Morphological defects and uniformity issues of 4H-SiC homoepitaxial layers grown on off-oriented (0001)Si faces

The morphological defects and uniformity of 4H-SiC epilayers grown by hot wall CVD at 1500 degrees C on off-oriented (0001) Si faces are characterized by atomic force microscope, Nomarski optical microscopy, and Micro-Raman spectroscopy. Typical morphological defects including triangular defects, wavy steps, round pits, and groove defects are observed in mirror-like SiC epilayers. The preparation of the substrate surface is necessary for the growth of high-quality 4H-SiC epitaxial layers with low-surface defect density under optimized growth conditions. (c) 2006 Elsevier Ltd. All rights reserved.

Electron irradiation-induced defects in InP pre-annealed at high temperature

Electron irradiation-induced deep level defects have been studied in InP which has undergone high-temperature annealing in phosphorus and iron phosphide ambients, respectively. In contrast to a high concentration of irradiation-induced defects in as-grown and phosphorus ambient annealed InP, InP pre-annealed in iron phosphide ambient has a very low concentration of defects. The phenomenon has been explained in terms of a faster recombination of radiation-induced defects in the annealed InP. The radiation-induced defects in the annealed InP have been compared and studied. (c) 2006 Elsevier Ltd. All rights reserved.

Growth of high quality semi-insulating InP single crystal by suppression of compensation defects

Deep level defects in as-grown and annealed SI-InP samples were investigated by thermally stimulated current spectroscopy. Correlations between electrical property, compensation ratio, thermal stability and deep defect concentration in SI-InP were revealed. An optimized crystal growth condition for high quality SI-InP was demonstrated based on the experimental results.

Improvement of the electrical property of semi-insulating InP by suppression of compensation defects

Semi-insulating (SI) InP obtained by iron phosphide ambient annealing has very low concentration of deep level defects and better electrical property than SI-InP annealed in phosphorus ambient. The defect suppression phenomenon correlates with Fe diffusion and substitution in the annealing process. Analysis of the experimental result suggests that a high activation ratio of incorporated Fe in InP has an effect of defect suppression in Fe-doped and Fe-diffused SI-InP.

STUDY OF MICROSTRUCTURE AND DEFECTS IN HYDROGENATED MICROCRYSTALLINE SILICON FILMS

Microcrystalline silicon films were deposited by very high frequency (VHF) plasma-enhanced chemical vapor deposition (PECVD) with different hydrogen dilution. The microstructure of these films was investigated using Raman spectroscopy and infrared absorption (IR) spectra. The crystalline, amorphous, and grain boundary volume fractions X-c, X-a and X-gb were estimated from Raman measurements. An interface structure factor (R-if) is proposed to characterize the grain boundary volume fractions in IR spectroscopy. The density of states (DOS) of the microcrystalline crystalline silicon films were studied by phase-shift analysis of modulated photocurrent (MPC) and photoconductivity spectroscopy. It was observed that DOS increases with increasing grain boundary volume fractions, while the values of electron mobility-lifetime product mu T-e(e) disease.

STRUCTURAL DEFECTS AND THEIR ELECTRICAL-ACTIVITY IN GERMANIUM IMPLANTED SILICON

The electrical and structural characteristics of secondary defects in regrown amorphous layers formed in n-type Si(100) with a resistivity of 2 OMEGA cm and 6 OMEGA cm using Ge+ ions, has been studied. The amorphous layers with a thickness of 460 nm are formed by implantation of 1 x 10(15) Ge+ cm-2 at an energy of 400 keV. Both conventional furnace and rapid thermal annealing were used to regrow the amorphous layer and the residual defects have been characterised in terms of their concentration depth distribution and activation energies using C-V and DLTS. Structural information has been obtained from RBS and XTEM. By choosing suitable anneal conditions it is possible to eliminate extended defects, apart from a low concentration of end of range dislocation loops. However, a substantial population of electrically active point defects remain after simple low thermal budget anneals. In a sample implanted with 1 x 10(15) Ge+ cm-2 at 400 keV a region of deep donors approximately 460 nm from the surface is always present When the samples are annealed at higher temperatures (> 850-degrees the total deep donor concentration is reduced by one order of magnitude. Other electrically active defects not observable in the low (750-degrees-C) temperature annealed layers become apparent during anneals at intermediate temperatures.

MANY-BEAM SIMULATIONS AND OBSERVATIONS OF LARGE-ANGLE CONVERGENT-BEAM ELECTRON-DIFFRACTION IMAGING OF CRYSTAL DEFECTS

Many-beam dynamical simulations and observations have been made for large-angle convergent-beam electron diffraction (LACBED) imaging of crystal defects, such as stacking faults and dislocations. The simulations are based on a general matrix formulation of dynamical electron diffraction theory by Peng and Whelan, and the results are compared with experimental LACBED images of stacking faults and dislocations of Si angle crystals. Excellent agreement is achieved.

DELINEATION OF DEFECTS IN SIMOX STRUCTURES USING A CHEMICAL ETCHING TECHNIQUE

Residual defects in the overlayer of fully annealed SIMOX material have been studied by means of a chemical etching technique. The etching procedure has been calibrated and an optimum recipe is reported. Observations using optical microscopy and transmission electron microscopy have been used to quantify the defect densities and good agreement between the two techniques has been established, confirming that the optimised chemical etching process can be used with confidence to determine the dislocation density for values < 10(7) cm-2.

ELECTRICAL CHARACTERS OF OXYGEN DEFECTS IN SILICON SUBJECTED TO INTRINSIC GETTERING TREATMENT

The influence of oxygen defects on the resistivity and mobility of silicon wafers is discussed. Grinding processes were performed on the surfaces of samples in order to obtain the information on interior defects of the samples. Spreading resistivity and Hall measurements prove that SiO(x) complexes alone result in resistivity increase and mobility decrease. Deep level transient spectroscopy experiments prove that SiO(x) complexes alone are electrically active. A mechanism of carrier scattering by electrically active SiO(x) complex is proposed to explain the changes of resistivity and mobility.

AN ANALYSIS OF CHARGE STATES FOR LOCAL VIBRATIONAL-MODES BY OXYGEN DEFECTS IN SEMI-INSULATING GAAS

The high-resolution spectral measurements for new local vibrational modes near 714 cm-1 due to the oxygen defect in semi-insulating GaAs are analyzed on the basis of a model calculation by self-consistent bond orbital approach. Two charge states of oxygen atom with 1 and 2 extra electrons are assigned to be responsible for these local modes. The observed frequencies are explained by the properties of Ga-O-1 and Ga-O-2 bonds and the calculated cohesive energy indicates that the O-2 state is stable. The results are in good agreement with the kinetic analysis.