倾斜角沉积技术制备ZnS双折射雕塑薄膜

使用倾斜角沉积（GLAD）的电子束蒸发技术，制备了倾斜角度在60°～85°之间的ZnS双折射雕塑薄膜（STF）。使用X射线衍射（XRD）和扫描电镜（SEM）检测了ZnS薄膜的结晶状态和断面形貌，使用Lamda-900分光光度计测量了薄膜在不同的偏振光入射时的透过率。研究发现，室温下倾斜沉积ZnS薄膜断面为倾斜柱状结构，且薄膜的结晶程度不高。在相同的监控厚度时，随倾斜角度增大，沉积到基片上的薄膜厚度逐渐变小，但仍然大于余弦曲线显示的理论厚度。根据偏振光垂直入射时薄膜的透过光谱计算了不同角度沉积的薄膜的折射率

Investigation on microstructure and optical properties of titanium dioxide coatings annealed at various temperature

TiO2 coatings were prepared on fused silica with conventional electron beam evaporation deposition. After TiO2 thin films were annealed at different temperatures for 4 h, several properties were investigated by X-ray diffraction (XRD), spectrometer.. photoelectron spectroscopy (XPS) and AFM. It was found that with the annealing temperature increasing, the transmittance of TiO2 coatings decreased, and the cutoff wavelength shifted to long wavelength in near ultraviolet band. Especially, when coatings were annealed at high temperature, the optical loss is very serious, which can be attributed to the scattering and the absorption of TiO2 coatings. XRD patterns revealed that only anatase phase was observed in TiO2 coatings regardless of the different annealing temperatures. XPS results indicated that the fine chemical shift of TiO2 2p(1/2) should be attributed to existence of oxygen vacancies around Ti+4 ion. The investigation on surface morphology by AFM showed that the RMS of titania thin films gradually increases from less than 0.40 nm to 5.03 nm and it should be ascribed to the growth of titanium dioxide grain size with the increase of annealing temperature. (C) 2005 Elsevier B.V. All rights reserved.

Stress, absorptance and laser-induced damage threshold properties of 355-nm HR coatings

A number of 355-nm Al2O3/MgF2 high-reflectance (HR) coatings were prepared by electron-beam evaporation. The influences of the number of coating layers and deposition temperature on the 355-nm Al2O3/MgF2 HR coatings were investigated. The stress was measured by viewing the substrate deformation before and after coating deposition using an optical interferometer. The laser-induced damage threshold (LIDT) of the samples was measured by a 355-nm Nd:YAG laser with a pulse width of 8 ns. Transmittance and reflectance of the samples were measured by a Lambda 900 spectrometer. It was found that absorptance was the main reason to result in a low LIDT of 355-nm Al2O3/MgF2 HR coatings. The stress in Al2O3/MgF2 HR coatings played an unimportant role in the LIDT, although MgF2 is known to have high tensile stress.

Layer uniformity of glancing angle deposition

Some results of an investigation on the layer thickness uniformity of glancing angle deposition are presented. A zirconia monolayer has been deposited by glancing angle deposition to analyze the layer thickness uniformity. The experimental results indicate that the thickness variation over the substrate is less than 0. 1%, which is considered as good uniformity. It is found that the non-uniformity of experimental results is larger than that of the theoretical results. (c) 2005 Elsevier Ltd. All rights reserved.

Study of Al2O3/MgF2 HR coatings at 355 nm

With the present work we tried to study the effective methods to improve the laser-induced damage threshold (LIDT) and reflectance of HR coatings at 355 nm. The work presented in this paper wits part of an ongoing study about vacuum annealing. It was dedicated to study the effects Of Vacuum annealing with different temperature gradients on the structure, optical properties and laser-induced damage threshold (LIDT) of 355nm Al2O3/MgF2HR coatings. A number of samples were prepared by electron beam evaporation using the same deposition process with an optimal deposition temperature of 280 degrees C. After deposition, samples were annealed in the coating chamber for 3 h with different temperature gradients. Morphologies of the samples were observed by Leica-DMRXE. Microscope, Structure of the samples had been characterized by X-ray diffraction (XRD). Transmittance and reflectance of the samples were measured by Lambda 900 Spectrometer, The LIDT of the samples was measured by a 355 nm Nd:YAG laser with a pulse width of 8 ns. It was found that the temperature gradient of vacuum annealing had significant effects on the morphology, structure, absorption, and LIDT of the samples, (c) 2005 Elsevier Ltd. All rights reserved.

Overcoat dependence of laser-induced damage threshold of 355 nm HR coatings

A series of HR coatings, with and without overcoat, were prepared by electron beam evaporation using the same deposition process. The laser-induced damage threshold (LIDT) was measured by a 355 nm Nd:YAG laser with a pulse width of 8 ns. Damage morphologies of samples were observed by Leica-DMRXE Microscope. The stress was measured by viewing the substrate deformation before and after coatings deposition using an optical interferometer. Reflectance of the samples was measured by Lambda 900 Spectrometer. The theoretical results of electric field distributions of the samples were calculate by thin film design software (TFCalc). It was found that SiO2 overcoat had improved the LIDT greatly, while MgF2 overcoat had little effect on the LIDT because of its high stress in the HR coatings. The damage morphologies were different among HR coatings with and without overcoats. (c) 2005 Elsevier B.V. All rights reserved.

Structure and optical properties of ZnS thin films grown by glancing angle deposition

The glancing angle deposition (GLAD) technique was used to deposit ZnS films by electron beam evaporation method. The cross sectional scanning electron microscopy (SEM) image illustrated a highly orientated microstructure composed of slanted column. The atomic force microscopy (APM) analysis indicated that incident flux angle had significant effects on the nodule size and surface roughness. Under identical nominal thickness, the actual thickness of the GLAD films is related to the incident flux angle. The refractive index and in-plane birefringence of the GLAD ZnS films were discussed, and the maximum bireffingence Delta n = 0.036 was obtained at incident flux angle of alpha = 80 degrees. Therefore, the glancing angle deposition technique is a promising way to create a columnar structure with enhanced birefringent property. (c) 2005 Elsevier B.V. All rights reserved.

Structure and UV emission of nanocrystal ZnO films by thermal oxidation of ZnS films

ZnO films prepared by the thermal oxidation of the ZnS films through thermal evaporation are reported. The as-deposited ZnS films have transformed to ZnO films completely at 400 degrees C. The 400-700 degrees C annealed films with a preferential c-axis (002) orientation have a hexagonal wurtzite structure. The band gap of ZnO films shifts towards longer wavelength with the increase of the annealing temperature. The relationship between the band gap energy of ZnO films and the grain size is discussed. The shift of the band gap energy can be ascribed to the quantum confinement effect in nanocrystal ZnO films. The photoluminescence spectra of ZnO films show a dominant ultraviolet emission and no deep level or trap state defect emission in the green region. It confirms the absence of interstitial zinc or oxygen vacancies in ZnO films. These results indicate that ZnO film prepared by this simple thermal oxidation method is a promising candidate for optoelectronic devices and UV laser. (c) 2005 Elsevier BN. All rights reserved.

Surface morphology and properties of zirconia thin films prepared at different deposition rates

ZrO2 thin films were prepared on BK7 glass substrates by electron beam evaporation deposition method. The influence of deposition rate varying from 1.2 to 6.3 nm s(-1) on surface morphology and other properties of ZrO2 films were examined. With increasing deposition rate, the surface defect density increased. The decrease in half width at full maximum in X-ray diffraction pattern with deposition rate indicates an increase in crystal dimension with increasing deposition rate. Electron beam deposited ZrO2 films are known to be inhomogeneous. From the change of the peak transmittance value, it can be deduced that the inhomogeneity of ZrO2 films strengthened gradually with increasing deposition rate. The type of surface defects changed from nodules to craters when the deposition rate was high enough.

沉积温度对电子束蒸发HfO2薄膜残余应力的影响

采用电子束蒸发沉积方法在BK7玻璃基底和熔融石英基底上沉积了HfO2薄膜，研究了不同沉积温度下的应力变化规律。利用ZYGO干涉仪测量了基片镀膜前后曲率半径的变化，计算了薄膜应力。结果发现在所考察的实验条件下HfO2薄膜的残余应力均为张应力，应力值随沉积温度的升高先增大后减小。两种基底上薄膜的残余应力的主要产生机制不同。对于BK7玻璃基底HfO2薄膜的残余应力起决定作用的是内应力，熔融石英基底上HfO2薄膜的残余应力在较低沉积温度下制备的薄膜起决定作用的是热应力，在沉积温度进一步升高后内应力开始起决定作用。

电子束蒸发制备平板偏振膜激光损伤特性研究

采用电子束蒸发沉积技术制备了平板偏振膜。用Lambda900分光光度计测试了其光学性能。在中心波长1053nm处P偏振光的透过率Tp〉98％，S偏振光的透过率Ts〈0．5％，消光比T，／瓦〉200：1，带宽约为20nm。用波长1064nm，脉宽12ns的脉冲激光进行损伤阈值测试，获得P偏振光的损伤阈值为17．2J／cm^2，S偏振光的损伤阈值为19．6J／cm^2。用Nomarski显微镜对薄膜的损伤形貌进行观察，并用Alpha-500型台阶仪对损伤深度进行测试。结果表明，P偏振光的激光损伤为界面损伤与缺

退火对电子束热蒸发193nm Al2O3/MgF2反射膜性能的影响

设计并镀制了193nm Al2O3/MgF2反射膜,对它们在空气中分别进行了250-400℃的高温退火,测量了样品的透射率光谱曲线和绝对反射率光谱曲线.发现样品在高反射区的总的光学损耗随退火温度的升高而下降,而后趋于饱和.采用总积分散射的方法对样品在不同退火温度下的散射损耗进行了分析,发现随着退火温度的升高散射损耗有所增加.因此,总的光学损耗的下降是由于吸收损耗而不是散射损耗起主导作用.对Al2O3材料的单层膜进行了同等条件的退火处理,由它们光学性能的变化推导出它们的折射率和消光系数的变化,从而解释了相应

电子束蒸发氧化锆薄膜的粗糙度和光散射特性

利用电子束蒸发工艺，以Ag层为衬底，沉积了中心波长为632．8nm的氧化锆（ZrO2）薄膜，膜层厚度在80-480nm范围内变化．研究了不同厚度样品的粗糙度变化规律和表面散射特性．结果发现，随着膜层厚度的逐渐增加．其表面均方根（RMS）粗糙度和总积分散射（TIS）均呈现出先减小后增大的趋势．利用非相关表面粗糙度的散射模型对样品的TIS特性进行了理论计算，所得结果与测量结果相一致．

Defect-induced failure of optical coating filters

Optical filters composed of Ag, Al2O3, and ZnSe films were prepared on BK7 substrates by evaporation. By employing spectrophotometer, microscope, scanning electron microscope (SEM), and energy dispersive spectrum (EDS) analysis, the moisture-dependent stability of the samples was tested. The experimental results revealed that filter failure often occurs initially at defect sites. Small sputtering particles and pinhole are found to be two types of defects that induced the optical coating filter failure. The mechanisms of the defect-induced failure of the filters also are discussed in the article. (C) 2005 Elsevier Ltd. All rights reserved.

HfO2薄膜的结构对抗激光损伤阈值的影响

利用蒸发氧化铪和离子辅助蒸发金属铪反应沉积氧化铪薄膜，对两种工艺下制备的氧化铪薄膜进行光学和结构以及激光损伤特性的研究，实验结果表明，用金属铪反应沉积的氧化铪薄膜不仅结构均匀，并且具有较高的激光损伤阈值．文章对损伤阈值和薄膜的结构及光学特性之间的关系进行了讨论。