A plasma sputtering decoration route to producing thickness-tunable ZnO/TiO2 core/shell nanorod arrays

We report a radio frequency magnetron sputtering method for producing TiO2 shell coatings directly on the surface of ZnO nanorod arrays. ZnO nanorod arrays were firstly fabricated on transparent conducting oxide substrates by a hydrothermal route, and subsequently decorated with TiO2 by a plasma sputtering deposition process. The core/shell nanorods have single-crystal ZnO cores and anatase TiO2 shells. The shells are homogeneously coated onto the whole ZnO nanorods without thickness change. This approach enables us to tailor the thickness of the TiO2 shell for desired photovoltaic applications on a one-nanometer scale. The function of the TiO2 shell as a blocking layer for increasing charge separation and suppression of the surface recombination was tested in dye-sensitized solar cells. The enhanced photocurrent and open-circuit voltage gave rise to increased photovoltaic efficiency and decreased dark current, indicating successful functioning of the TiO2 shell.

Structural and magnetic properties of insulating Zn1-xCoxO thin films

Cobalt-doped ZnO (Zn1-xCoxO) thin films were fabricated by reactive magnetron cosputtering. The processing conditions were carefully designed to avoid the occurrence of Co precipitations. The films are c-axis oriented, and the solubility limit of Co in ZnO is less than 17%, determined by x-ray diffraction. X-ray photoemission spectroscopy measurements show Co ions have a chemical valance of 2+. In this paper, hysteresis loops were clearly observed for Zn1-xCoxO films at room temperature. The coercive field, as well as saturation magnetization per Co atom, decreases with increasing Co content, within the range of 0.07

Trapping of neutral Rb-87 atoms on an atomchip

We report an experiment of trapping of neutral Rb-87 atoms on a, self-made atomchip. The H-shaped atomchip is made by magnetron sputtering technology, which is different from the atomchip technology of other teams. We collect 3 x 10(6) Rb-87 atoms in the mirror magneto-optical trap (MOT) using the external MOT coils, and 1 X 10(5) Rb-87 atoms are transferred to U-MOT using U-shaped wire in chip and a pair of bias coils.

Analysis on the spin reorientation of GdFeCo/DyFeCo exchange-coupled double-layer films

In this paper, GdFeCo/DyFeCo exchange-coupled double-layer films used for center aperture type magnetically induced super resolution were investigated through experiments and theoretical calculation. The samples were prepared by magnetron sputtering method. The polar Kerr effect was measured to prove the spin reorientation of the readout layer. Theoretical study of magnetization profiles was performed on the basis of the mean-field theory and the continuum model. The theoretical results showed that the magnetization orientation of the readout layer changed gradually from in-plane to out-of-plane with the rise of the temperature. Theoretical analysis explained the experimental results successfully. (c) 2005 Elsevier B.V. All rights reserved.

新型AgInSbTe相变薄膜的结晶活化能研究

利用磁控溅射法制备了新型AgInSbTe相变薄膜，热处理前后的X射线衍射(XRD)表明了薄膜在热作用下从非晶态转变到晶态．通过非晶态薄膜粉末的示差扫描量热(DSC)实验测定了不同升温速率条件下的结晶峰温度，计算了粉末的摩尔结晶活化能、原子激活能和频率因子,从结晶活化能E可以判断出新型AgInSbTe相变薄膜具有较高的结晶速度，可以用于高速可擦重写相变光盘．

Optical properties and structure of Sb-rich AgInSbTe phase change thin films

A new composition content quaternary-alloy-based phase change thin film, Sb-rich AgInSbTe, has been prepared by DC-magnetron sputtering on a K9 glass substrate. After the film has been subsequently annealed at 200degreesC for 30 min, it becomes a crystalline thin film. The diffraction peak of antimony (Sb) are observed by shallow (0.5 degree) x-ray diffraction in the quaternary alloy thin film. The analyses of the measurement from differential scanning calorimetry (DSC) show that the crystallization temperature of the phase change thin film is about 190degreesC and increases with the heating rate. By Kissinger plot, the activation energy for crystallization is determined to be 3.05eV. The reflectivity, refractive index and extinction coefficient of the crystalline and amorphous phase change thin films are presented. The optical absorption coefficient of the phase change thin films as a function of photon energy is obtained from the extinction coefficient. The optical band gaps of the amorphous and crystallization phase change thin films are 0.265eV and 1.127eV, respectively.

激光辐照引起Ge2Sb2Te5非晶态薄膜的电/光性质变化

研究了激光辐照引起Ge2Sb2Te5非晶态薄膜的电/光性质变化,当激光功率为580mW时薄膜的方块电阻有四个数量级（10^7～10^3Ω/□）的突变;对电阻发生突变前、中、后的三个样品进行了XRD测试,结果表明,随着激光功率的增大,薄膜由非晶态向晶态转变,用椭偏仪测试了结构转变前、中、后三个样品的光学常数,在可见光范围内薄膜的光学常数在波长相同情况下有：n（非晶态）〉n（中间态）〉n（晶态）,k（晶态）〉k（中间态）〉k（非晶态）,α（晶态）〉α（中间态）〉α（非晶态）,结合电阻变化曲线和XRD图谱讨论了激光辐照Ge2Sb2Te5非晶态薄膜的电/光性质变化同激光功率和结构转变之间的关系.

Write-once medium with Fe-Doped BiOx thin films for blue laser recording

Fe:BiOx films are fabricated on K9 glass substrates by rf-magnetron sputtering of a BiFeO target under argon atmosphere with increasing sputtering power from 80 to 200 W at room temperature. It is found that the thin films grown at the sputtering power of 160W can be formed at an appropriate deposition rate and have an improved surface morphology. The XPS result reveals that the films investigated are comprised of Bi, Fe and O elements. A typical XRD pattern shows that no phase transition occurs in the films up to 400 degrees C. The results of the blue laser recording test demonstrate that the Fe:BiOx films have good writing sensitivity for blue laser beam (406.7 nm) and good stability after reading 10000 times. The recording marks of 200nm or less are obtained. These results indicate that the introduction of Fe into BiOx films can reduce the mark size and improve the stability of the films.

Si underlayer induced nano-ablation in AgInSbTe thin films

AgInSbTelSi thin films on glass substrates are prepared by dc magnetron sputtering at room temperature. Using Si underlayer as the thermal diffusion layer, the super-resolution nano-ablation holes with a size of 70nm in the AgInSbTe phase change films are obtained by a far-field focused laser experimental setup, with laser wavelength 405nm and objective-lens numerical aperture 0.90. The nano-ablation formation mechanism is analysed and discussed via the thermal diffusion of sample structures.

Structural change of laser-irradiated Ge2Sb2Te5 films studied by electrical property measurement

Sheet resistance of laser-irradiated Ge2Sb2Te5 thin films prepared by magnetron sputtering was measured by the four-point probe method. With increasing laser power the sheet resistance undergoes an abrupt drop from 10(7) to 10(3) Omega/square at about 580 mW. The abrupt drop in resistance is due to the structural change from amorphous to crystalline state as revealed by X-ray diffraction (XRD) study of the samples around the abrupt change point. Crystallized dots were also formed in the amorphous Ge2Sb2Te5 films by focused short pulse laser-irradiated, the resistivities at the crystallized dots and the non-crystallized area are 3.375 x 10(-3) and 2.725 Omega m, sheet resistance is 3.37 x 10(4) and 2.725 x 10(7) Omega/square respectively, deduced from the I-V Curves that is obtained by conductive atomic force microscope (C-AFM). (C) 2008 Elsevier B.V. All rights reserved.

Si（111）衬底上ZnO薄膜的磁控溅射法制备及表征

采用磁控溅射法在(111)单晶硅衬底上沉积了ZnO薄膜，并研究了退火温度对ZnO薄膜晶体质量、晶粒度大小、应力和光致发光谱的影响。X射线衍射(XRD)表明薄膜为高度c轴择优取向。不同退火温度下的ZnO薄膜应力有明显变化。应力分布最为均匀的退火温度为500℃。室温下对ZnO薄膜进行了光谱分析，可观测到明显的紫光发射(波长为380nm左右)。实验结果表明，用磁控溅射法在单晶硅衬底上能获得高质量的ZnO薄膜。

射频磁控溅射法制备TiO2-xNX薄膜的结构性能研究

利用射频磁控溅射法室温下在Si（100）衬底上制备了N掺杂的TiO2薄膜，并且采用x射线衍射（XRD）、X射线光电子能谱（XPS）和透射光谱对薄膜进行了表征。XRD结果表明在纯Ar和N2（33．3％）／Ar气氛下制备的TiO2-xNx薄膜均为单一的金红石相，薄膜结晶性良好，呈高度（211）择优取向，而在N2（50．0％）／Ar下制备的薄膜结晶性明显变差；对于N掺杂的TiO2薄膜，XPS表明部分N原子进入TiO2晶格，并且以N—Ti—O、N—O键以及间隙式N原子形式存在；透射光谱表明掺N后的TiO2薄膜吸收边发生了红移。

非晶硅薄膜制备及其晶化特性研究

用磁控溅射法在K9玻璃上沉积了非晶硅（a—Si）膜和a—Si／Al膜，并将其在流动的N2气氛下进行退火。对退火前后的样品进行Raman光谱、XRD和SEM表征和分析。Raman光谱表明随着退火温度的升高，a-Si膜的散射峰出现了明显的蓝移，但XRD结果表明薄膜仍为非晶态；而a—Si／Al膜在温度很低时就已经开始晶化。

LiGaO_2衬底上ZnO外延膜的结构与光学特性

采用磁控溅射法在(001)、(100)及(010)LiGaO2衬底上制备了ZnO薄膜,通过X射线衍射(XRD)、原子力显微镜(AFM)、透过光谱以及光致发光谱(PL)对薄膜的结构、形貌及光学性质进行了表征。结果表明LiGaO2衬底不同晶面上制备的ZnO薄膜具有不同的择优取向,在(001)(、100)及(010)LiGaO2上分别获得了[0001][、1100]及[1120]取向的ZnO薄膜;不同取向的ZnO薄膜表面形貌差异较大;薄膜在可见光波段具有较高的透过率;在ZnO薄膜的光致发光谱中只观察到了位于378 nm的紫外发射峰,而深能级发射几乎观察不到,(1100)取向的薄膜紫外发射峰强度最大,半高宽也最小,薄膜光致发光性质的差异主要和晶粒尺寸有关。

Growth and characterization of ZnO films on (0 0 1), (1 0 0) and (0 1 0) LiGaO2 substrates

ZnO films were fabricated on LiGaO2 (0 0 1), (10 0) and (0 10) planes by RF magnetron sputtering. The structural, morphological and optical properties of as-grown ZnO films were investigated by X-ray diffraction (XRD), atomic force microscopy (AFM), Raman spectra and photoluminescence (PL) spectra. It is found that the orientation of ZnO films is strongly dependent on the substrate plane. [0 0 0 11, [1 (1) over bar 00] and [11 (2) over bar0] oriented ZnO films are deposited on LiGaO2 (001), (100) and (010), respectively. AFM shows the (0001) ZnO film consists of well-aligned regular hexagonal grains. Raman spectra reveal a tensile stress in the (0 0 0 1) ZnO film and a compressive stress in (110 0) and (112 0) ZnO films. PL spectra of all ZnO films exhibit only a near-band-edge UV emission peak. (C) 2008 Elsevier B.V. All rights reserved.