制备工艺条件对薄膜微结构的影响

用不同的方法在石英玻璃，YAG晶体，K9玻璃和LiNbO3晶体等几种衬底上制备了ZrO2，HfO2和TiO2薄膜。HfO2薄膜利用电子束蒸发（EB）、离子束辅助（IAD）和双束离子束溅射（DIBS）三种方法沉积。对其中的一些样品进行了不同温度下的退火处理，对所有的样品进行X射线衍射（XRD）测试，以获得不同条件下得到的薄膜的晶相及晶粒尺寸等的微结构参数。实验结果表明，薄膜的晶相结构以及晶粒尺寸强烈地依赖于沉积过程的各种技术参数，如衬底的种类、沉积温度、沉积方法和退火温度。利用薄膜表面扩散以及薄膜成核长大热

Influence of different post-treatments on the structure and optical properties of zinc oxide thin films

Zinc oxide (ZnO) films with c-oriented were grown on fused quartz glass substrates at room temperature using dc reactive magnetron sputtering. The as-grown films were annealed at 700 degrees C in air and bombarded by ion beam, respectively. The effects of post-treatments on the structural and optical properties of the ZnO films were investigated by X-ray diffraction (XRD), photoluminescence (PL), optical transmittance and absorption measurements. The XRD spectra indicate that the crystal quality of ZnO films has been improved by both the post-treatments. Compared with the as-grown sample, both annealed and bombarded samples exhibited blueshift in the UV emission peaks, and a strong green emission was found in the annealed ZnO film. In both optical transmittance and absorption spectra, a blueshift of the band-gap edge was observed in the bombarded film, while a redshift was observed in the annealed film. (c) 2004 Elsevier B.V. All rights reserved.

Influences of CO2 laser irradiation on the structure and photoluminescence of zinc oxide thin films

CO2 laser irradiation experiments on ZnO thin films are reported. The structural, optical, luminescent and vibrational properties of the samples were investigated by X-ray diffraction (XRD), transmittance, photoluminescence (PL) and Raman measurements. XRD results show that the crystalline of the irradiated films was improved. The (002) peaks of irradiated ZnO films shift to. higher 20 angles due to the stress relaxation in the case of laser beam irradiation. From optical transmittance spectra, all films exhibit high transmittance in the visible range, the optical band edge of irradiated films showed a redshift compared with that of as-grown films. Compared with the as-grown films, the photoluminescence emission (in particular the relative intensities of visible emissions) intensities of irradiated samples enhanced. In the Raman scattering spectral both the A I. and E modes exhibited slight Raman blueshift. (c) 2005 Elsevier B.V. All rights reserved.

ZnO : Zn phosphor thin films prepared by face-to-face annealing

ZnO:Zn phosphor thin films were prepared by face-to-face annealing at 450 degrees C in air. The effects of the face-to-face annealing on the structural and optical properties of the ZnO films were investigated by X-ray diffraction (XRD), photoluminescence (PL), optical transmittance and absorption measurements. Measurement results showed that the crystal quality of ZnO films was improved by face-to-face annealing. Both UV light emission and visible light emission were enhanced compared to those of open annealing films. The UV emission peak was observed to have a blueshift towards higher energy. The optical band-gap edge of as-annealed films shifted towards longer wavelength. (c) 2005 Elsevier B.V.. All rights reserved.

不同沉积参量下ZrO_2薄膜的微结构和激光损伤阈值

ZrO2采用X射线衍射(XRD)技术分析了不同充氧条件和沉积温度对ZrO2溥膜组成结构的影响，并对不同工艺下制备的薄膜的表面粗糙度和激光损伤阈值进行了测量。结果发现随着氧压的升高，ZrO2溥膜将由单斜相多晶态逐渐转变为非晶态结构，而随着基片温度的增加，溥膜将由非晶态逐渐转变为单斜相多晶态。同时发现随着氧压升高晶粒尺寸减小，而随着沉积温度增加，晶粒尺寸增大。氧压增加时工艺对表面粗糙度有一定程度的改善，而沉积温度升高，工艺对表面粗糙度的改善不明显。晶粒尺寸大小变化与表面粗糙度变化存在对应关系。激光损伤测量表明

Annealing effects on electron-beam evaporated Al2O3 films

The effects of post-deposited annealing on structure and optical properties of electron-beam evaporated Al2O3 single layers were investigated. The films were annealed in air for 1.5 h at different temperatures from 250 to 400 degrees C. The optical constants and cut-off wavelength were deduced. Microstructure of the samples was characterized by X-ray diffraction (XRD). Profile and surface roughness measurement instrument was used to determine the rms surface roughness. It was found that the cut-off wavelength shifted to short wavelength as the annealing temperature increased and the total optical loss decreased. The film structure remained amorphous even after annealing at 400 degrees C temperature and the samples annealed at higher temperature had the higher rms surface roughness. The decreasing total optical loss with annealing temperature was attributed to the reduction of absorption owing to oxidation of the film by annealing. Guidance to reduce the optical loss of excimer laser mirrors was given. (c) 2004 Elsevier B.V. All rights reserved.

铬过渡层对银膜光学性质及附着力的影响

研究了在玻璃基底上采用不同厚度的铬膜作过渡层，对银膜的光学性质及其附着力的影响。光谱测量结果表明，随着铬膜层厚度的增加，银膜的反射率先增大后减小。与直接镀在玻璃基底上的银膜的反射率相比，铬膜层厚度为8～14nm时，银膜的反射率较低；铬膜层厚度为17～21nm时，银膜的反射率得到提高，其中铬膜厚度为17nm时，银膜的反射率最高；继续增加铬膜层的厚度，银膜的反射率又降低，说明采用一定厚度的铬膜作过渡层可以提高银膜的反射率。X射线衍射（XRD）结构分析表明，一定厚度的铬膜改善了银膜的结晶程度，使薄膜的晶粒度增大

退火对ZrO2薄膜微结构及激光损伤阈值的影响

利用电子束蒸发方法在Yb:YAG晶体和熔融石英衬底上沉积单层ZrO2薄膜,分别在673 K和1 073 K的温度下经过12 h退火以后,通过X射线衍射(XRD)分析了薄膜晶相,计算了薄膜的晶粒尺寸;利用表面热透镜技术获得了薄膜的吸收;测量了退火后薄膜的激光损伤阈值.实验结果表明:两种衬底上的薄膜结构受到退火温度和衬底表面结构的影响,高温退火有利于单斜相的形成,含单斜相的ZrO2薄膜具有较高的激光损伤阈值,而由于衬底的吸收,Yb:YAG晶体上薄膜的损伤阈值远小于石英衬底上薄膜的损伤阈值.

退火对电子束热蒸发Al2O3薄膜性能影响的实验研究

用电子束热蒸发方法镀制了Al2O3材料的单层膜，对它们在空气中进行了250～400℃的高温退火。对样品的透射率光谱曲线进行了测量，计算了样品的消光系数、折射率和截止波长。通过X射线衍射仪(XRD)测量分析了薄膜的微观结构，采用表面轮廓仪测量了样品的表面均方根粗糙度。结果发现随着退火温度的提高光学损耗下降，薄膜结构在退火温度为400℃时仍然为无定形态，样品的表面粗糙度随退火温度的升高而增加。引起光学损耗下降起主导作用的是吸收而不是散射，吸收损耗的下降主要是由于退火使材料吸收空气中的氧而进一步氧化，从而使薄膜

沉积温度对HfO2薄膜残余应力的影响

用电子柬蒸发方法制备了HfO2薄膜，根据镀膜前后基片曲率半径的变化，用Stoney公式计算了薄膜应力。讨论了沉积温度对薄膜残余应力的影响。结果发现，HfO2薄膜的残余应力均为张应力，应力值随沉积温度的升高先增大后减小，在280℃左右出现极大值。对样品进行了XRD测试，从微观结构上对实验结果进行了分析，发现微结构演变引起的内应力变化是引起薄膜残余应力改变的主要因素，HfO2薄膜在所选沉积温度60～350℃内出现了晶态转变，堆积密度随温度升高而增大。

高真空室中的水蒸气对HfO2薄膜性能的影响

本文研究了在镀膜过程中真空室内水蒸气的含量对HfO2薄膜物理性能的影响。用电子束蒸发和光电极值监控的方法在BK7基底上制备HfO2薄膜。利用残余气体分析仪在线监测了真空室内的残余气氛组成。分别用Lambda 900光谱仪、X射线衍射方法、表面热透镜技术和1064nm的激光器测试了薄膜的光学性能、微结构、吸收和激光损伤阈值。实验发现，附加冷阱装置有助于我们有效控制镀膜过程中的水汽含量，且在水蒸气含量较少的真空室内镀制的薄膜具有较高的折射率，较小的晶粒尺寸，较低的弱吸收值和较高的损伤阈值。

Influence of annealing temperature on structure, optical loss and laser-induced damage threshold of TiO2 thin films

TiO2 thin films are prepared on fused silica with conventional electron beam evaporation deposition. After annealed at different temperatures for 4h, the spectra and XRD patterns of the TiO2 thin film are obtained. Weak absorption of coatings is measured by the surface thermal lensing technique, and laser-induced damage threshold (LIDT) is determined. It is found that with the increasing annealing temperature, the transmittance of TiO2 films decreases. Especially when coatings are annealed at high temperature over 1173K, the optical loss is very serious. Weak absorption detection indicates that the absorption of coatings decreases firstly and then increases, and the absorption and defects play major roles in the LIDT of TiO2 thin films.

Influence of deposition conditions on the microstructure of oxides thin films

Thin films of ZrO2, HfO2 and TiO2 were deposited on kinds of substrates by electron beam evaporation (EB), ion assisted deposition (IAD) and dual ion beam sputtering (DIBS). Then some of them were annealed at different temperatures. X-ray diffraction (XRD) was applied to determine the crystalline phase and the grain size of these films, and the results revealed that their microstructures strongly depended on the deposition conditions such as substrate, deposition temperature, deposition method and annealing temperature. Theory of crystal growth and migratory diffusion were applied to explain the difference of crystalline structures between these thin films deposited and treated under various conditions. (c) 2007 Elsevier B.V. All rights reserved.

8.0nm反射式偏振膜的设计和制备

讨论了软X射线反射式偏振膜的设计原理和方法,利用设计软件模拟设计了8.0nm处的Mo/B4C偏振膜.对影响多层膜性能的参量进行了详细的误差分析.利用磁控溅射镀膜机进行了偏振膜的制备研究,X射线小角衍射测量了多层膜的周期厚度,测量数据的拟合结果与设计值吻合很好.

Al2O3和Cr过渡层对Ag膜光学性质及其附着力的影响

研究了在玻璃基底上镀制Al2O3和Cr过渡层对Ag膜反射率及附着力的影响.分光光度计测试了Ag膜的反射率,结果表明,与Cr过渡层相比,Al2O3过渡层对Ag膜反射率的降低相对较小;而且,随着Al2O3厚度的增加,Ag膜的反射率先增大后减小.XRD与AES测试表明,引入Al2O3或Cr可明显细化Ag晶粒,减弱Ag膜（111）织构;Al2O3作过渡层时,Al原子向Ag层中扩散显著;而Cr作过渡层时,只有少量Cr原子扩散进入Ag层.因此,Al2O3作过渡层能显著增强薄膜与玻璃基体之间的附着力.