Growth and structural properties of GaN films on flat and vicinal SiC(0001) substrates

Initial stage GaN growth by molecular-beam epitaxy (MBE) on SiC(0001) substrate is followed by in situ scanning tunneling microscopy. Comparison is made between growth on nominally flat and vicinal substrate surfaces and the results reveal characteristic differences between the two. Ex situ transmission electron microscopy (TEM) and X-ray diffraction (XRD) rocking curve measurements of the films show lower density of defects and better structural quality of the vicinal film. We suggest the improved structural quality of the vicinal film is related to the characteristic difference in its initial stage nucleation and coalescence proccsses than that of the flat film.

Photoluminescence of nanocrystalline SiC films prepared by rf magnetron sputtering

Amorphous Sic films are deposited on Si (111) substrates by rf magnetron sputtering and then annealed at 1200 degreesC for different times by a dc self-heating method in a vacuum annealing system. The crystallization of the amorphous Sic is determined by Raman scattering at room temperature and X-ray diffraction. The experimental result indicates that the Sic nanocrystals have formed in the films. The topography of the as-annealed films is characterized by atomic force microscopy. Measurements of photoluminescence of the as-annealed films show blue or violet light emission from the nanocrystalline Sic films and photoluminescence peak shifts to short wavelength side as the annealing time decreases.

Epitaxial growth of SiC on complex substrates

Epitaxial growth of SiC on complex substrates was carried out at substrate temperature from 1200 degreesC to 1400 degreesC. Three kinds of new complex substrates, c-plane sapphire, AlN/sapphire, and GaN/AlN/sapphire, were used in this study. We obtained a growth rate in the range of 1-6 mum/h. Thick (6 mum) SIC epitaxial layers with no cracks were successfully obtained on AlN/sapphire and GaN/AlN/sapphire substrates. X-ray diffraction patterns have confirmed that single-crystal SiC was obtained on these complex substrates. Analysis of optical transmission spectra of the SIC grown on sapphire substrates shows the lowest-energy gap near 2.2 eV, which is the value for cubic SiC. The undoped SIC showed n-type electrical conductivity. (C) 2001 Elsevier Science B.V. All rights reserved.

Homoepitaxial growth and device characteristics of SiC on Si-face (0001) 6H-SiC

Homoepitaxial growth of SiC on a Si-face (0 0 0 1) GH-SIC substrate has been performed in a modified gas-source molecular beam epitaxy system with Si2H6 and C2H4 at temperatures ranging 1000 1450 degreesC while keeping a constant SiC ratio (0.7) in the gas phase. X-ray diffraction patterns, Raman scattering measurements. and low-temperature photoluminescence spectra showed single-crystalline SiC. Mesa-type SiC p-n junctions were obtained on these epitaxial layers, and their I-V characteristics are presented. (C) 2001 Elsevier Science B.V. All rights reserved.

Raman study on residual strains in thin 3C-SiC epitaxial layers grown on Si(001)

Raman scattering measurement has been used to study the residual strains in the thin 3C-SiC/Si(001) epilayers with a variation of film thickness from 0.1 to 1.2 mu m. which were prepared by chemical vapor deposition (CVD)growth. Two methods have been exploited to figure our the residual strains and the exact LO bands. The final analyzing results show that residual strains exist in the 3C-SiC epilayers. The average stress is 1.3010 GPa, and the relative change of the lattice constant is 1.36 parts per thousand. Our measurements also show that 3C-SiC phonons are detectable even for the samples with film thickness in the range of 0.1 to 0.2 mu m. (C) 2000 Published by Elsevier Science S.A. All rights reserved.

The effects of carbonized buffer layer on the growth of SiC on Si

Carbonized buffer layers were formed with C2H4 on Si(100) and Si(111) substrates using different methods and SIC epilayers were grown on each buffer layer at 1050 degrees C with simultaneous supply of C2H4 and Si2H6. The structure of carbonized and epitaxy layers was analyzed with in situ RHEED. The buffer layers formed at 800 degrees C were polycrystalline on both Si(100) and Si(111) substrates whereas they were single crystals, with twins on Si(100) and without tu ins on Si(111)substrates. when formed with a gradual rise in substrate temperature from 300 degrees C to growth temperature. Raising the substrate temperature slowly results in the formation of more twins. Epilayers grown on carbonized polycrystalline lavers are polycrystalline. Single crystal epilayers without twins grow on single crystalline buffer layers without twins or with a few twins. (C) 1999 Elsevier Science B.V. All rights reserved.