Photoluminescence of erbium-doped hydrogenated amorphous SiOx(0 < x < 2)

Hydrogenated amorphous SiOx films are fabricated via plasma enhanced chemical vapor deposition technique. After erbium implantation and rapid thermal annealing, photoluminescence (PL) are measured at 77 K and room temperature (RT), respectively. We observed the strong PL at 1.54 mu m at RT. The 1.54 mu m PL intensity changes with the variation of concentration of oxygen. The most intense PL at 77 K in a-SiOx:H (Er) corresponds to O/Si = 1.0 and at RT to O/Si = 1.76. Based on our results, we propose that Er ions contributed to PL come from O-rich region in the film. Er ions in Si-rich region have no relation with FL. Temperature dependence of the intensity of the 1.54 mu m line of the Er3+ transition displays a very weak temperature quenching in Er-doped hydrogenated amorphous Si. The PL intensity at 250 K is a little more one half of that at 15 K.

Improvement of thin silicon on sapphire (SOS) film materials and device performances by solid phase epitaxy

The increased emphasis on sub-micron CMOS/SOS devices has placed a demand for high quality thin silicon on sapphire (SOS) films with thickness of the order 100-200 nm. It is demonstrated that the crystalline quality of as-grown thin SOS films by the CVD method can be greatly improved by solid phase epitaxy (SPE) process: implantation of self-silicon ions and subsequent thermal annealing. Subsequent regrowth of this amorphous layer leads to a greater improvement in silicon layer crystallinity and channel carrier mobility, evidenced, respectively, by double crystal X-ray diffraction and electrical measurements. We concluded that the thin SPE SOS films are suitable for application to high-performance CMOS circuitry. (C) 2000 Elsevier Science S.A. All rights reserved.

Void-like defects in annealed Czochralski silicon

Void-like defects of octahedron structure having {111} facets were observed in annealed Czochralski silicon. The amorphous coverage of SiOx and SiCx on the inner surface of the defects was identified using transmission electron microscopy and electron energy-loss spectroscopy. It is suggested that these defects are a kind of amorphous precipitate origin. A mechanism for the generation of these defects and the previously reported solid amorphous precipitates is proposed. (C) 1998 American Institute of Physics. [S0003-6951(98)02842-3].

Heterojunction solar cells with n-type nanocrystalline silicon emitters on p-type c-Si wafers

Hydrogenated nanocrystalline silicon (nc-Si:H) n-layers have been used to prepare heterojunction solar cells on flat p-type crystalline silicon (c-Si) wafers. The nc-Si:H n-layers were deposited by radio-frequency (RF) plasma enhanced chemical vapor deposition (PECVD), and characterized using Raman spectroscopy, optical transmittance and activation energy of dark-conductivity. The nc-Si:H n-layers obtained comprise fine grained nanocrystallites embedded in amorphous matrix, which have a wider bandgap and a smaller activation energy. Heterojunction solar cells incorporated with the nc-Si n-layer were fabricated using configuration of Ag (100 nm)/1T0 (80 nm)/n-nc-Si:H (15 nm)/buffer a-Si:H/p-c-Si (300 mu m)/Al (200 nm), where a very thin intrinsic a-Si:H buffer layer was used to passivate the p-c-Si surface, followed by a hydrogen plasma treatment prior to the deposition of the thin nanocrystalline layer. The results show that heterojunction solar cells subjected to these surface treatments exhibit a remarkable increase in the efficiency, up to 14.1% on an area of 2.43 cm(2). (c) 2006 Elsevier B.V. All rights reserved.

STUDY OF MICROSTRUCTURE AND DEFECTS IN HYDROGENATED MICROCRYSTALLINE SILICON FILMS

Microcrystalline silicon films were deposited by very high frequency (VHF) plasma-enhanced chemical vapor deposition (PECVD) with different hydrogen dilution. The microstructure of these films was investigated using Raman spectroscopy and infrared absorption (IR) spectra. The crystalline, amorphous, and grain boundary volume fractions X-c, X-a and X-gb were estimated from Raman measurements. An interface structure factor (R-if) is proposed to characterize the grain boundary volume fractions in IR spectroscopy. The density of states (DOS) of the microcrystalline crystalline silicon films were studied by phase-shift analysis of modulated photocurrent (MPC) and photoconductivity spectroscopy. It was observed that DOS increases with increasing grain boundary volume fractions, while the values of electron mobility-lifetime product mu T-e(e) disease.

Blue Luminescent Properties of Silicon Nanowires Grown by a Solid-Liquid-Solid Method

Silicon nanowires (SiNWs) were grown directly from n-(111) single-crystal silicon (c-Si) substrate based on a solid-liquid-solid mechanism, and Au film was used as a metallic catalyst. The room temperature photoluminescence properties of SiNWs were observed by an Xe lamp with an exciting wavelength of 350 nm. The results show that the SiNWs exhibit a strongly blue luminescent band in the wavelength range 400-480 nm at an emission peak position of 420 nm. The luminescent mechanism of SiNWs indicates that the blue luminescence is attributed to the oxygen-related defects, which are in SiOx amorphous oxide shells around the crystalline core of SiNWs.

RECRYSTALLIZATION, IMPURITY MIGRATION AND OPTICAL ACTIVATION OF YB-IMPLANTED SILICON INDUCED BY RAPID THERMAL ANNEALING

The rapid thermal annealing temperature dependence of the recrystallization, Yb migration and its optical activation were studied for Yb-implanted silicon. For the annealing regime 800-1000-degrees-C, the Yb segregates both at the crystal/amorphous interface and at the surface, which is different from the usual segregation of Er at the crystal/amorphous interface, and the efficiency of optical activation also increases with annealing temperature. However, the amorphous layer regrows completely and no photoluminescence is observed after the annealing at 1200-degrees-C.

STRUCTURAL DEFECTS AND THEIR ELECTRICAL-ACTIVITY IN GERMANIUM IMPLANTED SILICON

The electrical and structural characteristics of secondary defects in regrown amorphous layers formed in n-type Si(100) with a resistivity of 2 OMEGA cm and 6 OMEGA cm using Ge+ ions, has been studied. The amorphous layers with a thickness of 460 nm are formed by implantation of 1 x 10(15) Ge+ cm-2 at an energy of 400 keV. Both conventional furnace and rapid thermal annealing were used to regrow the amorphous layer and the residual defects have been characterised in terms of their concentration depth distribution and activation energies using C-V and DLTS. Structural information has been obtained from RBS and XTEM. By choosing suitable anneal conditions it is possible to eliminate extended defects, apart from a low concentration of end of range dislocation loops. However, a substantial population of electrically active point defects remain after simple low thermal budget anneals. In a sample implanted with 1 x 10(15) Ge+ cm-2 at 400 keV a region of deep donors approximately 460 nm from the surface is always present When the samples are annealed at higher temperatures (> 850-degrees the total deep donor concentration is reduced by one order of magnitude. Other electrically active defects not observable in the low (750-degrees-C) temperature annealed layers become apparent during anneals at intermediate temperatures.

DIRECT ION-BEAM DEPOSITION OF CARBON-FILMS ON SILICON IN THE ION ENERGY-RANGE OF 15-500 EV

Direct ion beam deposition of carbon films on silicon in the ion energy range of 15-500 eV and temperature range of 25-800-degrees-C has been studied. The work was carried out using mass-separated C+ and CH3+ ions under ultrahigh vacuum. The films were characterized with x-ray photoelectron spectroscopy, Raman spectroscopy, transmission electron microscopy, and transmission electron diffraction analysis. In the initial stage of the deposition, carbon implanted into silicon induced the formation of silicon carbide, even at room temperature. Further carbon ion bombardment then led to the formation of a carbon film. The film properties were sensitive to the deposition temperature but not to the ion energy. Films deposited at room temperature consisted mainly of amorphous carbon. Deposition at a higher temperature, or post-deposition annealing, led to the formation of microcrystalline graphite. A deposition temperature above 800-degrees-C favored the formation of microcrystalline graphite with a preferred orientation in the (0001) direction. No evidence of diamond formation in these films was observed.

INTERFACIAL FORMATION PROCESS AND REACTIONS BETWEEN AU AND HYDROGENATED AMORPHOUS SI STUDIED BY XPS AND AES

Interfacial formation processes and reactions between Au and hydrogenated amorphous Si have been studied by photoemission spectroscopy and Auger electron spectroscopy. A three-dimensional growth of Au metal cluster occurs at initial formation of the Au/a-Si:H interface. When Au deposition exceeds a critical time, Au and Si begin interdiffusing and react to create an Au-Si alloy region. Annealing enhances interdiffusion and a Si-rich region exists on the topmost surface of Au films on a-Si:H.

PHOTOEMISSION-STUDY OF THE INTERFACIAL FORMATION PROCESS AND REACTIONS BETWEEN AL AND HYDROGENATED AMORPHOUS SI

Using photoemission spectroscopy and Auger electron spectroscopy, the interfacial formation process and the reactions between Al and hydrogenated amorphous Si are probed, and annealing behaviors of the Al/a-Si:H system are investigated as well. It is found that a three-dimensional growth of Al metal clusters which includes reacted Al and non-reacted metal Al occurs at the initial Al deposition time, reacted Al and Si alloyed layers exist in the Al/a-Si:H interface, and non-reacted Al makes layer-by-layer growth forming a metal Al layer on the sample surface. The interfacial reactions and element interdiffusion of Al/a-Si:H are promoted under the vacuum annealing.

PHOTOLUMINESCENCE SPECTRUM STUDY OF THE GAAS/SI EPILAYER GROWN BY USING A THIN AMORPHOUS SI FILM AS BUFFER LAYER

Recently, we reported successful growth of high-quality GaAs/Si epilayers by using a very thin amorphous Si film as buffer layer. In this paper, the impurity properties of this kind of GaAs/Si epilayers have been studied by using PL spectrum, SIMS and Hall measurement. Compared to a typical PL spectrum of the GaAs/Si epilayers grown by conventional two-step method, a new peak was observed in our PL spectrum at the energy of 1.462 eV, which is assigned to the band-to-silicon acceptor recombination. The SIMS analysis indicates that the silicon concentration in this kind of GaAs/Si epilayers is about 10(18) cm(-3). But its carrier concentration (about 4 x 10(17) cm(-3)) is lower than the silicon concentration. The lower carrier concentration in this kind of GaAs/Si epilayer can be interpreted both as the result of higher compensation and as the result of the formation of the donor-defect complex. We also found that the high-quality and low-Si-concentration GaAs/Si epilayers can be regrown by using this kind of GaAs/Si epilayer as substrate. The FWHM of the X-ray (004) rocking curve from this regrowth GaAs epilayer is 118 '', it is much less than that of the first growth GaAs epilayer (160 '') and other reports for the GaAs/Si epilayer grown by using conventional two-step method (similar to 200 '').

Raman scattering and infrared absorption of silicon nanocrystals in silicon oxide matrix

Structural dependence on annealing of a-SiOx:H was studied by using infrared absorption and Raman scattering. The appearance of Raman peaks in the range of 513-519cm(-1) after 1170 degreesC annealing was interpreted as the formation nanocrystalline silicon with the sizes from 3-10nm. The Raman spectra also show the existence of amorphous-like silicon phase, which is associated with Si-Si bond re-construction at boundaries of silicon nanocrystallites. The presence of the shoulder at 980cm(-1) of Si-O-Si stretching vibration at 1085cm(-1) in infrared spectra imply that except that SiO2 phase, there is silicon sub-oxide phase in the films annealed at 1170 degreesC. This sub-oxide phase is located at the interface between Si crystallites and SiO2, and thus support the shell model for the mixed structures of Si grains and SiO2 matrix.

Improvement of thin silicon on sapphire (SOS) film materials and device performances by solid phase epitaxy

The increased emphasis on sub-micron CMOS/SOS devices has placed a demand for high quality thin silicon on sapphire (SOS) films with thickness of the order 100-200 nm. It is demonstrated that the crystalline quality of as-grown thin SOS films by the CVD method can be greatly improved by solid phase epitaxy (SPE) process: implantation of self-silicon ions and subsequent thermal annealing. Subsequent regrowth of this amorphous layer leads to a greater improvement in silicon layer crystallinity and channel carrier mobility, evidenced, respectively, by double crystal X-ray diffraction and electrical measurements. We concluded that the thin SPE SOS films are suitable for application to high-performance CMOS circuitry. (C) 2000 Elsevier Science S.A. All rights reserved.

Behavior of crystalline silicon under huge electronic excitations: A transient thermal spike description

Recent experimental works devoted to the phenomena of mixing observed at metallic multilayers Ni/Si irradiated by swift heavy ions irradiations make it necessary to revisit the insensibility of crystalline Si under huge electronic excitations. Knowing that Ni is an insensitive material, such observed mixing would exist only if Si is a sensitive material. In order to extend the study of swift heavy ion effects to semiconductor materials, the experimental results obtained in bulk silicon have been analyzed within the framework of the inelastic thermal spike model. Provided the quenching of a boiling ( or vapor) phase is taken as the criterion of amorphization, the calculations with an electron-phonon coupling constant g(300 K) = 1.8 x 10(12) W/cm(3)/K and an electronic diffusivity D-e(300 K) = 80 cm(2)/s nicely reproduce the size of observed amorphous tracks as well as the electronic energy loss threshold value for their creation, assuming that they result from the quenching of the appearance of a boiling phase along the ion path. Using these parameters for Si in the case of a Ni/Si multilayer, the mixing observed experimentally can be well simulated by the inelastic thermal spike model extended to multilayers, assuming that this occurs in the molten phase created at the Ni interface by energy transfer from Si. (C) 2009 Elsevier B. V. All rights reserved.