Reflectance-difference spectroscopy study of the Fermi-level position of low-temperature-grown GaAs

The results of a reflectance-difference spectroscopy study of GaAs grown on (100) GaAs substrates by low-temperature molecular-beam epitaxy (LT-GaAs) are presented. In-plane optical anisotropy resonances which come from the linear electro-optic effect produced by the surface electric field are observed. The RDS line shape of the resonances clearly shows that the depletion region of LT-GaAs is indeed extremely narrow (much less than 200 Angstrom). The surface potential is obtained from the RDS resonance amplitude without the knowledge of space-charge density. The change of the surface potential with post-growth annealing temperatures reflects a complicated movement of the Fermi level in LT-GaAs. The Fermi level still moves for samples annealed at above 600 degrees C, instead of being pinned to the As precipitates. This behavior can be explained by the dynamic properties of defects in the annealing process.

Investigation of GaAs/AlGaAs interfaces by reflectance-difference spectroscopy

The in-plane optical anisotropy of several GaAs/AlGaAs quantum well samples with different well widths has been measured at room temperature by reflectance-difference spectroscopy (RDS). The RDS line shapes are found to be similar in all the samples examined here, which dominantly consist of two peak-like signals corresponding to 1HH-->1E and 1LH-->1E transition. As the well width is decreased, or the 1 ML InAs layer is inserted at one interface, the intensity of the anisotropy increases quickly. Our detail analysis shows that the anisotropy mainly arises from the anisotropic interface roughness. The results demonstrate that the RDS technique is sensitive to the interface structures.

Detection of indium segregation effects in InGaAs/GaAs quantum wells using reflectance-difference spectrometry

The influence of the Indium segregation on the interface asymmetry in InGaAs/GaAs quantum wells have been studied by reflectance-difference spectroscopy (RDS). It is found that the anisotropy of the 2H1E (2HH --> 1E) transition is very sensitive to the degree of the interface asymmetry. Calculations taking into account indium segregation yield good agreement with the observed anisotropy structures. It demonstrates that the anisotropy intensity ratio of the 1L1E (1LH --> 1E) and 2H1E transitions measured by RDS can be used to characterize the interface asymmetry. (C) 2002 Elsevier Science B.V. All rights reserved.

The two- to three-dimensional growth transition of InAs/GaAs epitaxy layer studied by reflectance difference spectroscopy

In this work, we have adopted reflectance difference spectroscopy to study the evolution of InAs layer grown at different temperatures in GaAs matrix. Associated with the two- to three-dimensional growth transition of InAs layer, the transition energies and the in-plane optical anisotropy of InAs wetting layer exhibit abrupt changes. This provides a new way to decide the critical thickness h(c) for the growth transition. The obtained h(c)s are compared with those determined by atomic force microscope measurement, and discrepancy is found at high temperatures. The origin of the difference is clarified and the variations in hc with temperature are further discussed. (C) 2010 American Institute of Physics. [doi:10.1063/1.3494043]

Difference of ZSM-5 zeolites synthesized with various templates

ZSM-5 zeolites with similar SUM ratio were synthesized successfully using various templates (n-butylamine (BTA), ethylamine (ETA), isopropylamine (IPA), ethylenediamine (EDA), ethanol (ETL), ethanol-ammonium (ETL-AM) and no template (NT)) under hydrothermal conditions. The samples were characterized by XRD, SEM, XRF, NH3-TPD and BET surface area measurements in order to understand the template effects and the differences of the ZSM-5 samples. The synthesis of ZSM-5 with organic templates was relatively easier than those with inorganic templates and without template. SEM results revealed that ZSM-5 synthesized with different templates had different morphology and particle size. The Si/Al ratio and BET specific surface area of the sample with ethanol as template was the lowest. NH3-TPD results showed that the sample synthesized without template had fewer strong acid sites than others. n-Hexane cracking reaction was carried out over the samples to evaluate the catalytic properties. All ZSM-5 zeolites were effective in n-hexane cracking reaction, especially for the sample synthesized without template. (C) 2004 Elsevier B.V. All rights reserved.

Temperature variation through 2000 years in China: An uncertainty analysis of reconstruction and regional difference

Chinese Academy of Sciences [KZCX2-YW-315, KZCX2-YW-Q1-01]; National Natural Science Foundation of China [40625002, 90502009, 200905006]; Office of Science (BER), U. S. Department of Energy ; EU/FP7 [212250]

Study on the difference of photochromic and thermochromic mechanism of ethylenediamine trimolybdate

Ethylenediamine trimolybdate ((C2H10N2)[Mo3O10], denoted as ENTMo) shows unusual photochromic and thermochromic properties. The color of the white ENTMo compounds becomes reddish brown gradually under UV irradiation, and changes gradually to blue-black upon annealing. XRD patterns and FT-IR spectra verify that the crystal structure of the colored samples is almost unchanged except distortion. UV-vis diffuse reflectance spectra (DRS) and ESR spectra of the photochromic and the thermochromic samples could confirm that there must exist difference between thermochromic and photochromic mechanism.

Digital simulation in a thin layer spectroelectrochemical cell with minigrid platinum electrode by microregion approximation explicit finite difference method

The microregion approximation explicit finite difference method is used to simulate cyclic voltammetry of an electrochemical reversible system in a three-dimensional thin layer cell with minigrid platinum electrode. The simulated CV curve and potential scan-absorbance curve were in very good accordance with the experimental results, which differed from those at a plate electrode. The influences of sweep rate, thickness of the thin layer, and mesh size on the peak current and peak separation were also studied by numerical analysis, which give some instruction for choosing experimental conditions or designing a thin layer cell. The critical ratio (1.33) of the diffusion path inside the mesh hole and across the thin layer was also obtained. If the ratio is greater than 1.33 by means of reducing the thickness of a thin layer, the electrochemical property will be far away from the thin layer property.

The effect of pH difference between two phases on the partition of lysozyme in aqueous two-phase system

In the investigation of effect of KSCN on the partitioning of lysozyme in PEG2000/ammonium sulfate aqueous two-phase system, it was found that the KSCN could alter the pH difference between the two phases. and thus affect the partition of lysozyme. The relationship between partition coefficients of lysozyme and pH differences between two phases was discussed.

Dependence of linear electro-optic coefficient on difference in the atomic sizes in zinc blende crystals

Covalent radii of the bonding elements have strong effects on the linear electro-optic coefficients of zinc blende crystals; these effects can be quantitatively determined by investigating the relation between the difference in the atomic sizes rho and the magnitude of the linear electro-optic tensor coefficient r(41). It is interesting to note that for the same cation Zn2+, Ga3+, or In3+ the magnitude of r(41) increases with increased covalent radius of the bonded anion r(beta). Especially with the increasing tendency of the parameter rho, the magnitude of r(41) of crystals that have a same cation will increase suddenly when the value of r(beta) becomes larger. (C) 1997 Academic Press.