Hydrostatic pressure effect on photoluminescence from a GaN0.015As0.985/GaAs quantum well

Photoluminescence from a GaN0.015As0.985/GaAs quantum well has been measured at 15 K under hydrostatic pressure up to 9 GPa. Both the emissions from the GaNAs well and GaAs barrier are observed. The GaNAs-related peak shows a much weaker pressure dependence compared to that of the GaAs band gap. A group of new peaks appear in the spectra when the pressure is beyond 2.5 GPa, which is attributed to the emissions from the N isoelectronic traps in GaAs. The pressure dependence of the GaNAs-related peaks was calculated using the two-level model with the measured pressure coefficients of the GaAs band gap and N level as fitting parameters. It is found that the calculated results deviate seriously from the experimental data. An increasing of the emission intensity and the linewidth of the GaNAs-related peaks was also observed and briefly discussed. (C) 2001 American Institute of Physics.

A narrow photoluminescence linewidth of 19.2 meV at 1.35 mu m from In0.5Ga0.5As/GaAs quantum island structure grown by molecular beam epitaxy

A self-organized In0.5Ga0.5As/GaAs quantum island structure emitting at 1.35 mum at room temperature has been successfully fabricated by molecular beam epitaxy via cycled (InAs)(1)/GaAs)(1)monolayer deposition method. The photoluminescence measurement shows that a very narrow linewidth of 19.2 meV at 300 K has been reached for the first time, indicating effective suppression of inhomogeneous broadening of optical emission from the In0.5Ga0.5As island structure due to indium segregation reduction by introducing an AlAs layer and the strain reduction by inserting an In0.2Ga0.8As layer overgrown on the top of islands. The mound-like morphology of the islands elongated along the [1 (1) over bar0] azimuth are observed by the atomic force microscopy measurement, which reveals the fact that strain in the islands is partially relaxed along the [1 (1) over bar0] direction. Our results present important information for the fabrication of 1.3 mum wavelength quantum dot devices.

Growth and photoluminescence of epitaxial CeO2 film on Si (111) substrate

A CeO2 film with a thickness of about 80nm was deposited by a mass-analysed low-energy dual ion beam deposition technique on an Si(111) substrate. Reflection high-energy electron diffraction and x-ray diffraction measurements showed that the film is a single crystal. The tetravalent state of Ce in the film was confirmed by x-ray photoelectron spectroscopy measurements, indicating that stoichiometric CeO2 was formed. Violet/blue light emission (379.5 nm) was observed at room temperature, which may be tentatively explained by charge transitions from the 4f band to the valence band of CeO2.

Different transfer paths for thermally activated electrons and holes in self-organized Ge/Si(001) islands in a multilayer structure

We investigated the temperature dependence (10-250 K) of the photoluminescence (PL) emission spectrum of self-organized Ge/Si(001) islands in a multilayer structure. With elevated temperature, we find that the thermally activated holes and electrons are gathered by the Ge islands in different ways. The holes drift from the wetting layer into the islands, while the electrons, confined in Si due to type-II band alignment, leak into the Ge islands by the electrostatic interaction with the holes accumulated there. It results in an increase of the integrated intensity of island-related PL at a certain temperature range and a reduction of the phonon energy in the phonon-assisted PL of the islands by involving a type-I transition into a type-II transition. (C) 2001 American Institute of Physics.

Structural anisotropy and optical properties of InxGa1-xAs quantum dots on GaAs(001)

InAs and InxGa1-xAs (x = 0.2 and 0.5) self-organized quantum dots (QDs) were fabricated on GaAs(0 0 1) by molecular beam epitaxy (MBE) and characterized by atomic force microscopy (AFM), transmission electron microscopy (TEM), acid photoluminescence polarization spectrum (PLP). Both structural and optical properties of InxGa1-xAs QD layer are apparently different from those of InAs QD layer. AFM shows that InxGa1-xAs QDs tend to be aligned along the [1 (1) over bar 0] direction, while InAs QDs are distributed randomly. TEM demonstrates that there is strain modulation along [1 1 0] in the InxGa1-xAs QD layers. PLP shows that In0.5Ga0.5As islands present optical anisotropy along [1 1 0] and [1 (1) over bar 0] due to structural and strain field anisotropy for the islands. (C) 2001 Elsevier Science B.V. All rights reserved.

Photoluminescence properties of self-organized InGaAs/GaAs quantum dot structures

Optical properties of InGaAs/GaAs self-organized quantum dots (QDs) structures covered by InxGa1-x As capping layers with different In contents chi ranging from 0. 0 (i.e., GaAs) to 0. 3 were investigated systematically by photoluminescence (PL) measurements. Red-shift of the PL peak energies of the InAs QDs covered by InxGa1-xAs layers with narrower linewidth and less shifts of the PL emissions via variations of the measurement temperatures were observed compared with that covered by GaAs layers. Calculation and structural measurements confirm that the red-shift of the PL peaks are mainly due to strain reduction and suppression of the In/Ga intermixing due to the InxGa1-xAs cover layer, leading to better size uniformity and thus narrowing the PL linewidth of the QDs. 1. 3 mum wavelength emission with very narrow linewidth of only 19. 2 meV at room temperature was successfully obtained from the In0.5Ga0.5As/GaAs QDs covered by the In0.2Ga0.8As layer.

Photoluminescence studies of type-II self-assembled InAlAs/AlGaAs QDs grown on (311)A GaAs substrate

The photoluminescence (PL) spectra of self-assembled In0.55Al0.45As/Al0.45Ga0.5As quantum dots (QD) grown on (311)A GaAs substrate were measured. The type- I character of PL related to the X valley was verified by excitation power dependence of peak position and the PL spectra under different pressure , which was attributed to the type- II transition from X valley in Al0.5Ga0.5As to heavy holes in In0.55Al0.45As The high energy Gamma -related transition was also observed above 70K and assigned as the transition between Gamma valley and heavy holes in In-0.55 Al0.45As. The X-valley split was discussed to interpret the observed second X-related peak under pressure.

Temperature quenching mechanisms for photoluminescence of MBE-grown chlorine-doped ZnSe epilayers

We report on a detailed investigation on the temperature-dependent behavior of photoluminescence from molecular beam epitaxy (MBE)-grown chlorine-doped ZnSe epilayers. The overwhelming neutral donor bound exciton ((ClX)-X-0) emission at 2.797 eV near the band edge with a full-width at half-maximum (FWHM) of similar to 13 meV reveals the high crystalline quality of the samples used. In our experiments, the quick quenching of the (ClX)-X-0 line above 200 K is mainly due to the presence of a nonradiative center with a thermal activation energy of similar to 90 meV, The same activation energy and similar quenching tendency of the (ClX)-X-0 line and the I-3 line at 2.713 eV indicate that they originate from the same physical mechanism. We demonstrate for the first time that the dominant decrease of the integrated intensity of the I, line is due to the thermal excitation of the "I-3 center"-bound excitons to its free exciton states, leaving the "I-3 centers" as efficient nonradiative centers. The optical performance of ZnSe materials is expected to be greatly improved if the density of the "I-3 center" can be controlled. The decrease in the luminescence intensity at moderately low temperature (30-200 K) of the (ClX)-X-0 line is due to the thermal activation of neutral-donor-bound excitons ((ClX)-X-0) to free excitons. (C) 2000 Published by Elsevier Science B.V.

1.35 mu m photoluminescence from In0.5Ga0.5As/GaAs islands grown by molecular beam epitaxy via cycled (InAs)(1)/(GaAs)(1) monolayer deposition

1.35 mum photoluminescence (PL) with a narrow linewidth of only 19.2 meV at room temperature has been achieved in In0.5Ga0.5As islands structure grown on GaAs (1 0 0) substrate by solid-source molecular beam epitaxy. Atomic force microscopy (AFM) measurement reveals that the 16-ML-thick In0.5Ga0.5As islands show quite uniform InGaAs mounds morphology along the [ 1(1) over bar 0] direction with a periodicity of about 90 nm in the [1 1 0] direction. Compared with the In0.5Ga0.5As alloy quantum well (QW) of the same width, the In0.5Ga0.5As islands structure always shows a lower PL peak energy and narrower full-width at half-maximum (FWHM), also a stronger PL intensity at low excitation power and more efficient confinement of the carriers. Our results provide important information for optimizing the epitaxial structures of 1.3 mum wavelength quantum dots devices. (C) 2000 Elsevier Science B.V. All rights reserved.

Strong temperature dependence of photoluminescence properties in visible InAlAs quantum dots

Strong temperature dependence of optical properties has been studied in visible InAlAs/AlGaAs quantum dots, by employing photoluminescence (PL) and time-resolved photoluminescence (TRPL) measurements. The fast redshift of the exciton emission peak was observed at much lower temperature range compared to that observed in the InAs/GaAs QDs. In TRPL we did not observe the constant decay time even at low temperature. Instead, the observed decay time increases quickly with increasing temperature, showing 2D properties in the transient dynamic process. We attributed our results to the strong lateral coupling effect, which results in the formation of the local minibands or extended states from the discrete energy levels. (C) 2000 Elsevier Science B.V. All rights reserved.

Photoluminescence and microstructure of the Erbium-Doped hydrogenated amorphous SiOx(0 < x < 2)

The hydrogenated amorphous SiOx films (a-SiOx:H) with various oxygen contents have been prepared using plasma enhanced chemical vapor deposition technique. The films were implanted with erbium and annealed by rapid thermal annealing. An intense photoluminescence (PL) of Er at 1.54 mum has been observed at 77 K and at room temperature. The PL intensity depends strongly on both the oxygen content of the film and the rapid thermal annealing temperature and reaches its maximum if the ratio of O/Si in the film is approximately equal to 1.0 at 77 K and to 1.76 at room temperature. The microstructure of the film also has strong influences on the PL intensity. The PL intensity at 250 K is slightly more than a half of that at 15 K. It means that the temperature quenching effect of the PL intensity is very weak.

Photoluminescence of ZnO : Tb nanoparticles

Terbium-doped zinc oxide nanoparticles have been prepared by hydrolyzing zinc acetate and terbium acetate. Nanoparticle-matrix-facilitated photoluminescence which is related to Tb3+ ions has been observed for ZnO:Tb nanoparticles. The dependence of emission intensity on doping concentration of Tb3+ ions has been investigated. An energy transfer from excited states of ZnO hosts to dopants is disclosed by the fact that the emission intensity of Tb3+ centers increases with increasing Tb content at the expense of emission from defect states in ZnO matrix.

Photoluminescence studies on pseudomorphic delta-doped AlGaAs/InGaAs/GaAs quantum wells

Photoluminescence (PL) measurements were performed on several series of single-side Si-doped pseudomorphic high electron mobility transistors (p-HEMTs) quantum well (QW) samples, with different spacer layer widths, well widths and Si delta -doped concentrations , under different temperatures and excitation power densities. The dynamic competitive luminescence mechanism between the radiations of e2-hh1 and e1-hh1 was discussed in detail. The confining potential, subband energies, corresponding envelope functions, subband occupations and transferring efficiency etc., were calculated by self-consistent finite differential method at different temperatures in comparison with the present experiment results. The relative variation of the integrated luminescence intensity of the two transitions (e1-hh1 and e2-hh1) was found to be dependent on the temperature and the structure's properties, e. g. spacer layer width, dopant concentration and well width.

Photoluminescence of InAs quantum dots grown on GaAs surface

InAs quantum dots (QDs) grown on GaAs surface are investigated. The observed abnormal photoluminescence (PL) properties, including extremely sharp high-energy peaks, almost temperature-independent linewidth, and fast thermal quenching, are discussed in terms of the strong quantum confinement effects due to the absence of a cap layer and the lack of carrier redistribution channel caused by the small number of QDs capable of contributing to PL and the high-density surface defects. (C) 2000 American Institute of Physics. [S0003-6951(00)01244-4].

Temperature dependence of photoluminescence of an n-i-p-i GaAs superlattice

Both the photoluminescence peaks corresponding to the vertical transitions and the nonvertical transitions in an n-i-p-i GaAs superlattice are clearly observed. The redshifts of the two peaks with increasing temperature are: discussed in terms of the temperature-dependent carrier separation effect.