a ratio and will be used in techniques aimed to improve the probability of achieving spectral coupling of a single QD to a cavity mode.

掺镁近化学计量比LiTaO3晶体的生长及光学性能

在同成分LiTaO3熔体中掺入一定剂量的K2O,采用顶部籽晶提拉法生长掺镁近化学计量比LiTaO3晶体。对晶体分别进行光谱分析,畴结构和抗光损伤阈值的测定。结果表明：与同成分掺镁LiTaO3晶体相比较,其紫外吸收边出现明显蓝移,红外吸收峰变弱。腐蚀晶片的晶相显微镜观察结果表明：掺镁近化学剂量比晶体的畴结构是较为规则的六边形;晶体的抗光致散射能力明显提高。

大尺寸Ce：Lu1.6Y0.4SiO5闪烁晶体的生长和光谱特性

采用中频感应提拉法生长出尺寸为Ф60mm×110mm的Ce：Lu1.6Y0.4SiO5（LYSO）晶体,与LSO晶体相比,LYSO晶体的优势是提高了晶体质量、降低了熔点和原料成本等.在室温下测试了LYSO晶体的透过光谱、激发光谱和发射光谱,结果表明Y的加入使LSO晶体的吸收边向短波方向偏移.Ce^3＋的4f^1→5d^1跃迁吸收导致紫外区产生三个吸收带.发射光谱具有Ce^3＋典型的双峰特征,经Gaussian多峰值拟合,双峰395nm和418nm归属于Ce1发光中心,而435nm的发光峰与Ce2发光中心有