mc-Si : H/c-Si solar cell prepared by PECVD

Hetero-junction solar cells with an me-Si: H window layer were achieved. The open voltage is increased while short current is decreased with increasing the mc-Si:H layer's thickness of emitter layer. The highest of V-oc of 597 mV has obtained. When fixed the thickness of 30 nm, changing the N type from amorphous silicon layer to micro-crystalline layer, the efficiency of the hetero-junction solar cells is increased. Although the hydrogen etching before deposition enables the c-Si substrates to become rough by AFM images, it enhances the formation of epitaxial-like micro-crystalline silicon and better parameters of solar cell can be obtained by implying this process. The best result of efficiency is 13.86% with the V-oc of 549.8 mV, J(sc) of 32.19 mA center dot cm(-2) and the cell's area of 1 cm(2).

PIXE analysis of Fe content in Fe-implanted GaN film

The diluted magnetic semiconductors (DMSs) were achieved by the ion implantation. Fe+ ions (250 keV) were implanted into n-type GaN at room temperature with doses ranging from 8 X 10(15) cm(-2) to 8 X 10(16) cm(-2) and subsequently rapidly annealed at 800 degrees C for 5 m in N-2 ambient. PIXE was employed to determine the Fe-implanted content. The magnetic property was measured by the Quantum Design MPMS SQUID magnetometer. No secondary phases or clusters are detected within the sensitivity of XRD. Apparent ferromagnetic hysteresis loops measured at 10 K were presented. The relationships between the Fe-implanted content and the ferromagnetic property are discussed. (c) 2006 Elsevier B.V. All rights reserved.

Local environment of Er3+ in Er-doped Si nanoclusters embedded in SiO2 films

The local environment of Er3+ in heavily Er-doped (Er, 2.5 at. %) Si nanoclusters embedded in SiO2 films annealed at various temperatures was investigated by using the fluorescence-extended x-ray absorption fine structure spectroscopy. The results show that annealing caused a large effect on the local environment of Er3+ surrounded by O atoms and the 1.54 mu m photoluminescence intensity. The correlation between the local environment around Er3+ and the corresponding 1.54 mu m photoluminescence was discussed. (c) 2006 American Institute of Physics.

Strong room-temperature ferromagnetism in Cu-implanted nonpolar GaN films

This work was supported by the Natural Science Foundation of China (Grant No. 60876068) and The Project sponsored by SRF for ROCS (Grant No. 08Y1010000), SEM

Strain-induced anodization of SiGe/Si multiple layers to form high density SiGe/Si heterogeneous nanorods

Nation Natural Science Foundation of China 50672079 60676027 60837001 60776007; National Basic Research Program of China (973 Program) 2007CB613404; China-MOST International Sci & Tech Cooperation and Exchange 2008DFA51230

ZnO thin films on Si(111) grown by pulsed laser deposition from metallic Zn target

ZnO thin films with highly c-axis orientation have been fabricated on p-type Si(1 1 1) substrates at 400 degrees C by pulsed laser deposition (PLD) from a metallic Zn target with oxygen pressures between 0.1 and 0.7 mbar. Experimental results indicate that the films deposited at 0.3 and 0.5 mbar have better crystalline and optical quality and flatter surfaces than the films prepared at other pressures. The full width at half maximum (FWHM) of (0 0 0 2) diffraction peak decreases remarkably from 0.46 to 0.19 degrees with increasing annealing temperature for the film prepared at 0.3 mbar. In photoluminescence (PL) spectra at room temperature, the annealed film at 700 degrees C exhibits a smaller ultraviolet (UV) peak FWHM of 108 meV than the as-grown film (119 meV). However, an enhanced deep-level emission is observed. Possible origins to above results are discussed. (c) 2006 Elsevier B.V. All rights reserved.

Nonlinear optical response of nc-Si-SiO2 films studied with femtosecond four-wave mixing technique

Nonlinear optical properties of silicon nanocrystals (nc-Si) embedded in SiO2 films are investigated using time-resolved four-wave mixing technique with a femtosecond laser. the off-resonant third-order nonlinear susceptibility chi((3)) is observed to be 1.3 x 10(-10) esu at 800 nm. The relaxation time of the film is fast as short as 50 fs. The off-resonant nonlinearity is predominantly electronic in origin and enhanced due to quantum confinement.

High quality microcrystalline Si films by hydrogen dilution profile

Novel hydrogen dilution profiling (HDP) technique was developed to improve the uniformity in the growth direction of mu c-Si:H thin films prepared by hot wire chemical vapor deposition (HWCVD). It was found that the high H dilution ratio reduces the incubation layer from 30 nm to less than 10 nm. A proper design of hydrogen dilution profiling improves the uniformity of crystalline content, X-c, in the growth direction and restrains the formation of micro-voids as well. As a result the compactness of mu c-Si:H films with a high crystalline content is enhanced and the stability of mu c-Si:H thin film against the oxygen diffusion is much improved. Meanwhile the HDP mu c-Si:H films exhibit the low defect states. The high nucleation density from high hydrogen dilution at early stage is a critical parameter to improve the quality of mu c-Si:H films. (c) 2006 Published by Elsevier B.V.

Comparison between double crystals X-ray diffraction micro-Raman measurement on composition determination of high Ge content Si1_xGex layer epitaxied on Si substrate

It is important to acquire the composition of Si1-xGex layer, especially that with high Ge content, epitaxied on Si substrate. Two nondestructive examination methods, double crystals X-ray diffraction (DCXRD) and micro-Raman measurement, were introduced comparatively to determine x value in Si1-xGex: layer, which show that while the two methods are consistent with each other when x is low, the results obtained from double crystals X-ray diffraction are not credible due to the large strain relaxation occurring in Si1-xGex layers when Ge content is higher than about 20%. Micro-Raman measurement is more appropriate for determining high Ge content than DCXRD.

Electro-optic coefficients of Si0.75Ge0.25/Si/Si0.5Ge0.5 asymmetric superlattice measured by polarization-maintaining fiber-optic Mach-Zehnder interferometer

Ten-period 5.5 nm Si0.75Ge0.25/10.3 nm Si/2.5 nm Si0.5Ge0.5 trilayer asymmetric superlattice was prepared on Si (001) substrate by ultrahigh vacuum chemical vapor deposition at 500 degrees C. The stability of Mach-Zehnder interferometer was improved by utilizing polarization-maintaining fibers. According to the electro-optic responses of the superlattice with the light polarization along [110] and [-110], respectively, both electro-optic coefficients gamma(13) and gamma(63) of such asymmetric superlattice were measured. gamma(13) and gamma(63) are 2.4x10(-11) and 1.3x10(-11) cm/V, respectively, with the incident light wavelength at 1.55 mu m. (c) 2006 American Institute of Physics.

Strain analysis of InP/InGaAsP wafer bonded on Si by X-ray double crystalline diffraction

Wafer bonding between p-Si and an n-InP-based InGaAsP multiple quantum well (MQW) wafer was achieved by a direct wafer bonding method. In order to investigate the strain at different annealing temperatures, four pre-bonded pairs were selected, and pair one was annealed at 150 degrees C, pair two at 250 degrees C, pair three at 350 degrees C, and pair four at 450 degrees C, respectively. The macroscopical strains on the bonded epitaxial layer include two parts, namely the internal strain and the strain caused by the mismatching of the crystalline orientation between InP (100) and Si (100). These strains were measured by the X-ray double crystalline diffraction, and theoretical calculations of the longitudinal and perpendicular thermal strains at different annealing temperatures were calculated using the bi-metal thermostats model, both the internal strain and the thermal strain increase with the annealing temperature. Normal thermal stress and the elastic biaxial thermal strain energy were also calculated using this model. (c) 2006 Elsevier B.V. All rights reserved.

Effects of edge dislocations and intentional Si doping on the electron mobility of n-type GaN films

The effects of dislocations and Si doping on the electrical properties of n-type GaN grown by metal organic chemical vapor deposition (MOCVD) are investigated. It is found that both electron mobility and carrier concentration are strongly influenced by edge dislocations. A moderate Si doping during the GaN growth improves the electron mobility, but the best doping effect depends on the dislocation density of the sample. High quality about 4-mu m-thick MOCVD-grown GaN film with a room temperature electron mobility as high as 1005 cm(2)/V s is obtained by optimizing growth conditions. (c) 2006 American Institute of Physics.

Reduction of dislocations in GaN epilayer grown on Si (111) substrates using a GaN intermedial layer

GaN intermedial layers grown under different pressures are inserted between GaN epilayers and AlN/Si(111) substrates. In situ optical reflectivity measurements show that a transition from the three-dimensional (3D) mode to the 2D one occurs during the GaN epilayer growth when a higher growth pressure is used during the preceding GaN intermedial layer growth, and an improvement of the crystalline quality of GaN epilayer will be made. Combining the in situ reflectivity and transmission electron microscopy (TEM) measurements, it is suggested that the lateral growth at the transition of growth mode is favourable for bending of dislocation lines, thus reducing the density of threading dislocations in the epilayer.

Metal catalysis-free, direction-controlled planar growth of single-crystalline alpha-Si3N4 nanowires on Si(100) substrate

Single-crystalline alpha-Si3N4 nanowires are controlled to grow perpendicular to the wet-etched trenches in the SiO0.94 film on the plane of the Si substrate without metal catalysis. A detailed characterization is carried out by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The photoluminescence at 600 nm from alpha-Si3N4 nanowires is attributed to the recombination at the defect state formed by the Si dangling bond N3 equivalent to Si-center dot. The growth mechanism is considered to be related to the catalysis and nitridation of SiO nanoclusters preferably re-deposited around the inner corner of the trenches, as well as faster Si diffusion along the slanting side walls of the trenches. This simple direction-controlled growth method is compatible with the CMOS process, and could facilitate the fabrication of alpha-Si3N4 nanoelectronic or nanophotonic devices on the Si platform.

Effects of ZnO interlayers on thick GaN/Si film prepared by RF magnetron sputtering

We have successfully prepared a high-quality 2 mu m-thick GaN film with three inserted 30 nm-thick ZnO interlayers on Si (111) substrate without cracks by magnetron sputtering. The effects of the thickness and number of ZnO interlayers on the crystal quality of the GaN films were studied. It was found that the GaN crystal quality initially improved with the increase of the thickness of ZnO interlayers, but deteriorated quickly when the thickness exceeded 30 nm. Multiple ZnO interlayers were used as an effective means to further improve the crystal quality of the GaN film. By increasing the number of interlayers up to three, the cracks can be constrained to a certain extent, and the crystal quality of the GaN film greatly improved. (c) 2006 Elsevier B.V. All rights reserved.