Ferromagnetic modification of GaN film by Cu+ ions implantation

The structural and magnetic properties of Cu+ ions-implanted GaN films have been reported. Eighty kilo-electron-volt Cu+ ions were implanted into n-type GaN film at room temperature with fluences ranging from 1 x 10(16) to 8 x 10(16) cm(-2) and subsequently annealed at 800 degrees C for 1 h in N-2 ambient. PIXE was employed to determine the Cu-implanted content. The magnetic property was measured by the Quantum Design MPMS SQUID magnetometer. No secondary phases or clusters were detected within the sensitivity of XRD. Raman spectrum measurement showed that the Cu ions incorporated into the crystal lattice positions of GaN through substitution of Ga atoms. Apparent ferromagnetic hysteresis loops measured at 10 K were presented. The experimental result showed that the ferromagnetic signal strongly increased with Cu-implanted fluence from 1 x 10(16) to 8 x 10(16) cm(-2).

Growth parameter dependence of magnetic property of CrAs thin film

This paper has systematically investigated the substrate temperature and thickness dependence of surface morphology and magnetic property of CrAs compound films grown on GaAs by molecular-beam epitaxy. It finds that the substrate temperature affects the surface morphology and magnetic property of CrAs thin film more potently than the thickness.

PIXE analysis of Fe content in Fe-implanted GaN film

The diluted magnetic semiconductors (DMSs) were achieved by the ion implantation. Fe+ ions (250 keV) were implanted into n-type GaN at room temperature with doses ranging from 8 X 10(15) cm(-2) to 8 X 10(16) cm(-2) and subsequently rapidly annealed at 800 degrees C for 5 m in N-2 ambient. PIXE was employed to determine the Fe-implanted content. The magnetic property was measured by the Quantum Design MPMS SQUID magnetometer. No secondary phases or clusters are detected within the sensitivity of XRD. Apparent ferromagnetic hysteresis loops measured at 10 K were presented. The relationships between the Fe-implanted content and the ferromagnetic property are discussed. (c) 2006 Elsevier B.V. All rights reserved.

Study on optical band gap of boron-doped nc-Si : H film

The optical band gap (E-g) of the boron (B)-doped hydrogenated nano-crystalline silicon (nc-Si:H) films fabricated using plasma enhanced chemical vapor deposition (PECVD) was investigated in this work. The transmittance of the films were measured by spectrophotometric and the E-g was evaluated utilizing three different relations for comparison, namely: alphahnu=C(hnu-E-g)(3), alphahnu=B-0(hnu-E-g)(2), alphahnu=C-0(hnu-E-g)(2). Result showed that E-g decreases with the increasing of Boron doping ratio, hydrogen concentration, and substrate's temperature (T-s), respectively. E-g raises up with rf power density (P-d) from 0.45W.cm(-2) to 0.60w.cm(-2) and then drops to the end. These can be explained for E-g decreases with disorder in the films.

EFFECT OF TOTAL HYDROGEN CONTENT IN SILICON-NITRIDE SENSITIVE FILM ON PERFORMANCE OF ISFET

Quantitative determinations of the hydrogen content and its profile in silicon nitride sensitive films by the method of resonant nuclear reaction have been carried out. At a deposition temperature of 825-degrees-C, hydrogen exists in an LPCVD silicon nitride sensitive film and the hydrogen content on its surface is in the range (8-16) x 10(21) cm-3, depending on the different deposition processes used. This hydrogen content is larger than the (2-3) x 10(21) cm-3 in its interior part, which is homogeneous. Meanwhile, we observe separate peaks for the chemical bonding configurations of Si-H and N-H bonds, indicated by the infrared absorption bands Si-O (1106 cm-1), N-H (1200 cm-1), Si-H-3 (2258 cm-1) and N-H-2 (3349 cm-1), respectively. The worse linear range of the ISFET is caused by the presence of oxygen on the surface of the silicon nitride sensitive film. The existence of chemical bonding configurations of Si-H, N-H and N-Si on its surfaces is favourable for its pH response.

Study on optical band gap of boron-doped nc-Si : H film

The optical band gap (E-g) of the boron (B)-doped hydrogenated nano-crystalline silicon (nc-Si:H) films fabricated using plasma enhanced chemical vapor deposition (PECVD) was investigated in this work. The transmittance of the films were measured by spectrophotometric and the E-g was evaluated utilizing three different relations for comparison, namely: alphahnu=C(hnu-E-g)(3), alphahnu=B-0(hnu-E-g)(2), alphahnu=C-0(hnu-E-g)(2). Result showed that E-g decreases with the increasing of Boron doping ratio, hydrogen concentration, and substrate's temperature (T-s), respectively. E-g raises up with rf power density (P-d) from 0.45W.cm(-2) to 0.60w.cm(-2) and then drops to the end. These can be explained for E-g decreases with disorder in the films.

Polyamide thin film composite membranes prepared from isomeric biphenyl tetraacyl chloride and m-phenylenediamine

Three novel of isomeric tetra-functional biphenyl acid chloride: 3,3',5,5'-biphenyl tetraacyl chloride (mm-BTEC), 2,2',4,4'-biphenyl tetraacyl chloride (om-BTEC), and 2,2',5,5'-biphenyl tetraacyl chloride (op-BTEC) were synthesized, and used as new monomers for the preparation of the thin film composite (TFC) reverse osmosis (RO) membranes through interfacial polymerization with m-phenylenediamine (MPDA). The results of membrane performance test showed that membranes prepared from om-BTEC and op-BTEC had higher flux at the expanse of rejection compared with membranes prepared from mm-BTEC.

Pyrazine-containing Acene-Type Molecular Ribbons with up to 16 Rectilinearly Arranged Fused Aromatic Rings

A series of acene-type conjugated molecules(1-5) containing 2-6 pyrazine units and up to 16 rectilinearly arranged fused aromatic rings were synthesized by condensation coupling of 1,2-diamines and 1,2-diketones. The energy gap of the molecules estimated from absorption edge decreases with an increase in molecular length, indicating the well-delocalized nature of the molecules. The cyclic voltarnmetry measurements suggest that the n-type properties of these ribbonlike pyrazine derivatives are dependent on the molecular length and the number of the pyrazine units.

Square lamellar structure having phase-separated microdomain in H-shaped block copolymer thin film

The morphology of a H-shaped block copolymer (poly(ethylene glycol) backbone and polystyrene branches (PS)(2)PEG(PS)(2)) in a thin film has been investigated. A peculiar square lamella that has a phase-separated microdomain at its surface is obtained after spin coating. The experimental temperature plays a critical role in the lamellar formation. The copolymer first self-assembles into square lamellar micelles with an incomplete crystalline core due to the crystallizability of PEG.

Carbon nanotube/gold nanoparticles/polyethylenimine-functionalized ionic liquid thin film composites for glucose biosensing

A novel glucose biosensor based on immobilization of glucose oxidase (GOD) in thin films of polyethylenimine-functionalized ionic liquid (PFIL), containing a mixture of carbon nanotubes (CNT) and gold nanoparticles (AuNPs) and deposited on glassy carbon electrodes, was developed. Direct electrochemistry of glucose oxidase in the film was observed, with linear glucose response up to 12 mM. The PFIL-stabilized gold nanoparticles had a diameter of 2.4 +/- 0.8 nm and exhibited favorable stability (stored even over one month with invisible change in UV-vis spectroscopic measurements).

Order-Order Transition of C -> sdG -> sL -> S in ABC Triblock Copolymer Thin Film Induced by Solvent Vapor

The morphology transition of polystyrene-block-poly(butadiene)-block-poly(2-vinylpyridine) (SBV) triblock thin film induced in benzene vapor showing weak selectivity for PS is investigated. The order-order transitions (OOT) in the sequence of core-shell cylinders (C), sphere in 'diblock gyroid' (sdG), sphere in lamella (sL) and sphere (S) are observed. The projection along (111) direction in Gyroid phase (sdG(111)) is found to epitaxially grow from C(001) in the film.

Very low hysteresis organic thin-film transistors

Very low hysteresis vanadyl-phthalocyanine/para-sexiphenyl thin-film transistors (TFTs) have been fabricated using benzocyclobutenone (BCBO) derivatives/tantalum pentoxide (Ta2O5)/BCBO triple gate dielectrics. The field effect mobility, on/off current ratio and threshold voltage of organic TFTs are 0.45 cm(2) V-1 s(-1), 3.5 x 10(4) and -6.8 V, respectively. To clarify the mechanism of hysteresis, devices with different dielectrics have been studied. It is found that the bottom BCBO derivatives (contact with a gate electrode) block the electron injection from a gate electrode to dielectrics.

Weak Epitaxy Growth of Copper Hexadecafluorophthalocyanine (F16CuPc) on p-Sexiphenyl Monolayer Film

Weak epitaxy growth (WEG) behavior and mechanism of copper hexadecafluorophthalocyanine (F16CuPc) on p-sexiphenyl (p-6P) monolayer film were investigated by atomic force microscopy (AFM), selected area electron diffraction (SEAD), and wide-angle X-ray diffraction (WAXD). High-quality F16CuPc films with high order, large size, and molecular-level smoothness were obtained successfully by WEG method. It was identified that there exists incommensurate epitaxial relation between highly oriented F16CuPc and p-6P films. The geometrical channels of p-6P monolayer surface induce the nucleation and growth of F16CuPc molecules.

The first liquid crystalline phthalocyanine derivative capable of edge-on alignment for solution processed organic thin-film transistors

Tetraoctyl-substituted vanadyl phthalocyanine (OVPc4C8) as a new NIR-absorbing discotic liquid crystalline material can form highly ordered thin films with edge-on alignment of the molecules and molecular packing mode identical to that in the phase II of OVPc for solution processed OTFTs with mobility up to 0.017 cm(2) V-1 s(-1).

Nonenzymatic glucose sensor based on renewable electrospun Ni nanoparticle-loaded carbon nanofiber paste electrode

A novel nonenzymatic glucose sensor was developed based on the renewable Ni nanoparticle-loaded carbon nanofiber paste (NiCFP) electrode. The NiCF nanocomposite was prepared by combination of electrospinning technique with thermal treatment method. The scanning electron microscopy (SEM) and transmission electron microscopy (TEM) images showed that large amounts of spherical nanoparticles were well dispersed on the surface or embedded in the carbon nanofibers. And the nanoparticles were composed of Ni and NiO, as revealed by energy dispersive X-ray spectroscopy (EDX) and X-ray powder diffraction (XRD). In application to nonenzymatic glucose determination, the renewable NiCFP electrodes, which were constructed by simply mixing the electrospun nanocomposite with mineral oil, exhibited strong and fast amperometric response without being poisoned by chloride ions. Low detection limit of 1 mu M with wide linear range from 2 mu M to 2.5 mM (R = 0.9997) could be obtained.