Photoluminescence and transmission spectra of nanocrystalline GaAs1-xSbx embedded in silica films

The composite films of the nanocrystalline GaAs1-xSbx-SiO2 have been successfully deposited on glass and GaSb substrates by radio frequency magnetron co-sputtering. The 10K photoluminescence (PL) properties of the nanocrystalline GaAs1-xSbx indicated that the PL peaks of the GaAs1-xSbx nanocrystals follow the quantum confinement model very closely. Optical transmittance spectra showed that there is a large blue shift of optical absorption edge in nanocrystalline GaAs1-xSbx-SiO2 composite films, as compared with that of the corresponding bulk semiconductor, which is due to the quantum confinement effect.

Rapidly Infrared-Assisted Cooperatively Self-Assembled Highly Ordered Multiscale Porous Materials

In this paper, cooperative self-assembly (CSA) of colloidal spheres with different sizes was studied. It was found that a complicated jamming effect makes it difficult to achieve an optimal self-assembling condition for construction of a well-ordered stacking of colloidal spheres in a relatively short growth time by CSA. Through the use of a characteristic infrared (IR) technique to significantly accelerate local evaporation on the growing interface without changing the bulk growing environment, a concise three-parameter (temperature, pressure, and IR intensity) CSA method to effectively overcome the jamming effect has been developed. Mono- and multiscale inverse opals in a large range of lattice scales can be prepared within a growth time (15-30 min) that is remarkably shorter than the growth times of several hours for previous methods. Scanning electron microscopy images and transmittance spectra demonstrated the superior crystalline and optical qualities of the resulting materials. More importantly, the new method enables optimal conditions for CSA without limitations on sizes and materials of multiple colloids. This strategy not only makes a meaningful advance in the applicability and universality of colloidal crystals and ordered porous materials but also can be an inspiration to the self-assembly systems widely used in many other fields, such as nanotechnology and molecular bioengineering.

Photoinduced effects in amorphous Ge-Se films

With light illumination from an Ar ion laser, the photoinduced changes in vacuum evaporated amorphous GeSe2 films; were investigated with the X-ray diffraction (XRD), infrared absorption (IR), scanning electron microscope (SEM), transmitting electron microscope (TEM) and transmittance spectra analysis. It was observed that the optical transmittance edges of films shifted to shorter wavelength according to annealing and light illumination and the shift in well-annealed films could be recovered by annealing at 200 degrees C for 1 h in Ar air. The magnitude of shift increased with the increase of the intensity of illumination light and the illumination time. By sides, photoinduced crystallization was also observed in the exposed regions of GeSe2 films and more of it was observed with stronger intensity of illumination light.

SiO2 对Bi2O3-B2O3 玻璃体系光学、热学及结构的 影响

Glasses with compositions 50Bi2O3-xB2O3- (50-x)SiO2(x=0, 10, 20, 30, 40, 50) in mol% have been prepared by using a normal melt-quench technique. The effect of SiO2 addition on thermal stability, optical properties and structural characteristic on Bi2O3-B2O3 glass were systematically investigated by using XRD, DTA, ultraviolet-visible transmittance spectra, midinfrared transmittance spectra and Raman spectra. The experimental results demonstrate that, with the addition of SiO2, thermal stability of glass samples has been obviously improved. Once the amount of SiO2 is too much, the glass samples tend to be phase seperation which results in the decrease of thermal stability. With increasing SiO2 content, the UV cutoff edge firstly shifts to short-wave band and then shifts to long-wave band, and the transmittance of mid-infrared has been greatly improved. With substitution of SiO2 for B2O3, the [BO3] triangles and [BO4] tetrahedral groups are gradually replaced by [SiO4]. [BiO6] octahedral and [SiO4] tetrahedral units are connected forming a vibrational mode of Bi-O-Si. The physical chemistry and optical performance of Bi2O3-B2O3 glass were greatly improved by addition of SiO2.

Effect of bismuth oxide introduction on spectroscopic properties of Er3+/Yb3+ co-doped aluminophosphate glasses

The absorption spectra, emission spectra and infrared spectra of Er3+/Yb3+ co-doped xBi(2)O(3)-(65 - x)P2O5-4Yb(2)O(3)-11Al(2)O(3)-5BaO-15Na(2)O were measured and investigated. Spontaneous emission probability, radiative lifetime and branching ratios of Er3+ were calculated according to the Judd-Ofelt theory. The role of substitution of Bi2O3 for P2O5 on luminescence of Er3+/Yb3+ co-doped aluminophosphate glasses has been investigated. The calculated radiative lifetimes (tau(rad)) for I-4(13/2) and I-4(11/2) were decreasing with Bi2O3 content increases, whereas the measured total lifetime (tau(meas)) for I-4(13/2) showed linearly increasing trends. The effect of Bi2O3 introduction on OH- groups was also discussed according to the IR transmittance spectra of glasses. It was found that FWHM of glasses were not affected with the substitution of Bi2O3 for P2O5. The emission spectra intensity increased with Bi2O3 content due to the decreases of phonon energy and OH- content in glasses. (C) 2007 Elsevier B.V. All rights reserved.

Influence of oxygen partial pressure on the structure and photoluminescence of direct current reactive magnetron sputtering ZnO thin films

The effects of oxygen partial pressure on the structure and photoluminescence (PL) of ZnO films were studied. The films were prepared by direct current (DC) reactive magnetron sputtering with various oxygen concentrations at room temperature. With increasing oxygen ratio, the structure of films changes from zinc and zinc oxide phases, single-phase ZnO, to the (002) orientation, and the mechanical stresses exhibit from tensile stress to compressive stress. Films deposited at higher oxygen pressure show weaker emission intensities, which may result from the decrease of the oxygen vacancies and zinc interstitials in the film. This indicates that the emission in ZnO film originates from the oxygen vacancy and zinc interstitial-related defects. From optical transmittance spectra of ZnO films, the plasma edge shifts towards the shorter wavelength with the improvement of film stoichiometry. (C) 2004 Elsevier B.V. All rights reserved.

Influences of CO2 laser irradiation on the structure and photoluminescence of zinc oxide thin films

CO2 laser irradiation experiments on ZnO thin films are reported. The structural, optical, luminescent and vibrational properties of the samples were investigated by X-ray diffraction (XRD), transmittance, photoluminescence (PL) and Raman measurements. XRD results show that the crystalline of the irradiated films was improved. The (002) peaks of irradiated ZnO films shift to. higher 20 angles due to the stress relaxation in the case of laser beam irradiation. From optical transmittance spectra, all films exhibit high transmittance in the visible range, the optical band edge of irradiated films showed a redshift compared with that of as-grown films. Compared with the as-grown films, the photoluminescence emission (in particular the relative intensities of visible emissions) intensities of irradiated samples enhanced. In the Raman scattering spectral both the A I. and E modes exhibited slight Raman blueshift. (c) 2005 Elsevier B.V. All rights reserved.

The effects of oxygen partial pressure on the optical absorption edge and the UV emission energy of ZnO films

The optical absorption edge and ultraviolet (UV) emission energy of ZnO films deposited by direct current (DC) reactive magnetron sputtering at room temperature have been investigated. With the oxygen ratio increasing, the structure of films changes from zinc and zinc oxide coexisting phase to single-phase ZnO and finally to the highly (002) orientation. Both the grain size and the stress of ZnO film vary with the oxygen partial pressure. Upon increasing the oxygen partial pressure in the growing ambient, the visible emission in the room-temperature photoluminescence spectra was suppressed without sacrificing the band-edge emission intensity in the ultraviolet region. The peaks of photoluminescence spectra were located at 3.06---3.15 eV. From optical transmittance spectra of ZnO films, the optical band gap edge was observed to shift towards shorter wavelength with the increase of oxygen partial pressure.

退火对电子束热蒸发Al2O3薄膜性能影响的实验研究

用电子束热蒸发方法镀制了Al2O3材料的单层膜，对它们在空气中进行了250～400℃的高温退火。对样品的透射率光谱曲线进行了测量，计算了样品的消光系数、折射率和截止波长。通过X射线衍射仪(XRD)测量分析了薄膜的微观结构，采用表面轮廓仪测量了样品的表面均方根粗糙度。结果发现随着退火温度的提高光学损耗下降，薄膜结构在退火温度为400℃时仍然为无定形态，样品的表面粗糙度随退火温度的升高而增加。引起光学损耗下降起主导作用的是吸收而不是散射，吸收损耗的下降主要是由于退火使材料吸收空气中的氧而进一步氧化，从而使薄膜

用于掺钛蓝宝石激光系统的高反膜的激光损伤

用电子束蒸发制备了用于掺钛蓝宝石啁啾脉冲放大激光系统的TiO2/HfO2/SiO2高反膜，其带宽约为176nm（R>98%, λ0=800nm），激光损伤阈值（LIDT）为2.4 J/cm2。通过TiO2和HfO2单层膜的透过光谱计算了这两种材料的折射率和消光系数。高反膜的性能主要由高折射率材料决定：折射率越高，反射带越宽；消光系数越小，薄膜吸收越小，LIDT越高。最后，讨论了高反膜的激光损伤机制。

光学薄膜膜厚自动控制系统的研究

介绍了一种利用光电极值法同时控制规整膜系和非规整膜系的方法,利用VC＋＋编写程序实现对光学监控信号的采集、处理及停镀点的自动判断,实现了规整膜系和非规整膜系膜层厚度的自动控制.并利用该膜厚自动控制系统实验制备了规整膜系和非规整膜系多层膜,实验结果表明：利用该系统镀制的薄膜重复性良好,且光谱曲线和理论光谱曲线吻合较好.该系统解决了非规整膜系的监控问题,由计算机控制膜层的停镀点,排除了人的主观因素对薄膜的性能及其制备的重复性产生的影响,提高了薄膜镀制的重复性和成品率.

沉积速率对热舟蒸发LaF3薄膜性能的影响

用热舟蒸发方法在不同的沉积速率下制备了LaF3单层膜,并对部分单层膜进行了真空退火。分别采用X射线衍射(XRD),Lambda 900 光谱仪和355 nm Nd∶YAG脉冲激光测试了薄膜的晶体结构、透射光谱和激光损伤阈值(LIDT),并通过透射光谱计算得到样品的折射率和消光系数。实验结果表明,增大沉积速率有利于LaF3薄膜的结晶和择优生长,可以提高薄膜的致密性和折射率,但薄膜的抗激光损伤能力有所下降;沉积速率太大,又会恶化薄膜的结晶性能,同时薄膜中产生大量孔洞,薄膜的机械强度降低,导致薄膜的折射率减小和

沉积温度对热舟蒸发MgF2薄膜性能的影响

采用热舟蒸发方法沉积了氟化镁（MgF2）材料的单层膜，沉积温度从200℃上升到350℃，间隔为50℃。测量了样品的透射率和反射率光谱曲线，进行了表面粗糙度的标定，并在此基础上进行了光学损耗及散射损耗的计算。同时对355nm波长处的激光诱导损伤阈值进行了测量。结果表明：随着沉积温度的升高，光学损耗增加;在短波长范围散射损耗在光学损耗中所占比例很小，光学损耗的增加主要由吸收损耗引起；在355nm波长处的损伤阈值变化与吸收损耗的变化趋势相关，损伤机制主要是吸收起主导作用。样品的微缺陷密度也是影响损伤阈值的一个重要因素，损伤阈值随缺陷密度的增加而降低。

355nm增透膜的设计、制备与性能

用热舟蒸发法结合修正挡板技术制备了355 nm LaF3/MgF2增透膜,并对部分样品进行了真空退火。采用Lambda 900光谱仪测试了增透膜的低反光谱和透射光谱,并考察了其光谱稳定性;使用脉冲8 ns的355 nm激光测试了增透膜的激光损伤阈值(LIDT);采用Normarski显微镜对增透膜的表面缺陷密度和破斑形貌进行了观察。实验结果表明,制备得到的增透膜的剩余反射率较低,光谱稳定性好;真空退火对增透膜的激光损伤阈值没有改善;增透膜的破环形貌为散点形式,结合破斑深度测试表明薄膜的破坏源于薄膜和基底界面的缺陷点。JGS1熔石英基底由于有好的表面状况、固有的高激光损伤阈值和以其为基底的增透膜具有更低的表面场强,使得其上的增透膜有更高的抗激光损伤能力。

Optical properties and microstructure of Ta2O5 biaxial film

This study investigates the optical properties and microstructure of Ta2O5 film deposited with the glancing angle deposition technique. The tilted nanocolumn microstructure, examined with scanning electron microscopy, induces the optical anisotropy of thin film. The optical properties of thin film are characterized with an inverse synthesis method. Based on the Cauchy model, the dispersion equations of optical constants of film are determined from the transmittance spectra measured at normal and oblique incidence over 400-800 nm. The starting values derived with an envelope method quicken the optimization process greatly. The dispersion of the principal indices N-1, N-2, and N-3 and the thickness d of thin film are presented statistically. A good agreement between the measured optical properties and theoretical calculation is obtained, which validates the model established for thin film produced by glancing angle deposition. (C) 2008 Optical Society of America