Fabrication of Nano-structured VOx Film by Low Temperature Ion Beam Sputtering and Reductive Annealing

VOx thin films have been fabricated by low temperature ion beam sputtering and post reductive annealing process. Semiconductor-metal phase transition is observed for the film annealed at 400 degrees C for 2 hours. The film also shows a polycrystal structure with grain size from 50nm to 150nm. The VOx thin films fabricated by this process have a TCR up to -2.7% at room temperature. Our results indicate a promising fabrication method of the nano-structured VOx film with relatively high TCR and semiconductor-metal phase transition.

A DUAL ION-BEAM EPITAXY SYSTEM

The design and characteristics of a dual ion beam epitaxy system (DIBE) are discussed. This system is composed of two beam lines, each providing a mass-separated ion beam converging finally with the other into the target chamber. The ions are decelerated and deposited on a substrate which can be heated to a temperature of 800-degrees-C. Currents of a few hundred microamperes are available for both beams and the deposit energies are in the range from tens to 1000 eV. The pressure of the target chamber during processing is about 7 x 10(-6) Pa. Preliminary experiments have proved that compound semiconductor materials such as GaN can be synthesized using the DIBE system.

X-ray-diffraction study of quasipseudomorphic ErSi1.7 layers formed by channeled ion-beam synthesis

ErSi1.7 layers with high crystalline quality (chi(min) of Er is 1.5%) have been formed by 90 keV Er ion implantation to a dose of 1.6X10(17)/cm(2) at 450 degrees C using channeled implantation. The perpendicular and parallel elastic strain e(perpendicular to)=-0.94%+/-0.02% and e(parallel to)=1.24%+/-0.08% of the heteroepitaxial erbium silicide layers have been measured with symmetric and asymmetric x-ray reflections using a double-crystal x-ray diffractometer. The deduced tetragonal distortion e(T(XRD))=e(parallel to)-e(perpendicular to)=2.18%+/-0.10%, which is consistent with the value e(T(RBS))2.14+/-0.17% deduced from the Rutherford backscattering and channeling measurements. The quasipseudomorphic growth of the epilayer and the stiffness along a and c axes of the epilayer deduced from the x-ray diffraction are discussed.

High-Power and High-Efficiency 650nm-Band AlGaInP Visible Laser Diodes Fabricated by Ion Beam Etching

High power and high-slope efficiency 650nm band real-refractive-index ridge waveguide AlGaInP laser diodes with compressive strained MQW active layer are formed by pure Ar ion beam etching process.Symmetric laser mesas with high perpendicularity,which are impossible to obtain by traditional wet etching method due to the use of a 15°-misoriented substrate,are obtained by this dry etching method.Laser diodes with 4μm wide,600μm long and 10%/90% coat are fabricated.The typical threshold current of these devices is 46mA at room temperature,and a stable fundamental-mode operation over 40mW is obtained.Very high slope efficiency of 1.4W/A at 10mW and 1.1W/A at 40mW are realized.