Ultraviolet-blue electroluminescence from Gd3Ga5O12 : Ag

UV-blue light was obtained from a thin-film electroluminescence device using Gd3Ga5O12:Ag as a light-emitting layer, which was deposited by using electron-beam evaporation. The crystal composition and structure of Gd3Ga5O12:Ag were studied by x-ray powder diffraction, The Gd3Ga5O12:Ag has a photoluminescence emission which peaked at around 397 and 467 nm, which were attributed to the oxide vacancies and Ag+, respectively. The brightness of 32 cd/m(2) was obtained when an alternating voltage of 130 V at 1 kHz was applied. (C) 2000 American Institute of Physics. [S0003-6951(00)05031-2].

Blue-violet photoluminescence from large-scale highly aligned boron carbonitride nanofibers

We report on the strong blue-violet photoluminescence (PL) at room temperature from the large-scale highly aligned boron carbonitride (BCN) nanofibers synthesized by bias-assisted hot filament chemical vapor deposition. The photoluminescence peak wavelength shifts in the range of 470-390 nm by changing the chemical composition of the BCN nanofibers, which shows an interesting blue and violet-light-emitting material with adjustable optical properties. The mechanism for the shift of the PL peaks at room temperature is also discussed. (C) 2000 American Institute of Physics. [S0003-6951(00)04427-2].

Sputtering of ZnO buffer layer on Si for GaN blue light emitting materials

The preparation of high quality ZnO/Si substrates for the growth of GaN blue light emitting materials is considered. ZnO thin films have been deposited on Si(100) and Si(lll) substrates by conventional magnetron sputtering. Morphology, crystallinity and c-axis preferred orientation of ZnO thin films have been investigated by transmitting electron microscopy (TEM), X-ray diffraction (XRD) and X-ray rocking curve (XRC). It is proved that the ZnO thin films have perfect structure. The full-width-at-half-maximum (FWHM) of the ZnO(002) XRC of these films is about 1 degrees, while the minimum is 0.353 degrees. This result is better than the minimum FWHM (about 2 degrees) reported by other research groups. Moreover, comparison and discussion are given on film structure of ZnO/Si(100) and ZnO/Si(lll).

Observation of field-driven blue shift in delta-doped Si n-i-p-i multiple quantum wells

We report the observation of the field-driven blue shift at near absorption edge in the photo-current response spectra of delta-doped Si n-i-p-i multiple quantum wells due to the widening of the effective energy gap. This phenomenon differs from the observed results in GaAs/AlGaAs and GeSi/Si superlattices, because the physical mechanisms of forming energy band in these superlattice samples are different. Our experimental results are interpreted satisfactorily by the theoretical calculation. (C) 1999 Elsevier Science Ltd. All rights reserved.

High-efficiency GaN-based blue LEDs grown on nano-patterned sapphire substrates for solid-state lighting - art. no. 684103

Nano-patterning sapphire substrates technique has been developed for nitrides light-emitting diodes (LEDs) growths. It is expected that the strain induced by the lattice misfits between the GaN epilayers and the sapphire substrates can be effectively accommodated via the nano-trenches. The GaN epilayers grown on the nano-patterned sapphire substrates by a low-pressure metal organic chemical vapor deposition (MOCVD) are characterized by means of scanning electron microscopy (SEM), high-resolution x-ray diffraction (HRXRD) and photoluminescence (PL) techniques. In comparison with the planar sapphire substrate, about 46% increment in device performance is measured for the InGaN/GaN blue LEDs grown on the nano-patterned sapphire substrates.

High-brightness GaN-based blue LEDs grown on a wet-patterned sapphire substrate - art. no. 68410T

Patterning sapphire substrate can relax the stress in the nitride epilayer, reduce the threading dislocation density, and significantly improve device performance. In this article, a wet-etching method for sapphire substrate is developed. The effect of substrate surface topographies on the quality of the GaN epilayers and corresponding device performance are investigated. The GaN epilayers grown on the wet-patterned sapphire substrates by MOCVD are characterized by means of scanning electrical microscopy (SEM), atomic force microscopy (AFM), high-resolution x-ray diffraction (HRXRD), and photoluminescence (PL) techniques. In comparison with the planar sapphire substrate, about a 22% increase in device performance with light output power of 13.31 mW@20mA is measured for the InGaN/GaN blue LEDs grown on the wet-patterned sapphire substrate.

Blue Luminescent Properties of Silicon Nanowires Grown by a Solid-Liquid-Solid Method

Silicon nanowires (SiNWs) were grown directly from n-(111) single-crystal silicon (c-Si) substrate based on a solid-liquid-solid mechanism, and Au film was used as a metallic catalyst. The room temperature photoluminescence properties of SiNWs were observed by an Xe lamp with an exciting wavelength of 350 nm. The results show that the SiNWs exhibit a strongly blue luminescent band in the wavelength range 400-480 nm at an emission peak position of 420 nm. The luminescent mechanism of SiNWs indicates that the blue luminescence is attributed to the oxygen-related defects, which are in SiOx amorphous oxide shells around the crystalline core of SiNWs.

Generation of the high efficiency high peak-power femtosecond blue optical pulse

The analysis and calculation of the compensation for the phase mismatch of the frequency-doubling using the frequency space chirp introduced from prisms are made. The result shows that suitable lens can compensate the phase mismatch in a certain extent resulting from wide femtosecond spectrum when the spectrum is space chirped. By means of this method, the experiment of second harmonic generation is carried out using a home-made femtosecond KLM Ti:sapphire laser and BBO crystal. The conversion efficiency of SHG is 63 %. The average output power of blue light is 320 mW. The central wavelength is 420 nm. The spectrum bandwidth is 5.5 nm. It can sustain the pulse width of 33.6 fs. The tuning range of blue light is 404-420 nm,when the femtosecond Ti:sapphire optical pulse is tuned using the prisms in the cavity.

Room-Temperature Continuous-Wave Operation of InGaN-Based Blue-Violet Laser Diodes with a Lifetime of 15.6 Hours

We report our recent progress of investigations on InGaN-based blue-violet laser diodes (LDs). The room-temperature (RT) cw operation lifetime of LDs has extended to longer than 15.6 h. The LD structure was grown on a c-plane free-standing (FS) GaN substrate by metal organic chemical vapor deposition (MOCVD). The typical threshold current and voltage of LD under RT cw operation are 78 mA and 6.8 V, respectively. The experimental analysis of degradation of LD performances suggests that after aging treatment, the increase of series resistance and threshold current can be mainly attributed to the deterioration of p-type ohmic contact and the decrease of internal quantum efficiency of multiple quantum well (MQW), respectively.

Material Growth and Device Fabrication of GaN-Based Blue-Violet Laser Diodes

Studies on first GaN-based blue-violet laser diodes(LDs) in China mainland are reported.High quality GaN materials as well as GaN-based quantum wells laser structures are grown by metal-organic chemical vapor deposition method.The X-ray double-crystal diffraction rocking curve measurements show the full-width half maximum of 180" and 185" for (0002) symmetric reflection and (10(-1)2) skew reflection,respectively.A room temperature mobility of 850cm2/(V·s) is obtained for a 3μm thick GaN film.Gain guided and ridge geometry waveguide laser diodes are fabricated with cleaved facet mirrors at room temperature under pulse current injection.The lasing wavelength is 405.9nm.A threshold current density of 5kA/cm2 and an output light power over 100mW are obtained for ridge geometry waveguide laser diodes.

Blue-shift photoluminescence from porous InAlAs

A porous InAlAs structure was first obtained by electrochemical etching. Nano-pore arrays were formed when the In0.52Al0.48As membrane was anodized at constant voltages in an HF aqueous solution. These self-assembled structures showed evident blue-shift photoluminescence emissions. While a quantum size effect alone underestimates the blue-shift energy for a sample with a relatively large average pore wall thickness, a novel effect caused by the asymmetric etching is proposed to account for this phenomenon. The results inferred from the x-ray double crystal diffraction are in good agreement with the experimental data.