1 x 4 Ge-on-SOI PIN Photodetector Array for Parallel Optical Interconnects

High-quality Ge film was epitaxially grown on silicon on insulator using the ultrahigh vacuum chemical vapor deposition. In this paper, we demonstrated that the efficient 1 4 germanium-on-silicon p-i-n photodetector arrays with 1.0 mu m Ge film had a responsivity as high as 0.65 A/W at 1.31 mu m and 0.32 A/W at 1.55 mu m, respectively. The dark current density was about 0.75 mA/cm(2) at 0 V and 13.9 mA/cm(2) at 1.0 V reverse bias. The detectors with a diameter of 25 mu m were measured at 1550 nm incident light under 0 V bias, and the result showed that the 3-dB bandwidth is 2.48 GHz. At a reverse bias of 3 V, the bandwidth is about 13.3 GHz. The four devices showed a good consistency.

InGaN/GaN p-i-n Photodiodes Fabricated with Mg-Doped p-InGaN Layer

Mg-doped p-InGaN layers with In composition of about 10% are grown by metalorganic chemical vapor deposition (MOCVD). The effect of the annealing temperature on the p-type behavior of Mg-doped InGaN is studied. It is found that the hole concentration in p-InGaN increases with a rising annealing temperature in the range of 600 850 C, while the hole mobility remains nearly unchanged until the annealing temperature increases up to 750 C, after which it decreases. On the basis of conductive p-type InGaN growth, the p-In0.1Ga0.9N/i-In0.1Ga0.9N/n-GaN junction structure is grown and fabricated into photodiodes. The spectral responsivity of the InGaN/GaN p-i-n photodiodes shows that the peak responsivity at zero bias is in the wavelength range 350-400 nm.

1.55 mu m Ge islands resonant-cavity-enhanced detector with high-reflectivity bottom mirror

A 1.55 mum Ge islands resonant-cavity-enhanced (RCE) detector with high-reflectivity bottom mirror was fabricated by a simple method. The bottom mirror was deposited in the hole formed by anisotropically etching in a basic solution from the back side of the sample with the buried SiO2 layer in silicon-on-insulator substrate as the etch-stop layer. Reflectivity spectrum indicates that the mirror deposited in the hole has a reflectivity as high as 99% in the range of 1.2-1.65 mum. The peak responsivity of the RCE detector at 1543.8 nm is 0.028 mA/W and a full width at half maximum of 5 nm is obtained. Compared with the conventional p-i-n photodetector, the responsivity of RCE detector has a nearly threefold enhancement. (C) 2004 American Institute of Physics.

Influence of Mg content on molecular-beam-epitaxy-grown ZnMgS ultraviolet photodetectors

Zn1-xMgxS-based Schottky barrier ultraviolet (UV) photodetectors were fabricated using the molecular-beam-epitaxy (MBE) technique. The influence of Mg content on MBE-grown Zn1-xMgxS-based UV photodetectors has been investigated in details with a variety of experimental techniques, including photoresponse (PR), capacitance-voltage, deep level transient Fourier spectroscopy (DLTFS) and photoluminescence (PL). The room-temperature PR results show that the abrupt long-wavelength cutoffs covering 325, 305 295. and 270 nm with Mg contents of 16%, 44%, 57%, and 75% in the Zn1-xMgxS active layers, respectively, were achieved. But the responsivity and the external quantum efficiency exhibited a slight decrease with the Mg content increasing. In good agreement with the PR results, both of the integrated intensity of the PL spectra obtained from Zn1-xMgxS thin films with different Mg compositions (x = 31% and 52%, respectively) and the DLTFS spectra obtained from Zn1-xMgxS-based (x = 5% and 45%, respectively) UV photodetector samples clearly revealed a significant concentration increase of the non-radiative deep traps with increasing Mg containing in the ZnMgS active layers. Our experimental results also indicate that the MBE-grown ZnMgS-based photodetectors can offer the promising characteristics for the detection of short-wavelength UV radiation. (C) 2004 Elsevier B.V. All rights reserved.

Long-wavelength SiGe/Si MQW resonant-cavity-enhanced photodiodes (RCE-PD)

Si1-xGex/Si optoelectronic devices are promising for the monolithic integration with silicon-based microelectronics. SiGe/Si MQW RCE-PD (Resonant-Cavity-Enhanced photodiodes) with different structures were investigated in this work. Design and fabrication of top- and bottom-incident RCE-PD, such as growth of SiGe MQW (Multiple Quantum Wells) on Si and SOI (Si on insulator) wafers, bonding between SiGe epitaxial wafer and SOR (Surface Optical Reflector) consisting Of SiO2/Si DBR (Distributed Bragg Reflector) films on Si, and performances of RCE-PD, were presented. The responsivity of 44mA/W at 1.314 mum and the FWHM of 6nm were obtained at bias of 10V. The highest external quantum efficiency measured in the investigation is 4.2%.

Silicon membrane resonant-cavity-enhanced photodetector

A Si resonant-cavity-enhanced (RCE) photodiode was fabricated on a silicon membrane. The Si membrane was formed by etching from the back side of the silicon-on-insulator substrate with the buried SiO2 layer as etch-stop layer. A gold layer was deposited serving as an electrode layer and bottom mirror of the RCE photodiode. The photodiode had an external quantum efficiency of 33.8% at the resonant wavelength of 848 nm and a full width at half maximum (FWHM) of 17 nm. The responsivity was 4.6 times that of a conventional Si p-i-n photodiode with the same absorption layer thickness. (c) 2005 American Institute of Physics.

Tuning of detection wavelength in a resonant-cavity-enhanced quantum-dot-embedded photodiode by changing detection angle

We have fabricated a resonant-cavity-enhanced photodiode (RCE-PD) with InGaAs quantum dots (QDs) as an active medium. This sort of QD-embedded RCE-PD is capable of a peak external quantum efficiency of 32% and responsivity of 0.27A/W at 1.058 mu m with a full width at half maximum (FWHM) of 5 nm. Angle-resolved photocurrent response eventually proves that with the detection angle changing from 0 degrees to 60 degrees, the peak-current wavelength shifts towards the short wavelength side by 37 nm, while the quantum efficiency remains larger than 15%.

Design of a fibre-optic disc accelerometer: theory and experiment

Mechanical principles of fibre-optic disc accelerometers (FODA) different from those assumed in previous calculation methods are presented. An FODA with a high sensitivity of 82 rad/ g and a resonance frequency of 360 Hz is designed and tested. In this system, the minimum measurable demodulation phase of the phase-generated carrier (PGC) is 10(-5) rad, and the minimum acceleration reaches 120 ng theoretically. This kind of FODA, with its high responsivity, all-optic-fibre configuration, small size, light weight and stiff shell housing, ensures effective performance in practice.

Performance improvement of GaN based Schottky barrier ultraviolet photodetector by adding a thin AlGaN window layer

We propose a new structure of GaN based Schottky barrier ultraviolet photodetector, in which a thin n-type AlGaN window layer is added on the conventional n(-)-GaN/n(+)-GaN device structure. The performance of the Schottky barrier ultraviolet photodetector is found to be improved by the new structure. The simulation result shows that the new structure can reduce the negative effect of surface states on the performance of Schottky barrier GaN photodetectors, improving the quantum efficiency and decreasing the dark current. The investigations suggest that the new photodetector can exhibit a better responsivity by choosing a suitably high carrier concentration and thin thickness for the AlGaN window layer.

Visible blind p(+)-pi-n(-)-n(+) ultraviolet photodetectors based on 4H-SiC homoepilayers

p(+)-pi-n(-)-n(+) ultraviolet photodetectors based on 4H-SiC homoepilayers have been presented. The growth of the 4H-SiC homoepilayers was carried out in a LPCVD system. The size of the active area of the photodetectors was 300 x 300 mu m(2). The dark and illuminated I-V characteristics had been measured at reverse biases form 0 to 20 V at room temperature, and the illuminated current was at least two orders of magnitude than that of dark current below 13 V bias. The peak value zones of the photoresponse were located at 280-310 nm at different reverse biases, and the peak value located at 300 nm was 100 times greater than the cut-off response value in 380 nm at a bias of 10V, which showed the device had good visible blind performance. A small red-shift about 5 nm on the peak responsivity occurred when reverse bias increased from 5 to 15 V. (c) 2006 Elsevier Ltd. All rights reserved.

High-performance 1.55 mu m low-temperature-grown GaAs resonant-cavity-enhanced photodetector

A 1.55 mu m low-temperature-grown GaAs (LT-GaAs) photodetector with a resonant-cavityenhanced structure was designed and fabricated. A LT-GaAs layer grown at 200 degrees C was used as the absorption layer. Twenty- and fifteen-pair GaAs/AlAs-distributed Bragg reflectors were grown as the bottom and top mirrors. A responsivity of 7.1 mA/W with a full width at half maximum of 4 nm was obtained at 1.61 mu m. The dark current densities are 1.28x10(-7) A/cm(2) at the bias of 0 V and 3.5x10(-5) A/cm(2) at the reverse bias of 4.0 V. The transient response measurement showed that the photocarrier lifetime in LT-GaAs is 220 fs. (c) 2006 American Institute of Physics.

Liquid-phase-epitaxy-grown InAsxSb1-x/GaAs for room-temperature 8-12 mu m infrared detectors

High-quality InAsxSb1-x (0 < x <= 0.3) films are grown on GaAs substrates by liquid phase epitaxy and electrical and optical properties of the films are investigated, revealing that the films exhibit Hall mobilities higher than 2x10(4) cm(2) V-1 s(-1) and cutoff wavelengths longer than 10 mu m at room temperature (RT). Photoconductors are fabricated from the films, and notable photoresponses beyond 8 mu m are observed at RT. In particular, for an InAs0.3Sb0.7 film, a photoresponse of up to 13 mu m with a maximum responsivity of 0.26 V/W is obtained at RT. Hence, the InAsxSb1-x films demonstrate attractive properties suitable for room-temperature, long-wavelength infrared detectors. (c) 2006 American Institute of Physics.

1.55-mu m resonant cavity enhanced photodiode based on MBE grown Ge quantum dots

Self-assembly Ge quantum dots (QD) on Si and Si/Ge mutli-quantum-wells (MQW) are grown by MBE. The island size and island density was investigated by atomics force microscopy. Ten-layer and twenty-layer MQW were selected for photodiode device fabrication. In photoluminescence (PL), a broad peak around 1.55-mu m wavelength was observed with higher peak intensity for the 10-layer MQW which had less defects than the 20-layer sample. Resonant cavity enhanced (RCE) photodiodes were fabricated by bonding on a SOI wafer. Selected responsivity at 1.55 mu m was successfully demonstrated. (c) 2005 Elsevier B.V. All rights reserved.

Fabrication of Ge nano-dot heterojunction phototransistors for improved light detection at 1.55 mu m

Heterojunction phototransistors (HPTs) with several Ge/Si nano-dot layers as the absorption region are fabricated to obtain improved light detectivity at 1.55 mu m. The HPT detectors are of n-p-n type with ten layers of Ge(8ML)/Si(45nm) incorporated in the base-collector junction and are grown by an ultrahigh-vacuum chemical-vapor deposition system. The detectors are operated with normal incidence. Because of the good quality of the grown material and fabrication process, the dark current is only 0.71pA/mu m(2) under 5 V bias and the break-down voltage is over 20 V. Compared to the positive-intrinsic-negative (PIN) reference detector with the same absorption layer, the responsivity is improved over 17 times for normal incidence at 1.55 mu m.

Metal-semiconductor-metal ultraviolet photodetector based on GaN

A metal-semiconductor-metal (MSM) ultraviolet photodetector has been fabricated using unintentionally doped n-GaN films grown on sapphire substrates. Its dark current, photocurrent under the illumination with lambda = 360 nm light, responsivity, and the dependence of responsivity on bias voltage were measured at room temperature. The dark current of the photodetector is 1.03 nA under 5 V bias, and is 15.3 nA under 10 V bias. A maximum responsivity of 0.166 A/W has been achieved under the illumination with lambda = 366 nm light and 15 V bias. It exhibits a typical sharp band-edge cutoff at the wavelength of 366 nm, and a high responsivity at the wavelength from 320 nm to 366 nm. Its responsivity under the illumination with lambda = 360 nm light increases when the bias voltage increases.