247 resultados para Single-crystal
Resumo:
In this paper, we investigate the mechanism of tunable parametric superfluorescence (PS) based on the second harmonic generation and parametric processes taking place in the same nonlinear crystal (BBO). The tunable spectra of PS has been generated between 480 nm and 530 nm, which is pumped by the second-harmonic from the high-power Ti: sapphire laser system at 1 kHz repetition rate. We present the generation mechanism of PS theoretically and simulate the process of PS ring using the amplification transfer function. The experiment and the theory show that PS will appear when the phase matching angle for second-harmonic generation is close to the optimal pump angle for optical parametric generation, and then the tunable spectra of PS are generated by slightly adjusting the crystal angle. The result provides a theoretical basis for controlling the generation of PS and quantum entanglement states, which is of great significance for the development of quantum imaging, quantum communications and other applieations.
Resumo:
GaAs single crystals have been grown under high gravity conditions, up to 9g0, by a recrystallization method with decreasing temperature. The impurity striations in GaAs grown under high gravity become weak and indistinct with smaller striation spacings. The dislocation density of surcharge-grown GaAs increases with increase of centrifugal force. The cathodoluminescence results also show worse perfection in the GaAs grown at high gravity than at normal earth gravity.
Resumo:
The deviation from the stoichiometric composition of single-crystal 'Er2Co17' has been determined by theoretical analysis. It is found that the composition of this single-crystal 'Er2Co17' is rich in cobalt, and its real composition is suggested to be Er2-deltaCo17+2 delta (delta = 0.14) on the basis of a comparison of calculations based on the single-ion model with a series of experiments. The values of the Er-Co exchange field H-ex and the crystalline-electric-field (CEF) parameters A(n)(m) at the rare-earth (R) site in the 'Er2Co17' compound are also evaluated at the same time. The experiments provide the following data: the temperature dependence of the spontaneous magnetization of the compounds and the normalized magnetic moment of the Er ion, the magnetization curves dong the crystallographic axes at 4.2 K and 200 K, and the temperature dependence of the magnetization along the crystallographic axes in a field of 4 T.
Resumo:
The wafer processing of Indium Phosphide (InP) is so important that it is getting more and more attentions. Lapping is a basic step just following the ingot cutting. In this paper, the influences of various processing parameters on the lapped wafer quality and lapping rate have been checked, the double-crystal X-ray diffraction results about lapped wafers also were presented here. According to the experimental results, the optimum lapping conditions have been obtained.
Resumo:
C-60 Single crystals grown by a single-temperature-gradient technique were characterized by synchrotron radiation white beam x-ray topography and x-ray double crystal diffraction with Cu K-alpha 1 radiation on conventional x-ray source. The results show that the crystal is rather well crystallized, The x-ray topographies give an evidence of dendritic growth mechanism of C-60 Single crystal, and x-ray double crystal diffraction rocking curve shows that there are mosaic structural defects in the sample. A phase transition st 249+/-1.5% K from a simple cubic to a face centered cubic structure is confirmed by in situ observation of synchrotron radiation white beam x-ray topography with the temperature varing from 230 to 295 K.
Resumo:
High concentrations of Si and Zn were implanted into (0001) AlN bulk crystal grown by the self-seeded physical vapor transport (PVT) method. Cathode luminescence (CL) and photoluminescence (PL) spectroscopy were used to investigate the defects and properties of the implanted AlN. PL spectra of the implanted AlN are dominated by a broad near-band luminescence peak between 200 and 254 nm. After high temperature annealing, implantation induced lattice damages are recovered and the PL intensity increases significantly, suggesting that the implanted impurity Si and Zn occupy lattice site of Al. CL results imply that a 457 nm peak is Al vacancy related. Resistance of the AlN samples is still very high after annealing, indicating a low electrical activation efficiency of the impurity in AlN single crystal.
Resumo:
Unintentionally doped and Si-doped single crystal n-GaN films have been grown on alpha-Al2O3 (0001) substrates by LP-MOCVD. Room temperature photoluminescence measurement showed that besides the bandedges, the spectrum of an undoped sample was a broad deep-level emission band peaking from 2.19 to 2.30eV, whereas the spectrum for a Si-doped sample was composed of a dominant peak of 2.19eV and a shoulder of 2.32eV. At different temperatures, photoconductance buildup and its decay were also observed for both samples.. The likely origins of persistent photoconductivity and yellow luminescence, which might be associated with deep defects inclusive of either Ga vacancy(V-Ga)/Ga vacancy complex induced by impurities or N antisite (N-Ga), will be proposed.
Resumo:
Argon gas, as a protective environment and carrier of latent heat, has an important effect on the temperature distribution in crystals and melts. Numeric simulation is a potent tool for solving engineering problems. In this paper, the relationship between argon gas flow and oxygen concentration in silicon crystals was studied systematically. A flowing stream of argon gas is described by numeric simulation for the first time. Therefore, the results of experiments can be explained, and the optimum argon flow with the lowest oxygen concentration can be achieved. (C) 2002 Elsevier Science B.V. All rights reserved.
Resumo:
Low noise field effect transistors and analogue switch integrated circuits (ICs) have been fabricated in semi-insulating gallium arsenide (SI-GaAs) wafers grown in space by direct ion-implantation. The electrical behaviors of the devices and the ICs have surpassed those fabricated in the terrestrially grown SI-GaAs wafers. The highest gain and the lowest noise of the transistors made from space-grown SI-GaAs wafers are 22.8 dB and 0.78 dB, respectively. The threshold back-gating voltage of the ICs made from space-grown SI-GaAs wafers is better than 8.5 V The con-elation between the characterizations of materials and devices is studied systematically. (C) 2002 COSPAR. Published by Elsevier Science Ltd. All rights reserved.
Resumo:
Controlled vertical drying deposition method was used to make high-quality single crystal close-packed colloidal films formed of different radii polystyrene latex spheres on glass substrates coming from a low concentration water suspension (0.1% volume fraction). Regardless of the spheres radii the film thickness was about 6.3 microns. However, cracks destroyed the crystalline film structure during the colloidal film growth. The effect of particle radius (85-215 nm range) on film cracking was systematically studied using in situ optical fracture monitoring. Primary parallel cracks run along the vertical growth direction, later followed by secondary branched cracks in-between the primary cracks due to residual water evaporation. Quantitative theoretical relationship between the cracks spacing and particles radius was derived and shows good agreement with experimental observations. Normalized cracks spacing is related to a reciprocal ratio of the dimensionless particle radius.