Resumo:
利用飞秒激光对ZnO晶体进行辐照,对辐照前后的晶体样品进行发光光谱及拉曼光谱检测。辐照后发光光谱的某些发光峰强度有明显增强,但未产生新的发光峰,表明没有新的缺陷结构产生,但晶体内锌空位、间隙位锌、间隙位缺陷浓度增加。拉曼光谱结果表明,辐照后ZnO晶体未产生相变,但随着辐照激光功率的增大,拉曼峰327 cm-1,437 cm-1强度明显减弱,表明在飞秒激光辐照作用下氧化锌的结晶程度下降。但574 cm-1峰值却随着辐照功率的增大而变大,分析表明该拉曼峰很可能是由于晶体内间隙位缺陷所致。同时实验过程中观察到飞
Resumo:
Raman scattering experiments for nominally pure and uranium doped CaF2 single crystals were presented. In all crystals, the Raman active T_(2g) vibration mode of CaF2 was observed, whose frequency shift and full-width at half-maximum (FWHM) broadening correspond well with defects and impurities in CaF2 lattice. Additional Raman peaks develop in nominally pure CaF2 with high etch pits density and U^(6+):CaF2 crystals. Part of additional Raman peaks in the experimental results, which are assumed due to vibration modes from F- interstitials and vacancies, are in well agreement with the theoretical predications by employing the Green-function formulation.
Resumo:
The effects of oxygen partial pressure on the structure and photoluminescence (PL) of ZnO films were studied. The films were prepared by direct current (DC) reactive magnetron sputtering with various oxygen concentrations at room temperature. With increasing oxygen ratio, the structure of films changes from zinc and zinc oxide phases, single-phase ZnO, to the (002) orientation, and the mechanical stresses exhibit from tensile stress to compressive stress. Films deposited at higher oxygen pressure show weaker emission intensities, which may result from the decrease of the oxygen vacancies and zinc interstitials in the film. This indicates that the emission in ZnO film originates from the oxygen vacancy and zinc interstitial-related defects. From optical transmittance spectra of ZnO films, the plasma edge shifts towards the shorter wavelength with the improvement of film stoichiometry. (C) 2004 Elsevier B.V. All rights reserved.
Resumo:
Atomic configurations and formation energies of native defects in an unsaturated GaN nanowire grown along the [001] direction and with (100) lateral facets are studied using large-scale ab initio calculation. Cation and anion vacancies, antisites, and interstitials in the neutral charge state are all considered. The configurations of these defects in the core region and outermost surface region of the nanowire are different. The atomic configurations of the defects in the core region are same as those in the bulk GaN, and the formation energy is large. The defects at the surface show different atomic configurations with low formation energy. Starting from a Ga vacancy at the edge of the side plane of the nanowire, a N-N split interstitial is formed after relaxation. As a N site is replaced by a Ga atom in the suboutermost layer, the Ga atom will be expelled out of the outermost layers and leaves a vacancy at the original N site. The Ga interstitial at the outmost surface will diffuse out by interstitialcy mechanism. For all the tested cases N-N split interstitials are easily formed with low formation energy in the nanowires, indicating N-2 molecular will appear in the GaN nanowire, which agrees well with experimental findings.
Resumo:
This paper studies the electronic structure and native defects intransparent conducting oxides CuScO2 and CuYO2 using the first-principle calculations. Some typical native copper-related and oxygen-related defects, such as vacancy, interstitials, and antisites in their relevant charge state are considered. The results of calculation show that, CuMO2 (M = Sc, Y) is impossible to shown-type conductivity ability. It finds that copper vacancy and oxygen interstitial have relatively low formation energy and they are the relevant defects in CuScO2 and CuYO2. Copper vacancy is the most efficient acceptor, and under O-rich condition oxygen antisite also becomes important acceptor and plays an important role in p-type conductivity.
Resumo:
We have systematically investigated the magnetic properties of Si-doped (Ga,Mn)As films. When the Si content is low, both Curie temperature (T-C) and carrier density (p) decrease compared with undoped (Ga,Mn)As, whereas a monotonic increase of T-C and p is observed with further increase in the doping content of Si. We discuss the possible mechanism for the changes obtained by different Si doping contents and attribute the results to a competition between the existence of Si-Ga (Si substitutes for Ga site) that acts as a donor and Si-I (Si interstitials) which is in favor of the improvement of ferromagnetism. (C) 2008 Elsevier B.V. All rights reserved.
Resumo:
Native point defects in the rutile TiO2 are studied via first-principles pseudopotential calculations. Except for the two antisite defects, all the native point defects have low formation energies. Under the Ti-rich growth condition, high concentrations of titanium interstitials and oxygen vacancies would form spontaneously in p-type samples; whereas high concentrations of titanium vacancies would form spontaneously in n-type samples regardless of the oxygen partial pressure. (c) 2007 Elsevier B.V. All rights reserved.
Resumo:
We studied the effects of hydrogen plasma treatment on the electrical and optical properties of ZnO films deposited by radio frequency magnetron sputtering. It is found that the ZnO H film is highly transparent with the average transmittance of 92% in the visible range. Both carrier concentration and mobility are increased after hydrogen plasma treatment, correspondingly, the resistivity of the ZnO H films achieves the order of 10(-3) cm. We suggest that the incorporated hydrogen not only passivates most of the defects and/or acceptors present, but also introduces shallow donor states such as the V-O-H complex and the interstitial hydrogen H-i. Moreover, the annealing data indicate that H-i is unstable in ZnO, while the V-O-H complex remains stable on the whole at 400 degrees C, and the latter diffuses out when the annealing temperature increases to 500 degrees C. These results make ZnO H more attractive for future applications as transparent conducting electrodes.
Resumo:
The depth distribution of the hole density p in 500 nm-thick (Ga,Mn)As layers is investigated. From Raman scattering spectra, it is found that the gradients of p are opposite in the as-grown and annealed layers. At the region around the free surface, with increasing etching depth, p significantly increases in the as-grown layer; however, p decreases distinctly in the annealed layer. Then, in the bulk, p becomes almost homogeneous for both cases. The etching-depth dependence of Curie temperature obtained from magnetic measurements is in agreement with the distribution characterization of p. These results suggest that annealing induces outdiffusion of Mn interstitials towards the free surface, and incomplete outdiffusion during the growth leads to an accumulation of Mn interstitials around the free surface of the as-grown (Ga,Mn)As. (c) 2006 Elsevier B.V. All rights reserved.
Resumo:
Defects in ZnO films grown by radio-frequency reactive magnetron sputtering under variable ratios between oxygen and argon gas have been investigated by using the monoenergetic positron beam technique. The dominate intrinsic defects in these ZnO samples are O vacancies (V-O) and Zn interstitials (Zn-i) when the oxygen fraction in the O-2/Ar feed gas does not exceed 70% in the processing chamber. On the other hand, zinc vacancies are preponderant in the ZnO Elms fabricated in richer oxygen environment. The concentration of zinc vacancies increases with the increasing (2) fraction. For the oxygen fraction 85%, the number of zinc vacancies that could trap positrons will be smaller. It is speculated that some unknown defects could shield zinc vacancies. The concentration of zinc vacancies in the ZnO films varies with the oxygen fraction in the growth chamber, which is in agreement with the results of photoluminescence spectra.
Resumo:
Point defects in III-V compound semiconductors were analyzed systematically in this paper. The effects of substitutes, antisites, interstitials, and vacancies on lattice parameters in III-V compound semiconductors were calculated with a simple model. The formation energies of vacancies in compound semiconductors can be obtained by this calculation. A practical technique established on this model has been utilized for measuring the stoichiometry in GaAs. The relationship between stoichiometry and deep level centers in GaAs was also investigated.
Resumo:
Atomic and electronic properties of N-N split interstitial in GaN nanowires have been investigated using first principles calculations. The formation energy calculations show that the N-N interstitial favors substituting an N atom at the surface of the nanowires. The interstitial induces localized states in the band gap of GaN nanowires.
Resumo:
The influences of arsenic interstitials and dislocations on the lattice parameters of undoped semi-insulating (SI) GaAs single crystals were analyzed. It was shown that the dislocations in such crystals serve as effective gettering sites for arsenic interstitials due to the deformation energy of dislocations. The average excess arsenic in GaAs epilayers grown by molecular-beam epitaxy (MBE) at low temperatures (LT) is about 1%, and the lattice parameters of these epilayers are larger than those of liquid-encapsulated Czochralski-grown (LEG) SI-GaAs by about 0.1%. The atomic ratio, [As]/([Ga] + [As]), in SI-GaAs grown by low-pressure (LP) LEC is the nearest to the strict stoichiometry compared with those grown by high-pressure (HP) LEC and vertical gradient freeze (VGF). After multiple wafer annealing (MWA), the crystals grown by HPLEC become closer to be strictly stoichiometric.
Resumo:
A model for analyzing the correlation between lattice parameters and point defects in semiconductors has been established. The results of this model for analyzing the substitutes in semiconductors are in accordance with those from Vegard's law and experiments. Based on this model, the lattice strains caused by the antisites, the tetrahedral and octahedral single interstitials, and the interstitial couples are analyzed. The superdilation in lattice parameters of GaAs grown at low temperatures by molecular-beam epitaxy can be interpreted by this model, which is in accordance with the experimental results. This model provides a way of analyzing the stoichiometry in bulk and epitaxial compound semiconductors nondestructively.
Resumo:
The structural properties of GaAs grown at low temperatures by molecular beam epitaxy (LTMBE GaAs) were studied. The excess arsenic atoms in LTMBE GaAs exist in the form of arsenic interstitial couples (i,e, two ns atoms share the one host site), and cause an increase in the lattice parameter of LTMBE GaAs. Annealing at above 300 degrees C, the arsenic interstitial couples decomposed, and As precipitates formed, resulting in a decrease in the lattice parameter.