RBS STUDIES OF THE LATTICE DAMAGE CAUSED BY 1 MEV SI+ IMPLANTATION INTO AL0.3GA0.7AS/GAAS SUPERLATTICES AT ELEVATED-TEMPERATURE

The lattice damage accumulation in GaAs and Al0.3Ga0.7As/GaAs superlattices by 1 MeV Si+ irradiation at room temperature and 350-degrees-C has been studied. For irradiations at 350-degrees-C, at lower doses the samples were almost defect-free after irradiation, while a large density of accumulated defects was induced at a higher dose. The critical dose above which the damage accumulation is more efficient is estimated to be 2 x 10(15) Si/cm2 for GaAs, and is 5 x 10(15) Si/cm2 for Al0.8Ga0.7As/GaAs superlattice for implantation with 1.0 MeV Si ions at 350-degrees-C. The damage accumulation rate for 1 MeV Si ion implantation in Al0.3Ga0.7As/GaAs superlattice is less than that in GaAs.

Low-Temperature Growth of ZnO Films on GaAs by Metal Organic Chemical Vapor Deposition

ZnO thin films were grown on GaAs （001） substrates by metal-organic chemical vapor deposition （MOCVD） at low temperatures ranging from 100 to 400℃. DEZn and 1-12 O were used as the zinc precursor and oxygen precursor, respectively. The effects of the growth temperatures on the growth characteristics and optical properties of ZnO films were investigated. The X-ray diffraction measurement （XRD） results indicated that all the thin films were grown with highly c- axis orientation. The surface morphologies and crystal properties of the films were critically dependent on the growth temperatures. Although there was no evidence of epitaxial growth, the scanning electron microscopy （SEM） image of ZnO film grown at 400℃ revealed the presence of ZnO microcrystallines with closed packed hexagon structure. The photoluminescence spectrum at room temperature showed only bright band-edge （3. 33eV） emissions with little or no deep-level e- mission related to defects.

Stable Temperature Characteristics of InAs/GaAs Quantum Dots at Long Wavelength Emission

The time-resolved photoluminescence and steady photoluminescence (TRPL and PL) spectra on self-assembled InAs/GaAs quantum dots (QDs) are investigated. By depositing GaAs/InAs short period superlattices (SLs), 1. 48 μtm emission is obtained at room temperature. Temperature dependent PL measurements show that the PL intensity of the emission is very steady. It decays only to half as the temperature increases from 15 K to room temperature, while at the same time, the intensity of the other emission decreases by a factor of 5 orders of magnitude. These two emissions are attributed to large-size QDs and short period superlattices (SLs), respectively. Large-size QDs are easier to capture and confine carriers,which benefits the lifetime of PL, and therefore makes the emission intensity insensitive to the temperature.

High Temperature Characteristics of 3C-SiC/Si Heterojunction Diodes Grown by LPCVD

The high temperature (300～480K) characteristics of the n-3C-SiC/p-Si heterojunction diodes (HJD) fabricated by low-pressure chemical vapor deposition on Si (100) substrates are investigated.The obtained diode with best rectifying properties has 1.8×104 of ratio at room temperature,and slightly rectifying characteristics with 3.1 of rectification ratio is measured at 480K of an ambient temperature .220V of reverse breakdown voltage is acquired at 300K.Capacitance-voltage characteristics show that the abrupt junction model is applicable to the SiC/Si HJD structure and the built-in voltage is 0.75V.An ingenious equation is employed to perfectly simulate and explain the forward current density-voltage data measured at various temperatures.The 3C-SiC/Si HJD represents a promising approach for the fabrication of high quality heterojunction devices such as SiC-emitter heterojunction bipolar transistors.

Temperature Dependence of Characteristics for Multimode Interference Based 3-dB Coupler in SOI

The temperature dependence of characteristics for multimode interference (MMI) based 3-dB coupler in silicon-on-insulator is analyzed, which originates from the relatively high thermo-optic coefficient of silicon. For restricted interference 3-dB MMI coupler, the output power uniformity is ideally 0 at room temperature and becomes 0. 32 dB when temperature rises up to 550 K. For symmetric interference 3-dB MMI coupler, the power uniformity keeps ideally 0 due to its intrinsic symmetric interference mechanism. With the temperature rising, the excess loss of the both devices increases. The performance deterioration due to temperature variety is more obvious to restricted interference MMI 3-dB coupler, comparing with that of symmetric interference MMI 3-dB coupler.

Growth of Cubic GaN by MOCVD at High Temperature

High quality cubic GaN (c-GaN) is grown by metalorganic vapor deposition (MOCVD) at an increased growth temperature of 900 ℃, with the growth rate of 1.6 μm/h. The full width at half maximum (FWHM) of room temperature photoluminescence (PL) for the high temperature grown GaN film is 48meV. It is smaller than that of the sample grown at 830 ℃. In X-ray diffraction (XRD) measurement, the high temperature grown GaN shows a (002) peak at 20° with a FWHM of 21'. It can be concluded that, although c-GaN is of metastable phase, high growth temperature is still beneficial to the improvement in its crystal quality. The relationship between the growth rate and growth temperature is also discussed.

The effect of low temperature GaAs nucleation on the growth of GaN on Silicon (001) during MOVPE process

High quality cubic GaN was grown on Silicon (001) by metalorganic vapor phase epitaxy (MOVPE) using a GaAs nucleation layer grown at low temperature. The influence of various nucleation conditions on the GaN epilayers' quality was investigated. We found that the GaAs nucleation layer grown by atomic layer epitaxy (ALE) could improve the quality of GaN films by depressing the formation of mixed phase. Photoluminescence (PL) and X-ray diffraction were used to characterize the properties of GaN epilayers. High quality GaN epilayers with PL full width at half maximum (FWHM) of 130meV at room temperature and X-ray FWHM of 70 arc-min were obtained by using 10-20nm GaAs nucleation layer grown by ALE.

High temperature operation of 650nm AlGaInP quantum well laser diodes grown by LP-MOCVD

Low threshold current and high temperature operation of 650nm AlGaInP quantum well laser diodes grown by low pressure metal organic chemical vapor deposition (LP-MOCVD) are reported in this paper. 650nm laser diodes with threshold current as low as 22-24mA at room temperature, and the operating temperature over 90 degrees C at CW output power 5 mW were achieved in this study. These lasers are stable during 72 hours burn in under 5mW at 90 degrees C.

Influence of processing temperature on microstructure and microhardness of copper subjected to high-pressure torsion

Cu samples were subjected to high-pressure torsion (HPT) with up to 6 turns at room temperature (RT) and liquid nitrogen temperature (LNT), respectively. The effects of temperature on grain refinement and microhardness variation were investigated. For the samples after HPT processing at RT, the grain size reduced from 43 mu m to 265 nm, and the Vickers microhardness increased from HV52 to HV140. However, for the samples after HPT processing at LNT, the value of microhardness reached its maximum of HV150 near the center of the sample and it decreased to HV80 at the periphery region. Microstructure observations revealed that HPT straining at LNT induced lamellar structures with thickness less than 100 nm appearing near the central region of the sample, but further deformation induced an inhomogeneous distribution of grain sizes, with submicrometer-sized grains embedded inside micrometer-sized grains. The submicrometer-sized grains with high dislocation density indicated their nonequilibrium nature. On the contrary, the micrometer-sized grains were nearly free of dislocation, without obvious deformation trace remaining in them. These images demonstrated that the appearance of micrometer-sized grains is the result of abnormal grain growth of the deformed fine grains.

Experimental Setup for Assessing the Energetic Materials Deflagration Propagation under High Temperature and High Pressure Conditions

The technology of "explosion in fractures" is one of new synthetic engineering methods used in low permeability reservoirs. The most important problem arose from the technology is to assess the deflagration propagation capability of milky explosives in rock fractures. In order to investigate detailed this problem in the laboratory, an experimental setup was designed and developed in which different conditions can be simulated. The experimental setup mainly includes two parts. One is the experimental part and the other is the measurement part. In the experimental setup, the narrow slots with different width can be simulated; meanwhile, different initial pressures and initial temperatures can be loaded on the explosives inside the narrow slots. The initial pressure range is from 0-60 MPa, and the initial temperatures range is from room temperature to 100 V. The temperature and the velocity of deflagration wave can be measured; meanwhile the corresponding pressure in the narrow slot is also measured. In the end, some typical measurement results are briefly presented and discussed.

Temperature effects of CsI(Tl) crystal detector with APD readout

The temperature dependences of the light output of CsI(Tl) crystal grown at IMP and of the gain of the Hamamatsu S8664-1010 avalanche photodiode (APD) have been investigated systematically. The light output of the CsI(Tl) crystal increases with temperature by 0.67%/degrees C in the region from -2 degrees C to 8 degrees C, and by 0.33%/degrees C in the region from 8 degrees C to 25 degrees C, while the gain of the tested APD decreases by -3.68%/degrees C (working voltage 400V) on average in the room temperature range. The best energy resolution 5.1% of the CsI(Tl) with APD was obtained for the 662keV gamma ray from Cs-137 radiation source.

Temperature annealing of tracks induced by ion irradiation of graphite

Highly oriented pyrolytic graphite (HOPG) samples were irradiated by Xe ions of initial kinetic energy of 3 MeV/u. The irradiations were performed at temperatures of 500 and 800 K. Scanning tunneling microscopy (STM) images show that the tracks occasionally have elongated structures under high-temperature irradiation. The track creation yield at 800 K is by three orders of magnitude smaller compared to that obtained during room-temperature irradiation. STM and Raman spectra show that amorphization occurs in graphite samples irradiated at 500 K to higher fluences, but not at 800 K. The obtained experimental results clearly reveal that the irradiation under high temperature causes track annealing.

Raman investigation of ion-implanted ZnO films

ZnO thin films were implanted at room temperature with 80 keV N+ or 400 keV Xe+ ions. The implantation fluences of N+ and Xe+ ranged from 5.0 x 10(14) to 1.0 x 10(17)/cm(2), and from 2.0 x 10(14) to 5.0 x 10(15)/cm(2), respectively. The samples were analyzed using Raman spectroscopy and the Raman scattering modes of the N- and Xe-ion implanted samples varying with implantation fluences were investigated. It was found that Raman peaks (bands) at 130 and 578 cm(-1) appeared in the spectra of ion-implanted ZnO samples, which are independent of the ion species, whereas a new peak at 274 cm(-1) was found only in N-ion implanted samples, and Raman band at 470 cm(-1) was found clearly in Xe-ion implanted samples. The relative intensity (peak area) increased with the increasing of the implantation fluences. From the comparison of the Raman spectra of N- and Xe-ion implanted ZnO samples and considering the damage induced by the ions, we analyzed the origin of the observed new Raman peaks (bands) and discussed the structure changes of ZnO films induced by N- and Xe-ion implantations.

Particle Size-Dependent Charge Ordering and Magnetic Properties in Pr0.55Ca0.45MnO3

A series of Pr0.55Ca0.45MnO3 compounds with average particle size ranging from 2000 to 30 nm have been synthesized by the sol-gel method and their charge ordering (CO) and magnetic properties are investigated. It is observed that with particle size decreasing, the CO transition is gradually suppressed and finally disappears upon particle size down to 35 nm, while the ferromagnetism (FM) emerges and exhibits a nonmonotonous variation with a maximum at 45 nm samples. The FM components in all samples never reach long-range ordering but rather only show short-range clusters. A new explanation considering the coupling between lattice, charge, and spin in the system is raised to understand the suppression of the CO state, Both the competition between the CO/AFM and FM states and the core-shell model are employed to explain the variation of the FM phase. These results may provide a deeper insight into the physics of particle size effect on the charge ordering manganite.

Low-temperature synthesis of oil-soluble CdSe, CdS, and CdSe/CdS core - Shell nanocrystals by using various water-soluble anion precursors

Colloidal CdSe and CdS quantum dots were synthesized at low temperatures (60-90 degrees C) by a two-phase approach at a toluene-water interface. Oil-soluble cadmium myristate (Cd-MA) was used as cadmium source, and water-soluble Na2S, thiourea, NaHSe, Na2SeSO3, and selenourea were used as sulfur and selenium sources, respectively. When a cadmium precursor in toluene and a selenium precursor in water were mixed, CdSe nanocrystals were achieved at a toluene-water interface in the range of 1.2-3.2 nm in diameter. Moreover, we also synthesized highly luminescent CdSe/CdS core-shell quantum dots by a two-phase approach using poorly reactive thiourea as sulfur source in an autoclave at 140 degrees C or under normal pressure at 90 degrees C. Colloidal solutions of CdSe/CdS core-shell nanocrystals exhibit a photoluminescence quantum yield (PL QY) up to 42% relative to coumarin 6 at room temperature.