Magnetron Sputtering Growth of InAs0.3Sb0.7 Films on (100) GaAs Substrates: Strong Effect of Growth Conditions on Film Structure

The growth of highly lattice-mismatched InAs0.3Sb0.7 films on (100) GaAs Substrates by magnetron Sputtering has been investigated and even epitaxial lnAs(0.3)Sb(0.7) films have been successfully obtained. A strong effect of the growth conditions on the film structure was observed, revealing that there was a growth mechanism transition from three-dimensional nucleation growth to epitaxial layer-by-layer growth mode when increasing the substrate temperature. A qualitative explanation for that transition was proposed and the critical conditions for the epitaxial layer-by-layer growth mode were also discussed.

Properties of high k gate dielectric gadolinium oxide deposited on Si(100) by dual ion beam deposition (DIBD)

Gadolinium oxide thin films have been prepared on silicon (100) substrates with a low-energy dual ion-beam epitaxial technique. Substrate temperature was an important factor to affect the crystal structures and textures in an ion energy range of 100-500 eV. The films had a monoclinic Gd2O3 structure with preferred orientation ((4) over bar 02) at low substrate temperatures. When the substrate temperature was increased, the orientation turned to (202), and finally, the cubic structure appeared at the substrate temperature of 700 degreesC, which disagreed with the previous report because of the ion energy. The AES studies found that Gadolinium oxide shared Gd2O3 structures, although there were a lot of oxygen deficiencies in the films, and the XPS results confirmed this. AFM was also used to investigate the surface images of the samples. Finally, the electrical properties were presented. (C) 2004 Elsevier B.V. All rights reserved.

InAs0.3Sb0.7 films grown on (100) GaSb substrates with a buffer layer by liquid-phase epitaxy

The growth of InAsxSb1-x films on (100) GaSb substrates by liquid-phase epitaxy (LPE) has been investigated and epitaxial InAs0.3Sb0.7 films with InAs0.9Sb0.09 buffer layers have been successfully obtained. The low X-ray rocking curve FHWM values of InAs0.3Sb0.7 layer shows the high quality of crystal-orientation structure. Hall measurements show that the highest electron mobility in the samples obtained is 2.9 x 10(4) cm(2) V-1 s(-1) and the carrier density is 2.78 x 10(16)cm(-3) at room temperature (RT). The In As0.3Sb0.7 films grown on (10 0) GaSb substrates exhibit excellent optical performance with a cut-off wavelength of 12 mu m. (c) 2007 Elsevier B.V. All rights reserved.

Adsorption of His-tagged peptide to Ni, Cu and Au (100) surfaces: Molecular dynamics simulation

Molecular dynamics (MD) simulations are performed to study the interaction of His-tagged peptide with three different metal surfaces in explicit water. The equilibrium properties are analyzed by using pair correlation functions (PCF) to give an insight into the behavior of the peptide adsorption to metal surfaces in water solvent. The intermolecular interactions between peptide residues and the metal surfaces are evaluated. By pulling the peptide away from the peptide in the presence of solvent water, peeling forces are obtained and reveal the binding strength of peptide adsorption on nickel, copper and gold. From the analysis of the dynamics properties of the peptide interaction with the metal surfaces, it is shown that the affinity of peptide to Ni surface is the strongest, while on Cu and An the affinity is a little weaker. In MD simulations including metals, the His-tagged region interacts with the substrate to an extent greater than the other regions. The work presented here reveals various interactions between His-tagged peptide and Ni/Cu/Au surfaces. The interesting affinities and dynamical properties of the peptide are also derived. The results give predictions for the structure of His-tagged peptide adsorbing on three different metal surfaces and show the different affinities between them, which assist the understanding of how peptides behave on metal surfaces and of how designers select amino sequences in molecule devices design. (c) 2007 Elsevier Ltd. All rights reserved.

简单金属在[100]单轴应力下的理论强度

本文讨论了利用赝势理论,按照Born稳定性判据,计算简单金属理论强度的方法。然后计算了六种简单金属(Li,Na,K,Rb,Cs和Pb)在0K和[100]单轴应力下的理论拉伸与压缩强度。

Single sub-100 attosecond pulse generation in a two-colour time-gating laser field

We theoretically propose a method of generating a single sub-100 attosecond (as) pulse with a two-colour time-gating laser field. The field is synthesized by an 8 fs/800 nm (three optical cycles) pulse and a 24 fs/2400 nm (three optical cycles) pulse with an optimal time delay between them. In our simulation, we obtain a supercontinuum with an extremely broad spectrum of 150 eV and generate an isolated attosecond pulse with 96 as pulse duration without any dispersion compensation.

Epitaxial growth of ZnO films on (100) and (001) gamma-LiAlO2 substrates by pulsed laser deposition

Structural and optical properties were investigated for ZnO films grown on (100) and (001) gamma-LiAlO2 (LAO) substrates by pulsed laser deposition method. According XRD results, it is intuitionistic that (100) LAO is suitable for fabricating high quality ZnO film, while (001) LAO is unsuitable. The FWHM of XRD, stress in film and FWHM of UV PL spectra for ZnO films on (100) LAO show a decreasing with increasing substrate temperature from 300 to 600 degrees C. ZnO film fabricated at 600 degrees C has the greatest grain size, the smallest stress (0.47 Gpa) and PL FWHM value (similar to 85 meV). This means that the substrate temperature of 600 degrees C is optimum for ZnO film deposited on (100) LAO. Moreover, it was found that the UV PL spectra intensity of ZnO film is not only related to the grain size and stoichiometric, but also depends on the stress in the film.

Growth and properties of ZnO thin film on beta-Ga2O3(100) substrate by pulsed laser deposition

Zinc oxide (ZnO) thin films were grown on the beta-Ga2O3 (100) substrate by pulsed laser deposition (PLD). X-ray diffraction (XRD) indicated that the ZnO films are c-axis oriented. The optical and electrical properties of the films were investigated. The room temperature Photoluminescence (PL) spectrum showed a near band emission at 3.28 eV with two deep level emissions. Optical absorption indicated a visible exciton absorption at room temperature. The as-grown films had good electrical properties with the resistivities as low as 0.02 Omega cm at room temperature. Thus, beta-Ga2O3 (100) substrate is shown to be a suitable substrate for fabricating ZnO film. (c) 2006 Elsevier B.V. All rights reserved.

Composite substrate LiGaO2(001)/beta-Ga2O3(100) fabricated by vapor transport equilibration

Highly (001) orientation LiGaO2 layers have been successfully fabricated on (100) beta-Ga2O3 surface by vapor transport equilibration (VTE) technique. The temperature is very important for the WE treatment. At low temperature (800 degrees C), LiGaO(2)layers are textured. As the temperature was raised to 1100 C the layer becomes highly oriented in the [100] direction. It shows that the best temperature for WE treatment is 1100 degrees C. This technique is promising to fabricate small lattice mismatch composite substrate of LiGaO2 (001)//beta-Ga2O3 (100) for GaN films. (c) 2006 Elsevier B.V. All rights reserved.

Structural, optical and electrical properties of ZnO films grown on c-plane sapphire and (100)gamma-LiAlO2 by pulse laser deposition

ZnO thin films were grown on single-crystal gamma-LiAlO2 (LAO) and sapphire (0001) substrate by pulsed laser deposition (PLD). The structural, optical and electrical properties of ZnO films were investigated. The results show that LAO is more suitable for fabricating ZnO films than sapphire substrate and the highest-quality ZnO film was attained on LAO at the substrate temperature of 550 degrees C. However, when the substrate temperature rises to 700 degrees C, lithium would diffuse from the substrate (LAO) into ZnO film which makes ZnO film on LAO becomes polycrystalline without preferred orientation, the stress in ZnO film increases dominantly and the resistivity of the film decreases exponentially. (c) 2005 Elsevier B.V. All rights reserved.

Deposition of ZnO thin films on (100) γ-LiAlO2 substrate

Optical properties for ZnO thin films grown on (100) γ-LiAlO2 (LAO) substrate by pulsed laser deposition method were investigated. The c-axis oriented ZnO films were grown on (100) γ-LiAlO2 substrates at the substrate temperature of 550 Celsius degrees. The transmittance of the films was over 85%. Peaks attributed to excitons were shown in absorption spectra, which indicated that thin films had high crystallinity. Photoluminescence spectra with the maximum peak at 540 nm were observed at room temperature, which seemed to be ascribed to oxygen vacancy in the ZnO films caused by diffusion of Li from the substrates into the films during the deposition.

用PLD法在MgO（100）衬底十生长ZnO薄膜的结构和光学特性

用脉冲激光沉积法在MgO（100）衬底上沉积了ZnO薄膜．衬底温度分别为400℃、550℃和700℃．利用X射线衍射（XRD）和光致发光谱（PL）对薄膜的结构和光学性能进行研究．x射线衍射的结果表明，在400℃和550℃下生长的ZnO薄膜具有高度c一轴择优取向．仉足当衬底温度升高到700℃时，薄膜由单一的择优取向变为有两个较强的择优取向．通过光致发光谱可以发现，在550℃下生长的ZnO薄膜具有强的紫外发射和窄的FWHM，并且紫外发光峰的强度与ZnO薄膜的结晶质量密切相关．

Nonpolar m-plane thin film GaN and InGaN/GaN light-emitting diodes on LiAlO2(100) substrates

The nonpolar m-plane (1 (1) over bar 00) thin film GaN and InGaN/GaN light-emitting diodes (LEDs) grown by metal-organic chemical vapor deposition on LiAlO2 (100) substrates are reported. The LEDs emit green light with output power of 80 mu W under a direct current of 20 mA for a 400x400 mu m(2) device. The current versus voltage (I-V) characteristic of the diode shows soft rectifying properties caused by defects and impurities in the p-n junction. The electroluminescence peak wavelength dependence on injection current, for currents in excess of 20 mA, saturates at 515-516 nm. This proves the absence of polarization fields in the active region present in c-plane structures. The light output intensity versus current (L-I) characteristic of the diode exhibits a superlinear relation at low injection current caused by nonradiative centers providing a shunt path and a linear light emission zone at high current level when these centers are saturated. (c) 2007 American Institute of Physics.