Nano-polypyrrole supercapacitor arrays prepared by layer-by-layer assembling method in anodic aluminum oxide templates

A novel method for preparing nano-supercapacitor arrays, in which each nano-supercapacitor consisted of electropolymerized Polypyrrole (PPy) electrode / porous TiO2 separator / chemical polymerized PPy electrode, was developed in this paper. The nano-supercapacitors were fabricated in the nano array pores of anodic aluminum oxide template using the bottom-up, layer-by-layer synthetic method. The nano-supercapacitor diameter was 80 nm, and length 500 nm. Based on the charge/discharge behavior of nano-supercapacitor arrays, it was found that the PPy/TiO2/PPy array supercapacitor devices performed typical electrochemical supercapacitor behavior. The method introduced here may find application in manufacturing nano-sized electrochemical power storage devices in the future for their use in the area of microelectronic devices and microelectromechanical systems.

TiO2/ZnO core/shell nano-heterostructure arrays as photo-electrodes with enhanced visible light photoelectrochemical performance

The present article reports a facile method for preparing the vertically-aligned 1D arrays of a new type of type II n-n TiO2/ZnO core/shell nano-heterostructures by growing the nano-shell of ZnO on the electrochemically fabricated TiO2 nanotubes core for visible light driven photoelectrochemical applications. The strong interfacial interaction at the type II heterojunction leads to an effective interfacial charge separation and charge transport. The presence of various defects such as surface states, interface states and other defects in the nano-heterostructure enable it for improved visible light photoelectrochemical performance. The presence of such defects has also been confirmed by the UV-vis absorption, cathodoluminescence, and crystallographic studies. The TiO2/ZnO core/shell nano-heterostructures exhibit strong green luminescence due to the defect transitions. The TiO2/ZnO core/shell nano-heterostructures photo-electrode show significant enhancement of visible light absorption and it provides a photocurrent density of 0.7 mA cm(-2) at 1 V vs. Ag/AgCl, which is almost 2.7 times that of the TiO2/ZnO core/shell nano-heterostructures under dark conditions. The electrochemical impedance spectroscopy results demonstrate that the substantially improved photoelectrochemical and photo-switching performance of the nano-heterostructures photo-anode is because of the enhancement of interfacial charge transfer and the increase in the charge carrier density caused by the incorporation of the ZnO nano-shell on TiO2 nanotube core.

Friction properties of bio-mimetic nano-fibrillar arrays

Nano-fibrillar arrays are fabricated using polystyrene materials. The average diameter of each fiber is about 300 nm. Experiments show that such a fibrillar surface possesses a relatively hydrophobic feature with a water contact angle of 142 degrees. Nanoscale friction properties are mainly focused on. It is found that the friction force of polystyrene nano-fibrillar surfaces is obviously enhanced in contrast to polystyrene smooth surfaces. The apparent coefficient of friction increases with the applied load, but is independent of the scanning speed. An interesting observation is that the friction force increases almost linearly with the real contact area, which abides by the fundamental Bowden-Tabor law of nano-scale friction.

High-density metallic nano-emitter arrays and their field emission characteristics

We report the fabrication and field emission properties of high-density nano-emitter arrays with on-chip electron extraction gate electrodes and up to 106 metallic nanotips that have an apex curvature radius of a few nanometers and a the tip density exceeding 108 cm−2. The gate electrode was fabricated on top of the nano-emitter arrays using a self-aligned polymer mask method. By applying a hot-press step for the polymer planarization, gate–nanotip alignment precision below 10 nm was achieved. Fabricated devices exhibited stable field electron emission with a current density of 0.1 A cm−2, indicating that these are promising for applications that require a miniature high-brightness electron source.

Characteristics of polypyrrole (PPy) nano-tubules made by templated ac electropolymerization

Electrochemical alternating current (ac) method designed for the synthesis of polypyrrole (PPy) nano-tubule arrays is the topic of this paper. Two-step anodic aluminum oxide (AAO) membrane is used as a template. The morphology of PPy nano-tubules is observed by SEM and discussed. FTIR spectra exhibit that the peaks of PPy nano-tubules shift compared to conventional PPy film. (c) 2005 Elsevier Ltd. All rights reserved.

Blue-shift photoluminescence from porous InAlAs

A porous InAlAs structure was first obtained by electrochemical etching. Nano-pore arrays were formed when the In0.52Al0.48As membrane was anodized at constant voltages in an HF aqueous solution. These self-assembled structures showed evident blue-shift photoluminescence emissions. While a quantum size effect alone underestimates the blue-shift energy for a sample with a relatively large average pore wall thickness, a novel effect caused by the asymmetric etching is proposed to account for this phenomenon. The results inferred from the x-ray double crystal diffraction are in good agreement with the experimental data.

A quantification of the interaction and spatial ordering in nano-arrays

This paper reports on the use of a local order measure to quantify the spatial ordering of a quantum dot array (QDA). By means of electron ground state energy analysis in a quantum dot pair, it is demonstrated that the length scale required for such a measure to characterize the opto-electronic properties of a QDA is of the order of a few QD radii. Therefore, as local order is the primary factor that affects the opto-electronic properties of an array of quantum dots of homogeneous size, this order was quantified through using the standard deviation of the nearest neighbor distances of the quantum dot ensemble. The local order measure is successfully applied to quantify spatial order in a range of experimentally synthesized and numerically generated arrays of nanoparticles. This measure is not limited to QDAs and has wide ranging applications in characterizing order in dense arrays of nanostructures.

Numerical simulation of self-organized nano-islands in plasma-based assembly of quantum dot arrays

This work presents the details of the numerical model used in simulation of self-organization of nano-islands on solid surfaces in plasma-assisted assembly of quantum dot structures. The model includes the near-substrate non-neutral layer (plasma sheath) and a nanostructured solid deposition surface and accounts for the incoming flux of and energy of ions from the plasma, surface temperature-controlled adatom migration about the surface, adatom collisions with other adatoms and nano-islands, adatom inflow to the growing nano-islands from the plasma and from the two-dimensional vapour on the surface, and particle evaporation to the ambient space and the two-dimensional vapour. The differences in surface concentrations of adatoms in different areas within the quantum dot pattern significantly affect the self-organization of the nano-islands. The model allows one to formulate the conditions when certain islands grow, and certain ones shrink or even dissolve and relate them to the process control parameters. Surface coverage by selforganized quantum dots obtained from numerical simulation appears to be in reasonable agreement with the available experimental results.

Synthesis and characterization of nano-MnO2 for electrochemical supercapacitor studies

Nanostructured MnO2 was synthesized at ambient condition by reduction of potassium permanganate with aniline. Powder X-ray diffraction, thermal analysis (thermogravimetric and differential thermal analysis), Brunauer-Emmett-Teller surface area, and infrared spectroscopy studies were carried out for physical and chemical characterization. The as-prepared MnO2 was amorphous and contained particles of 5-10 nm diameter. Upon annealing at temperatures >400°C, the amorphous MnO2 attained crystalline α-phase with a concomitant change in morphology. A gradual conversion of nanoparticles to nanorods is evident from scanning electron microscopy and transmission electron microscopy (TEM) studies. High-resolution TEM images suggested that nanoparticles and nanorods grow in different crystallographic planes. Capacitance behavior was studied by cyclic voltammetry and galvanostatic charge-discharge cycling in a potential range from -0.2 to 1.0 V vs SCE in 0.1 M sodium sulfate solution. Specific capacitance of about 250 F g-1 was obtained at a current density of 0.5 mA cm-2(0.8 A g-1).

Photoluminescence decay rate engineering of CdSe quantum dots in ensemble arrays embedded with gold nano-antennae

We discuss experimental results on the ability to significantly tune the photoluminescence decay rates of CdSe quantum dots embedded in an ordered template, using lightly doped small gold nanoparticles (nano-antennae), of relatively low optical efficiency. We observe both enhancement and quenching of photoluminescence intensity of the quantum dots varying monotonically with increasing volume fraction of added gold nanoparticles, with respect to undoped quantum dot arrays. However, the corresponding variation in lifetime of photoluminescence spectra decay shows a hitherto unobserved, non-monotonic variation with gold nanoparticle doping. We also demonstrate that Purcell effect is quite effective for the larger (5 nm) gold nano-antenna leading to more than four times enhanced radiative rate at spectral resonance, for largest doping and about 1.75 times enhancement for off-resonance. Significantly for spectral off-resonance samples, we could simultaneously engineer reduction of non-radiative decay rate along with increase of radiative decay rate. Non-radiative decay dominates the system for the smaller (2 nm) gold nano-antenna setting the limit on how small these plasmonic nano-antennae could be to be effective in engineering significant enhancement in radiative decay rate and, hence, the overall quantum efficiency of quantum dot based hybrid photonic assemblies.

MEMS-based Tunable Optical Filter Arrays for Nano-Spectrometer in the Visible Spectral Range

Optische Spektrometer sind bekannte Instrumente für viele Anwendungen in Life Sciences, Produktion und Technik aufgrund ihrer guten Selektivität und Sensitivität zusammen mit ihren berührungslosen Messverfahren. MEMS (engl. Micro-electro-mechanical system)-basierten Spektrometer werden als disruptive Technologie betrachtet, in der miniaturisierte Fabry-Pérot Filter als sehr attraktiv für die optische Kommunikation und 'Smart Personal Environments', einschließlich des medizinischen Anwendungen, zu nennen sind. Das Ziel dieser Arbeit ist, durchstimmbare Filter-Arrays mit kostengünstigen Technologien herzustellen. Materialien und technologische Prozesse, die für die Herstellung der Filter-Arrays benötigt werden, wurden untersucht. Im Rahmen dieser Arbeit, wurden durchstimmbare Fabry Pérot Filter-Arrays für den sichtbaren Spektralbereich untersucht, die als Nano-Spektrometer eingesetzt werden. Darüber hinaus wurde ein Modell der numerischen Simulation vorgestellt, die zur Ermittlung eines optimales geometrisches Designs verwendet wurde, wobei sich das Hauptaugenmerk der Untersuchung auf die Durchbiegung der Filtermembranen aufgrund der mechanischen Verspannung der Schichten richtet. Die geometrische Form und Größe der Filtermembranen zusammen mit der Verbindungsbrücken sind von entscheidender Bedeutung, da sie die Durchbiegung beeinflussen. Lange und schmale Verbindungsbrücken führen zur stärkeren Durchbiegung der Filtermembranen. Dieser Effekt wurde auch bei der Vergrößerung der Durchmesser der Membran beobachtet. Die Filter mit spiralige (engl. curl-bent) Verbindungsbrücken führten zu geringerer Deformation als die mit geraden oder gebogenen Verbindungsbrücken. Durchstimmbare Si3N4/SiO2 DBR-basierende Filter-Arrays wurden erfolgreich hergestellt. Eine Untersuchung über die UV-NIL Polymere, die als Opferschicht und Haltepfosten-Material der Filter verwendet wurden, wurde durchgeführt. Die Polymere sind kompatibel zu dem PECVD-Verfahren, das für die Spiegel-Herstellung verwendet wird. Die laterale Strukturierung der DBR-Spiegel mittels des RIE (engl. Reactive Ion Etching)-Prozesses sowie der Unterätz-Prozess im Sauerstoffplasma zur Entfernung der Opferschicht und zum Erreichen der Luftspalt-Kavität, wurden durchgeführt. Durchstimmbare Filter-Arrays zeigten einen Abstimmbereich von 70 nm bei angelegten Spannungen von weniger als 20 V. Optimierungen bei der Strukturierung von TiO2/SiO2 DBR-basierenden Filtern konnte erzielt werden. Mit der CCP (engl. Capacitively Coupling Plasma)-RIE, wurde eine Ätzrate von 20 nm/min erreicht, wobei Fotolack als Ätzmaske diente. Mit der ICP (engl. Inductively Coupling Plasma)-RIE, wurden die Ätzrate von mehr als 60 nm/min mit einem Verhältniss der Ar/SF6 Gasflüssen von 10/10 sccm und Fotolack als Ätzmasken erzielt. Eine Ätzrate von 80 bis 90 nm/min wurde erreicht, hier diente ITO als Ätzmaske. Ausgezeichnete geätzte Profile wurden durch den Ätzprozess unter Verwendung von 500 W ICP/300 W RF-Leistung und Ar/SF6 Gasflüsse von 20/10 sccm erreicht. Die Ergebnisse dieser Arbeit ermöglichen die Realisierung eines breiten Spektralbereichs der Filter-Arrays im Nano-Spektrometer.

Structure-controlled, vertical graphene-based, binder-free electrodes from plasma-reformed butter enhance supercapacitor performance

Vertical graphene nanosheets (VGNS) hold great promise for high-performance supercapacitors owing to their excellent electrical transport property, large surface area and in particular, an inherent three-dimensional, open network structure. However, it remains challenging to materialise the VGNS-based supercapacitors due to their poor specific capacitance, high temperature processing, poor binding to electrode support materials, uncontrollable microstructure, and non-cost effective way of fabrication. Here we use a single-step, fast, scalable, and environmentally-benign plasma-enabled method to fabricate VGNS using cheap and spreadable natural fatty precursor butter, and demonstrate the controllability over the degree of graphitization and the density of VGNS edge planes. Our VGNS employed as binder-free supercapacitor electrodes exhibit high specific capacitance up to 230 F g−1 at a scan rate of 10 mV s−1 and >99% capacitance retention after 1,500 charge-discharge cycles at a high current density, when the optimum combination of graphitic structure and edge plane effects is utilised. The energy storage performance can be further enhanced by forming stable hybrid MnO2/VGNS nano-architectures which synergistically combine the advantages from both VGNS and MnO2. This deterministic and plasma-unique way of fabricating VGNS may open a new avenue for producing functional nanomaterials for advanced energy storage devices.

Low-temperature assembly of ordered carbon nanotip arrays in low-frequency, high-density inductively coupled plasmas

High-density inductively coupled plasma (ICP)-assisted self-assembly of the ordered arrays of various carbon nanostructures (NS) for the electron field emission applications is reported. Carbon-based nano-particles, nanotips, and pyramid-like structures, with the controllable shape, ordering, and areal density are grown under remarkably low process temperatures (260-350 °C) and pressures (below 0.1 Torr), on the same Ni-based catalyst layers, in a DC bias-controlled floating temperature regime. A high degree of positional and directional ordering, elevated sp2 content, and a well-structured graphitic morphology are achieved without the use of pre-patterned or externally heated substrates.