Fracture properties of silicon carbide thin films by bulge test of long rectangular membrane

This paper reports the mechanical properties and fracture behavior of silicon carbide (3C-SiC) thin films grown on silicon substrates. Using bulge testing combined with a refined load-deflection model of long rectangular membranes, which takes into account the bending stiffness and prestress of the membrane material, the Young's modulus, prestress, and fracture strength for the 3C-SiC thin films with thicknesses of 0.40 and 1.42 mu m were extracted. The stress distribution in the membranes under a load was calculated analytically. The prestresses for the two films were 322 +/- 47 and 201 +/- 34 MPa, respectively. The thinner 3C-SiC film with a strong (111) orientation has a plane-gstrain moduli of 415 +/- 61 GPa, whereas the thicker film with a mixture of both (111) and (110) orientations exhibited a plane-strain moduli of 329 +/- 49 GPa. The corresponding fracture strengths for the two kinds of SiC films were 6.49 +/- 0.88 and 3.16 +/- 0.38 GPa, respectively. The reference stresses were computed by integrating the local stress of the membrane at the fracture over edge, surface, and volume of the specimens and were fitted with Weibull distribution function. For the 0.40-mu m-thick membranes, the surface integration has a better agreement between the data and the model, implying that the surface flaws are the dominant fracture origin. For the 1.42-mu m-thick membranes, the surface integration presented only a slightly better fitting quality than the other two, and therefore, it is difficult to rule out unambiguously the effects of the volume and edge flaws.

Characterization of silicon carbide thin films and their use in colour sensor

A series of hydrogenated amorphous silicon carbide (a-Si1-xCx:H) films were prepared by plasma-enhanced chemical vapour deposition (PECVD) using a gas mixture of silane, methane, and hydrogen as the reactive source. The previous results show that a high excitation frequency, together with a high hydrogen dilution ratio of the reactive gases, allow an easier incorporation of the carbon atoms into the silicon-rich a-Si1-xCx:H film, widen the valence controllability. The data show that films with optical gaps ranging from about 1.9 to 3.6 eV could be produced. In this work the influence of the hydrogen dilution ratio of the reactive gases on the a-Si1-xCx:H film properties was investigated. The microstuctural and photoelectronic properties of the silicon carbide films were characterized by Rutherford backscattering spectrometry (RBS), elastic recoil detection analysis (ERDA), and FT-IR spectrometry. The results show that a higher hydrogen dilution ratio enhances the incorporation of silicon atoms in the amorphous carbon matrix for carbon-rich a-Si1-xCx:H films. One pin structure was prepared by using the a-Si1-xCx:H film as the intrinsic layer. The light spectral response shows that this structure fits the requirement for the top junction of colour sensor. (c) 2004 Elsevier B.V. All rights reserved.

Fracture properties of silicon carbide thin films charcterized by bulge test of long membranes

The mechanical properties and fracture behavior of silicon carbide (3C-SiC) thin films grown on silicon substrates were characterized using bulge testing combined with a refined load-deflection model for long rectangular membranes. Plane-strain modulus E-ps, prestress so, and fracture strength s(max) for 3C-SiC thin films with thickness of 0.40 mu m and 1.42 mu m were extracted. The E, values of SiC are strongly dependent on grain orientation. The thicker SIC film presents lower so than the thinner film due to stress relaxation. The s(max) values decrease with increasing film thickness. The statistical analysis of the fracture strength data were achieved by Weibull distribution function and the fracture origins were predicted.

Growth and Characterization of Silicon Carbide Thin Films Using a Nontraditional Hollow Cathode Sputtering Technique

Silicon carbide (SiC) is considered a suitable candidate for high-power, high-frequency devices due to its wide bandgap, high breakdown field, and high electron mobility. It also has the unique ability to synthesize graphene on its surface by subliming Si during an annealing stage. The deposition of SiC is most often carried out using chemical vapor deposition (CVD) techniques, but little research has been explored with respect to the sputtering of SiC. Investigations of the thin film depositions of SiC from pulse sputtering a hollow cathode SiC target are presented. Although there are many different polytypes of SiC, techniques are discussed that were used to identify the film polytype on both 4H-SiC substrates and Si substrates. Results are presented about the ability to incorporate Ge into the growing SiC films for the purpose of creating a possible heterojunction device with pure SiC. Efforts to synthesize graphene on these films are introduced and reasons for the inability to create it are discussed. Analysis mainly includes crystallographic and morphological studies about the deposited films and their quality using x-ray diffraction (XRD), reflection high energy electron diffraction (RHEED), transmission electron microscopy (TEM), scanning electron microscopy (SEM), atomic force microscopy (AFM), Auger electron spectroscopy (AES) and Raman spectroscopy. Optical and electrical properties are also discussed via ellipsometric modeling and resistivity measurements. The general interpretation of these analytical experiments indicates that the films are not single crystal. However, the majority of the films, which proved to be the 3C-SiC polytype, were grown in a highly ordered and highly textured manner on both (111) and (110) Si substrates.

Tuning the functional properties of Silicon Carbide Thin Film and Nanowires

The present thesis has been devoted to the synthesis and investigation of functional properties of silicon carbide thin films and nanowires. The work took profit from the experience of the research group in the synthesis of 3C-SiC from vapour phase. 3C-SiC thin films Thin films heteroepitaxy on silicon substrates was carried out in a vapour phase epitaxy reactor. The initial efforts were committed to the process development in order to enhance the crystal quality of the epi-layer. The carbonization process and a buffer layer procedure were optimized in order to obtain good quality monocrystalline 3C-SiC layers. The films characterization was used not only to improve the entire process, but also to assess the crystalline quality and to identify the defects. Methyltrichlorosilane (MTS) was introduced during the synthesis to increase the growth rate and enhance crystalline quality. The effect of synthesis parameters such as MTS flow and process temperature was studied in order to promote defect density reduction and the release of the strain due to lattice mismatch between 3C-SiC and silicon substrate. In-growth n-type doping was implemented using a nitrogen gas line and the effect of different synthesis parameters on doping level was studied. Raman measurements allowed a contactless characterization and evaluation of electrically active dopant. The effect of MTS on nitrogen incorporation was investigated and a promotion of dopant concentration together with a higher growth rate were demonstrated. This result allows to obtain higher doping concentrations without deteriorating crystal quality in 3C-SiC and, to the best of our knowledge, it has never been demonstrated before. 3C-SiC nanowires Core-shell SiC-SiO2 nanowires were synthesized using a chemical vapour deposition technique in an open tube configuration reactor on silicon substrates. Metal catalyst were used to promote a uniaxial growth and a dense bundle of nanowires 100 µm long and 60 nm thick was obtained. Substrate preparation was found to be fundamental in order to obtain a uniform nanowire density. Morphological characterization was carried out using scanning electron microscopy and the analysis of structural, compositional, optical properties is reported.

Hardness of silicon nitride thin films characterised by nanoindentation and nanoscratch deconvolution methods

Plasma enhanced chemical vapour deposition silicon nitride thin films are widely used in microelectromechanical system devices as structural materials because the mechanical properties of those films can be tailored by adjusting deposition conditions. However, accurate measurement of the mechanical properties, such as hardness, of films with thicknesses at nanometric scale is challenging. In the present study, the hardness of the silicon nitride films deposited on silicon substrate under different deposit conditions was characterised using nanoindentation and nanoscratch deconvolution methods. The hardness values obtained from the two methods were compared. The effect of substrate on the measured results was discussed.

Fracture Properties of LPCVD Silicon Nitride and Thermally Grown Silicon Oxide Thin Films From the Load-Deflection of Long Si3N4 and SiO2/Si3N4 Diaphragms

The bulge test is successfully extended to the determination of the fracture properties of silicon nitride and oxide thin films. This is achieved by using long diaphragms made of silicon nitride single layers and oxide/nitride bilayers, and applying comprehensive mechanical model that describes the mechanical response of the diaphragms under uniform differential pressure. The model is valid for thin films with arbitrary z-dependent plane-strain modulus and prestress, where z denotes the coordinate perpendicular to the diaphragm. It takes into account the bending rigidity and stretching stiffness of the layered materials and the compliance of the supporting edges. This enables the accurate computation of the load-deflection response and stress distribution throughout the composite diaphragm as a function of the load, in particular at the critical pressure leading to the fracture of the diaphragms. The method is applied to diaphragms made of single layers of 300-nm-thick silicon nitride deposited by low-pressure chemical vapor deposition and composite diaphragms of silicon nitride grown on top of thermal silicon oxide films produced by wet thermal oxidation at 950 degrees C and 1050 degrees C with target thicknesses of 500, 750, and 1000 mn. All films characterized have an amorphous structure. Plane-strain moduli E-ps and prestress levels sigma(0) of 304.8 +/- 12.2 GPa and 1132.3 +/- 34.4 MPa, respectively, are extracted for Si3N4, whereas E-ps = 49.1 +/- 7.4 GPa and sigma(0) = -258.6 +/- 23.1 MPa are obtained for SiO2 films. The fracture data are analyzed using the standardized form of the Weibull distribution. The Si3N4 films present relatively high values of maximum stress at fracture and Weibull moduli, i.e., sigma(max) = 7.89 +/- 0.23 GPa and m = 50.0 +/- 3.6, respectively, when compared to the thermal oxides (sigma(max) = 0.89 +/- 0.07 GPa and m = 12.1 +/- 0.5 for 507-nm-thick 950 degrees C layers). A marginal decrease of sigma(max) with thickness is observed for SiO2, with no significant differences between the films grown at 950 degrees C and 1050 degrees C. Weibull moduli of oxide thin films are found to lie between 4.5 +/- 1.2 and 19.8 +/- 4.2, depending on the oxidation temperature and film thickness.

Bulge testing and fracture properties of plasma-enhanced chemical vapor deposited silicon nitride thin films

The mechanical properties and fracture behavior of silicon nitride (SiNx) thin film fabricated by plasma-enhanced chemical vapor deposition is reported. Plane-strain moduli, prestresses, and fracture strengths of silicon nitride thin film; deposited both oil a bare Si substrate and oil a thermally oxidized Si substrate were extracted using bulge testing combined with a refined load-deflection model of long rectangular membranes. The plane-strain modu i and prestresses of SiNx thin films have little dependence on the substrates, that is, for the bare Si substrate, they are 133 +/- 19 GPa and 178 +/- 22 MPa, respectively, while for the thermally oxidized substrate, they are 140 +/- 26 Gila and 194 +/- 34 MPa, respectively. However, the fracture strength values of SiNx films grown on the two substrates are quite different, i.e., 1.53 +/- 0.33 Gila and 3.08 +/- 0.79 GPa for the bare Si substrate a A the oxidized Si substrate, respectively. The reference stresses were computed by integrating the local stress of the membrane at the fracture over the edge, Surface, and volume of the specimens and fitted with the Weibull distribution function. For SiNx thin film produced oil the bare Si Substrate, the Volume integration gave a significantly better agreement between data and model, implying that the volume flaws re the dominant fracture origin. For SiNx thin film grown on the oxidized Si substrate, the fit quality of surface and edge integration was significantly better than the Volume integration, and the dominant surface and edge flaws could be caused by buffered HF attacking the SiNx layer during SiO2 removal. Crown Copyright (C) 2008 Published by Elsevier B.V. All rights reserved.

Fracture properties of PECVD silicon nitride thin films by long rectangular memrane bulge test

Bulge test combined with a refined load-deflection model for long rectangular membrane was applied to determine the mechanical and fracture properties of PECVD silicon nitride (SiNx) thin films. Plane-strain modulus E-ps prestress s(0), and fracture strength s(max) of SiNx thin films deposited both on bare Si substrate and on SiO2-topped Si substrate were extracted. The SiNx thin films on different substrates possess similar values of E-ps and s(0) but quite different values of s(max). The statistical analysis of fracture strengths were performed by Weibull distribution function and the fracture origins were further predicted.