SbOx thin films used for write-once blue laser recording

SbOx thin films are deposited by reactive dc-magnetron sputtering from all antimony metal target in Ar+O-2 with the relative O-2 content 7%. It is found that the as-deposited films call represent a two-component system comprising amorphous Sb and amorphous Sb2O3. The crystallization of Sb is responsible for the changes of optical properties of the films. The results of the static, test show that the SbOx thin films have good writing sensitivity for blue laser beams and the recording marks are very clear and circular. High reflectivity contrast of about 41% is obtained at a writing power 6 mW and writing pulse width 300 ns. In addition, the films show a good stability after reading 10000 times.

Write-once blue laser recording using silicon doped SbOx thin films prepared by reactive dc-magnetron sputtering

Si:SbOx films have been deposited by reactive dc-magnetron sputtering from a Sb target with Si chips attached in Ar + O-2 with the relative O-2 content 7%. The as-deposited films contained Sb metal, Sb2O3, SiO, Si2O3 and SiO2. The crystallization of Sb was responsible for the changes of optical properties of the films. The results of the blue laser recording test showed that the films had good writing sensitivity for blue laser beam (406.7 nm), and the recording marks were still clear even if the films were deposited in air 60 days, which demonstrated that doping silicon in SbOx films can improve the stability of SbOx films. High reflectivity contrast of about 36% was obtained at a writing power 6 mW and writing pulse width 300 ns. (c) 2007 Elsevier B.V. All rights reserved.

Write-once medium with Fe-Doped BiOx thin films for blue laser recording

Fe:BiOx films are fabricated on K9 glass substrates by rf-magnetron sputtering of a BiFeO target under argon atmosphere with increasing sputtering power from 80 to 200 W at room temperature. It is found that the thin films grown at the sputtering power of 160W can be formed at an appropriate deposition rate and have an improved surface morphology. The XPS result reveals that the films investigated are comprised of Bi, Fe and O elements. A typical XRD pattern shows that no phase transition occurs in the films up to 400 degrees C. The results of the blue laser recording test demonstrate that the Fe:BiOx films have good writing sensitivity for blue laser beam (406.7 nm) and good stability after reading 10000 times. The recording marks of 200nm or less are obtained. These results indicate that the introduction of Fe into BiOx films can reduce the mark size and improve the stability of the films.

氧化铋薄膜用于蓝光可录存储的研究

利用直流磁控溅射法在不同氧氩分压比条件下制备了BiOx薄膜。通过对薄膜在蓝光作用前后的反射率对比度变化的研究发现，氧氩分压比为50％时制备的薄膜具有最佳的光学对比度。利用X射线衍射仪(XRD)、X光电子能谱(XPS)和光谱仪研究了薄膜热处理前后的结构和光谱性质的变化。研究结果表明薄膜光学性质变化主要由薄膜中氧化铋的相变引起。蓝光静态测试结果显示氧氩分压比为50％条件下制备的BiOx薄膜具有很好好的记录敏感度，在11mW的记录功率和800ns的记录脉宽条件下，得到了52％的反射率对比度。此外，BiOx薄膜表现出了非常好的读出稳定性。

Compact continuous-wave blue lasers by direct frequency doubling of laser diodes with periodically poled lithium niobate waveguide crystals

A compact continuous-wave blue laser has been demonstrated by direct frequency doubling of a laser diode with a periodically poled lithium niobate (PPLN) waveguide crystal. The optimum PPLN temperature is near 28 degreesC, and the dependence of waveguide crystals on crystal temperature is less sensitive than that of bulk crystals. A total of 14.8 mW of 488-nm laser power has been achieved. (C) 2005 Optical Society of America.

Optimal recording wavelength for nonvolatile photorefractive holograms in Ce : Cu : LiNbO

Three wavelengths of red, green and blue of recording beams are systemically tested for the UV-assistant recording and optical fixing of holograms in a strongly oxidized Ce:Cu:LiNbO3 crystal. Three different photorefractive phenomena are observed. It is shown that the green beams will optimally generate a critical strong nonvolatile hologram with quick sensitivity and the optimal switching technique could be jointly used to obtain a nearly 100% high diffraction. Theoretical verification is given, and a prescription on the doping densities and on the oxidation/reduction states of the material to match a defined recording wavelength for high diffraction is suggested.

Analysis on the high luminous flux white light from GaN-based laser diode

We fabricated a phosphor-conversion white light using an InGaN laser diode that emits 445 nm and phosphor that emits in the yellow region when excited by the blue laser light. At 500 mA injection current the luminous flux and the luminous efficacy were 113 lm and 44 lm/W, respectively. The relationship of the luminous flux and the luminous efficacy of the white light with an injection current were discussed. Based on the evaluation method for luminous efficacy of light sources established by the Commission International de I'Eclairage (CIE) and the phosphor used in this experiment, a theoretical analysis of the experiment results and the maximum luminous efficacy of this white light fabrication method were also presented.

Structure and properties of amorphous thin film for optical data storage

In this paper the magnetic and magneto-optical properties of amorphous rare earth-transition metal (RE-TM) alloys as well as the magnetic coupling in the multi-layer thin films for high density optical data storage are presented. Using magnetic effect in scanning tunneling microscopy the clusters structure of amorphous RE-TM thin films has been observed and the perpendicular magnetic anisotropy in amorphous RE-TM thin films has been interpreted. Experimental results of quick phase transformation under short pulse laser irradiation of amorphous semiconductor and metallic alloy thin films for phase change optical recording are reported. A step-by-step phase transformation process through metastable states has been observed. The waveform of crystallization propagation in micro-size spot during laser recording in amorphous semiconductor thin films is characterized and quick recording and erasing mechanism for optical data storage with high performance are discussed. The nonlinear optical effects in amorphous alloy thin films have been studied. By photo-thermal effect or third order optical nonlinearity, the optical self-focusing is observed in amorphous mask thin films. The application of amorphous thin films with super-resolution near field structure for high-density optical data storage is performed. (c) 2007 Elsevier B.V. All rights reserved.

半导体激光直接倍频的488nm蓝光激光器

利用波导型准相位匹配周期极化反转铌酸锂（PPLN）晶体直接倍频波长为976nm的连续半导体激光二极管，在最佳晶体工作温度（28℃）下，获得了波长为488nm的连续蓝光输出，最大输出功率大于20mW。所用的晶体尺寸为8mm×1．4mm×1mm，波导截面为4．5μm×3．5μm，极化周期为5．2μm。研究了波导型周期极化反转铌酸锂晶体的倍频效率与温度的关系，与普通的周期极化反转铌酸锂相比，倍频效率与温度关系的敏感度较低。同时，由于晶体可以在室温下工作，简化了加温与温控部件，提高了整机的工作效率。在此实验的基础

The growth and characterization of GaN grown on a gamma-Al2O3/(001) Si substrate by metalorganic vapor phase epitaxy

Wurtzite single crystal GaN films have been grown onto a gamma-Al2O3/Si(001) substrate in a horizontal-type low pressure MOVPE system. A thin gamma-Al2O3 layer is an intermediate layer for the growth of single crystal GaN on Si although it is only an oriented polycrystal film as shown by reflection high electron diffraction. Moreover, the oxide is not yet converted to a fully single crystal film, even at the stage of high temperature for the GaN layer as studied by transmission electron microscopy. Double crystal x-ray linewidth of (0002) peak of the 1.3 mu m sample is 54 arcmin and the films have heavy mosaic structures. A near band edge peaking at 3.4 eV at room temperature is observed by photoluminescence spectroscopy. Raman scattering does not detect any cubic phase coexistence.

Growth and characterization of GaN on LiGaO2 and LiAlO2

The nearly lattice-matched LiGaO2 and LiAlO2 substrates have been used for the growth of GaN by LP-MOVPE. GaN epilayers have been grown on the two substrates at very low input partial pressure of hydrogen and relatively low growth temperature. The difference in the growth rate, crystal and optical qualities of hexagonal GaN epilayers grown on LiAlO2 and LiGaO2 substrate with two polar domains are investigated. LiAlO2 and LiGaO2 single crystal with a single domain structure and an adequate surface plane are promising substrates for the growth of high quality of hexagonal GaN thin films.

Yellow luminescence mechanism and persistent photoconductivity in n-GaN single crystal films grown on alpha-Al2O3(0001) substrates by LP-MOCVD

Unintentionally doped and Si-doped single crystal n-GaN films have been grown on alpha-Al2O3 (0001) substrates by LP-MOCVD. Room temperature photoluminescence measurement showed that besides the bandedges, the spectrum of an undoped sample was a broad deep-level emission band peaking from 2.19 to 2.30eV, whereas the spectrum for a Si-doped sample was composed of a dominant peak of 2.19eV and a shoulder of 2.32eV. At different temperatures, photoconductance buildup and its decay were also observed for both samples.. The likely origins of persistent photoconductivity and yellow luminescence, which might be associated with deep defects inclusive of either Ga vacancy(V-Ga)/Ga vacancy complex induced by impurities or N antisite (N-Ga), will be proposed.

Rare earth doped beta-diketone complexes as promising high-density optical recording materials for blue optoelectronics

Some kinds of rare earth beta-diketone complexes with blue-violet light absorption edge were synthesized using the ligands of thenoyltrifluoroacctone (HTTA), 2, 2'-dipyridyl (BIPY) and different metal ions (Gd3+, Sm3+ and La3+). Their contents, structures and optoelectronic parameters were monitored by elemental analysis, MS, IR and UV spectra. The solubility of rare earth beta-diketone complexes in 2, 2, 3, 3-tetrafluoro-1-propanol (TFP) and absorption properties of their films in the region 300-800 nm were measured. The influence on the difference of absorption maximum from rare earth beta-diketone complexes to beta-diketone ligand by different metal ions was studied. In addition, the thermal stability of rare earth beta-diketone complexes was also reported. (C) 2005 Elsevier B.V. All rights reserved.

Design and construction of a static tester for blue ray optical storage

Blue ray optical storage is one of the important trends in the area of information storage, and attracts a number of researchers. Static tester for blue ray optical storage plays an important role in storage media research. We designed and constructed a static tester, in which modularization makes it very convenient to expand function. Employment of modulation/demodulation technique weakens test error so as to increase test precision. Focus move mode and the nano-positioners facilitate the relocation of recording marks. Only one laser with wavelength 406.7 nm is used. In this paper, system design and characteristics are represented in detail, and some experimental results are also given to show that the static tester can perform successfully, acting as research platform for blue ray optical storage. (c) 2005 Elsevier GmbH. All rights reserved.

UV-blue upconverted emission from Nd3+-doped InF3-based heavy-metal fluoride glasses for blue upconversion fibre laser

We report spectral properties and thermal stability of Nd3+-doped InF3-based heavy-metal fluoride glasses. Fluoroindate glasses in the chemical compositions (in mol%) of (38-x)InF3-16BaF(2)-20ZnF(2)-20SrF(2)-3GdF(3)-1GaF(3-)2NaF-xNdF(3) (x = 0.1, 0.5, 1, 2, 3) have been prepared under a controlled atmosphere in a dry box. Strong UVblue upconversion emission from a green excitation wavelength has been observed and the involved mechanisms have been explained. Near-infrared emission occurs simultaneously upon excitation of the UV-blue upconversion emissions with a cw Ar(+)laser. The upconversion spectra have revealed four dominant emissions at 354, 380, 412 and 449 nm, which belong to the transitions of D-4(3/2) -> I-4(9/2), D-4(3/2) -> I-4(11/2) and P-2(3/2) -> I-4(9/2), D-4(3/2) -> I-4(13/2) and P-2(3/2) -> I-4(11/2), D-4(3/2) -> I-4(15/2) and P-2(3/2) -> I-4(13/2), respectively.